Hierarchical Metal-Organic Framework Films with Controllable Meso/Macroporosity.

ABSTRACT: The structuring of the metal-organic framework material ZIF-8 as films and membranes through the vapor-phase conversion of ZnO fractal nanoparticle networks is reported. The extrinsic porosity of the resulting materials can be tuned from 4% to 66%, and the film thickness can be controlled from 80 nm to 0.23 mm, for areas >100 cm². Freestanding and pure metal-organic frameworks (MOF) membranes prepared this way are showcased as separators that minimize capacity fading in model Li-S batteries.

SUBMITTER: Bo R

PROVIDER: S-EPMC7740079 | biostudies-literature | 2020 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Hierarchical Metal-Organic Framework Films with Controllable Meso/Macroporosity.

Bo Renheng R Taheri Mahdiar M Liu Borui B Ricco Raffaele R Chen Hongjun H Amenitsch Heinz H Fusco Zelio Z Tsuzuki Takuya T Yu Guihua G Ameloot Rob R Falcaro Paolo P Tricoli Antonio A

Advanced science (Weinheim, Baden-Wurttemberg, Germany) 20201113 24

The structuring of the metal-organic framework material ZIF-8 as films and membranes through the vapor-phase conversion of ZnO fractal nanoparticle networks is reported. The extrinsic porosity of the resulting materials can be tuned from 4% to 66%, and the film thickness can be controlled from 80 nm to 0.23 mm, for areas >100 cm<sup>2</sup>. Freestanding and pure metal-organic frameworks (MOF) membranes prepared this way are showcased as separators that minimize capacity fading in model Li-S bat ...[more]

PMID: 33344131

Similar Datasets

Electrostatic Design of Polar Metal-Organic Framework Thin Films.

Project description:In recent years, optical and electronic properties of metal-organic frameworks (MOFs) have increasingly shifted into the focus of interest of the scientific community. Here, we discuss a strategy for conveniently tuning these properties through electrostatic design. More specifically, based on quantum-mechanical simulations, we suggest an approach for creating a gradient of the electrostatic potential within a MOF thin film, exploiting collective electrostatic effects. With a suitable orientation of polar apical linkers, the resulting non-centrosymmetric packing results in an energy staircase of the frontier electronic states reminiscent of the situation in a pin-photodiode. The observed one dimensional gradient of the electrostatic potential causes a closure of the global energy gap and also shifts core-level energies by an amount equaling the size of the original band gap. The realization of such assemblies could be based on so-called pillared layer MOFs fabricated in an oriented fashion on a solid substrate employing layer by layer growth techniques. In this context, the simulations provide guidelines regarding the design of the polar apical linker molecules that would allow the realization of MOF thin films with the (vast majority of the) molecular dipole moments pointing in the same direction.

| S-EPMC7761790 | biostudies-literature

Infrared crystallography for framework and linker orientation in metal-organic framework films.

Project description:Pore alignment and linker orientation influence diffusion and guest molecule interactions in metal-organic frameworks (MOFs) and play a pivotal role for successful utilization of MOFs. The crystallographic orientation and the degree of orientation of MOF films are generally determined using X-ray diffraction. However, diffraction methods reach their limit when it comes to very thin films, identification of chemical connectivity or the orientation of organic functional groups in MOFs. Cu-based 2D MOF and 3D MOF films prepared via layer-by-layer method and from aligned Cu(OH)2 substrates were studied with polarization-dependent Fourier-transform infrared (FTIR) spectroscopy in transmission and attenuated total reflection configuration. Thereby, the degrees for in-plane and out-of-plane orientation, the aromatic linker orientation and the initial alignment during layer-by-layer MOF growth, which is impossible to investigate by laboratory XRD equipment, was determined. Experimental IR spectra correlate with theoretical explanations, paving the way to expand the principle of IR crystallography to oriented, organic-inorganic hybrid films beyond MOFs.

| S-EPMC8278957 | biostudies-literature

Mixed hierarchical local structure in a disordered metal-organic framework.

Project description:Amorphous metal-organic frameworks (MOFs) are an emerging class of materials. However, their structural characterisation represents a significant challenge. Fe-BTC, and the commercial equivalent Basolite® F300, are MOFs with incredibly diverse catalytic ability, yet their disordered structures remain poorly understood. Here, we use advanced electron microscopy to identify a nanocomposite structure of Fe-BTC where nanocrystalline domains are embedded within an amorphous matrix, whilst synchrotron total scattering measurements reveal the extent of local atomic order within Fe-BTC. We use a polymerisation-based algorithm to generate an atomistic structure for Fe-BTC, the first example of this methodology applied to the amorphous MOF field outside the well-studied zeolitic imidazolate framework family. This demonstrates the applicability of this computational approach towards the modelling of other amorphous MOF systems with potential generality towards all MOF chemistries and connectivities. We find that the structures of Fe-BTC and Basolite® F300 can be represented by models containing a mixture of short- and medium-range order with a greater proportion of medium-range order in Basolite® F300 than in Fe-BTC. We conclude by discussing how our approach may allow for high-throughput computational discovery of functional, amorphous MOFs.

| S-EPMC8024318 | biostudies-literature

Seed-mediated evolution of hierarchical metal-organic framework quaternary superstructures.

Project description:The idea of hierarchy, widely observed in natural and artificial worlds, has been extensively explored in chemistry and materials science. Similar to proteins which contain primary, secondary, tertiary and quaternary structures, varying levels of hierarchy in metal-organic framework (MOF) superstructures can also be achieved. In this work, we initiate a systematic study on the morphological evolution of hierarchical superstructures with the assistance of seeded growth and explore the assembly of multiple modular MOFs into superstructures with enhanced hierarchy and diversity. By utilizing MOF-74-III spherulite superstructures as seeds, multiple quaternary architectures were obtained depending on the lengths of organic linker precursors. The resulting superstructures with superior hierarchy represent a unique porous material which contains multiple modules with diverse morphologies. To the best of our knowledge, this is the first report that utilizes tertiary superstructures as seeds in MOF synthesis, which leads to unusual and diverse behaviors during secondary growth. This synthetic approach not only provides a facile method to establish hierarchy in porous materials, but also enables the fabrication of multiscale heterostructures through secondary growth on MOF seeds.

| S-EPMC7069373 | biostudies-literature

Comparison of Fabrication Methods of Metal-Organic Framework Optical Thin Films.

Project description:Homogeneous metal-organic frameworks (MOFs)-based optical thin films have attracted increasing attention, since they can potentially be used as active components in optical/opt-electrical devices, and how to fabricate MOF thin films with high quality is the premise of practically using them. Herein, five fabrication methods of MOF films are systematically investigated and compared from the aspects of appearance, reflectivity, micro-morphology, surface roughness, and optical properties of the films. The famous robust Zr-based MOF, UiO-66 (UiO = University of Oslo) is chosen as a model, and the five methods are spin-coating, dip-coating, self-assembly, direct growth, and the stepwise layer by layer growth method. This study provides fundamental support for the application of MOFs in the optical field.

| S-EPMC6164412 | biostudies-literature

Thin Films of Metal-Organic Framework Interfaces Obtained by Laser Evaporation.

Project description:Properties such as large surface area, high pore volume, high chemical and thermal stability, and structural flexibility render zeolitic imidazolate frameworks (ZIFs) well-suited materials for gas separation, chemical sensors, and optical and electrical devices. For such applications, film processing is a prerequisite. Herein, matrix-assisted pulsed laser evaporation (MAPLE) was successfully used as a single-step deposition process to fabricate ZIF-8 films. By correlating laser fluency and controlling the specific transfer of lab-synthesized ZIF-8, films with user-controlled physical and chemical properties were obtained. Films' characteristics were evaluated by scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectroscopy, X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and X-ray photoelectron spectroscopy (XPS). The analysis showed that frameworks of ZIF-8 can be deposited successfully and controllably to yield polycrystalline films. The deposited films maintained the integrity of the individual ZIF-8 framework, while undergoing minor crystalline and surface chemistry changes. No significant changes in particle size were observed. Our study demonstrated control over both the MAPLE deposition conditions and the outcome, as well as the suitability of the listed deposition method to create composite architectures that could potentially be used in applications ranging from selective membranes to gas sensors.

| S-EPMC8224316 | biostudies-literature

Metal organic framework synthesis in the presence of surfactants: towards hierarchical MOFs?

Project description:The effect of synthesis pH and H2O/EtOH molar ratio on the textural properties of different aluminium trimesate metal organic frameworks (MOFs) prepared in the presence of the well-known cationic surfactant cetyltrimethylammonium bromide (CTAB) at 120 °C was studied with the purpose of obtaining a MOF with hierarchical pore structure. Depending on the pH and the solvent used, different topologies were obtained (namely, MIL-96, MIL-100 and MIL-110). On the one hand, MIL-110 was obtained at lower temperatures than those commonly reported in the literature and without additives to control the pH; on the other hand, MIL-100 with crystallite sizes as small as 30 ± 10 nm could be easily synthesized in a mixture of H2O and EtOH with a H2O/EtOH molar ratio of 3.4 at pH 2.6 in the presence of CTAB. The resulting material displays a hierarchical porosity that combines the microporosity from the MOF and the non-ordered mesopores defined in between the MOF nanoparticles. Interestingly, the maximum of the pore size distribution could be varied between 3 and 33 nm. Finally, at pH 2.5 and using water as a solvent, platelets of MIL-96, a morphology never observed before for this MOF, were synthesized with a (001) preferential crystal orientation, the (001) plane running parallel to the bipyramidal cages of the MIL-96 topology.

| S-EPMC4456781 | biostudies-literature

Nanostructured and oriented metal-organic framework films enabling extreme surface wetting properties.

Project description:We report on the synthesis of highly oriented and nanostructured metal-organic framework (MOF) films featuring extreme surface wetting properties. The Ni- and Co- derivatives of the metal-catecholate series (M-CAT-1) were synthesized as highly crystalline bulk materials and thin films. Oriented pillar-like nanostructured M-CAT-1 films exhibiting pronounced needle-like morphology on gold substrates were established by incorporating a crystallization promoter into the film synthesis. These nanostructured M-CAT-1 MOF films feature extreme wetting phenomena, specifically superhydrophilic and underwater superoleophobic properties with water and underwater oil-contact angles of 0° and up to 174°, respectively. The self-cleaning capability of the nanostructured, needle-like M-CAT-1 films was illustrated by measuring time-dependent oil droplet rolling-off a tilted surface. The deposition of the nanostructured Ni-CAT-1 film on a large glass substrate allowed for the realization of an efficient, transparent, antifog coating, enabling a clear view even at extreme temperature gaps up to ?120 °C. This work illustrates the strong link between MOF film morphology and surface properties based on these framework materials.

| S-EPMC6808203 | biostudies-literature

Convergent and Divergent Paired Electrodeposition of Metal-Organic Framework Thin Films.

Project description:Employing the environmentally friendly methods for synthesis of the metal-organic frameworks (MOFs) is an urgent need and sustainable development in the synthesis of these compounds is essential. In this way, ignoring the counter electrode reaction is a potentially negative point from green chemistry standpoint which increases some issues like energy consumption and reaction time. We wish to introduce the "paired electrodeposition" (PED) technique as a new method for the simultaneous synthesis and deposition of the MOF thin films (MOFTFs). This protocol implements the uniform pattern of two MOFTF modified substrates by "convergent (CPED: Zna/Znc-MOFTFs) and divergent (DPED: Cua/Znc-MOFTFs) paired electrodeposition" via a one-step synthesis. With the rule of thumb, enhanced energy efficiency and atom economy, increasing electrochemical yield, time-saving along with a variety of products are advantages of this technique. Besides, the "Electrode Modification Efficiency" has introduced for the evaluation of functionality and modification efficiency of electrochemical heterogeneous systems, especially MOFTFs. To investigate this concept, we synthesized Zn3(BTC)2 and Cu3(BTC)2 as MOF models under constant current electrolysis in water and at room temperature. This work can make a breakthrough in the green synthesis of metal-organic frameworks.

| S-EPMC6778079 | biostudies-other

Competitive coordination strategy for the synthesis of hierarchical-pore metal-organic framework nanostructures.

Project description:Metal-organic frameworks (MOFs) usually have micropores smaller than 2 nm, which may restrict their applications in some cases. Hierarchical-pore MOFs (H-MOFs) are a new family of MOF materials, possessing both micro- and mesopores to address this problem. Here we demonstrate a competitive coordination strategy for the synthesis of H-MOF nanostructures, such as two-dimensional (2D) H-MOF nanosheets and H-MOF nanocubes, evolving through an etching process tuned by a competitive ligand. The as-synthesized 2D H-MOF nanosheets can serve as a substrate to in situ immobilize Pd nanoparticles to achieve a surfactant-free Pd catalyst, by means of a simple soaking method of Pd2+ precursors. Combined with the unique structure and gas adsorption capacity of H-MOF-5, the Pd-H-MOF-5 catalyst exhibits superior catalytic performance.

| S-EPMC5450591 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data