Chitosan Modified Cationic Polyacrylamide Initiated by UV-H₂O₂ for Sludge Flocculation and New Insight on the Floc Characteristics Study.

ABSTRACT: In the present study, a novel graft modified flocculant CTS-g-PAMD was synthesized and applied to conduct sludge conditioning and dewatering. CTS-g-PAMD was copolymerized with AM, DMC and chitosan (CTS) under UV-H₂O₂ initiation. In addition, the effects of single factor experiments on the molecular weight (MW) CTS grafting efficiency (GE) of CTS-g-PAMD were determined and the optimal copolymerization conditions were achieved. The GE of CTS-g-PAMD reached 91.1% and the MW was 4.82 × 10⁶ Da. As revealed from the characterized results of Fourier-transform infrared spectra (FT-IR), ¹H/ NMR, X-ray diffraction (XRD), scanning electron microscopic (SEM) and X-ray photoelectron spectroscopy (XPS), the successful synthesis of CTS-g-PAMD was confirmed, which is considered to be conducive to explaining sludge dewatering performance. Under the optimal conditions (pH = 7.0, flocculant dosage = 35 mg/L), the best flocculating performance (FCMC: 73.7%; SRF: 4.7 × 10¹² m·kg^-1, turbidity: 9.4 NTU) and large and dense sludge flocs (floc size d₅₀ = 379.142 µm, floc fractal dimension D_f = 1.58) were formed. The DMC and CTS chain segments exhibiting cationic properties significantly improved the positive charge density and enhanced the electrical patching effect of CTS-g-PAMD. The long molecular chain of CTS-g-PAMD exhibited superior extensibility, which enhanced bridging effect on adsorption. Moreover, the sludge floc after undergoing CTS-g-PAMD conditioning exhibited robust shear resistance and regeneration ability. After the sludge floc was crushed and broken, a large and dense sludge floc was formed, helping significantly reduce the sludge specific resistance (SRF), turbidity and cake moisture content (FCMC) and enhance the sludge dewatering effect. The novel CTS-g-PAMD flocculant shows promising practical applications and high market value.

SUBMITTER: Chen J

PROVIDER: S-EPMC7698928 | biostudies-literature | 2020 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Chitosan Modified Cationic Polyacrylamide Initiated by UV-H2O2 for Sludge Flocculation and New Insight on the Floc Characteristics Study.

Chen Jie J Xu Xiaojun X Nie Rui R Feng Li L Li Xuhao X Liu Bingzhi B

Polymers 20201118 11

In the present study, a novel graft modified flocculant CTS-g-PAMD was synthesized and applied to conduct sludge conditioning and dewatering. CTS-g-PAMD was copolymerized with AM, DMC and chitosan (CTS) under UV-H2O2 initiation. In addition, the effects of single factor experiments on the molecular weight (MW) CTS grafting efficiency (GE) of CTS-g-PAMD were determined and the optimal copolymerization conditions were achieved. The GE of CTS-g-PAMD reached 91.1% and the MW wa ...[more]

PMID: 33218149

Similar Datasets

Project description:BackgroundCationic polyacrylamide copolymers (PAMs) are used for sludge dewatering in municipal waste water treatment and might enter the environment by spreading of the sludge on agricultural land. Concern has been expressed since little is known about the degradation of PAMs in soils. To obtain detailed information on the polymer's fate in the soil compartment, the degradation of 14C-radiolabelled PAM in an outdoor lysimeter was studied.ResultsNo plant uptake and leaching of radioactivity was observed. There was practically no vertical movement of polymer and no transformation products found at the end of the study. For the top 10 cm soil layer, a mass balance was established throughout the study. About 10% of applied radioactivity was not extractable from soil even with a matrix destructive method, and this was concluded to be bound residue. Characterization of extractable radioactivity by means of GPC-analysis showed a significant decrease of the molecular weight of the PAM with time. The decrease in molecular weight indicates a breakdown of the polymer backbone (the C-C-chain), and is assumed to be primary degradation. The total radioactivity content in the 10 cm top soil layer was quantified every 6 months over a period of 3 years. The results show a significant decrease of the total radioactivity over time and this is defined as ultimate degradation following the definition of OECD and EPA. Based on the data, a half-life time of 2.0 × 103 days and a rate constant of 0.00035/day were calculated. With a χ2 of 12.0 the results of the calculation are thus valid and reliable. The rate constant indicates a mineralization of 22.5% within a period of 2 years based on the total recovered radioactivity. This half-life time is solely based on mineralization and does not take into account the degradation of the polymer backbone, hydrolysis of the side chains, incorporation into the soil matrix, and thus is a conservative approach.Conclusions14C-PAM degrades very slowly in soil after land-spreading as a component of sewage sludge. Even in a very conservative evaluation which only considered the loss of radioactivity, a half-life time of 5.4 years was determined.

Dataset Information

Chitosan Modified Cationic Polyacrylamide Initiated by UV-H₂O₂ for Sludge Flocculation and New Insight on the Floc Characteristics Study.

Publications

Chitosan Modified Cationic Polyacrylamide Initiated by UV-H<sub>2</sub>O<sub>2</sub> for Sludge Flocculation and New Insight on the Floc Characteristics Study.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets