Flexural Strength of 3D-Printing Resin Materials for Provisional Fixed Dental Prostheses.

ABSTRACT: The clinical application of 3D-printed provisional restorations is increasing due to expansion of intraoral scanners, easy dental computer-aided design (CAD) software, and improved 3D printing speed. This study compared flexural strength of 3D-printed three-unit fixed dental prostheses with that of conventionally fabricated and milled restorations. A metal jig of two abutments and pontic space and an indenter for flexural strength measurement were fabricated. A three-unit fixed dental prosthesis was designed and manufactured using three additive manufacturing technologies, with subtractive manufacturing and a conventional method as controls. Digital light processing (DLP) group specimens were prepared from a polymethyl methacrylate (PMMA)-based resin and printed with a DLP printer. Stereolithography (SLA) group specimens were prepared from PMMA-based resin and printed with an SLA printer, and fused deposition modeling (FDM) group specimens were from a polylactic acid-based resin and printed with an FDM printer. Flexural strength was investigated using a universal testing machine, and the results were statistically analyzed. DLP and SLA groups had significantly higher flexural strength than the conventional group (p < 0.001). No significant difference was observed in flexural strength between DLP and SLA groups. The FDM group showed only dents but no fracture. The results of this study suggest that provisional restorations fabricated by DLP and SLA technologies provide adequate flexural strength for dental use.

SUBMITTER: Park SM

PROVIDER: S-EPMC7559938 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Flexural Strength of 3D-Printing Resin Materials for Provisional Fixed Dental Prostheses.

Park Sang-Mo SM Park Ji-Man JM Kim Seong-Kyun SK Heo Seong-Joo SJ Koak Jai-Young JY

Materials (Basel, Switzerland) 20200908 18

The clinical application of 3D-printed provisional restorations is increasing due to expansion of intraoral scanners, easy dental computer-aided design (CAD) software, and improved 3D printing speed. This study compared flexural strength of 3D-printed three-unit fixed dental prostheses with that of conventionally fabricated and milled restorations. A metal jig of two abutments and pontic space and an indenter for flexural strength measurement were fabricated. A three-unit fixed dental prosthesis ...[more]

PMID: 32911702

Similar Datasets

Project description:BackgroundThree-dimensional (3D) printing technology has revolutionized dentistry, particularly in fabricating provisional restorations. This systematic review and meta-analysis aimed to thoroughly evaluate the flexural strength of provisional restorations produced using 3D printing while considering the impact of different resin materials.MethodsA systematic search was conducted across major databases (ScienceDirect, PubMed, Web of Sciences, Google Scholar, and Scopus) to identify relevant studies published to date. The inclusion criteria included studies evaluating the flexural strength of 3D-printed provisional restorations using different resins. Data extraction and quality assessment were performed using the CONSORT scale, and a meta-analysis was conducted using RevMan 5.4 to pool results.ResultsOf the 1914 initially identified research articles, only 13, published between January 2016 and November 2023, were included after screening. Notably, Digital Light Processing (DLP) has emerged as the predominant 3D printing technique, while stereolithography (SLA), Fused Deposition Modeling (FDM), and mono-liquid crystal displays (LCD) have also been recognized. Various printed resins have been utilized in different techniques, including acrylic, composite resins, and methacrylate oligomer-based materials. Regarding flexural strength, polymerization played a pivotal role for resins used in 3D or conventional/milled resins, revealing significant variations in the study. For instance, SLA-3D and DLP Acrylate photopolymers displayed distinct strengths, along with DLP bisacrylic, milled PMMA, and conventional PMMA. The subsequent meta-analysis indicated a significant difference in flexure strength, with a pooled Mean Difference (MD) of - 1.25 (95% CI - 16.98 - 14.47; P < 0.00001) and a high I2 value of 99%, highlighting substantial heterogeneity among the studies.ConclusionsThis study provides a comprehensive overview of the flexural strength of 3D-printed provisional restorations fabricated using different resins. However, further research is recommended to explore additional factors influencing flexural strength and refine the recommendations for enhancing the performance of 3D-printed provisional restorations in clinical applications.

Project description:One therapeutical alternative in the treatment of functional disorders is the use of printed oral splints. The mechanical properties of these materials are highly essential to their clinical effectiveness, and their performance may vary depending on factors such as cleaning, post-polymerization, or their orientation during construction. The objective of this in vitro investigation is to evaluate the effectiveness of the selected materials in terms of their biaxial flexural strength in relation to the criteria listed above. Splint materials were used in the printing of 720 discs. The printing process was carried out in different orientations in relation to the building platform. Either an automatic or manual cleaning process was performed on the samples. For post-polymerization, either an LED or Xenon light was utilized. A piston-on-three-ball test was used to measure the biaxial flexural strength (BFS) of the materials after they were stored in water for either 24 h or 60 days. The homogeneity of the data was controlled by employing the Levene method, and the differences between the groups were analyzed using the ANOVA and Bonferroni methods. After being stored for twenty-four hours, the mean BFS ranged anywhere from 79 MPa to 157 MPa. Following a period of sixty hours, the BFS exhibited a substantial drop and revealed values that ranged from 72 to 127 MPa. There was no significant difference that could be identified between the materials or between the various cleaning processes. The results of post-polymerization showed that the LED light produced higher means than the Xenon light did. In terms of position, the mean values varied greatly, with 0°'s mean value being 101 MPa, 45°'s mean value being 102 MPa, and 90°'s mean value being 115 MPa. The use of a build orientation of 90° and post-polymerization with LED light resulted in significantly increased biaxial flexural strength. According to this study, this design should be implemented in order to ensure that splint materials have the highest possible strength.

Dataset Information

Flexural Strength of 3D-Printing Resin Materials for Provisional Fixed Dental Prostheses.

Publications

Flexural Strength of 3D-Printing Resin Materials for Provisional Fixed Dental Prostheses.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets