Rietveld refinement of the langbeinite-type phosphate K2Ni0.5Hf1.5(PO4)3.

ABSTRACT: Polycrystalline potassium nickel(II) hafnium(IV) tris-(orthophosphate), a langbeinite-type phosphate, was synthesized by a solid-state method. The three-dimensional framework of the title compound is built up from two types of [MO6] octa-hedra [the M sites are occupied by Hf:Ni in ratios of 0.754?(8):0.246?(8) and 0.746?(8):0.254?(8), respectively] and [PO4] tetra-hedra are connected via O vertices. The K+ cations are located in two positions within large cavities of the framework, having coordination numbers of 9 and 12. The Hf, Ni and K sites lie on threefold rotation axes, while the P and O atoms are situated in general positions.

SUBMITTER: Zhou L

PROVIDER: S-EPMC7534254 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Rietveld refinement of the langbeinite-type phosphate K2Ni0.5Hf1.5(PO4)3.

Zhou Liang L Butenko Denys S DS Ogorodnyk Ivan V IV Klyui Nickolai I NI Zatovsky Igor V IV

Acta crystallographica. Section E, Crystallographic communications 20200911 Pt 10

Polycrystalline potassium nickel(II) hafnium(IV) tris-(orthophosphate), a langbeinite-type phosphate, was synthesized by a solid-state method. The three-dimensional framework of the title compound is built up from two types of [MO6] octa-hedra [the M sites are occupied by Hf:Ni in ratios of 0.754 (8):0.246 (8) and 0.746 (8):0.254 (8), respectively] and [PO4] tetra-hedra are connected via O vertices. The K+ cations are located in two positions ...[more]

PMID: 33117578

Similar Datasets

Rietveld refinement of langbeinite-type K(2)YHf(PO(4))(3).

Project description:Potassium yttrium hafnium tris-(orthophosphate) belongs to the langbeinite-family and is built up from [MO(6)] octa-hedra [in which the positions of the two independent M sites are mutually occupied by Y and Hf in a 0.605?(10):0.395?(10) ratio] and [PO(4)] tetra-hedra connected via vertices into a three-dimensional framework. This framework is penetrated by large closed cavities in which the two independent K atoms are located; one of the K atoms is nine-coordinated and the other is 12-coordinated by surrounding O atoms. The K, Y and Hf atoms lie on threefold rotation axes, whereas the P and O atoms are located in general positions.

| S-EPMC2977454 | biostudies-other

Rietveld refinement of the langbeinite-type mixed-metal phosphate K2Ni0.5Zr1.5(PO4)3.

Project description:Dipotassium [nickel(II) zirconium(IV)] tris-(orthophosphate) was prepared from a self-flux in the system K2O-P2O5-NiO-K2ZrF6. The title compound belongs to the langbeinite family and is built up from two [MO6] octa-hedra [M = Ni:Zr with mixed occupancy in ratios of 0.21?(4):0.79?(4) and 0.29?(4):0.71?(4), respectively] and [PO4] tetra-hedra inter-linked via vertices into a (3) ?[M 2(PO4)3] framework. Two independent K(+) cations are located in large cavities of the framework, with coordination numbers to O(2-) anions of nine and twelve. The K, Ni, and Zr sites are located on threefold rotation axes.

| S-EPMC4120588 | biostudies-literature

Al(0.5)Nb(1.5)(PO(4))(3).

Project description:Single crystals of the title compound, aluminium niobium triphosphate, Al(0.5)Nb(1.5)(PO(4))(3), have been synthesized by a high-temperature reaction in a platinium crucible. The Al(III) and Nb(V) atoms occupy the same site on the axis, with disorder in the ratio of 1:3. The fundamental building units of the title structure are isolated Al/NbO(6) octa-hedra and PO(4) tetra-hedra (. 2 symmetry), which are further inter-locked by corner-sharing O atoms, leading to a three-dimensional framework structure with infinite channels along the a axis.

| S-EPMC3051931 | biostudies-literature

A new langbeinite-type phosphate: K(2)AlSn(PO(4))(3).

Project description:Single crystals of the title compound, dipotassium aluminium tin(IV) tris-[phosphate(V)], K(2)AlSn(PO(4))(3), were synthesized by a high temperature reaction in a platinum crucible. In the structure, the Al(III) and Sn(IV) atoms occupy the same site on a threefold rotation axis with occupational disorder in a 1:1 ratio. In the three-dimensional structure, Al/SnO(6) octa-hedra and PO(4) tetra-hedra are inter-connected via their vertices, yielding a [Al/SnP(3)O(12)](n) framework. The K atoms (site symmetry 3) reside in the large cavities delimited by the [Al/SnP(3)O(12)](n) framework, and are surrounded by 12 O atoms.

| S-EPMC3201338 | biostudies-literature

Reducing interfacial resistance of a Li1.5Al0.5Ge1.5(PO4)3 solid electrolyte/electrode interface by polymer interlayer protection.

Project description:High interfacial resistance of an electrode/electrolyte interface is the most challenging barrier for the expanding application of all-solid-state lithium batteries (ASSLBs). To address this challenge, poly(propylene carbonate)-based solid polymer electrolytes (PPC-SPEs) were introduced as interlayers combined with a Li1.5Al0.5Ge1.5(PO4)3 (LAGP) solid state electrolyte (SSE), which successfully decreased the interfacial resistance of the SSE/electrolyte interface by suppressing the reduction reaction of Ge4+ against the Li metal, as well as producing intimate contact between the cathode and electrolyte. This work provides a systematic analysis of the interfacial resistance of the cathode/SSE, Li/SSE and the polymer/LAGP interfaces. As a consequence, the interfacial resistance of the Li/SSE interface decreased about 35%, and the interfacial resistance of the cathode/SSE interface decreased from 3.2 × 104 to 543 Ω cm2. With a PPC-LAGP-PPC sandwich structure composite electrolyte (PLSSCE), the all-solid-state LiFePO4/Li cell showed a high capacity of 148.1 mA h g-1 at 0.1C and a great cycle performance over 90 cycles.

| S-EPMC9050224 | biostudies-literature

Rietveld refinement of whitlockite-related K(0.8)Ca(9.8)Fe(0.2)(PO(4))(7).

Project description:The title compound, K(0.8)Ca(9.8)Fe(0.2)(PO(4))(7) (potassium deca-calcium iron hepta-phosphate), belongs to the whitlockite family. The structure is built up from several types of metal-oxygen polyhedra: two [CaO(8)], one [CaO(7)] and one [(Ca/Fe)O(6)] polyhedron with a mixed Ca/Fe occupancy in a 0.8:0.2 ratio, as well as three tetra-hedral [PO(4)] units. Of the 18 sites in the asymmetric unit, the site with the mixed Ca/Fe occupation, the K site, one P and one O site are on special positions 6a with 3 symmetry, whereas all other sites are on general positions 18b. The linkage of metal-oxygen polyhedra and [PO(4)] tetra-hedra via edges and corners results in formation of a three-dimensional framework with composition [Ca(9.8)Fe(0.2)(PO(4))(7)](0.8-). The remaining K atoms (site-occupation factor = 0.8) are located in large closed cavities and are nine-coordinated by oxygen.

| S-EPMC2979107 | biostudies-literature

Rietveld refinement of the crystal structures of Rb2 XSi5O12 (X = Ni, Mn).

Project description:The synthetic leucite silicate framework mineral analogues Rb2 XSi5O12 {X = Ni [dirubidium nickel(II) penta-silicate] and Mn [dirubidium manganese(II) penta-silicate]} have been prepared by high-temperature solid-state synthesis. The results of Rietveld refinements, using X-ray powder diffraction data collected using Cu Kα X-rays, show that the title compounds crystallize in the space group Pbca and adopt the cation-ordered structure of Cs2CdSi5O12 and other leucites. The structures consist of tetra-hedral SiO4 and XO4 units sharing corners to form a partially substituted silicate framework. Extraframework Rb(+) cations sit in channels in the framework. All atoms occupy the 8c general position for this space group. In these refined structures, silicon and X atoms are ordered onto separate tetra-hedrally coordinated sites (T-sites). However, the Ni displacement parameter and the Ni-O bond lengths suggest that for the X = Ni sample, there may actually be some T-site cation disorder.

| S-EPMC4770953 | biostudies-literature

Parametric Rietveld refinement.

Project description:In this paper the method of parametric Rietveld refinement is described, in which an ensemble of diffraction data collected as a function of time, temperature, pressure or any other variable are fitted to a single evolving structural model. Parametric refinement offers a number of potential benefits over independent or sequential analysis. It can lead to higher precision of refined parameters, offers the possibility of applying physically realistic models during data analysis, allows the refinement of 'non-crystallographic' quantities such as temperature or rate constants directly from diffraction data, and can help avoid false minima.

| S-EPMC2483475 | biostudies-literature

Synergistic Effect of Pt and Dual Ni/Co Cations in Hydrotalcite-Derived Pt/Ni1.5Co0.5AlO Catalysts for Promoting Soot Combustion.

Project description:In this article, the catalysts of hydrotalcite-derived Ni1.5Co0.5AlO nanosheet-supported highly dispersed Pt nanoparticles (Ptn/Ni1.5Co0.5AlO, where n% is the weigh percentage of the Pt element in the catalysts) were elaborately fabricated by the gas-bubble-assisted membrane--reduction method. The specific porous structure formed by the stack of hydrotalcite-derived Ni1.5Co0.5AlO nanosheets can increase the transfer mass efficiency of the reactants (O2, NO, and soot) and the strong Pt-Ni1.5Co0.5AlO interaction can weaken the Ni/Co-O bond for promoting the mobility of lattice oxygen and the formation of surface-oxygen vacancies. The Ptn/Ni1.5Co0.5AlO catalysts exhibited excellent catalytic activity and stability during diesel soot combustion under the loose contact mode between soot particles and catalysts. Among all the catalysts, the Pt2/Ni1.5Co0.5AlO catalyst showed the highest catalytic activities for soot combustion (T50 = 350 °C, TOF = 6.63 × 10-3 s-1). Based on the characterization results, the catalytic mechanism for soot combustion is proposed: the synergistic effect of Pt and dual Ni/Co cations in the Pt/Ni1.5Co0.5AlO catalysts can promote the vital step of catalyzing NO oxidation to NO2 in the NO-assisted soot oxidation mechanism. This insight into the synergistic effect of Pt and dual Ni/Co cations for soot combustion provides new strategies for reducing the amounts of noble metals in high-efficient catalysts.

| S-EPMC9965507 | biostudies-literature

Interface-engineered ferroelectricity of epitaxial Hf0.5Zr0.5O2 thin films.

Project description:Ferroelectric hafnia-based thin films have attracted intense attention due to their compatibility with complementary metal-oxide-semiconductor technology. However, the ferroelectric orthorhombic phase is thermodynamically metastable. Various efforts have been made to stabilize the ferroelectric orthorhombic phase of hafnia-based films such as controlling the growth kinetics and mechanical confinement. Here, we demonstrate a key interface engineering strategy to stabilize and enhance the ferroelectric orthorhombic phase of the Hf0.5Zr0.5O2 thin film by deliberately controlling the termination of the bottom La0.67Sr0.33MnO3 layer. We find that the Hf0.5Zr0.5O2 films on the MnO2-terminated La0.67Sr0.33MnO3 have more ferroelectric orthorhombic phase than those on the LaSrO-terminated La0.67Sr0.33MnO3, while with no wake-up effect. Even though the Hf0.5Zr0.5O2 thickness is as thin as 1.5 nm, the clear ferroelectric orthorhombic (111) orientation is observed on the MnO2 termination. Our transmission electron microscopy characterization and theoretical modelling reveal that reconstruction at the Hf0.5Zr0.5O2/ La0.67Sr0.33MnO3 interface and hole doping of the Hf0.5Zr0.5O2 layer resulting from the MnO2 interface termination are responsible for the stabilization of the metastable ferroelectric phase of Hf0.5Zr0.5O2. We anticipate that these results will inspire further studies of interface-engineered hafnia-based systems.

| S-EPMC10063548 | biostudies-literature