Evaluation of the corrosion resistance of a Ni-P coating deposited on additive manufacturing steel: A dataset

ABSTRACT: This article presents the data set obtained for the research work entitled “Effect of a Ni-P coating on the corrosion resistance of an additive manufacturing carbon steel immersed in a 0.1 M NaCl solution” [1]. Microstructural, mechanical, and electrochemical characterization (using the electrochemical impedance and electrochemical noise spectroscopy technique) is performed on a material obtained by additive manufacturing and the influence of a Ni-P coating on it. The layer sizes and hardness of the substrate are measured, as well as the thickness of the coating and its hardness, values for corrosion resistance, resistance to electrochemical noise and location indices are calculated. The data show an adequate deposition rate for the type of coating, as well as the increase in corrosion resistance when the coating is applied to the steel by additive manufacturing.

SUBMITTER: Agredo Diaz D

PROVIDER: S-EPMC7452479 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Preparation and corrosion resistance of superhydrophobic Ni-Co-Al<sub>2</sub>O<sub>3</sub> coating on X100 steel.

Project description:X100 steel is easy to be corroded because of the high salt content in alkaline soils. The Ni-Co coating can slow down the corrosion but still cannot meet the requirements of modern demands. Based on this, in this study, on the basis of adding Al2O3 particles to the Ni-Co coating to strengthen its corrosion resistance, combined with superhydrophobic technology to inhibit corrosion, a micro/nano layered Ni-Co-Al2O3 coating with a new combination of cells and papillae was electrodeposited on X100 pipeline steel, and superhydrophobicity was integrated into it using a low surface energy modification method to improve wettability and corrosion resistance. SEM, XRD, XPS, FTIR spectroscopy, contact angle, and an electrochemical workstation were used to investigate the superhydrophobic materials' microscopic morphology, structure, chemical composition, wettability, and corrosion resistance. The co-deposition behavior of nano Al2O3 particles can be described by two adsorption steps. When 15 g L-1 nano Al2O3 particles were added, the coating surface became homogeneous, with an increase in papilla-like protrusions and obvious grain refinement. It had a surface roughness of 114 nm, a CA of 157.9° ± 0.6°, and -CH2 and -COOH on its surface. The corrosion inhibition efficiency of the Ni-Co-Al2O3 coating reached 98.57% in a simulated alkaline soil solution, and the corrosion resistance was significantly improved. Furthermore, the coating had extremely low surface adhesion, great self-cleaning ability, and outstanding wear resistance, which was expected to expand its application in the field of metal anticorrosion.

| S-EPMC9972356 | biostudies-literature

Improving Corrosion Protection and Friction Resistance of Q235 Steel by Combining Noncovalent Action and Rotating Coating Method.

Project description:Developing waterborne epoxy (WEP) coatings with excellent corrosion resistance and tribological properties is a key aspect to solve the damage of Q235 steel. In this work, perylene bisimide (PBI) derivatives dispersion graphene (GR) were prepared by a π-π stacking, the highly orientated PBI0.5%/GR0.5%/WEP coating will be prepared by the rotating coating method. Especially, the impedance value reached about 109 Ω·cm2 when the PBI and GR ratio is 1:1. The impedance value of PBI0.5%/GR0.5%/WEP coating increased by 3 orders of magnitude compared with that of pure WEP coating (106 Ω·cm2). Additionally, the coefficient of friction of the coatings was 0.33; compared with that of WEP, the coefficient of friction decreased by 48%, and the wear resistance increased by 87.6%. The results show that the PBI0.5%/GR0.5%/WEP coatings exhibited excellent corrosion resistance and wear resistance properties due to the good dispersion and high orientation of PBI/GR in WEP. It is anticipated that our current work would guide the ongoing efforts to develop a more efficient method to overcome the poor dispersion of GR in waterborne epoxy resin and provide a green coating with excellent corrosion resistance and wear resistance properties.

| S-EPMC7992059 | biostudies-literature

Corrosion Resistance of a Sand Particle-Modified Enamel Coating Applied to Smooth Steel Bars.

Project description:The protective performance of a sand particle-modified enamel coating on reinforcing steel bars was evaluated in 3.5 wt% NaCl solution by electrochemical impedance spectroscopy (EIS). Seven percentages of sand particles by weight were investigated: 0%, 5%, 10%, 20%, 30%, 50% and 70%. The phase composition of the enamel coating and sand particles were determined with the X-ray diffraction (XRD) technique. The surface and cross-sectional morphologies of the sand particle-modified enamel coating were characterized using scanning electron microscopy (SEM). XRD tests revealed three phases of sand particles: SiO₂, CaCO₃ and MgCO₃. SEM images demonstrated that the enamel coating wetted well with the sand particles. However, a weak enamel coating zone was formed around the sand particles due to concentrated air bubbles, leading to micro-cracks as hydrogen gas pressure builds up and exceeds the tensile strength of the weak zone. As a result, the addition of sand particles into the enamel coating reduced both the coating and corrosion resistances.

| S-EPMC5456157 | biostudies-other

Micro-Texture Analyses of a Cold-Work Tool Steel for Additive Manufacturing.

Project description:Small objects of an alloy tool steel were built by selective laser melting at different scan speeds, and their microstructures were analyzed using electron backscatter diffraction (EBSD). To present an explicit correlation with the local thermal cycles in the objects, prior austenite grains were reconstructed using the EBSD mapping data. Extensive growth of austenitic grains after solidification could be detected by the disagreement between the networks of carbides and austenite grain boundaries. A rapid laser scan at 2000 mm/s led to less growth, but retained a larger amount of austenite than a slow one at 50 mm/s. The rapid scan also exhibited definite evolution of Goss-type textures in austenite, which could be attributed to the growth of austenitic grains under a steep temperature gradient. The local variations in the microstructures and the textures enabled us to speculate the locally different thermal cycles determined by the different process conditions, that is, scan speeds.

| S-EPMC7040591 | biostudies-literature

Improvement of AZ91 Alloy Corrosion Properties by Duplex NI-P Coating Deposition.

Project description:The corrosion behavior of duplex Ni-P coatings deposited on AZ91 magnesium alloy was studied. The electroless deposition process of duplex Ni-P coating consisted in the preparation of low-phosphorus Ni-P coating (5.7 wt.% of P), which served as a bond coating and high-phosphorus Ni-P coating (11.5 wt.% of P) deposited on it. The duplex Ni-P coatings with the thickness of 25, 50, 75 and 100 µm were deposited on AZ91 magnesium alloy. The electrochemical corrosion behavior of coated AZ91 magnesium alloy was investigated by electrochemical impedance spectroscopy and potentiodynamic polarization method in 0.1 M NaCl. Obtained results showed a significant improvement in the corrosion resistance of coated specimens when compared to uncoated AZ91 magnesium alloy. From the results of the immersion tests in 3.5 wt.% NaCl, 10% solution of HCl and NaOH and 5% neutral salt spray, a noticeable increase in the corrosion resistance with the increasing thickness of the Ni-P coating was observed.

| S-EPMC7142442 | biostudies-literature

Graphene-Reinforced Zn-Ni Alloy Composite Coating on Iron Substrates by Pulsed Reverse Electrodeposition and Its High Corrosion Resistance.

Project description:In this paper, a novel kind of graphene (Gr)-reinforced Zn-Ni alloy composite coating is successfully prepared on an iron substrate by pulsed reverse electrodeposition. Hydrophilic graphene oxide (GO) is directly added to the electrolyte and reduced to Gr during coating. The experimental results reveal that (1) there is an optimal adding amount (about 0.4 g/L) of GO in the electrolyte for achieving the highest mechanical properties and corrosion resistance; (2) the composite coating shows grain refinement and a dense microstructure due to heterogeneous nucleation sites provided from the Gr sheets during electrodeposition; and (3) compared to the regular Zn-Ni coating, the composite coating exhibits many enhancements, including hardness increase by 2.3 times, elastic modulus increase by 39%, and corrosion rate decrease from 37.66 to 1.30 mils/annum. This process has advantages such as being simple, effective, well repeatable, economical, and supporting large-scale production and is expected to be widely applied in electronics, automobiles, marine engineering, and military industries.

| S-EPMC8173559 | biostudies-literature

Corrosion Resistance of Heat-Treated Ni-W Alloy Coatings.

Project description:The paper presents research on evaluation of corrosion resistance of Ni-W alloy coatings subjected to heat treatment. The corrosion resistance was tested in 5% NaCl solution by the use of potentiodynamic polarization technique and electrochemical impedance spectroscopy. Characteristics of the Ni-W coatings after heat treatment were carried out using scanning electron microscopy, scanning Kelvin probe technique and X-ray diffraction. Suggested reasons for the improvement of properties of the heat treated Ni-W coating, obtained at the lowest current density value (125 mA?cm-2), are the highest tungsten content (c.a. 25 at.%) as well as the smallest and the most homogeneous electrochemically active surface area.

| S-EPMC7085042 | biostudies-literature

Crack resistance of a noble green hydrophobic antimicrobial sealing coating film against environmental corrosion applied on the steel-cement interface for power insulators.

Project description:Due to their great load-bearing capabilities, steel-cement interface structures are commonly employed in construction projects, and power utilities including electric insulators. The service life of the steel-cement interface is always decreasing owing to fracture propagation in the cement helped by steel corrosion. In this paper, a noble crack-resistant solution for steel-cement interfaces utilized in hostile outdoor environments is proposed. A Ce-rich, homogeneous, and thick hydrophobic sealing coating (HSC) is developed on the steel-cement interface after 60 minutes of immersion in a 60 000 ppm CeCl3·7H2O sealing coating solution. The specimens treated with optimized HSC film demonstrate fissure filling, lowest corrosion current (I corr) 2.3 × 10-7 A cm-2, maximum hardness (109 Hv), oxide-jacking resistance (40 years), hydrophobic characteristics, carbonation resistance, and bacterial corrosion resistance, resulting in a crack-free steel-cement interface. This work will pave the way for a new branch of environmentally acceptable coatings for the construction and power industries.

| S-EPMC8968190 | biostudies-literature

Oxidation Resistance and Microstructure Evaluation of a Polymer Derived Ceramic (PDC) Composite Coating Applied onto Sintered Steel.

Project description:Powder metallurgy is a competitive technology to produce ferrous near net shape parts for diverse engineering applications. However, their inherent porosity increases the susceptibility to oxidation and sealing their surface is mandatory to avoid premature degradation. Alongside, polymer derived ceramics (PDCs), such as silicon-carbonitride, have drawn attention concerning their high temperature and chemical stability. However, PDCs undergo volume shrinkage during ceramization that leads to defect formation. The shrinkage can be compensated by the addition of fillers, which are also capable of tailoring the ceramic resulting properties. This work evaluates the processing of PDC-based coatings loaded with ZrO? and glass fillers to compensate for the shrinkage, densify the coating and seal the sintered steel surface. Therefore, polymeric slurries were sprayed onto sintered steel substrates, which were pyrolyzed at different temperatures for microstructural and oxidation resistance evaluation. Microstructural modifications caused by the enhanced glass viscous flow during pyrolysis at 800 °C resulted in more homogeneous, dense and protective coatings, which reduced the mass gain up to 40 wt% after 100 h of oxidation at 450 °C in air in comparison to the uncoated substrate. Moreover, no macrocracks or spallation were detected, confirming the feasibility of PDC composite barrier coatings for sintered steels.

| S-EPMC6470509 | biostudies-literature

Tribocorrosion Failure Mechanism of TiN/SiOx Duplex Coating Deposited on AISI304 Stainless Steel.

Project description:TiN/SiOx duplex coatings were synthesized on AISI304 stainless steel by plasma immersion ion implantation and deposition (PIIID) followed by radio frequency magnetron sputtering (RFMS). The microstructure and tribocorrosion failure behaviors of the duplex coatings were investigated by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, atomic force microscopy, reciprocating-sliding tribometer, and electrochemical tests. The as-deposited duplex coating had a two-layered columnar growth structure consisting of face-centered cubic TiN and amorphous SiOx. Sliding tests showed that the TiN interlayer had good adhesion with the substrate, but the SiOx layer suffered from severe delamination failure. Friction force induced a number of micro-cracks in the coating, which provided channels for the diffusion of NaCl solution. The tribocorrosion test showed that the duplex coating exhibited a lower wear-performance in NaCl solution than in ambient atmosphere. Multi-scale chloride ion corrosion occurred simultaneously and substantially degraded the bonding strength of the columnar crystals or neighboring layers. Force-corrosion synergy damage eventually led to multi-degradation failure of the duplex coating. The presented results provide a comprehensive understanding of the tribocorrosion failure mechanism in coatings with duplex architecture.

| S-EPMC5457005 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data