Monitoring of Anthracene Using Nanoscale Au-Cu Bimetallic Alloy Nanoparticles Synthesized with Various Compositions.

ABSTRACT: Bimetallic alloy Au-Cu nanoparticles (Au-Cu alloy NPs) were synthesized using a chemical reduction method for sensing applications. Electronic absorption spectroscopy (UV-visible spectroscopy), X-ray diffraction (XRD), and scanning electron microscopy (SEM) were used for the confirmation and morphological studies of the synthesized nanoparticles. The composition of Au-Cu alloy NPs was studied by energy-dispersive spectroscopy (EDS). The high crystallinity of Au-Cu alloy NPs was demonstrated by XRD analysis. Both XRD and SEM analyses revealed that the nanoparticles' size ranges from 15 to 25 nm. Pyrrole was polymerized into polypyrrole (PPy) over a neat and clean glassy carbon electrode (GCE) by potentiodynamic polymerization. The sensitivity of GCE was improved by modifying it into a composite electrode. The composite electrode was developed by coating GCE with an overoxidized PPy polymer followed by Au-Cu alloy NPs. The ratio of Au and Cu was carefully controlled. The composite electrode (PPyox/Au-Cu/GCE) successfully detected an environmental toxin anthracene with a detection limit of 0.15 ?M, as evidenced by cyclic voltammetry (CV), square-wave voltammetry (SWV), and electrochemical impedance spectroscopy (EIS).

SUBMITTER: Latif-Ur-Rahman

PROVIDER: S-EPMC7482251 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Monitoring of Anthracene Using Nanoscale Au-Cu Bimetallic Alloy Nanoparticles Synthesized with Various Compositions.

Latif-Ur-Rahman Shah Afzal A Han Changseok C Jan Abdul Khaliq AK

ACS omega 20200824 35

Bimetallic alloy Au-Cu nanoparticles (Au-Cu alloy NPs) were synthesized using a chemical reduction method for sensing applications. Electronic absorption spectroscopy (UV-visible spectroscopy), X-ray diffraction (XRD), and scanning electron microscopy (SEM) were used for the confirmation and morphological studies of the synthesized nanoparticles. The composition of Au-Cu alloy NPs was studied by energy-dispersive spectroscopy (EDS). The high crystallinity of Au-Cu alloy NPs was demonstrated by X ...[more]

PMID: 32923808

Similar Datasets

Project description:It is well-known that Ag-Au bimetallic nanoplates have attracted significant research interest due to their unique plasmonic properties and surface-enhanced Raman scattering (SERS). In recent years, there have been many studies on the fabrication of bimetallic nanostructures. However, controlling the shape, size, and structure of bimetallic nanostructures still has many challenges. In this work, we present the results of the synthesis of silver nanoplates (Ag NPls), and Ag-Au bimetallic core/shell and alloy nanostructures, using seed-mediated growth under green LED excitation and a gold salt (HAuCl4) as a precursor of gold. The results show that the optical properties and crystal structure strongly depend on the amount of added gold salt. Interestingly, when the amount of gold(x) in the sample was less than 0.6 μmol (x < 0.6 μmol), the structural nature of Ag-Au was core/shell, in contrast x > 0.6 μmol gave the alloy structure. The morphology of the obtained nanostructures was investigated using the field emission scanning electron microscopy (FESEM) technique. The UV-Vis extinction spectra of Ag-Au nanostructures showed localized surface plasmon resonance (LSPR) bands in the spectral range of 402-627 nm which changed from two peaks to one peak as the amount of gold increased. Ag-Au core/shell and alloy nanostructures were utilized as surface enhanced Raman scattering (SERS) substrates to detect methylene blue (MB) (10-7 M concentration). Our experimental observations indicated that the highest enhancement factor (EF) of about 1.2 × 107 was obtained with Ag-Au alloy. Our detailed investigations revealed that the Ag-Au alloy exhibited significant EF compared to pure metal Ag and Ag-Au core/shell nanostructures. Moreover, the analysis of the data revealed a linear dependence between the logarithm of concentration (log C) and the logarithm of SERS signal intensity (log I) in the range of 10-7-10-4 M with a correlation coefficient (R 2) of 0.994. This research helps us understand better the SERS mechanism and the application of Raman spectroscopy on a bimetallic surface.

Dataset Information

Monitoring of Anthracene Using Nanoscale Au-Cu Bimetallic Alloy Nanoparticles Synthesized with Various Compositions.

Publications

Monitoring of Anthracene Using Nanoscale Au-Cu Bimetallic Alloy Nanoparticles Synthesized with Various Compositions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets