Chemical Recycling of End-of-Life Poly(lactide) via Zinc-Catalyzed Depolymerization and Polymerization.

ABSTRACT: The chemical recycling of poly(lactide) was investigated based on depolymerization and polymerization processes. Using methanol as depolymerization reagent and zinc salts as catalyst, poly(lactide) was depolymerized to methyl lactate applying microwave heating. An excellent performance was observed for zinc(II) acetate with turnover frequencies of up to 45000?h^-1. In a second step the monomer methyl lactate was converted to (pre)poly(lactide) in the presence of catalytic amounts of zinc salts. Here zinc(II) triflate revealed excellent performance for the polymerization process (yield: 91?%, M_n ?8970?g/mol). Moreover, the (pre)poly(lactide) was depolymerized to lactide, the industrial relevant molecule for accessing high molecular weight poly(lactide), using zinc(II) acetate as catalyst.

SUBMITTER: Cheung E

PROVIDER: S-EPMC7705614 | biostudies-literature | 2020 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Chemical Recycling of End-of-Life Poly(lactide) via Zinc-Catalyzed Depolymerization and Polymerization.

Cheung Even E Alberti Christoph C Enthaler Stephan S

ChemistryOpen 20201102 12

The chemical recycling of poly(lactide) was investigated based on depolymerization and polymerization processes. Using methanol as depolymerization reagent and zinc salts as catalyst, poly(lactide) was depolymerized to methyl lactate applying microwave heating. An excellent performance was observed for zinc(II) acetate with turnover frequencies of up to 45000 h-1. In a second step the monomer methyl lactate was converted to (pre)poly(lactide) in the presence of catalytic amounts of zi ...[more]

PMID: 33304737

Similar Datasets

Hydrogenative Depolymerization of End-of-Life Poly-(Bisphenol A Carbonate) Catalyzed by a Ruthenium-MACHO-Complex.

Project description:The valorization of waste to valuable chemicals can contribute to a more resource-efficient and circular chemistry. In this regard, the selective degradation of end-of-life polymers/plastics to produce useful chemical building blocks can be a promising target. We have investigated the hydrogenative depolymerization of end-of-life poly(bisphenol A carbonate). Applying catalytic amounts of the commercial available Ruthenium-MACHO-BH complex the end-of-life polycarbonate was converted to bisphenol A and methanol. Importantly, bisphenol A can be reprocessed for the manufacture of new poly-(bisphenol A carbonate) and methanol can be utilized as energy storage material.

| S-EPMC6905177 | biostudies-literature

Zinc-Catalyzed Highly Isoselective Ring Opening Polymerization of rac-Lactide.

Project description:A family of chiral zinc amido-oxazolinate complexes are shown to be highly active and isoselective initiators for the ring-opening polymerization (ROP) of rac-lactide, yielding isotactic stereoblock polylactides (PLA) with Pm up to 0.91. This represents the highest isoselectivity observed with zinc-based catalysts for ROP of rac-lactide.

| S-EPMC4105174 | biostudies-literature

Recycling of End-of-Life Poly(bisphenol A carbonate) via Alkali Metal Halide-Catalyzed Phenolysis.

Project description:The chemical recycling of end-of-life plastic waste streams can contribute to a resource-conserving and sustainable society. This matter of recycling is composed of a sequence of depolymerization and subsequent polymerization reactions. In this regard, we have studied the chemical recycling of end-of-life poly(bisphenol A carbonate) applying phenol as depolymerization reagent. In the presence of catalytic amounts of alkali metal halides as products bisphenol A and diphenyl carbonate were obtained in excellent turnover frequencies of up to 1392 h-1 and short reaction times. These depolymerization products offer the straightforward possibility to close the cycle by producing new poly(bisphenol A carbonate) and as second product phenol, which can be reused for further depolymerizations.

| S-EPMC6604237 | biostudies-literature

Heterolepic ?-Ketoiminate Zinc Phenoxide Complexes as Efficient Catalysts for the Ring Opening Polymerization of Lactide.

Project description:Zinc phenoxide complexes L1ZnOAr 1-4 (L1=Me2NC2H4NC(Me)CHC(Me)O) and L2ZnOAr 5-8 (L2=Me2NC3H6NC(Me)CHC(Me)O) with donor-functionalized ?-ketoiminate ligands (L1/2) and OAr substituents (Ar=Ph 1, 5; 2,6-Me2-C6H3 2, 6; 3,5-Me2-C6H3 3, 7; 4-Bu-C6H4 4, 8) with tuneable electronic and steric properties were synthesized and characterized. 1-8 adopt binuclear structures in the solid state except for 5, while they are monomeric in CDCl3 solution. 1-8 are active catalysts for the ring opening polymerization (ROP) of lactide (LA) in CH2Cl2 at ambient temperature and the catalytic activity is controlled by the electronic and steric properties of the OAr substituent, yielding polymers with high average molecular weight (M n) and moderately controlled molecular weight distribution (MWDs). 1 and 5 showed a living polymerization character and kinetic studies on the ROP of L-LA with 1 and 5 proved first order dependencies on the monomer concentration. Homonuclear decoupled 1H-NMR analyses of polylactic acid (PLA) formed with rac-LA proved isotactic enrichment of the PLA microstructure.

| S-EPMC6625107 | biostudies-literature

Ring-Opening Polymerization of L-Lactide Catalyzed by Potassium-Based Complexes: Mechanistic Studies.

Project description:Two non-toxic potassium compounds, 1 and 2, with a commercial oximate ligand have been prepared and fully spectroscopically characterized. Their activity as catalysts for the ring-opening polymerization (ROP) process of LLA has been studied, showing that they are extremely active and able to polymerize the monomer in a few minutes. For derivative 2, the presence of a crown ether in the potassium coordination sphere affects the nuclearity of the compound and consequently its solubility, with both aspects having an influence in the polymerization process. Detailed studies of the polymerization mechanism have been performed, and an unusual anionic mechanism was observed in absence of a co-initiator. Indeed, the monomer deprotonation generates a lactide enolate, which initiates the polymerization propagation. On the contrary, when a 1:1 ratio of cat:BnOH is used, a mixture of mechanisms is observed, the anionic mechanism and the activated monomer one, while from a cat:BnOH ratio of 1:2 and over, only the activated monomer mechanism is observed.

| S-EPMC9329769 | biostudies-literature

Hydrogenative Depolymerization of End-of-Life Polycarbonates by an Iron Pincer Complex.

Project description:Chemical recycling processes can contribute to a resource-efficient plastic economy. Herein, a procedure for the iron-catalyzed hydrogenation of the carbonate function of end-of-life polycarbonates under simultaneous depolymerization is presented. The use of a straightforward iron pincer complex leads to high rate of depolymerization of poly(bisphenol A carbonate) and poly(propylene carbonate) yielding the monomers bisphenol A and 1,2-propanediol, respectively, as products under mild reaction conditions. Furthermore, the iron complex was able to depolymerize polycarbonates containing goods and mixture of plastics containing polycarbonates.

| S-EPMC7418100 | biostudies-literature

Efficient Bulky Organo-Zinc Scorpionates for the Stereoselective Production of Poly(rac-lactide)s.

Project description:The direct reaction of the highly sterically demanding acetamidinate-based NNN'-scorpionate protioligand Hphbptamd [Hphbptamd = N,N'-di-p-tolylbis(3,5-di-tertbutylpyrazole-1-yl)acetamidine] with one equiv. of ZnMe2 proceeds in high yield to the mononuclear alkyl zinc complex [ZnMe(κ3-phbptamd)] (1). Alternatively, the treatment of the corresponding lithium precursor [Li(phbptamd)(THF)] with ZnCl2 yielded the halide complex [ZnCl(κ3-phbptamd)] (2). The X-ray crystal structure of 1 confirmed unambiguously a mononuclear entity in these complexes, with the zinc centre arranged with a pseudotetrahedral environment and the scorpionate ligand in a κ3-coordination mode. Interestingly, the inexpensive, low-toxic and easily prepared complexes 1 and 2 resulted in highly efficient catalysts for the ring-opening polymerisation of lactides, a sustainable bio-resourced process industrially demanded. Thus, complex 1 behaved as a single-component robust initiator for the living and immortal ROP of rac-lactide under very mild conditions after a few hours, reaching a TOF value up to 5520 h-1 under bulk conditions. Preliminary kinetic studies revealed apparent zero-order dependence on monomer concentration in the absence of a cocatalyst. The PLA materials produced exhibited narrow dispersity values, good agreement between the experimental Mn values and monomer/benzyl alcohol ratios, as well as enhanced levels of heteroselectivity, reaching Ps values up to 0.74.

| S-EPMC8309543 | biostudies-literature

Switchable Polymerization Catalysis Using a Tin(II) Catalyst and Commercial Monomers to Toughen Poly(l-lactide).

Project description:Sustainable plastics sourced without virgin petrochemicals, that are easily recyclable and with potential for degradation at end of life, are urgently needed. Here, copolymersand blends meeting these criteria are efficiently prepared using a single catalyst and existing commercial monomers l-lactide, propylene oxide, and maleic anhydride. The selective, one-reactor polymerization applies an industry-relevant tin(II) catalyst. Tapered, miscible block polyesters are formed with alkene groups which are postfunctionalized to modulate the polymer glass transition temperature. The polymers are blended at desirable low weight fractions (2 wt %) with commercial poly(l-lactide) (PLLA), increasing toughness, and elongation at break without compromising the elastic modulus, tensile strength, or thermal properties. The selective polymerization catalysis, using commercial monomers and catalyst, provides a straightforward means to improve bioplastics performances.

| S-EPMC8296665 | biostudies-literature

Functional lactide monomers: methodology and polymerization.

Project description:Side-chain-functionalized lactide analogues have been synthesized from commercially available amino acids and polymerized using stannous octoate as a catalyst. The synthetic strategy presented allows for the incorporation of any protected amino acid for the preparation of functionalized diastereomerically pure lactide monomers. The resulting functionalized cyclic monomers can be homopolymerized and copolymerized with lactides and then quantitatively deprotected forming new functional poly(lactide)-based materials. This strategy allows for the introduction of functional groups along a poly(lactide) (PLA) backbone that after deprotection can be viewed as chemical handles for further functionalization of PLA, yielding improved biomaterials for a variety of applications.

| S-EPMC2535916 | biostudies-literature

Chemical Degradation of End-of-Life Poly(lactic acid) into Methyl Lactate by a Zn(II) Complex.

Project description:The catalyzed methanolysis of end-of-life poly(lactic acid) (PLA) products by an ethylenediamine Zn(II) complex to form biodegradable methyl lactate was studied experimentally at 70, 90, and 110 °C. The PLA samples consisted of typical consumer waste materials, including a cup, a toy, and a three-dimensional (3D) printing material. High selectivities and yields (>94%) were possible depending on temperature and reaction time. Additionally, and to develop a predictive kinetic model, kinetic parameters (pre-exponential factor and activation energies) of the PLA transesterification reaction were first obtained from virgin PLA. These parameters were subsequently used to estimate the conversion of PLA, selectivity, and yield of methyl lactate after 1 and 4 h of the reaction, and the results were compared with the experimental values of the end-of-life PLA. Despite the presence of unknown additives in the PLA waste material and uncontrolled particle size, the model was able to predict the overall conversion, selectivity, and yield to an average deviation of 5, 7, and 12%, respectively. A greater agreement between the model and experimental values is observed for the higher temperatures and the longer reaction time. Larger deviations were observed for the PLA toy, which we attribute to the presence of additives, since despite its lower molecular weight, it possessed a higher structural strength.

| S-EPMC7304880 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data