Dataset Information

The Influence of Different Classes of Amino Acids on Calcium Phosphates Seeded Growth.

ABSTRACT: Amino acids (AAs) attract attention for elucidating the role of proteins in biomineralization and the preparation of functionalized biomaterials. The influence that AAs exert on calcium phosphate (CaP) mineralization is still not completely understood, as contradictory results have been reported. In this paper, the influence of the addition of different classes of AAs, charged (L-aspartic acid, Asp; L-lysine, Lys), polar (L-asparagine, Asn; L-serine, Ser; L-tyrosine, Tyr), and non-polar (L-phenylalanine, Phe), on CaP growth in the presence of octacalcium phosphate (OCP) and calcium hydrogenphosphate dihydrate (DCPD) seeds was investigated. In control systems (without AAs), a calcium-deficient apatite (CaDHA) layer was formed on the surface of OCP, while a mixture of CaDHA and OCP in the form of spherical aggregates was formed on the surface of DCPD crystals. Charged and non-polar promoted, while polar AAs inhibited CaDHA formation on the OCP seeds. In the case of DCPD, Lys, Asp, and Phe promoted CaP formation, while the influence of other AAs was negligible. The most efficient promotor of precipitation in both cases was non-polar Phe. No significant influence of AAs on the composition and morphology of precipitates was observed. The obtained results are of interest for understanding biomineralization processes and additive controlled material synthesis.

SUBMITTER: Mihelj Josipovic T

PROVIDER: S-EPMC7662258 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The Influence of Different Classes of Amino Acids on Calcium Phosphates Seeded Growth.

Mihelj Josipović Tea T Kovačević Monika M Mateša Sarah S Kostešić Marina M Matijaković Nives N Radatović Borna B Lyons Daniel M DM Kralj Damir D Dutour Sikirić Maja M

Materials (Basel, Switzerland) 20201027 21

Amino acids (AAs) attract attention for elucidating the role of proteins in biomineralization and the preparation of functionalized biomaterials. The influence that AAs exert on calcium phosphate (CaP) mineralization is still not completely understood, as contradictory results have been reported. In this paper, the influence of the addition of different classes of AAs, charged (L-aspartic acid, Asp; L-lysine, Lys), polar (L-asparagine, Asn; L-serine, Ser; L-tyrosine, Tyr), and non-polar (L-pheny ...[more]

PMID: 33121165

Similar Datasets

Project description:PurposeThis study developed light cured dental composites with added monocalcium phosphate monohydrate (MCPM), tristrontium phosphate (TSrP) and antimicrobial polylysine (PLS). The aim was to produce composites that have enhanced water sorption induced expansion, can promote apatite precipitation and release polylysine.Materials and methodsExperimental composite formulations consisted of light activated dimethacrylate monomers combined with 80 wt% powder. The powder phase contained a dental glass with and without PLS (2.5 wt%) and/or reactive phosphate fillers (15 wt% TSrP and 10 wt% MCPM). The commercial composite, Z250, was used as a control. Monomer conversion and calculated polymerization shrinkage were assessed using FTIR. Subsequent mass or volume changes in water versus simulated body fluid (SBF) were quantified using gravimetric studies. These were used, along with Raman and SEM, to assess apatite precipitation on the composite surface. PLS release was determined using UV spectroscopy. Furthermore, biaxial flexural strengths after 24 hours of SBF immersion were obtained.ResultsMonomer conversion of the composites decreased upon the addition of phosphate fillers (from 76 to 64%) but was always higher than that of Z250 (54%). Phosphate addition increased water sorption induced expansion from 2 to 4% helping to balance the calculated polymerization shrinkage of ~ 3.4%. Phosphate addition promoted apatite precipitation from SBF. Polylysine increased the apatite layer thickness from ~ 10 to 20 μm after 4 weeks. The novel composites showed a burst release of PLS (3.7%) followed by diffusion-controlled release irrespective of phosphate addition. PLS and phosphates decreased strength from 154 MPa on average by 17% and 18%, respectively. All formulations, however, had greater strength than the ISO 4049 requirement of > 80 MPa.ConclusionThe addition of MCPM with TSrP promoted hygroscopic expansion, and apatite formation. These properties are expected to help compensate polymerization shrinkage and help remineralize demineralized dentin. Polylysine can be released from the composites at early time. This may kill residual bacteria.

Dataset Information

The Influence of Different Classes of Amino Acids on Calcium Phosphates Seeded Growth.

Publications

The Influence of Different Classes of Amino Acids on Calcium Phosphates Seeded Growth.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets