Synthesis of Bio-Based Poly(Butylene Adipate-co-Butylene Itaconate) Copolyesters with Pentaerythritol: A Thermal, Mechanical, Rheological, and Molecular Dynamics Simulation Study.


ABSTRACT: Bio-based unsaturated poly(butylene adipate-co-butylene itaconate) (PBABI) aliphatic copolyesters were synthesized with pentaerythritol (PE) as a modifier, observing the melting point, crystallization, and glass transition temperatures were decreased from 59.5 to 19.5 °C and 28.2 to -9.1 °C as an increase of itaconate concentration, and Tg ranged from -54.6 to -48.1 °C. PBABI copolyesters tend to the amorphous state by the existence of the BI unit above 40 mol%. The yield strength, elongation, and Young's modulus at different BA/BI ratios were valued in a range of 13.2-13.8 MPa, 575.2-838.5%, and 65.1-83.8 MPa, respectively. Shear-thinning behavior was obtained in all BA/BI ratios of PBABI copolyesters around an angular frequency range of 20-30 rad s-1. Furthermore, the thermal and mechanical properties of PBABI copolyesters can be well regulated via controlling the itaconic acid contents and adding the modifier. PBABI copolyesters can be coated on a 3D air mesh polyester fabric to reinforce the mechanical property for replacing traditional plaster applications.

SUBMITTER: Chen CW 

PROVIDER: S-EPMC7564154 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

altmetric image

Publications

Synthesis of Bio-Based Poly(Butylene Adipate-<i>co</i>-Butylene Itaconate) Copolyesters with Pentaerythritol: A Thermal, Mechanical, Rheological, and Molecular Dynamics Simulation Study.

Chen Chin-Wen CW   Mao Hsu-I HI   Yang Zhi-Yu ZY   Huang Kuan-Wei KW   Yan Hao-Chen HC   Rwei Syang-Peng SP  

Polymers 20200903 9


Bio-based unsaturated poly(butylene adipate-co-butylene itaconate) (PBABI) aliphatic copolyesters were synthesized with pentaerythritol (PE) as a modifier, observing the melting point, crystallization, and glass transition temperatures were decreased from 59.5 to 19.5 °C and 28.2 to -9.1 °C as an increase of itaconate concentration, and T<sub>g</sub> ranged from -54.6 to -48.1 °C. PBABI copolyesters tend to the amorphous state by the existence of the BI unit above 40 mol%. The yield strength, el  ...[more]

Similar Datasets

| S-EPMC7033981 | biostudies-literature
| S-EPMC7285232 | biostudies-literature
| S-EPMC8401440 | biostudies-literature
| S-EPMC7600530 | biostudies-literature
| S-EPMC11359266 | biostudies-literature
| S-EPMC6415514 | biostudies-literature
| S-EPMC6643474 | biostudies-literature
| S-EPMC7565969 | biostudies-literature
| S-EPMC10857009 | biostudies-literature
| S-EPMC9609898 | biostudies-literature