How Thermal Aging Affects Ignition and Combustion Properties of Reactive Al/CuO Nanolaminates: A Joint Theoretical/Experimental Study.

ABSTRACT: The paper reports a joint experimental/theoretical study on the aging of reactive Al/CuO nanolaminates, investigating both structural modifications and combustion properties of aged systems. We first show theoretically that the long-term storage (over several decades) in ambient temperature marginally affects nanolaminates structural properties with an increase in an interfacial layer of only 0.3 nm after 30 years. Then, we observe that the first thermal aging step occurs after 14 days at 200 °C, which corresponds to the replacement of the natural Al/CuO interfaces by a proper ~11 nm thick amorphous alumina. We show that this aging step does impact the nanolaminates structure, leading, for thin bilayer thicknesses, to a substantial loss of the energetic reservoir: considering a stoichiometric Al/CuO stack, the heat of reaction can be reduced by 6-40% depending on the bilayer thickness ranging from 150 nm (40%) to 1 µm (6%). The impact of such thermal aging (14 days at 200 °C) and interfacial modification on the initiation and combustion properties have been evaluated experimentally and theoretically. Varying Al to CuO ratio of nanolaminates from 1 to 3, we show that ignition time of aged systems does not increase over 10% at initiation power densities superior to 15 W·mm-2. In contrast, burn rate can be greatly impacted depending on the bilayer thickness: annealing a stoichiometric nanolaminates with a bilayer thickness of 300 nm at 200 °C for 14 days lowers its burn rate by ~25%, whereas annealing a fuel rich nanolaminates with the same bilayer thickness under the same thermal conditions leads to a burn rate decrease of 20%. When bilayer thickness is greater than 500 nm, the burn rate is not really affected by the thermal aging. Finally, this paper also proposes a time-temperature diagram to perform accelerated thermal aging.

SUBMITTER: Esteve A

PROVIDER: S-EPMC7589912 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

How Thermal Aging Affects Ignition and Combustion Properties of Reactive Al/CuO Nanolaminates: A Joint Theoretical/Experimental Study.

Estève A A Lahiner G G Julien B B Vivies S S Richard N N Rossi C C

Nanomaterials (Basel, Switzerland) 20201021 10

The paper reports a joint experimental/theoretical study on the aging of reactive Al/CuO nanolaminates, investigating both structural modifications and combustion properties of aged systems. We first show theoretically that the long-term storage (over several decades) in ambient temperature marginally affects nanolaminates structural properties with an increase in an interfacial layer of only 0.3 nm after 30 years. Then, we observe that the first thermal aging step occurs after 14 days at 200 °C ...[more]

PMID: 33096914

Similar Datasets

Project description:The synthesis of optoelectrically enhanced nanomaterials should be continuously improved by employing time- and energy-saving techniques. The porous zinc oxide (ZnO) and copper-doped ZnO nanocomposites (NCs) were synthesized by the time- and energy-efficient solution combustion synthesis (SCS) approach. In this SCS approach, once the precursor-surfactant complex ignition point is reached, the reaction starts and ends within a short time without the need for any external energy. The TGA-DTA analysis confirmed that 500 °C was the point at which stable metal oxide was obtained. The doping and heterojunction strategy improved the optoelectric properties of the NCs more than the individual constituents, which then enhanced the materials' charge transfer and optical absorption capabilities. The porosity, nanoscale crystallite size (15-50 nm), and formation of Cu/CuO-ZnO NCs materials were confirmed from the XRD, SEM, and TEM/HRTEM analyses. The obtained d-spacing values of 0.275 and 0.234 nm confirm the formation of ZnO and CuO crystals, respectively. The decrease in photoluminescence intensity for the doped NCs corroborates a reduction in electron-hole recombination. On the Mott-Schottky analysis, the positive slope for ZnO confirms the n-type character, while the negative and positive slopes of the NCs confirm the p- and n-type characters, respectively. A diffusion-controlled type of charge transfer process on the electrode surface was confirmed from the cyclic voltammetric analysis. Thus, the overall analysis shows the applicability of the less expensive and more efficient SCS for several applications, such as catalysis and sensors. To confirm this, an organic catalytic reduction reaction of 4-nitrophenol to 4-aminophenol was tested. Within three and a half minutes, the catalytic reduction result showed the great potential of NCs over ZnO NPs. Thus, the energy- and time-saving SCS approach has a great future outlook as an industrial pollutant catalytic reduction application.

Dataset Information

How Thermal Aging Affects Ignition and Combustion Properties of Reactive Al/CuO Nanolaminates: A Joint Theoretical/Experimental Study.

Publications

How Thermal Aging Affects Ignition and Combustion Properties of Reactive Al/CuO Nanolaminates: A Joint Theoretical/Experimental Study.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets