Fracture Load of CAD/CAM Feldspathic Crowns Influenced by Abutment Material.

ABSTRACT: In vitro studies investigating the mechanical properties of dental reconstructions use various materials to replicate prepared teeth. However, no uniform recommendation exists as to which material is most suitable for standardized testing. The purpose of this study was to identify a material that resembles human dentin in fracture load tests. Sixteen human teeth were scanned with an intraoral scanner to obtain copies of the original crown morphology and were then prepared for crowns. Replica dies of the prepared teeth including the root morphology were fabricated with a Computer-aided design and computer-aided manufacturing (CAD/CAM) system and divided into four groups: (A) reinforced composite (RC); (B) human dentin (HD); (C) polymethyl methacrylate (PM); and (D) hybrid ceramic (HC). Sixty-four feldspar ceramic crowns were designed with the biocopy mode, fabricated with a CAD/CAM system, luted on the dies, and then with the roots embedded in polymethyl methacrylate. Care was taken to position all specimens of the same morphology identically. Thermo-mechanical load cycling was performed in a chewing simulator followed by fractural loading of the crowns. A mixed effect linear model was fitted to the data, and pairwise contrasts were estimated on the marginal means and corrected for multiple testing according to Tukey (? = 0.05). The means for fracture load (N) were 2435 N (95% CI (2162, 2709)) for hybrid ceramic, 1838 N (95% CI (1565, 2112)) for reinforced composite, 1670 N (95% CI (1396, 1943)) for human tooth and 1142 N (95% CI (868, 1415)) for polymethyl methacrylate abutment materials. Post-hoc pairwise contrasts revealed a statistically significant (p < 0.05) difference among all groups except for reinforced composite and human dentin (p = 0.76). The results indicate that the mechanical properties of abutment dies play a significant role for a possible substitution of natural teeth in in vitro studies.

SUBMITTER: Bencun M

PROVIDER: S-EPMC7435702 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Fracture Load of CAD/CAM Feldspathic Crowns Influenced by Abutment Material.

Bencun Mladen M Ender Andreas A Wiedemeier Daniel B DB Mehl Albert A

Materials (Basel, Switzerland) 20200802 15

In vitro studies investigating the mechanical properties of dental reconstructions use various materials to replicate prepared teeth. However, no uniform recommendation exists as to which material is most suitable for standardized testing. The purpose of this study was to identify a material that resembles human dentin in fracture load tests. Sixteen human teeth were scanned with an intraoral scanner to obtain copies of the original crown morphology and were then prepared for crowns. Replica die ...[more]

PMID: 32748827

Similar Datasets

Project description:ObjectivesTo evaluate and compare fracture resistance, translucency, and color reproducibility, as well as the effect of aging on the fracture load and color stability of novel monolithic CAD/CAM ceramics.Materials and methodsOne hundred crowns of uniform thickness were milled from five ceramic blocks (n = 20): partially crystallized lithium disilicate (PLD) and fully crystallized lithium disilicate (FLD), lithium metasilicate (LMS), 4Y-TZP (SMZ), and 5Y-TZP (UMZ) monolithic zirconia. PLD crowns were glazed, LMS was fired, and FLD was polished. SMZ and UMZ crowns were sintered and polished. Crowns were adhesively cemented to epoxy dies. Half of the crowns (n = 10) were subjected to 1.200.000 load cycles with thermal cycling. Color space values L, a, b defined by the Commission Internationale de l´Eclairage (CIELAB) were measured before and after aging, and (∆E) was calculated. Both aged and non-aged specimens were loaded until fracture in a universal testing machine and the fracture load was recorded. X-ray diffraction (XRD) and scanning electron microscope (SEM) fractographic analysis were carried out on fractured fragments of representative samples. For translucency and color reproducibility, 50 rectangular-shaped specimens were fabricated and processed as described previously. Color values were measured over black and white backgrounds, and the translucency parameter (TP) was computed. Using the shade verification mode, (∆E) to shade A3 was calculated. Data were statistically analyzed using one-way and two-way ANOVA, and t-test.ResultsAging did not affect fracture resistance significantly (p > 0.05). The highest mean fracture load was obtained for the SMZ and UMZ. A significant color change was observed after aging in all groups. The highest TP was noted for FLD. SMZ and UMZ had the best shade match.ConclusionsZirconia showed higher fracture resistance and color stability than lithium silicate ceramics. Lithium silicate ceramics were more translucent. The experimental FLD demonstrated high translucency.Clinical relevanceTested ceramics showed sufficient stability to withstand masticatory forces. Characterization of final restorations might be mandatory for better color match.

Dataset Information

Fracture Load of CAD/CAM Feldspathic Crowns Influenced by Abutment Material.

Publications

Fracture Load of CAD/CAM Feldspathic Crowns Influenced by Abutment Material.