Polymer Ligands Derived from Jute Fiber for Heavy Metal Removal from Electroplating Wastewater.

ABSTRACT: Industrial operations, domestic and agricultural activities worldwide have had major problems with various contaminants caused by environmental pollution. Heavy metal pollution in wastewater also a prominent issue; therefore, a well built and economical treatment technology is demanded for pollution-free wastewater. The present work emphasized pure cellulose extracted from jute fiber and further modification was performed by a free radical grafting reaction, which resulted in poly(methyl acrylate) (PMA)-grafted cellulose and poly(acrylonitrile)-grafted cellulose. Subsequently, poly(hydroxamic acid) and poly(amidoxime) ligands were prepared from the PMA-grafted cellulose and PAN-grafted cellulose, respectively. An adsorption study was performed using the desired ligands with heavy metals such as copper, cobalt, chromium and nickel ions. The binding capacity (qe) with copper ions for poly(hydroxamic acid) is 352 mg g-1 whereas qe for poly(amidoxime) ligand it was exhibited as 310 mg g-1. Other metal ions (chromium, cobalt and nickel) show significance binding properties at pH 6. The Langmuir and Freundlich isotherm study was also performed. The Freundlich isotherm model showed good correlation coefficients for all metal ions, indicating that multiple-layers adsorption was occurred by the polymer ligands. The reusability was evaluated and the adsorbents can be reused for 7 cycles without significant loss of removal performance. Both ligands showed outstanding metals removal capacity from the industrial wastewater as such 98% of copper can be removed from electroplating wastewater and other metals (cobalt, chromium, nickel and lead) can also be removed up to 90%.

SUBMITTER: Rahman ML

PROVIDER: S-EPMC7692318 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Polymer Ligands Derived from Jute Fiber for Heavy Metal Removal from Electroplating Wastewater.

Rahman Md Lutfor ML Fui Choong Jian CJ Ting Tang Xin TX Sarjadi Mohd Sani MS Arshad Sazmal E SE Musta Baba B

Polymers 20201029 11

Industrial operations, domestic and agricultural activities worldwide have had major problems with various contaminants caused by environmental pollution. Heavy metal pollution in wastewater also a prominent issue; therefore, a well built and economical treatment technology is demanded for pollution-free wastewater. The present work emphasized pure cellulose extracted from jute fiber and further modification was performed by a free radical grafting reaction, which resulted in poly(methyl acrylat ...[more]

PMID: 33137923

Similar Datasets

Project description:Activated carbon (AC) fiber is a carbonaceous material with a porous structure that has a tremendous scope of application in different fields. Conventionally, AC is derived from fossil fuel-based raw materials like polyacrylonitrile (PAN) and pitch. In this work, AC was synthesized from eco-friendly, renewable, and ubiquitous jute fiber. Systematically, the jute fiber was washed and pretreated with NaOH. Raw jute and NaOH-treated jute were carbonized/pyrolyzed at 500 °C for 1 h in presence of N2 gas. The carbonized carbon was activated with H3PO4 and KOH and again pyrolyzed at 650 °C for 1.5 h maintaining the inert condition. The different features of activated carbons were characterized with field emission-scanning electron microscope, energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray diffraction (XRD), and thermogravimetric analysis. The average yield of carbonized and activated carbons was recorded at 19 and 13.8%, respectively. The scanning electron microscopic images confirmed a honeycomb-like porous structure. It was observed that KOH-activated carbon exhibited a more porous structure than the H3PO4-activated carbons. The average pore diameter of activated carbons was noted to be 1.3 μm. The pore density was higher in case of KOH-activated carbons accounting for 2.15 pore/μm. The EDX analysis showed that H3PO4-activated carbons had more than 90% carbon atoms indicating a significant carbon content. The TEM images revealed that AC particles were in the nanoscale range. The average particle sizes of H3PO4-activated carbon and KOH-activated carbon were 36.38 and 32.8 nm, respectively. The XRD study demonstrated the highly disordered and low level of crystallinity of AC. It was detected that the AC showed much higher thermal resistance than the jute fiber. The H3PO4-activated carbon obtained from NaOH-treated jute remained at 84% even after 500 °C. A higher thermal resistance was achieved with H3PO4-activated carbon since it contains 0.56% phosphorus, which was confirmed by EDX investigation. It was found that a higher carbon yield was obtained from NaOH-treated jute. The porous structure of the material showed that it could be used as an adsorbent. Due to its high thermal stability, it is recommended for flame retardants and heat insulation applications as well.

Dataset Information

Polymer Ligands Derived from Jute Fiber for Heavy Metal Removal from Electroplating Wastewater.

Publications

Polymer Ligands Derived from Jute Fiber for Heavy Metal Removal from Electroplating Wastewater.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets