Effects of Lasers and Their Delivery Characteristics on Machined and Micro-Roughened Titanium Dental Implant Surfaces.

ABSTRACT: The aim of the study was to investigate the effects of neodymium: yttrium aluminium garnet (Nd:YAG) (1064 nm) and erbium: yttrium aluminium garnet (Er:YAG) (2940 nm) laser energy on titanium when delivered with conventional optics (focusing handpieces or plain ended optical fibres) or with a conical tip. Machined and micro-roughened implant discs were subjected to laser irradiation under a variety of energy settings either dry (without water) or wet (with water). Samples were scanned using a 3D non-contact laser profilometer and analysed for surface roughness, volume of peaks and the maximum diameter of the ablated area. Conical tip designs when used with both lasers showed no surface effect at any power setting on both machined and micro-roughened implant surfaces, regardless of the irrigation condition. When used with conventional delivery systems, laser effects on titanium were dose related, and were more profound with the Nd:YAG than with the Er:YAG laser. High laser pulse energies caused surface fusion which reduced the roughness of micro-roughened titanium surfaces. Likewise, repeated pulses and higher power densities also caused greater surface modifications. The presence of water reduced the influence of laser irradiation on titanium. It may be concluded that conical fibres can reduce unwanted surface modification, and this may be relevant to clinical protocols for debridement or disinfection of titanium dental implants.

SUBMITTER: Fenelon T

PROVIDER: S-EPMC7552764 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effects of Lasers and Their Delivery Characteristics on Machined and Micro-Roughened Titanium Dental Implant Surfaces.

Fenelon Thomas T Bakr Mahmoud M MM Walsh Laurence J LJ George Roy R

Bioengineering (Basel, Switzerland) 20200811 3

The aim of the study was to investigate the effects of neodymium: yttrium aluminium garnet (Nd:YAG) (1064 nm) and erbium: yttrium aluminium garnet (Er:YAG) (2940 nm) laser energy on titanium when delivered with conventional optics (focusing handpieces or plain ended optical fibres) or with a conical tip. Machined and micro-roughened implant discs were subjected to laser irradiation under a variety of energy settings either dry (without water) or wet (with water). Samples were scanned using a 3D ...[more]

PMID: 32796620

Similar Datasets

Project description:Animal studies and the scarce clinical trials available that have been conducted suggest that bioactive surfaces on dental implants could improve the osseointegration of such implants. The purpose of this systematic review was to compare the effectiveness of osseointegration of titanium (Ti) dental implants using bioactive surfaces with that of Ti implants using conventional surfaces such as sandblasted large-grit acid-etched (SLA) or similar surfaces. Applying the guidelines of the Preferred Reporting Items for Systematic Reviews and Meta-analyses (PRISMA) statement, the MEDLINE, PubMed Central and Web of Science databases were searched for scientific articles in April 2020. The keywords used were "dental implants", "bioactive surfaces", "biofunctionalized surfaces", and "osseointegration", according to the question: "Do bioactive dental implant surfaces have greater osseointegration capacity compared with conventional implant surfaces?" Risk of bias was assessed using the Cochrane Collaboration tool. 128 studies were identified, of which only 30 met the inclusion criteria: 3 clinical trials and 27 animal studies. The average STROBE (STrengthening the Reporting of OBservational studies in Epidemiology) and ARRIVE (Animal Research: Reporting of In Vivo Experiments) scores were 15.13 ± 2.08 and 17.7±1.4, respectively. Implant stability quotient (ISQ) was reported in 3 studies; removal torque test (RTT)-in 1 study; intraoral periapical X-ray and microcomputed tomography radiological evaluation (RE)-in 4 studies; shear force (SF)-in 1 study; bone-to-implant contact (BIC)-in 12 studies; and BIC and bone area (BA) jointly-in 5 studies. All animal studies reported better bone-to-implant contact surface for bioactive surfaces as compared to control implants with a statistical significance of p < 0.05. Regarding the bioactive surfaces investigated, the best results were yielded by the one where mechanical and chemical treatment methods of the Ti surfaces were combined. Hydroxyapatite (HA) and calcium-phosphate (Ca-Ph) were the most frequently used bioactive surfaces. According to the results of this systematic review, certain bioactive surfaces have a positive effect on osseointegration, although certain coating biomolecules seem to influence early peri-implant bone formation. Further and more in-depth research in this field is required to reduce the time needed for osseointegration of dental implants.

Project description:IntroductionMicro- or nano-topography can both provide antimicrobial properties and improve osseointegration of dental implant titanium surfaces. Laser treatment is one of the best surface microtexturing techniques. The aim of this study was to evaluate in vitro and in situ biofilm formation on a laser-treated titanium surface, comparing it with two conventional surfaces, machined and grit-blasted.MethodsFor the in vitro experiment, an oral microcosm biofilm model was developed on the surface of titanium disks and reference human enamel using a bioreactor for 48 h. For the in situ experiment, titanium implants with laser-treated, machined and grit-blasted surfaces were mounted on intraoral trays and worn by ten volunteers for 48 h. Biofilm formation was quantitatively evaluated, and surfaces were analyzed using confocal laser scanning microscopy, scanning electron microscopy and energy-dispersive X-ray spectroscopy.Results–in vitro studyBiofilm structures with a prevalence of viable cells covered most of the machined, grit-blasted and human enamel surfaces, whereas less dense biofilm structures with non-confluent microcolonies were observed on the laser-treated titanium. Laser-treated titanium showed the lowest biofilm formation, where microorganisms colonized the edges of the laser-created pits, with very few or no biofilm formation observed inside the pits.Results–in situ studyThe biofilm formation pattern observed was similar to that in the in vitro experiment. Confocal laser scanning microscopy showed complete coverage of the implant threads, with mostly viable cells in grit-blasted and machined specimens. Unexpectedly, laser-treated specimens showed few dead microbial cells colonizing the bottom of the threads, while an intense colonization was found on the threading sides.ConclusionThis data suggests that laser-created microtopography can reduce biofilm formation, with a maximum effect when the surface is blasted orthogonally by the laser beam. In this sense the orientation of the laser beam seems to be relevant for the biological interaction with biofilms.

Dataset Information

Effects of Lasers and Their Delivery Characteristics on Machined and Micro-Roughened Titanium Dental Implant Surfaces.

Publications

Effects of Lasers and Their Delivery Characteristics on Machined and Micro-Roughened Titanium Dental Implant Surfaces.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets