Lauric Acid Sophorolipid: Accelerating the Gelation of Silk Fibroin.

ABSTRACT: Silk fibroin (SF) hydrogels find wide applications in tissue engineering. However, their scope has been limited due to the long gelation time in ambient conditions. This paper shows the reduction in gelation time of silk fibroin to minutes upon doping with a newly synthesized lauric acid sophorolipid (LASL). LASL comprises a fatty acid, lauric acid (with a 12-carbon aliphatic chain), that is derivatized by glucose molecules using a non-pathogenic yeast Candida bombicola. LASL was characterized using spectroscopic (Fourier transform infrared spectroscopy) and chromatographic (high-performance liquid chromatography, thin-layer chromatography, and high-resolution mass spectrometry) methods. This gelation of SF is comparable to the effect of an anionic surfactant, sodium dodecyl sulfate (SDS). The microstructure of SF-LASL hydrogels was investigated by small-angle neutron scattering (SANS) measurements and exhibited the beads-on-a-necklace model. The rheological properties of these hydrogels show similarity to SF-SDS hydrogels, therefore presenting a greener alternative for tissue engineering applications.

SUBMITTER: Hirlekar S

PROVIDER: S-EPMC7658940 | biostudies-literature | 2020 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Lauric Acid Sophorolipid: Accelerating the Gelation of Silk Fibroin.

Hirlekar Swarali S Ray Debes D Aswal Vinod K VK Prabhune Asmita A AA Nisal Anuya A

ACS omega 20201102 44

Silk fibroin (SF) hydrogels find wide applications in tissue engineering. However, their scope has been limited due to the long gelation time in ambient conditions. This paper shows the reduction in gelation time of silk fibroin to minutes upon doping with a newly synthesized lauric acid sophorolipid (LASL). LASL comprises a fatty acid, lauric acid (with a 12-carbon aliphatic chain), that is derivatized by glucose molecules using a non-pathogenic yeast <i>Candida bombicola</i>. LASL was characte ...[more]

PMID: 33195908

Similar Datasets

Project description:The dissolution of Bombyx mori silk fibroin (SF) films in formic acid (FA) for the preparation of electrospinning dopes is widely exploited to produce electrospun SF scaffolds. The SILKBridge® nerve conduit is an example of medical device having in its wall structure an electrospun component produced from an FA spinning dope. Though highly volatile, residual FA remains trapped into the bulk of the SF nanofibers. The purpose of this work is to investigate the type and strength of the interaction between FA and SF in electrospun mats, to quantify its amount and to evaluate its possible toxicological impact on human health. The presence of residual FA in SF mats was detected by FTIR and Raman spectroscopy (new carbonyl peak at about 1,725 cm-1) and by solid state NMR, which revealed a new carbonyl signal at about 164.3 ppm, attributed to FA by isotopic 13C substitution. Changes occurred also in the spectral ranges of hydroxylated amino acids (Ser and Thr), demonstrating that FA interacted with SF by forming formyl esters. The total amount of FA was determined by HS-GC/MS analysis and accounted for 247 ± 20 μmol/g. The greatest part was present as formyl ester, a small part (about 3%) as free FA. Approximately 17% of the 1,500 μmol/g of hydroxy amino acids (Ser and Thr) theoretically available were involved in the formation of formyl esters. Treatment with alkali (Na2CO3) succeeded to remove the greatest part of FA, but not all. Alkali-treated electrospun SF mats underwent morphological, physical, and mechanical changes. The average diameter of the fibers increased from about 440 nm to about 480 nm, the mat shrunk, became stiffer (the modulus increased from about 5.5 MPa to about 7 MPa), and lost elasticity (the strain decreased from about 1 mm/mm to about 0.8 mm/mm). Biocompatibility studies with human adult dermal fibroblasts did not show significant difference in cell proliferation (313 ± 18 and 309 ± 23 cells/mm2 for untreated and alkali-treated SF mat, respectively) and metabolic activity. An in-depth evaluation of the possible toxicological impact of residual FA was made using the SILKBridge® nerve conduit as case study, following the provisions of the ISO 10993-1 standard. The Potential Patient Daily Intake, calculated from the total amount of FA determined by HS-GC/MS, was 2.4 mg/day and the Tolerable Exposure level was set to 35.4 mg/day. This allowed to obtain a value of the Margin of Safety of 15, indicating that the amount of FA left on SF mats after electrospinning does not raise concerns for human health.

Dataset Information

Lauric Acid Sophorolipid: Accelerating the Gelation of Silk Fibroin.

Publications

Lauric Acid Sophorolipid: Accelerating the Gelation of Silk Fibroin.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets