Electrospun polycaprolactone (PCL)-amnion nanofibrous membrane prevents adhesions and promotes nerve repair in a rat model of sciatic nerve compression.

ABSTRACT: Adhesion and scarring after neural surgery are detrimental to nerve regeneration and functional recovery. Amniotic membranes have been used in tissue repair due to their immunogenicity and richness in cytokines. In this study, an electrospun polycaprolactone (PCL)-amnion nanofibrous membrane was prepared for the treatment of sciatic nerve compression in a rat model. The effects of the PCL-amnion nanofibrous membrane on the prevention of adhesion formation and nerve regeneration were evaluated using electrophysiology and histological analyses. Compared with the medical chitosan hydrogel dressing, the PCL-amnion nanofibrous membrane significantly reduced peripheral nerve adhesion and promoted the rapid recovery of nerve conduction. Moreover, the immunohistochemical analysis identified more Schwann cells and less pro-inflammatory M1 macrophages in the PCL-amnion group. Western blot and RT-PCR results showed that the expression levels of type-Ⅰ and Ⅲ collagen in the PCL-treated rats were half of those in the control group after 12 weeks, while the expression level of nerve growth factor was approximately 3.5 times that found in the rats treated with medical chitosan hydrogel. In summary, electrospun PCL-amnion nanofibrous membranes can effectively reduce adhesion after neural surgery and promote nerve repair and regeneration. The long-term retention in vivo and sustained release of cytokines make PCL-amnion a promising biomaterial for clinical application.

SUBMITTER: Dong R

PROVIDER: S-EPMC7748280 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Electrospun polycaprolactone nanofibrous membranes loaded with baicalin for antibacterial wound dressing.

Project description:Due to the rise in bacterial resistance, the antibacterial extractions from Chinese herbs have been used more frequently for wound care. In this work, baicalin, an extraction from the Chinese herb Scutellaria baicalensis, was utilized as the antibacterial component in the poly(ε-caprolactone)/MXene (PCL/Ti3C2TX) hybrid nanofibrous membranes for wound dressing. The results revealed that the presence of Ti3C2TX aided in the diameter reduction of the electrospun nanofibers. The PCL hybrid membrane containing 3 wt% Ti3C2TX nanoflakes and 5 wt% baicalin exhibited the smallest mean diameter of 210 nm. Meanwhile, the antibacterial tests demonstrated that the PCL ternary hybrid nanofibers containing Ti3C2TX and baicalin exhibited adequate antibacterial activity against the Gram-positive bacterial S. aureus due to the good synergistic effects of Ti3C2TX naoflakes and baicalin. The addition of Ti3C2TX nanoflakes and baicalin could significantly improve the hydrophilicity of the membranes, resulting in the release of baicalin from the nanofibers. In addition, the cytotoxicity of the nanofibers on rat skeletal myoblast L6 cells confirmed their good compatibility with these PCL-based nanofibrous membrances. This work offers a feasible way to prepare antibacterial nanofibrous membranes using Chinese herb extraction for wound dressing applications.

| S-EPMC9240071 | biostudies-literature

Characterization, drug loading and antibacterial activity of nanohydroxyapatite/polycaprolactone (nHA/PCL) electrospun membrane.

Project description:Considering the important factor of bioactive nanohydoxyapatite (nHA) to enhance osteoconductivity or bone-bonding capacity, nHA was incorporated into an electrospun polycaprolactone (PCL) membrane using electrospinning techniques. The viscosity of the PCL and nHA/PCL with different concentrations of nHA was measured and the morphology of the electrospun membranes was compared using a field emission scanning electron microscopy. The water contact angle of the nanofiber determined the wettability of the membranes of different concentrations. The surface roughness of the electrospun nanofibers fabricated from pure PCL and nHA/PCL was determined and compared using atomic force microscopy. Attenuated total reflectance Fourier transform infrared spectroscopy was used to study the chemical bonding of the composite electrospun nanofibers. Beadless nanofibers were achieved after the incorporation of nHA with a diameter of 200-700 nm. Results showed that the fiber diameter and the surface roughness of electrospun nanofibers were significantly increased after the incorporation of nHA. In contrast, the water contact angle (132° ± 3.5°) was reduced for PCL membrane after addition of 10% (w/w) nHA (112° ± 3.0°). Ultimate tensile strengths of PCL membrane and 10% (w/w) nHA/PCL membrane were 25.02 ± 2.3 and 18.5 ± 4.4 MPa. A model drug tetracycline hydrochloride was successfully loaded in the membrane and the membrane demonstrated good antibacterial effects against the growth of bacteria by showing inhibition zone for E. coli (2.53 ± 0.06 cm) and B. cereus (2.87 ± 0.06 cm).

| S-EPMC5511808 | biostudies-other

Electrospun nanofibrous sheets of collagen/elastin/polycaprolactone improve cardiac repair after myocardial infarction.

Project description:Electrospun nanofibrous sheets get increasing attention in myocardial infarction (MI) treatment due to their good cytocompatibility to deliver transplanted stem cells to infarcted areas and due to mechanical characteristics to support damaged tissue. Cardiac extracellular matrix is essential for implanted cells since it provides the cardiac microenvironment. In this study, we hypothesized high concentrations of cardiac nature protein (NP), namely elastin and collagen, in hybrid polycaprolactone (PCL) electrospun nanofibrous sheets could be effective as cardiac-mimicking patch. Optimal ratio of elastin and collagen with PCL in electrospun sheets (80% NP/PCL) was selected based on cytocompatibility and mechanical characteristics. Bone-marrow (BM) c-kit(+) cells anchoring onto NP/PCL sheets exhibited increased proliferative capacity compared with those seeded on PCL in vitro. Moreover, we examined the improvement of cardiac function in MI mice by cell-seeded cardiac patch. Green Fluorescent Protein (GFP)-labeled BM c-kit(+) cells were loaded on 80% NP/PCL sheets which was transplanted into MI mice. Both 80% NP/PCL and c-kit(+)-seeded 80% NP/PCL effectively improved cardiac function after 4 weeks of transplantation, with reduced infarction area and restricted LV remodeling. C-kit(+)-seeded 80% NP/PCL was even superior to the 80% NP/PCL alone and both superior to PCL. GFP(+) cells were identified both in the sheets and local infarcted area where transplanted cells underwent cardiac differentiation after 4 weeks. To the best of our knowledge, this is the first report that sheets with high concentrations of nature proteins loaded with BM c-kit(+) cells might be a novel promising candidate for tissue-engineered cardiac patch to improve cardiac repair after MI.

| S-EPMC4859897 | biostudies-literature

Promotion of nerve regeneration by biodegradable nanofibrous scaffold following sciatic nerve transection in rats.

Project description:Peripheral nerve injuries (PNIs) are one of the common causes of morbidity and disability worldwide. Autograft is considered the gold standard treatment for PNIs. However, due to the complications associated with autografts, other sources are considered as alternatives. Recently, electrospun nanofibrous scaffolds have received wide attention in the field of tissue engineering. Exogenous tubular constructs with uniaxially aligned topographical cues to enhance the axonal re-growth are needed to bridge large nerve gaps between proximal and distal ends. Although several studies have used PLGA/PCL, but few studies have been conducted on developing a two-layer scaffold with aligned fibers properly orientated along the axis direction of the sciatic nerve to meet the physical properties required for suturing, transplantation, and nerve regeneration. In this study, we sought to design and develop PLGA-PCL-aligned nanofibers. Following the conventional examinations, we implanted the scaffolds into 7-mm sciatic nerve gaps in a rat model of nerve injury. Our in vivo evaluations did not show any adverse effects, and after eight weeks, an acceptable improvement was noted in the electrophysiological, functional, and histological analyses. Thus, it can be concluded that nanofiber scaffolds can be used as a reliable approach for repairing PNIs. However, further research is warranted.

| S-EPMC8021629 | biostudies-literature

Fabrication, characterization and adsorption properties of cucurbit[7]uril-functionalized polycaprolactone electrospun nanofibrous membranes.

Project description:The fabrication of electrospun nanofibers comprising cucurbit[7]uril (CB[7]) and poly(ε-caprolactone) (PCL) is reported. Various techniques such as SEM, FTIR, XRD, DSC and TG were utilized to characterize the morphology, composition and properties of the nanofibers. Uniform bead-free electrospun nanofibers were obtained from PCL/CB[7] mixed solutions and the average fiber diameter of the nanofibers increases with the increase of CB[7] content. The nanofibers are composed of a physical mixture of PCL and CB[7], and CB[7] itself is present in the PCL fiber matrix in an uncomplexed state. The static adsorption behavior of the PCL/CB[7] nanofibers towards methylene blue (MB) was also preliminary investigated. The results indicate that the adsorption of MB onto the nanofibrous membranes fits the second-order kinetic model and Langmuir isotherm model.

| S-EPMC6541341 | biostudies-literature

Electrospun Nanofibrous Conduit Filled with a Collagen-Based Matrix (ColM) for Nerve Regeneration.

Project description:Traumatic nerve defects result in dysfunctions of sensory and motor nerves and are usually accompanied by pain. Nerve guidance conduits (NGCs) are widely applied to bridge large-gap nerve defects. However, few NGCs can truly replace autologous nerve grafts to achieve comprehensive neural regeneration and function recovery. Herein, a three-dimensional (3D) sponge-filled nanofibrous NGC (sf@NGC) resembling the structure of native peripheral nerves was developed. The conduit was fabricated by electrospinning a poly(L-lactide-co-glycolide) (PLGA) membrane, whereas the intraluminal filler was obtained by freeze-drying a collagen-based matrix (ColM) resembling the extracellular matrix. The effects of the electrospinning process and of the composition of ColM on the physicochemical performance of sf@NGC were investigated in detail. Furthermore, the biocompatibility of the PLGA sheath and ColM were evaluated. The continuous and homogeneous PLGA nanofiber membrane had high porosity and tensile strength. ColM was shown to exhibit an ECM-like architecture characterized by a multistage pore structure and a high porosity level of over 70%. The PLGA sheath and ColM were shown to possess stagewise degradability and good biocompatibility. In conclusion, sf@NGC may have a favorable potential for the treatment of nerve reconstruction.

| S-EPMC10675555 | biostudies-literature

Three dimensional electrospun PCL/PLA blend nanofibrous scaffolds with significantly improved stem cells osteogenic differentiation and cranial bone formation.

Project description:Nanofibrous scaffolds that are morphologically/structurally similar to natural ECM are highly interested for tissue engineering; however, the electrospinning technique has the difficulty in directly producing clinically relevant 3D nanofibrous scaffolds with desired structural properties. To address this challenge, we have developed an innovative technique of thermally induced nanofiber self-agglomeration (TISA) recently. The aim of this work was to prepare (via the TISA technique) and evaluate 3D electrospun PCL/PLA blend (mass ratio: 4/1) nanofibrous scaffolds having high porosity of ∼95.8% as well as interconnected and hierarchically structured pores with sizes from sub-micrometers to ∼300 μm for bone tissue engineering. The hypothesis was that the incorporation of PLA (with higher mechanical stiffness/modulus and bioactivity) into PCL nanofibers would significantly improve human mesenchymal stem cells (hMSCs) osteogenic differentiation in vitro and bone formation in vivo. Compared to neat PCL-3D scaffolds, PCL/PLA-3D blend scaffolds had higher mechanical properties and in vitro bioactivity; as a result, they not only enhanced the cell viability of hMSCs but also promoted the osteogenic differentiation. Furthermore, our in vivo studies revealed that PCL/PLA-3D scaffolds considerably facilitated new bone formation in a critical-sized cranial bone defect mouse model. In summary, both in vitro and in vivo results indicated that novel 3D electrospun PCL/PLA blend nanofibrous scaffolds would be strongly favorable/desired for hMSCs osteogenic differentiation and cranial bone formation.

| S-EPMC5181114 | biostudies-literature

Tailoring weight ratio of PCL/PLA in electrospun three-dimensional nanofibrous scaffolds and the effect on osteogenic differentiation of stem cells.

Project description:Three-dimensional (3D) scaffolds as artificial ECMs have been extensively studied to mimic the critical features of natural ECMs. To develop more clinically relevant 3D scaffolds, electrospun nanofibrous scaffolds with different weight ratios of PCL/PLA (i.e., 100/0, 60/40, and 20/80) were fabricated via the thermally induced (nanofiber) self-agglomeration (TISA) method. The hypothesis was that, with the weight ratio increase of stiffer and more bioactive PLA in the 3D PCL/PLA blend scaffolds, the osteogenic differentiation of human mesenchymal stem cells (hMSCs) would be enhanced. The results indicated that, all of the 3D scaffolds were elastic/resilient and possessed interconnected and hierarchical pores with sizes from sub-microns to ∼300 μm; therefore, the morphological structures of these scaffolds were similar to those of natural ECMs. The PLA80 scaffolds exhibited the best overall properties in terms of density, porosity, water absorption capacity, mechanical properties, bioactivity, and cell viability. Furthermore, with increasing the PLA weight ratio, the alkaline phosphatase (ALP) activity, calcium content, and gene expression level were also increased, probably due to the improved stiffness/bioactivity of scaffold. Hence, the novel 3D electrospun PLA80 nanofibrous scaffold might be desired/favorable for the osteogenic differentiation of hMSCs.

| S-EPMC6174100 | biostudies-literature

A quantitative evaluation of sciatic nerve stiffness after compression by shear wave elastography in diabetic rats.

Project description:BackgroundOur study investigates the feasibility of using quantitative evaluation for nerve entrapment visualization by shear wave elastography (SWE) in diabetic rats.MethodsA total of 24 male Sprague-Dawley (SD) rats were included in this study. Before injection of streptozotocin (STZ), the experimental groups were assigned as the diabetic nerve compression (DNC) group (DNC, n=18) and the control group (CON, n=6). The DNC model was created by wrapping a silicone tube around the nerve, and then the DNC group was divided into the DNC 2-week (DNC2W, n=6), 4-week (DNC4W, n=6), and 8-week (DNC8W, n=6) groups according to the different duration time of sciatic nerve compression. The nerve stiffness was detected by SWE. Meanwhile, motor nerve conduction velocity (MNCV) was detected. These 2 indicators and histology of sciatic nerves were compared across the different groups.ResultsThe stiffness of the nerve depicted by SWE at the compression site increased markedly along with the duration time of compression (P<0.01). The MNCV decreased along with the duration time of nerve compression (P<0.05). The nerve stiffness depicted by SWE was negatively correlated with MNCV (r=-0.926; P<0.01). Myelinated fiber density significantly decreased as the duration time of nerve compression increased (P<0.01). Some differences were found between DNC4W and DNC8W groups, and CON and DNC2W groups (P<0.05) in average axon diameter, myelin sheath thickness, and g ratio.ConclusionsThe increased values of SWE, along with the increased duration of nerve compression, could reflect the severity of nerve entrapment in diabetic rats. Therefore, SWE may be used as a noninvasive and effective method to quantitatively evaluate the severity of diabetic nerve entrapment.

| S-EPMC7327375 | biostudies-literature

Organic and Inorganic PCL-Based Electrospun Fibers.

Project description:In this work, different nanocomposite electrospun fiber mats were obtained based on poly(e-caprolactone) (PCL) and reinforced with both organic and inorganic nanoparticles. In particular, on one side, cellulose nanocrystals (CNC) were synthesized and functionalized by "grafting from" reaction, using their superficial OH- group to graft PCL chains. On the other side, commercial chitosan, graphene as organic, while silver, hydroxyapatite, and fumed silica nanoparticles were used as inorganic reinforcements. All the nanoparticles were added at 1 wt% with respect to the PCL polymeric matrix in order to compare the different behavior of the woven no-woven nanocomposite electrospun fibers with a fixed amount of both organic and inorganic nanoparticles. From the thermal point of view, no difference was found between the effect of the addition of organic or inorganic nanoparticles, with no significant variation in the Tg (glass transition temperature), Tm (melting temperature), and the degree of crystallinity, leading in all cases to high crystallinity electrospun mats. From the mechanical point of view, the highest values of Young modulus were obtained when graphene, CNC, and silver nanoparticles were added to the PCL electrospun fibers. Moreover, all the nanoparticles used, both organic and inorganic, increased the flexibility of the electrospun mats, increasing their elongation at break.

| S-EPMC7361952 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data