Water Interactions in Hybrid Polyacrylate-Silicate Hydrogel Systems.

ABSTRACT: Hybrid polyacrylate-silicate hydrogels were obtained in the presence of N,N'-methylenebisacrylamide (NNMBA) as the cross-linking monomer and sodium thiosulphate/potassium persulphate (NTS/KPS) as the redox initiators. The results of the tests allowed us to conclude that a hybrid structure with a polyacrylate scaffolding and a silicate matrix had been obtained. The results of the rheological analysis revealed that the hydrogel sample with a 1:7 mass ratio of sodium water glass to the sodium polyacrylate is characterized by the highest complex viscosity. Thermal analysis (Thermogravimetry/Differential Scanning Calorimetry (TG/DSC)) showed that water begins to evaporate at higher temperatures, from 120 °C to even 180 °C. These results were confirmed by mid-infrared spectroscopy (MIR) and nuclear magnetic resonance spectroscopy (NMR) analysis. Differences in the intensity of the peaks derived from water in the MIR spectra indicate that most of the water is bounded. In turn, NMR results showed that the mobility of water molecules decreases as the amount of sodium water glass in the mixture increases.

SUBMITTER: Mastalska-Poplawska J

PROVIDER: S-EPMC7560421 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Water Interactions in Hybrid Polyacrylate-Silicate Hydrogel Systems.

Mastalska-Popławska Joanna J Stempkowska Agata A Habina-Skrzyniarz Iwona I Krzyżak Artur T AT Rutkowski Paweł P Izak Piotr P Rudny Jakub J Gawenda Tomasz T

Materials (Basel, Switzerland) 20200915 18

Hybrid polyacrylate-silicate hydrogels were obtained in the presence of <i>N</i>,<i>N</i>'-methylenebisacrylamide (NNMBA) as the cross-linking monomer and sodium thiosulphate/potassium persulphate (NTS/KPS) as the redox initiators. The results of the tests allowed us to conclude that a hybrid structure with a polyacrylate scaffolding and a silicate matrix had been obtained. The results of the rheological analysis revealed that the hydrogel sample with a 1:7 mass ratio of sodium water glass to th ...[more]

PMID: 32942635

Similar Datasets

Project description:The purpose of this study was to comparatively investigate the behavior of silicate and sol-silicate coatings non-modified or modified with an organosilane on wood and on wood pre-coated with silica-mineralized primers. Adhesion strength, morphology, and water permeability and related damages were studied to evaluate the possibility of utilizing such inorganic-based coating systems for durable protection of wood without or with relatively cheap and water-borne primers. Potassium silicate and potassium methylsiliconate aqueous solutions and a colloidal silica were used for the preparation of the coatings. The white coating paints were brushed on beech wood substrates at a rate of 220 g·m-2. The coatings exhibited good coverage ability. The pull-off adhesion strength values appeared to be related to pH following a polynomial law. The adhesion strength for the silicate coatings were adequate (above 3 MPa and up to 5 MPa) for wood, whereas the values for the sol-silicates were too low for practical applications. The adhesion values were in general higher for the samples cured in a climate room (23 ± 3 °C and 75 ± 2% relative humidity) than the samples cured in the ambient atmosphere of the laboratory (23 ± 3 °C and 25 ± 5% relative humidity). The presence of microdefects (cracks, holes) was revealed in the coating layers by optical and scanning electron microscopy. The surface roughness parameters assessed by confocal scanning laser microscopy were dependent on the magnification applied for their measurement. The arithmetic average roughness Sa was between 5 µm and 10 µm at magnification 5× and between 2.5 μm and 10 µm at magnification 20×. The maximum peak-to-valley height Sz confirmed the presence of open pores emerging through the coatings. The open pores constitute free pathways for water ingress through the coatings, and could explain the high water absorption of the coatings including the methysiliconate-containing silicate coating and despite the relatively high water contact angle and low wettability exhibited by this sample. The post-application of a hydrophobizing solution containing hexadecyltrimethoxysilane and dimethyloctadecyl[3-(trimethoxysilyl)propyl]ammonium chloride considerably reduced the water permeability, while application of nanosilica-containing organic primers increased the adhesion for the coatings. Silicate coatings with adhesion great enough and resistance against water damages can be generated on wood even without a primer using low silica-to-alkali ratio binders and an organosilane additive. The sol-silicate coatings appear to be applicable only with a primer. The improvement of the paint formulations to control the formation of microcracks and open pores could be useful to reduce the liquid water permeability and increase durability. Otherwise, the application of a hydrophobizing treatment can be used for this purpose.

Project description:Effective control of shale swelling and lost circulation using drilling fluid is considered the dominant strategy for maintaining borehole stability, especially drilling operations in deep oil and gas wells. In this work, a hybrid silicate that contains lithium silicate and potassium methyl silicate (PMS) was employed as a film-forming additive to reduce shale hydration and filtration loss in the high-temperature drilling fluid. Scanning electron microscopy (SEM) results revealed that a dense quartz crystal film coating on the shale can be formed in a hybrid silicate solution when the temperature exceeds 150 °C. The in situ-formed film on the shale surface with a thickness of 60-130 μm was composed of fibrous crystalline silica. Furthermore, the aqueous hybrid silicate exhibited enhanced hydration inhibition ability by preventing water invasion of the formation. Aqueous hybrid silicate with a concentration of 0.5-3 wt % lithium silicate and 0.1-0.2 mol/L PMS was first chosen to obtain the optimum concentration according to the hydration inhibition ability and film formation characteristics. The hybrid silicate was added into a drilling fluid formulation applicable in high-pressure and high-temperature conditions, and the rheological characteristics and filtration properties were investigated. The results confirmed that drilling fluids with the addition of hybrid silicate can mitigate variation of viscosity and yield point before and after aging at 180 and 220 °C. Besides, the filtration behavior was also improved by adding hybrid silicate into the drilling fluid. A lower filtration loss was observed at the concentration of 1.0 wt % lithium silicate and 0.2 mol/L potassium methyl silicate, which showed 63 and 50% HPHT fluid loss reduction for unweighted and weighted formulations at 205 °C and 3.5 MPa, respectively. In addition, the drilling fluid featured stable rheological and filtration properties and excellent shale hydration inhibition characteristics when exposed to high temperatures, making it a promising candidate for drilling in deep oil and gas wells.

Dataset Information

Water Interactions in Hybrid Polyacrylate-Silicate Hydrogel Systems.

Publications

Water Interactions in Hybrid Polyacrylate-Silicate Hydrogel Systems.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets