3D printing direct to industrial roll-to-roll casting for fast prototyping of scalable microfluidic systems.

ABSTRACT: Microfluidic technologies have enormous potential to offer breakthrough solutions across a wide range of applications. However, the rate of scale-up and commercialization of these technologies has lagged significantly behind promising breakthrough developments in the lab, due at least in part to the problems presented by transitioning from benchtop fabrication methods to mass-manufacturing. In this work, we develop and validate a method to create functional microfluidic prototype devices using 3D printed masters in an industrial-scale roll-to-roll continuous casting process. There were no significant difference in mixing performance between the roll-to-roll cast devices and the PDMS controls in fluidic mixing tests. Furthermore, the casting process provided information on the suitability of the prototype microfluidic patterns for scale-up. This work represents an important step in the realization of high-volume prototyping and manufacturing of microfluidic patterns for use across a broad range of applications.

SUBMITTER: Boutiette AL

PROVIDER: S-EPMC7769481 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

3D printing direct to industrial roll-to-roll casting for fast prototyping of scalable microfluidic systems.

Boutiette Amber L AL Toothaker Cristoffer C Corless Bailey B Boukaftane Chouaib C Howell Caitlin C

PloS one 20201228 12

Microfluidic technologies have enormous potential to offer breakthrough solutions across a wide range of applications. However, the rate of scale-up and commercialization of these technologies has lagged significantly behind promising breakthrough developments in the lab, due at least in part to the problems presented by transitioning from benchtop fabrication methods to mass-manufacturing. In this work, we develop and validate a method to create functional microfluidic prototype devices using 3 ...[more]

PMID: 33370381

Similar Datasets

Project description:Stereolithography based 3D printing of microfluidics for prototyping has gained a lot of attention due to several advantages such as fast production, cost-effectiveness, and versatility over traditional photolithography-based microfabrication techniques. However, existing consumer focused SLA 3D printers struggle to fabricate functional microfluidic devices due to several challenges associated with micron-scale 3D printing. Here, we explore the origins and mechanism of the associated failure modes followed by presenting guidelines to overcome these challenges. The prescribed method works completely with existing consumer class inexpensive SLA printers without any modifications to reliably print PDMS cast microfluidic channels with channel sizes as low as ~75 μm and embedded channels with channel sizes as low ~200 μm. We developed a custom multi-resin formulation by incorporating Polyethylene glycol diacrylate (PEGDA) and Ethylene glycol polyether acrylate (EGPEA) as the monomer units to achieve micron sized printed features with tunable mechanical and optical properties. By incorporating multiple resins with different mechanical properties, we were able to achieve spatial control over the stiffness of the cured resin enabling us to incorporate both flexible and rigid components within a single 3D printed microfluidic chip. We demonstrate the utility of this technique by 3D printing an integrated pressure-actuated pneumatic valve (with flexible cured resin) in an otherwise rigid and clear microfluidic device that can be fabricated in a one-step process from a single CAD file. We also demonstrate the utility of this technique by integrating a fully functional finger-actuated microfluidic pump. The versatility and accessibility of the demonstrated fabrication method have the potential to reduce our reliance on expensive and time-consuming photolithographic techniques for microfluidic chip fabrication and thus drastically lowering our barrier to entry in microfluidics research.

Project description:Inertial microfluidics has been broadly investigated, resulting in the development of various applications, mainly for particle or cell separation. Lateral migrations of these particles within a microchannel strictly depend on the channel design and its cross-section. Nonetheless, the fabrication of these microchannels is a continuous challenging issue for the microfluidic community, where the most studied channel cross-sections are limited to only rectangular and more recently trapezoidal microchannels. As a result, a huge amount of potential remains intact for other geometries with cross-sections difficult to fabricate with standard microfabrication techniques. In this study, by leveraging on benefits of additive manufacturing, we have proposed a new method for the fabrication of inertial microfluidic devices. In our proposed workflow, parts are first printed via a high-resolution DLP/SLA 3D printer and then bonded to a transparent PMMA sheet using a double-coated pressure-sensitive adhesive tape. Using this method, we have fabricated and tested a plethora of existing inertial microfluidic devices, whether in a single or multiplexed manner, such as straight, spiral, serpentine, curvilinear, and contraction-expansion arrays. Our characterizations using both particles and cells revealed that the produced chips could withstand a pressure up to 150?psi with minimum interference of the tape to the total functionality of the device and viability of cells. As a showcase of the versatility of our method, we have proposed a new spiral microchannel with right-angled triangular cross-section which is technically impossible to fabricate using the standard lithography. We are of the opinion that the method proposed in this study will open the door for more complex geometries with the bespoke passive internal flow. Furthermore, the proposed fabrication workflow can be adopted at the production level, enabling large-scale manufacturing of inertial microfluidic devices.

Project description:The mechanical and rheological characterizations of flexible investment casting patterns capable of 3D printing are reported. The wax pattern was composed of microcrystalline hydrocarbon wax (DMW7478), Piccotex 75 (a copolymer of α-methyl-styrene and vinyl toluene with a 75/25 molar ratio, respectively) and Escorene (a copolymer of ethylene and vinyl acetate with a 72/28 mass ratio, respectively). It was found that in order to obtain a wax pattern with appreciable mechanical properties, the content of the microcrystalline hydrocarbon wax in these blends should not exceed 30% (m/m). Thus, a series of patterns with 28% (m/m) wax and varying Piccotex and Escorene contents spanning from 0 to 72% (m/m) was prepared. The dependence of the dynamic viscosities of the wax patterns on the composition was described using a stretched exponential model, whereas their variations with the temperature were interpreted in terms of the Arrhenius-Guzman equation. Furthermore, the slopes of the lines fitted to the viscosity versus temperature curves at the pour point decreased linearly with the Piccotex content. Non-Newtonian changes in the shear stress with the shear rate and shear stress crystallization were observed at temperatures near the pour points. The mechanical properties were evaluated using the uniaxial tensile mode and by three-point bending experiments. It was found that the stress (σ) versus the relative elongation (ε) curves can effectively be rendered by means of the standard linear solid (SLS) viscoelastic model. In addition, it was also established that the Young's modulus varied according to a sigmoid-type curve with the piccotex content, while the yield stress decreased linearly with the concentration of Piccotex. In addition, based on the spooling suitability and printability, the patterns were rated and it was found that the most appropriate wax pattern compositions for 3D printing were those which contained 30% (m/m) and 35% (m/m) Piccotex.

Dataset Information

3D printing direct to industrial roll-to-roll casting for fast prototyping of scalable microfluidic systems.

Publications

3D printing direct to industrial roll-to-roll casting for fast prototyping of scalable microfluidic systems.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets