Lu-atom-ordered oxonitridoaluminosilicate Ba0.9Ce0.1LuAl0.2Si3.8N6.9O0.1.

ABSTRACT: A single crystal of Ba0.9Ce0.1LuAl0.2Si3.8N6.9O0.1 (barium cerium lutetium aluminosilicate nitride oxide) was obtained by heating a mixed powder of Ba3N2, Si3N4, Al, Lu2O3, and CeO2 at 2173?K for 1?h under N2 gas at 0.85?MPa. X-ray single-crystal structure analysis revealed that the title oxynitride is hexa-gonal (lattice constants: a = 6.0378?(5)?Å, c = 9.8133?(9)?Å; space group: P63 mc) and isostructural with BaYbSi4N7. (Ba,Ce) and Lu atoms occupy twelvefold and sixfold coordination sites, respectively.

SUBMITTER: Simura R

PROVIDER: S-EPMC7643228 | biostudies-literature | 2020 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Lu-atom-ordered oxonitridoaluminosilicate Ba0.9Ce0.1LuAl0.2Si3.8N6.9O0.1.

Simura Rayko R Yamane Hisanori H

Acta crystallographica. Section E, Crystallographic communications 20201006 Pt 11

A single crystal of Ba0.9Ce0.1LuAl0.2Si3.8N6.9O0.1 (barium cerium lutetium aluminosilicate nitride oxide) was obtained by heating a mixed powder of Ba3N2, Si3N4, Al, Lu2O3, and CeO2 at 2173 K for 1 h under N2 gas at 0.85 MPa. X-ray single-crystal structure analysis revealed that the title oxynitride is hexa-gonal (lattice constants: a = ...[more]

PMID: 33209337

Similar Datasets

Plasma engraved Bi0.1(Ba0.5Sr0.5)0.9Co0.8Fe0.2O3-δ perovskite for highly active and durable oxygen evolution.

Project description:The development of highly active and cost-effective catalysts based on noble metal free oxygen electro-catalysis is critical to energy storage and conversion devices. Herein, we highlight a plasma-treated Bi0.1(Ba0.5Sr0.5)0.9Co0.8Fe0.2O3-δ perovskite (denoted as P-Bi0.1BSCF) as a promising catalyst for oxygen evolution reaction (OER) in alkaline media. H2/Ar plasma engraving could significantly increase electrochemically active O22-/O- concentration and tune the electronic structure of Co ions efficiently, and consequently tailor the intrinsic electrocatalytic ability for OER. Of note, P-Bi0.1BSCF, with unique crystalline core/amorphous shell structure, exhibits an enhanced intrinsic OER activity and higher stability than the noble metal IrO2 catalyst, which outperforms most of the reported perovskite catalysts. The present work provides new insights into exploring efficient catalysts for OER, and it suggests that, in addition to the extensively applied for surface treatment of various catalysts such as carbons and metal oxides, the plasma engraved perovskite materials also exhibits great potential as precious metal-free catalysts.

| S-EPMC6414661 | biostudies-literature

Creating Ferromagnetic Insulating La0.9Ba0.1MnO3 Thin Films by Tuning Lateral Coherence Length.

Project description:In this work, heteroepitaxial vertically aligned nanocomposite (VAN) La0.9Ba0.1MnO3 (LBMO)-CeO2 films are engineered to produce ferromagnetic insulating (FMI) films. From combined X-ray photoelectron spectroscopy, X-ray diffraction, and electron microscopy, the elimination of the insulator-metal (I-M) transition is shown to result from the creation of very small lateral coherence lengths (with the corresponding lateral size ∼ 3 nm (∼7 u.c.)) in the LBMO matrix, achieved by engineering a high density of CeO2 nanocolumns in the matrix. The small lateral coherence length leads to a shift in the valence band maximum and reduction of the double exchange (DE) coupling. There is no "dead layer" effect at the smallest achieved lateral coherence length of ∼3 nm. The FMI behavior obtained by lateral dimensional tuning is independent of substrate interactions, thus intrinsic to the film itself and hence not related to film thickness. The unique properties of VAN films give the possibility for multilayer spintronic devices that can be made without interface degradation effects between the layers.

| S-EPMC8023513 | biostudies-literature

Aliovalent-doped sodium chromium oxide (Na0.9Cr0.9Sn0.1O2 and Na0.8Cr0.9Sb0.1O2) for sodium-ion battery cathodes with high-voltage characteristics.

Project description:NaCrO2 with high rate-capability is an attractive cathode material for sodium-ion batteries (NIBs). However, the amount of reversibly extractable Na+ ions is restricted by half, which results in relatively low energy density for practical NIB cathodes. Herein, we describe aliovalent-doped O3-Na0.9[Cr0.9Sn0.1]O2 (NCSnO) and O3-Na0.8[Cr0.9Sb0.1]O2 (NCSbO), both of which show high-voltage characteristics that translate to an increase in energy density. In contrast to NaCrO2, NCSnO and NCSbO can be reversibly charged to 3.80 and 3.95 V, respectively, delivering 0.5 Na+ along with Cr3+/4+ redox alone. The reversible chargeability to Na0.4[Cr0.9Sn0.1]O2 and Na0.3[Cr0.9Sb0.1]O2 is not associated with the suppression of Cr6+ formation. Both compounds show concentrations of Cr6+ that are higher than that of Na0.3CrO2, with an absence of O3' phases. This implies that aliovalent-doping contributes to a suppression of the Cr6+ migration into tetrahedral sites in the interslab space, which reduces the possibility of irreversible comproportionation. NCSnO and NCSbO deliver capacities comparable to that of NaCrO2, but show a higher average discharge voltage (2.94 V for NaCrO2; 3.14 V for NCSnO; 3.21 V for NCSbO), which leads to a noticeable increase in energy densities. The high-voltage characteristics of NCSnO and NCSbO are also validated via density-functional-theory calculations.

| S-EPMC9058423 | biostudies-literature

High-Efficiency Direct Ammonia Fuel Cells Based on BaZr0.1Ce0.7Y0.2O3- ? /Pd Oxide-Metal Junctions.

Project description:A direct ammonia-type intermediate temperature fuel cell is examined by means of a hydrogen membrane fuel cell (HMFC) comprising 1-µm-thick BaZr0.1Ce0.7Y0.2O3- ? (BZCY) thin-film electrolyte and Pd solid anode. It generates the maximum power density of 0.58 W cm-2 at 600 °C with ammonia fuels, and this value is found to be three times larger than the champion data of the recently reported direct ammonia-type proton-conducting ceramic fuel cells (PCFCs). AC impedance spectroscopy is performed to determine the interfacial polarization resistances, disclosing that the anodic overpotentials of HMFCs are at least one order of magnitude smaller than those of anode-supported PCFC under relatively high DC outputs. The anode reactions are driven by the oxidation of monoatomic hydrogen dissolving at the BZCY/Pd solid-solid interface, mediated via proton transfer from Pd to BZCY. The electrochemical analysis reveals that the BZCY/Pd junction forms Ohmic contact without growth of wide depletion layer and thus facilitates the proton transfer reactions because the interfacial region beneath Pd electrode can accommodate amounts of protonic defects as well as the bulk of BZCY due to the small depletion of holes under hole-proton thermodynamic equilibrium.

| S-EPMC6607173 | biostudies-literature

Boosting Upconversion Photoluminescence and Multielectrical Properties via Er-Doping-Modulated Vacancy Control in Ba0.85Ca0.15Ti0.9Zr0.1O3.

Project description:The lead-free 0.5(Ba0.7Ca0.3)TiO3-0.5Ba(Ti0.8Zr0.2)O3 (BCTZ) ceramics with Er doping have shown good upconversion photoluminescence (PL) and desirable optical temperature sensing properties. To bridge a relationship between the structure/intrinsic defects and properties of rare-earth-doped ferroelectrics, we designed and fabricated a series of BCTZ ceramics doped with 1 mol % Er3+ by combining the first-principles calculations and experimental measurements. Theoretically, we discovered that Er can occupy both A sites (i.e., replacing Ba or Ca) and B sites (i.e., replacing Ti or Zr) in the BCTZ lattice and highlighted that the Er-doping-induced vacancy concentration decreases for both the oxygen vacancies (V o) and cation vacancies (V c). Experimentally, the enhanced PL performance and the dielectric, ferroelectric, and piezoelectric properties of the Er-doped BCTZ ceramics have been observed. Finally, the physical origin of Er-induced property enhancement in BCTZ has been elaborated according to the charge density and chemical bonding analysis. These results open up a path to investigate the effects of site substitution and vacancies on optoelectronic properties of multifunctional rare-earth-doped ferroelectrics.

| S-EPMC6648785 | biostudies-literature

Evaluation of High-Temperature Hydrogen Sensors Based on BaCe0.6Zr0.3Y0.1O3-? and Sr(Ce0.9Zr0.1)0.95Yb0.05O3-? Perovskites for Industrial Applications.

Project description:In many industrial fields, there is a need to design and characterize on-line and on-board hydrogen monitoring tools able to operate under extreme conditions. One of these applications is in future nuclear fusion reactors, which will use hydrogen isotopes as a plasma fuel. In this context, the measurement of the concentration of these hydrogen isotopes will be of interest to ensure the correct operating conditions for such reactors. Hydrogen sensors based on solid-state electrolytes will be the first step in the development of new analytical tools able to quantify deuterium and tritium in aggressive environments. In the present work, amperometric hydrogen sensors were constructed and evaluated using two solid-state electrolytes, BaCe0.6Zr0.3Y0.1O3-? and Sr(Ce0.9Zr0.1)0.95Yb0.05O3-?. Prototype sensors were built in order to study their sensitivity in on-line measurements. The experiments were performed in a reactor with a hydrogen-controlled environment. The sensors were evaluated at 500 and 600 °C in amperometric mode by applying 2 and 4 V voltages between electrodes. Both sensors showed increases in sensitivity when the temperature or voltage were increased.

| S-EPMC7766507 | biostudies-literature

Ferromagnetic-like behavior of Bi0.9La0.1FeO3-KBr nanocomposites.

Project description:We studied magnetostatic response of the Bi0.9La0.1FeO3- KBr composites (BLFO-KBr) consisting of nanosized (≈100 nm) ferrite Bi0.9La0.1FeO3 (BLFO) conjugated with fine grinded ionic conducting KBr. When the fraction of KBr is rather small (less than 15 wt%) the magnetic response of the composite is very weak and similar to that observed for the BLFO (pure KBr matrix without Bi1-xLaxFeO3 has no magnetic response as anticipated). However, when the fraction of KBr increases above 15%, the magnetic response of the composite changes substantially and the field dependence of magnetization reveals ferromagnetic-like hysteresis loop with a remanent magnetization about 0.14 emu/g and coercive field about 1.8 Tesla (at room temperature). Nothing similar to the ferromagnetic-like hysteresis loop can be observed in Bi1-zLazFeO3 ceramics with z ≤ 0.15, which magnetization quasi-linearly increases with magnetic field. Different physical mechanisms were considered to explain the unusual experimental results for BLFO-KBr nanocomposites, but only those among them, which are highly sensitive to the interaction of antiferromagnetic Bi0.9La0.1FeO3 with ionic conductor KBr, can be relevant.

| S-EPMC6639540 | biostudies-literature

Atomic Layer Deposition of GdCoO3 and Gd0.9Ca0.1CoO3.

Project description:Thin films of the catalytically interesting ternary and quaternary perovskites GdCoO3 and Gd0.9Ca0.1CoO3 are fabricated by atomic layer deposition using metal ?-diketonates and ozone as precursors. The resulting thin films are amorphous as deposited and become single-oriented crystalline on LaAlO3(100) and YAlO3(100/010) after post-annealing at 650 °C in air. The crystal orientations of the films are tunable by choice and the orientation of the substrate, mitigated through the interface via solid face epitaxy upon annealing. The films exhibit no sign of Co2+. Additionally, high-aspect-ratio Si(100) substrates were used to document the suitability of the developed process for the preparation of coatings on more complex, high-surface-area structures. We believe that coatings of GdCoO3 and Gd1-xCaxCoO3 may find applications within oxidation catalysis.

| S-EPMC6982051 | biostudies-literature

Exploring the Antibacterial and Biosensing Applications of Peroxidase-Mimetic Ni0.1Cu0.9S Nanoflower.

Project description:Nanozymes, as artificial enzymes with the biological action of natural enzymes, have enormous potential in the fields of disease diagnosis, bacteriostasis, biosensing, etc. In this work, the Ni0.1Cu0.9S nanoflower was successfully synthesized through a one-step hydrothermal method. A combined strategy of Ni doping and morphology design was employed to adjust its electronic structure and active sites, endowing the Ni0.1Cu0.9S nanoflower with excellent peroxidase-like activity. Therefore, it can catalyze the decomposition of H2O2 to generate •OH with higher antibacterial activity, establishing a broad-spectrum antibacterial system based on the Ni0.1Cu0.9S nanoflower against E. coli and S. aureus, which avoids the harm of a high concentration of H2O2. Additionally, the colorless substrate TMB can be catalytically oxidized into blue ox-TMB via •OH. As a result, a colorimetric technique with rapid and accurate detection of ascorbic acid (AA) by the unaided eye was designed, in view of the specific inhibition effect towards the oxidation of TMB. This detection platform has a wide linear range (10~800 μM) with a low limit of detection (0.84 μM) and exhibits a satisfactory selectivity toward the detection of AA. This study sheds new light on the application of copper-containing nanozymes in the fields of biomedicine and bioassay.

| S-EPMC9599305 | biostudies-literature

Hydration of Proton-conducting BaCe0.9Y0.1O3-δ by Decoupled Mass Transport.

Project description:Mass relaxation profile of a perovskite-type oxide, BaCe0.9Y0.1O3-δ, was studied to understand decoupled diffusion of oxygen and hydrogen species during hydration/dehydration. The mass relaxation measurements are performed by thermogravimetric analysis (TGA) under various humidity conditions (Dry, -3.0 ≤ log(pH2O/atm) ≤ -1.6) at a constant oxygen partial pressure (log(pO2/atm) = -1.00 ± 0.01). The decoupled ions participated in hydration/dehydration reactions were proven to be at different ratios from the result introduced by the 8R m function. The enthalpy and entropy of non-stoichiometric hydration reaction, which considers each ratio of charge-carrier species, were -144.7 ± 3.7 kJ/mol and -147.8 ± 3.2 J/mol · K, respectively.

| S-EPMC5428669 | biostudies-literature