The Effect of Silica-Filler on Polyurethane Adhesives Based on Renewable Resource for Wood Bonding.

ABSTRACT: The aim of the study was to evaluate the applicability and performance of polyglycerol- and sucrose-based polyols as components of a simplified formulation of polyurethane adhesives. Colloidal silica was used as a viscosity control and reinforcing agent. The adhesives were examined in terms of reactivity, thermal stability, viscosity, work of adhesion, wetting, surface energy, and bonding strength on wooden substrates. Silica was found to increase gelling time, but markedly improved bonding strength and adhesion with substrates. Bonded solid beech wood samples prepared at 80, 110, and 130 °C showed shear strengths between 7.1 MPa and 9.9 MPa with 100% wood failure. The renewable resource-based polyols were demonstrated to be useful in formulation of polyurethane adhesives for furniture industry-especially with silica as a filler.

SUBMITTER: Maminski ML

PROVIDER: S-EPMC7598712 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

The Effect of Silica-Filler on Polyurethane Adhesives Based on Renewable Resource for Wood Bonding.

Mamiński Mariusz Ł MŁ Więcław-Midor Anna M AM Parzuchowski Paweł G PG

Polymers 20200924 10

The aim of the study was to evaluate the applicability and performance of polyglycerol- and sucrose-based polyols as components of a simplified formulation of polyurethane adhesives. Colloidal silica was used as a viscosity control and reinforcing agent. The adhesives were examined in terms of reactivity, thermal stability, viscosity, work of adhesion, wetting, surface energy, and bonding strength on wooden substrates. Silica was found to increase gelling time, but markedly improved bonding stre ...[more]

PMID: 32987650

Similar Datasets

Non-Furanic Humins-Based Non-Isocyanate Polyurethane (NIPU) Thermoset Wood Adhesives.

Project description:Predominantly non-furanic commercial humins were used to prepare humin-based non-isocyanate polyurethane (NIPU) resins for wood panel adhesives. Pure humin-based NIPU resins and tannin-humin NIPU resins were prepared, the latter to upgrade the humins' performance. Species in the raw humins and species formed in the NIPU resins were identified by Matrix Assisted Laser Desorption Ionization Time of Flight (MALDI ToF) spectrometry and Fourier Transform Infrared (FTIR). Humins, fulvic acid and derivatives, humic acid and its fragments, some lignans present and furanic oligomers present formed NIPU linkages. Thermomechanical analysis (TMA) showed that as with other biomaterials-based NIPU resins, all these resins also showed two temperature peaks of curing, the first around 130 °C and the second around 220 °C. A decrease in the Modulus of Elasticity (MOE) between the two indicated that the first curing period corresponded to linear growth of the oligomers forming a physical entanglement network. This then disentangled, and the second corresponded to the formation of a chemical cross-linked network. This second peak was more evident for the tannin-humin NIPU resins. All the laboratory particleboard made and tested either bonded with pure humins or with tannin-humin NIPU adhesives satisfied well the internal bond strength requirements of the relevant standard for interior grade panels. The tannin-humin adhesives performed clearly better than the pure humins one.

| S-EPMC7865859 | biostudies-literature

Lignosulfonate-Based Polyurethane Adhesives.

Project description:The feasibility of using lignosulfonate (LS) from acid sulphite pulping of eucalyptus wood as an unmodified polyol in the formulation of polyurethane (PU) adhesives was evaluated. Purified LS was dissolved in water to simulate its concentration in sulphite spent liquor and then reacted with 4,4'-diphenylmethane diisocyanate (pMDI) in the presence or absence of poly(ethylene glycol) with Mw 200 (PEG200) as soft crosslinking segment. The ensuing LS-based PU adhesives were characterized by infrared spectroscopy and thermal analysis techniques. The adhesion strength of new adhesives was assessed using Automated Bonding Evaluation System (ABES) employing wood strips as a testing material. The results showed that the addition of PEG200 contributed positively both to the homogenization of the reaction mixture and better crosslinking of the polymeric network, as well as to the interface interactions and adhesive strength. The latter was comparable to the adhesive strength recorded for a commercial white glue with shear stress values of almost 3 MPa. The optimized LS-based PU adhesive formulation was examined for the curing kinetics following the Kissinger and the Ozawa methods by non-isothermal differential scanning calorimetry, which revealed the curing activation energy of about 70 kJ·mol-1.

| S-EPMC8622556 | biostudies-literature

Fabrication of Wood-Rubber Composites Using Rubber Compound as a Bonding Agent Instead of Adhesives.

Project description:Differing from the hot-pressing method in the manufacturing of traditional wood-rubber composites (WRCs), this study was aimed at fabricating WRCs using rubber processing to improve water resistance and mechanical properties. Three steps were used to make WRCs, namely, fiber-rubber mixing, tabletting, and the vulcanization molding process. Ninety-six WRC panels were made with wood fiber contents of 0%-50% at rotor rotational speeds of 15-45 rpm and filled coefficients of 0.55-0.75. Four regression equations, i.e., the tensile strength (Ts), elongation at break (Eb), hardness (Ha) and rebound resilience (Rr) as functions of fiber contents, rotational speed and filled coefficient, were derived and a nonlinear programming model were developed to obtain the optimum composite properties. Although the Ts, Eb and Rr of the panels were reduced, Ha was considerably increased by 17%-58% because of the wood fiber addition. Scanning electron microscope images indicated that fibers were well embedded in rubber matrix. The 24 h water absorption was only 1%-3%, which was much lower than commercial wood-based composites.

| S-EPMC5456808 | biostudies-other

Graphene Materials Strengthen Aqueous Polyurethane Adhesives.

Project description:Carboxyl-functionalized graphene platelets (GP) and graphene oxide (GO) sheets were added to a commercial aqueous adhesive dispersion of thermoplastic polyurethane (TP) (Idrotex 200 from FacGB s.r.l.). For both additives, the weight percentage was of industrial interest, 0.01 and 0.1 wt %. The addition of GP/GO was carried out in a simple and scalable-up process that can be applied to other materials and additives. Mechanical, peel tests were applied on polyurethane strips (75 mm long, 15 mm wide, and 1.5 mm thick) prepared cutting extruded sheets obtained using Estane 58091, a 70D aromatic polyester-based TP. The tests with 0.01 wt % of GP showed statistically significant higher forces at first failure and maximum forces with respect to the pristine adhesive. Sample characterization was carried out with scanning electron microscopy, infrared spectroscopy, X-ray diffraction, and thermal analysis. A mechanism is suggested for the improved performance of the low-dose GP adhesive.

| S-EPMC6645141 | biostudies-literature

Peanut meal-based wood adhesives enhanced by urea and epichlorohydrin.

Project description:Peanut meal (PM) has recently emerged as a potential protein source for wood adhesives, owing to superior features such as high availability, renewability and eco-friendliness. However, the poor properties of unmodified PM-based wood adhesives, compared with their petroleum-derived counterparts, limit their use in high-performance applications. In order to promote the application of PM-based wood adhesives in plywood industry, urea (U) and epichlorohydrin (ECH) were used to enhance the properties of the adhesives and the modification mechanism was investigated. PM-based wood adhesives made with U and ECH were shown to possess sufficient water resistance and exhibited higher apparent viscosity and solid content than without. Fourier-transform infrared spectroscopy results suggested that U denatured PM protein and expose more reactive groups, allowing ECH to react better with U-treated PM protein to form a dense, cross-linked network which was the main reason for the improvement of the properties. The crystallinity increased from 2.7% to 11% compared with the control, indicating that the molecular structure of the resultant adhesive modified by U and ECH became more regular and compact owing to the cross-linked network structure. Thermogravimetry tests showed that decomposition temperature of the protein skeleton structure increased from 307°C to 314°C after U and ECH modification. Scanning electron microscopy images revealed that using U and ECH for adhesives resulted in a smooth protein surface which prevented moisture penetration and improved water resistance. PM-based adhesives thus represent potential candidates to replace petroleum-derived adhesives in the plywood industry, which will effectively promote the rapid development of eco-friendly adhesives and increase the added value of PM.

| S-EPMC6894569 | biostudies-literature

Plant Oil-Based Acrylic Latexes towards Multisubstrate Bonding Adhesives Applications.

Project description:To investigate the utility of acrylic monomers from various plant oils in adhesives manufacturing, 25-45 wt. % of high oleic soybean oil-based monomer (HOSBM) was copolymerized in a miniemulsion with commercially applied butyl acrylate (BA), methyl methacrylate (MMA), or styrene (St). The compositions of the resulting ternary latex copolymers were varied in terms of both "soft" (HOSBM, BA) and "rigid" (MMA or St) macromolecular fragments, while total monomer conversion and molecular weight of copolymers were determined after synthesis. For most latexes, results indicated the presence of lower and higher molecular weight fractions, which is beneficial for the material adhesive performance. To correlate surface properties and adhesive performance of HOSBM-based copolymer latexes, contact angle hysteresis (using water as a contact liquid) for each latex-substrate pair was first determined. The data showed that plant oil-based latexes exhibit a clear ability to spread and adhere once applied on the surface of materials differing by polarities, such as semicrystalline polyethylene terephthalate (PET), polypropylene (PP), bleached paperboard (uncoated), and tops coated with a clay mineral paperboard. The effectiveness of plant oil-based ternary latexes as adhesives was demonstrated on PET to PP and coated to uncoated paperboard substrates. As a result, the latexes with high biobased content developed in this study provide promising adhesive performance, causing substrate failure instead of cohesive/adhesive break in many experiments.

| S-EPMC9416654 | biostudies-literature

Fast Curing Multifunctional Tissue Adhesives of Sericin-Based Polyurethane-Acrylates for Sternal Closure.

Project description:The use of wire cerclage after sternal closure is the standard method because of its rigidity and strength. Despite this, they have many disadvantages such as tissue trauma, operator-induced failures, and the risk of infection. To avoid complications during sternotomy and promote tissue regeneration, tissue adhesives should be used in post-surgical treatment. Here, we report a highly biocompatible, biomimetic, biodegradable, antibacterial, and UV-curable polyurethane-acrylate (PU-A) tissue adhesive for sternal closure as a supportive to wire cerclage. In the study, PU-As were synthesized with variable biocompatible monomers, such as silk sericin, polyethylene glycol, dopamine, and an aliphatic isocyanate 4,4'-methylenebis(cyclohexyl isocyanate). The highest adhesion strength was found to be 4322 kPa, and the ex vivo compressive test result was determined as 715 kPa. The adhesive was determined to be highly biocompatible (on L-929 cells), biodegradable, and antibacterial (on Escherichia coli, Pseudomonas aeruginosa, and Staphylococcus aureus bacteria). Finally, after opening the sternum of rats, the adhesive was applied to bond the bones and cured with UV for 5 min. According to the results, there was no visible inflammation in the adhesive groups, while some animals had high inflammation in the cyanoacrylate and wire cerclage groups. These results indicate that the adhesive may be suitable for sternal fixation by preventing the disadvantages of the steel wires and promoting tissue healing.

| S-EPMC9501797 | biostudies-literature

Adhesives for Achieving Durable Bonds with Acetylated Wood.

Project description:Acetylation of wood imparts moisture durability, decay resistance, and dimensional stability to wood; however, making durable adhesive bonds with acetylated wood can be more difficult than with unmodified wood. The usual explanation is that the acetylated surface has fewer hydroxyl groups, resulting in a harder-to-wet surface and in fewer hydrogen bonds between wood and adhesive. This concept was evaluated using four different adhesives (resorcinol⁻formaldehyde, emulsion polymer isocyanate, epoxy, and melamine⁻formaldehyde) with unmodified wood, acetylated wood, and acetylated wood that had been planed. Strikingly, acetylation did not hinder adhesive bonds with a waterborne resorcinol⁻formaldehyde adhesive that bonded equally well to both unmodified and acetylated yellow poplar. An epoxy adhesive bonded better to the acetylated wood than to the unmodified wood, in contrast to an emulsion polymer isocyanate, which gave less durable bonds to acetylated than to unmodified wood. Planing of the acetylated wood surface prior to bonding reduced bond durability for the epoxy adhesive and increased the amount of surface hydroxyl groups, as measured using X-ray photoelectron spectroscopic analysis of the trifluoroacetic anhydride-treated wood. These experiments showed that wood modification is useful in understanding wood-adhesive interactions, in addition to determining how to develop adhesives for acetylated woods.

| S-EPMC6418570 | biostudies-literature

Eco-benign PVA/aluminum phosphate as an alternative to formaldehyde-based adhesives in wood-based panels.

Project description:Aluminum phosphate (AP) shows great potential to replace formaldehyde-based adhesives in the wood industry, except for its weak hygroscopic resistance and low wet bonding strength. This study chose PVA as an AP modifier to prepare a PVA-AP organic-inorganic hybrid adhesive (PAP). The preparation, bonding mechanism and heat resistant property of PAP were studied by using X-ray photoelectron spectroscopy (XPS), Fourier transforms infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetry-differential scanning calorimetry (TG-DSC), nuclear magnetic resonance (NMR) and scanning electron microscopy (SEM). The result showed that covalent bonds between PVA and AP were built. The mechanical properties of PAP improved remarkably; the dry and wet bonding strength are 2.28 and 0.79 MPa with 15.2% and 690% increment, respectively, compared to the control samples. The thermostabilities of PAP and plywood samples were improved. In conclusion, PVA could effectively improve the hygroscopic resistance and low wet bonding strength of AP adhesives.

| S-EPMC9042406 | biostudies-literature

Synthesis and Mechanical Performances of Polyurethane Bio-Based Adhesives Resulted from the Depolymerization of Lignocellulose Biomass.

Project description:The purpose of this study is to valorize biomass waste into products with added value for indoor applications. Thus, broadleaf sawdust was chemically processed by the solvolysis reaction in acid catalysis in the presence of diethylene glycol at 160 °C for 4 h. After filtration and removal of the unreacted biomass, the glycolysis product was used in 6 different polyurethane adhesive formulations for wood bonding. The adhesive films were characterized by FT-IR, TGA, and DMA, while the mechanical performances were investigated by tensile and three-point bending tests. An innovative method for the determination of the working time was proposed. After the displacement of the wood substrates by the tensile test, the bonded area was investigated by SEM analysis. To confirm a correlation between the mechanical performances of the adhesives and their structure/formulation, two-dimensional (2D) simulations were performed based on the tensile tests.

| S-EPMC10586253 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data