Reaction Behavior of a Silicide Electrode with Lithium in an Ionic-Liquid Electrolyte.

ABSTRACT: Silicides are attractive novel active materials for use in the negative-electrodes of next-generation lithium-ion batteries that use certain ionic-liquid electrolytes; however, the reaction mechanism of the above combination is yet to be clarified. Possible reactions at the silicide electrode are as follows: deposition and dissolution of Li metal on the electrode, lithiation and delithiation of Si, which would result from the phase separation of the silicide, and alloying and dealloying of the silicide with Li. Herein, we examined these possibilities using various analysis methods. The results revealed that the lithiation and delithiation of silicide occurred.

SUBMITTER: Domi Y

PROVIDER: S-EPMC7482255 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Reaction Behavior of a Silicide Electrode with Lithium in an Ionic-Liquid Electrolyte.

Domi Yasuhiro Y Usui Hiroyuki H Sugimoto Kai K Gotoh Kazuma K Nishikawa Kei K Sakaguchi Hiroki H

ACS omega 20200826 35

Silicides are attractive novel active materials for use in the negative-electrodes of next-generation lithium-ion batteries that use certain ionic-liquid electrolytes; however, the reaction mechanism of the above combination is yet to be clarified. Possible reactions at the silicide electrode are as follows: deposition and dissolution of Li metal on the electrode, lithiation and delithiation of Si, which would result from the phase separation of the silicide, and alloying and dealloying of the s ...[more]

PMID: 32923823

Similar Datasets

Project description:With the development of mobile electronic devices, there are more and more requirements for high-energy storage equipment. Traditional lithium-ion batteries, like lithium-iron phosphate batteries, are limited by their theoretical specific capacities and might not meet the requirements for high energy density in the future. Lithium-sulfur batteries (LSBs) might be ideal next-generation energy storage devices because they have nearly 10 times the theoretical specific capacities of lithium-ion batteries. However, the severe capacity decay of LSBs limits their application, especially at high currents. In this study, an ionic liquid (IL) electrolyte additive, TDA+TFSI, was reported. When 5% of the TDA+TFSI additive was added to a traditional ether-based organic electrolyte, the cycling performance of the LSBs was significantly improved compared with that of the LSBs with the pure traditional organic electrolyte. At a rate of 0.5 C, the discharge specific capacity in the first cycle of the LSBs with the 5% TDA+TFSI electrolyte additive was 1167 mAh g-1; the residual specific capacities after 100 cycles and 300 cycles were 579 mAh g-1 and 523 mAh g-1, respectively; and the average capacity decay rate per cycle was only 0.18% in 300 cycles. Moreover, the electrolyte with the TDA+TFSI additive had more obvious advantages than the pure organic ether-based electrolyte at high charge and discharge currents of 1.0 C. The residual discharge specific capacities were 428 mAh g-1 after 100 cycles and 399 mAh g-1 after 250 cycles, which were 13% higher than those of the LSBs without the TDA+TFSI additive. At the same time, the Coulombic efficiencies of the LSBs using the TDA+TFSI electrolyte additive were more stable than those of the LSBs using the traditional organic ether-based electrolyte. The results showed that the LSBs with the TDA+TFSI electrolyte additive formed a denser and more uniform solid electrolyte interface (SEI) film during cycling, which improved the stability of the electrochemical reaction.

Dataset Information

Reaction Behavior of a Silicide Electrode with Lithium in an Ionic-Liquid Electrolyte.

Publications

Reaction Behavior of a Silicide Electrode with Lithium in an Ionic-Liquid Electrolyte.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets