Superhydrophilic Polyurethane/Polydopamine Nanofibrous Materials Enhancing Cell Adhesion for Application in Tissue Engineering.

ABSTRACT: The use of nanofibrous materials in the field of tissue engineering requires a fast, efficient, scalable production method and excellent wettability of the obtained materials, leading to enhanced cell adhesion. We proposed the production method of superhydrophilic nanofibrous materials in a two-step process. The process is designed to increase the wettability of resulting scaffolds and to enhance the rate of fibroblast cell adhesion. Polyurethane (PU) nanofibrous material was produced in the solution blow spinning process. Then the PU fibers surface was modified by dopamine polymerization in water solution. Two variants of the modification were examined: dopamine polymerization under atmospheric oxygen (V-I) and using sodium periodate as an oxidative agent (V-II). Hydrophobic PU materials after the treatment became highly hydrophilic, regardless of the modification variant. This effect originates from polydopamine (PDA) coating properties and nanoscale surface structures. The modification improved the mechanical properties of the materials. Materials obtained in the V-II process exhibit superior properties over those from the V-I, and require shorter modification time (less than 30 min). Modifications significantly improved fibroblasts adhesion. The cells spread after 2 h on both PDA-modified PU nanofibrous materials, which was not observed for unmodified PU. Proposed technology could be beneficial in applications like scaffolds for tissue engineering.

SUBMITTER: Kopec K

PROVIDER: S-EPMC7555238 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Superhydrophilic Polyurethane/Polydopamine Nanofibrous Materials Enhancing Cell Adhesion for Application in Tissue Engineering.

Kopeć Kamil K Wojasiński Michał M Ciach Tomasz T

International journal of molecular sciences 20200916 18

The use of nanofibrous materials in the field of tissue engineering requires a fast, efficient, scalable production method and excellent wettability of the obtained materials, leading to enhanced cell adhesion. We proposed the production method of superhydrophilic nanofibrous materials in a two-step process. The process is designed to increase the wettability of resulting scaffolds and to enhance the rate of fibroblast cell adhesion. Polyurethane (PU) nanofibrous material was produced in the sol ...[more]

PMID: 32947971

Similar Datasets

Project description:Joints that connect thermoplastic polymer matrices (TPMs) and metals, which are obtained by comolding, are of growing importance in numerous applications. The overall performance of these constructs is strongly impacted by the TPM-metal interfacial strength, which can be tuned by tailoring the surface chemistry of the metal prior to the comolding process. In the present work, a model TPM-metal system consisting of poly(methyl methacrylate) (PMMA) and titanium is used to prepare comolded joints. The interfacial adhesion is quantified by wire pullout experiments. Pullout tests prior to and following surface modification are performed and analyzed. Unmodified wires show poor interfacial strength, with a work of adhesion (Ga) value of 3.8 J m-2. To enhance interfacial adhesion, a biomimetic polydopamine (PDA) layer is first deposited on titanium followed by a second layer of a poly(methyl methacrylate-co-methacrylic acid) (P(MMA-co-MAA)) copolymer prior to comolding. During processing, the MAA moieties of the copolymer thermally react with PDA, forming amide bonds, while MMA promotes the formation of secondary bonds and molecular interdigitation with the PMMA matrix. Control testing reveals that neither PDA nor the copolymer provides a substantial increase in adhesion. However, when used in combination, a significant increase in adhesion is detected. This observation indicates a pronounced synergistic effect between the two layers that strengthens the PMMA-titanium bonding. Enhanced adhesion is optimized by tuning the MMA-to-MAA ratio of the copolymer, which shows a maximum at a 24% MAA content and a greatly increased Ga value of 155 J m-2; this value corresponds to a 40-fold increase. Further growth in the Ga values at higher MAA contents is hindered by the thermal cross-linking of MAA; MAA contents above 24% restrict the formation of secondary bonds and molecular interdigitation with the PMMA chains. Our results provide new design principles to produce thermoplastic-metal comolded joints with strong interfaces.

Project description:Background:The main issue in cutaneous regeneration is to develop engineered scaffolds based on natural extracellular matrix to promote dynamics of skin progenitor cells and accelerate differentiation into mature keratinocytes. Methods:In this study, nanofibrous scaffolds composed of a blend poly (?-caprolactone) (PCL), silk fibroin (SF), soluble eggshell membrane (SESM), and Aloe vera (AV) gel were developed by electrospinning method and human basal cells were used to examine differentiation capacity toward keratinocyte-like cells. For this propose, cells were allocated to four distinct groups; control, PCL/SF, PCL/SF/SESM, and PCL/SF/SESM/AV. In all groups, cells were incubated with differentiation medium. Morphology, composition, hydrophilicity and mechanical features of PCL/SF, PCL/SF/SESM and PCL/SF/SESM/AV nanofibers were studied by scanning electron microscopy (SEM), Fourier transforms infrared spectroscopy (FT-IR), water contact angle and tensile tests. To examine the orientation of basal cells to mature keratinocytes, we performed immunofluorescence analysis by monitoring cytokeratin-19. The expression of genes such as involucrin, keratin-14 and -5 was monitored by real-time PCR assay. Results:PCL/SF, PCL/SF/SESM, and PCL/SF/SESM/AV had suitable physic chemical indices and biological activities to be applied as biomimetic scaffolds for the restoration cutaneous tissue. Compared to control, we found an increased basal cell proliferation at 7 and 14?days after plating on scaffolds and reach maximum levels in group PCL/SF/SESM/AV on day 14 (p?<?0.05). Electron microscopy showed cell flattening, morphological adaptation. An integrated cell-to-cell connection was generated after cell seeding on scaffolds in all groups. Immunofluorescence imaging showed the ability of basal cells to synthesize cytokeratin-19 in PCL/SF, PCL/SF/SESM, and positive control cells after exposure to differentiation medium. However, these values were less in PCL/SF/SESM/AV compared to other groups. Real-time PCR analysis showed the potency of all scaffolds to induce the transcription of involucrin, keratin-14 and -5, especially involucrin in PCL/SF/SESM/AV group compared to the negative control. Conclusion:Modulation of scaffolds with natural biopolymers could enable us to synthesize structures appropriate for cutaneous regeneration.

Dataset Information

Superhydrophilic Polyurethane/Polydopamine Nanofibrous Materials Enhancing Cell Adhesion for Application in Tissue Engineering.

Publications

Superhydrophilic Polyurethane/Polydopamine Nanofibrous Materials Enhancing Cell Adhesion for Application in Tissue Engineering.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets