Rheological Investigation of Relaxation Behavior of Polycarbonate/Acrylonitrile-Butadiene-Styrene Blends.

ABSTRACT: The rheological properties of polycarbonate/acrylonitrile-butadiene-styrene (PC/ABS) blends with various blend ratios are investigated at different temperatures to determine the shear dependent chain motions in a heterogeneous blend system. At low frequency levels under 0.1 rad/s, the viscosity of the material with a blend ratio of 3:7 (PC:ABS) is higher than that of pure ABS polymer. As the temperature increases, the viscosities of ABS-rich blends increase rather than decrease, whereas PC-rich blends exhibit decrease in viscosity. Results from the time sweep measurements indicate that ordered structures of PC and the formation and breakdown of internal network structures of ABS polymer occur simultaneously in the blend systems. Newly designed sequence test results show that the internal structures formed between PC and ABS polymers are dominant at low shear conditions for the blend ratio of 3:7 and effects of structural change and the presence of polybutadiene (PBD) become dominant at high shear conditions for pure ABS. The results of yield stress and relaxation time for PC/ABS blends support this phenomenon. The specimen with a blend ratio of 3:7 exhibited the highest value of yield stress at high temperature among others, which implies that the internal structure become stronger at higher temperature. The heterogeneity of ABS-rich blends increases whereas that of PC-rich blends decreases as temperature increases.

SUBMITTER: Seo JS

PROVIDER: S-EPMC7563493 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Rheological Investigation of Relaxation Behavior of Polycarbonate/Acrylonitrile-Butadiene-Styrene Blends.

Seo Jae Sik JS Jeon Ho Tak HT Han Tae Hee TH

Polymers 20200825 9

The rheological properties of polycarbonate/acrylonitrile-butadiene-styrene (PC/ABS) blends with various blend ratios are investigated at different temperatures to determine the shear dependent chain motions in a heterogeneous blend system. At low frequency levels under 0.1 rad/s, the viscosity of the material with a blend ratio of 3:7 (PC:ABS) is higher than that of pure ABS polymer. As the temperature increases, the viscosities of ABS-rich blends increase rather than decrease, whereas PC-rich ...[more]

PMID: 32854352

Similar Datasets

Project description:Fused filament fabrication is a 3D printing technique that has gained widespread use from homes to schools to workplaces. Thermoplastic filaments, such as acrylonitrile-butadiene-styrene (ABS) and polylactic acid (PLA), are extruded at temperatures near their respective glass transition temperature or melting point, respectively. Little has been reported on the inorganic elemental composition and concentrations present in these materials or the methods available for extracting that information. Because inorganic constituents may be included in the aerosolized particulates emitted during the printing process, identifying elements that could be present and at what specific concentrations is critical. The objective of the current research is to determine the range of metals present in thermoplastic filaments along with their relative abundance and chemical speciation as a function of polymer type, manufacturer, and color. A variety of filaments from select manufacturers were digested using a range of techniques to determine the optimal conditions for metal extraction from ABS and PLA polymers. The extraction potential for each method was quantified using by ICP-MS analysis. When possible, further characterization of the chemical composition of the filaments was investigated using X-ray Absorption spectroscopy to determine chemical speciation of the metal. Optimal digestion conditions were established using a high temperature, high pressure microwave-assisted acid digestion method to produce the most complete and repeatable extraction results. The composition and abundance of metals in the filaments varied greatly as a function of polymer, manufacturer, and color. Potential elements of concern present in the filaments at elevated concentration included that could pose a respiratory risk included Si, Al, Ti, Cu, Zn, and Sn. XAS analysis revealed a mixture of metal oxides, mineral, and organometallic compounds were present in the filaments that were being used to increase opaqueness impart color (dyes), polymeric catalysts, and flame retardants. This work shows that a variety of metals are present in the starting materials used for 3D printing and depending on their partitioning into 3D printed products and byproducts as well as the exposure route, may pose a health risk which merits further investigation.

Dataset Information

Rheological Investigation of Relaxation Behavior of Polycarbonate/Acrylonitrile-Butadiene-Styrene Blends.

Publications

Rheological Investigation of Relaxation Behavior of Polycarbonate/Acrylonitrile-Butadiene-Styrene Blends.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets