Sol-Gel Nanocomposite Coatings for Preventing Biofilm Formation on Contact Lens Cases.

ABSTRACT:

Purpose

To evaluate the efficacy of a nanosilver-based sol-gel coating in preventing biofilm formation on contact lens cases.

Methods

An organic-inorganic hybrid silica-zirconia sol formulation with immobilized silver nanoparticles was deposited on contact lens case coupons. The coated and uncoated coupons were subjected to biofilm formation to Gram-negative and Gram-positive keratitis isolates and ATCC strains using a standard protocol. The biofilms were evaluated using crystal violet, MTT assay, and scanning electron microscope (SEM) examination. The duration of efficacy of the coating was evaluated by exposing the coated and uncoated coupons to a multipurpose lens cleaning solution for various durations up to 30 days and comparing their biofilm characteristics. The cytotoxicity of the coated surface was assessed using cell culture studies.

Results

Cross-hatch tests and SEM confirmed the presence of a uniform, well-adhered coating on the surface. The coating resulted in a nearly 95% reduction in biofilm formation of the tested bacteria and was effective despite exposures of up to 30 days to a multipurpose lens cleaning solution. The coating did not exhibit cytotoxicity to human corneal epithelial cells.

Conclusions

The silver nanoparticle-based coating exhibits a good antibiofilm property for both Gram-negative bacilli and Gram-positive cocci and is promising for commercial use in preventing contact lens-related infections.

Translational relevance

Biofilm formation on lens cases continues to be an important concern. The proposed coating will help reduce such formations, thus reducing the risk of lens-associated microbial keratitis.

SUBMITTER: Tabbasum K

PROVIDER: S-EPMC7794269 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Study of biofilm formation in bacterial isolates from contact lens wearers.

Project description:Purpose:To detect biofilm forming capacity of bacterial isolates obtained from the conjunctiva, contact lens and accessories of contact lens wearers using phenotypic and genotypic methods. Methods:Bacterial strains were collected from the conjunctiva, contact lens and lens storage cases of contact lens wearers. The phenotypic detection of biofilm production was done using the tube method and congo red agar method. The biofilm-forming related genes, icaA, of Coagulase negative Staphylococcus (CONS) and Staphylococcus aureus, and pslA, of P. aeruginosa, were detected using PCR. Results:A total of 265 bacterial isolates which included S. aureus, CONS, Pseudomonas, Nil-fermenter Gram-negative bacilli (NFGNB), Bacillus spp, Diphtheroids, Micrococci, Klebsiella pneumonia, Klebsiella oxytoca, E. coli, Proteus mirabilis, Proteus vulgaris, Citrobacter koseri, Citrobacter freundii, Enterobacter cloacae, Moraxella were obtained. Of the 265 isolates, 53.5% were moderately positive, 33.2% strongly positive and 13.2% negative for biofilm production by tube method and 36.6% were moderately positive, 40% strongly positive and 23.3% negative for biofilm production by congo red agar method. Of the four S. aureus isolates, two (50%) showed the presence of icaA gene. Of the 23 CONS isolates, three (13%) showed the presence of icaA gene. All the Pseudomonas isolates were negative for presence pslA (1119 bp) gene though most of them were phenotypically positive for biofilm formation. Conclusion:Most of the bacterial isolates obtained from contact lens wearers had the potential to produce biofilms. Tube method and Congo red agar method exhibited significant statistical correlation (P-value = 0.006) and picked up a good number of biofilm-forming isolates, hence may be used for detection of biofilm production. The absence of biofilm-forming gene did not rule out the possibility for phenotypic biofilm production by bacteria.

| S-EPMC6951123 | biostudies-literature

Transparent Self-Cleaning Coatings Based on Colorless Polyimide/Silica Sol Nanocomposite.

Project description:We herein report transparent self-cleaning coatings based on polyimide-fluorinated silica sol (PIFSS) nanocomposite. Polyamic acid-silica sol (PASS) suspensions were synthesized by adding four different amounts of a silica sol suspension to each end-capped polyamic acid solution. The PASS suspensions were spin-coated on glass slides, thermally imidized and treated with triethoxy-1H,1H,2H,2H-perfluorodecylsilane (TEFDS) to prepare PIFSS coatings. The PIFSS coatings showed high resistance to separation from glass substrates and thermal stability. Furthermore, the PIFSS coatings on the glass substrate could be cleanly removed using polar aprotic solvents and repeated coating was possible. As the amount of silica sol particles in the PIFSS coating was increased, the hydrophobic contact angle increased. Among them, PIFSS-10 and PIFSS-15 coatings showed nearly superhydrophobic contact angles (144° and 148°, respectively) and good self-cleaning property. It was confirmed by SEM and AFM studies that their hydrophobic and self-cleaning properties are due to uniform particle distribution and relatively high surface roughness. PIFSS-10 coating showed a high transmittance value (88%) at 550 nm and good self-cleaning property, therefore suitable as a transparent self-cleaning coating. The advantages of the coating are that the fabrication process is simple, and the substrate is reusable. The PIFSS coating is expected to be applied in solar cell panels, windows, lenses and safety goggles.

| S-EPMC8659165 | biostudies-literature

Influence of Hybrid Sol-Gel Crosslinker on Self-Healing Properties for Multifunctional Coatings.

Project description:Self-healing polymers are a new class of material that has recently received a lot of attention because of the lifespan improvement it could bring to multiple applications. One of the major challenges is to obtain multifunctional materials which can self-heal and exhibit other interesting properties such as protection against corrosion. In this paper, the effect of the incorporation of an aminosilane on the properties of a self-healing organic polymer containing disulfide bond is studied on films and coatings for aluminium AA2024-T3 using simple one step in situ synthesis. Hybrid coatings with enhanced anticorrosion properties measured by EIS were obtained thanks to the formation of a protective oxide interface layer, while exhibiting wound closure after exposition at 75 °C. The thermal, mechanical and rheological properties of the films with different aminosilane amounts were characterized in order to understand the influence of the slight presence of the inorganic network. Stiffer and reprocessable hybrid films were obtained, capable to recover their mechanical properties after healing. The nanocomposite structure, confirmed by TEM, had a positive effect on the self-healing and stress relaxation properties. These results highlight the potential of sol-gel chemistry to obtain efficient anticorrosion and self-healing coatings.

| S-EPMC8465503 | biostudies-literature

<i>In situ</i> sol-gel synthesis of hyaluronan derivatives bio-nanocomposite hydrogels.

Project description:The main driving idea of the present study was the comparison between two different chemical modifications of hyaluronic acid (HA) followed by the development of nanocomposite hydrogels directly in situ by biomineralization of photocrosslinkable HA polymers through sol-gel synthesis. In this way, it has been possible to overcome some limitations due to classical approaches based on the physical blending of inorganic fillers into polymer matrix. To this aim, methacrylated and maleated HA, synthesized with similar degree of substitution (DS) were compared in terms of mechanical and physico-chemical properties. The success of in situ biomineralization was highlighted by reflect Fourier transform infrared spectroscopy and thermogravimetric analysis. Furthermore, mechanical characterization demonstrated the reinforcing effect of inorganic fillers evidencing a strong correlation with DS. The swelling behavior resulted to be correlated with filler concentration. Finally, the cytotoxicity tests revealed the absence of toxic components and an increase of cell proliferation over culture time was observed, highlighting these bio-nanocomposite hyaluronan derivatives as biocompatible hydrogel with tunable properties.

| S-EPMC6783703 | biostudies-literature

Optical Constants of Crystallized TiO₂ Coatings Prepared by Sol-Gel Process.

Project description:Titanium oxide coatings have been deposited by the sol-gel dip-coating method. Crystallization of titanium oxide coatings was then achieved through thermal annealing at temperatures above 400 °C. The structural properties and surface morphology of the crystallized coatings were studied by micro-Raman spectroscopy and atomic force microscopy, respectively. Characterization technique, based on least-square fitting to the measured reflectance and transmittance spectra, is used to determine the refractive indices of the crystallized TiO₂ coatings. The stability of the synthesized sol was also investigated by dynamic light scattering particle size analyzer. The influence of the thermal annealing on the optical properties was then discussed. The increase in refractive index with high temperature thermal annealing process was observed, obtaining refractive index values from 1.98 to 2.57 at He-Ne laser wavelength of 633 nm. The Raman spectroscopy and atomic force microscopy studies indicate that the index variation is due to the changes in crystalline phase, density, and morphology during thermal annealing.

| S-EPMC5521283 | biostudies-other

Influence of Addition of Antibiotics on Chemical and Surface Properties of Sol-Gel Coatings.

Project description:Infection is one of the most common causes that leads to joint prosthesis failure. In the present work, biodegradable sol-gel coatings were investigated as a promising controlled release of antibiotics for the local prevention of infection in joint prostheses. Accordingly, a sol-gel formulation was designed to be tested as a carrier for 8 different individually loaded antimicrobials. Sols were prepared from a mixture of MAPTMS and TMOS silanes, tris(tri-methylsilyl)phosphite, and the corresponding antimicrobial. In order to study the cross-linking and surface of the coatings, a battery of examinations (Fourier-transform infrared spectroscopy, solid-state 29Si-NMR spectroscopy, thermogravimetric analysis, SEM, EDS, AFM, and water contact angle, thickness, and roughness measurements) were conducted on the formulations loaded with Cefoxitin and Linezolid. A formulation loaded with both antibiotics was also explored. Results showed that the coatings had a microscale roughness attributed to the accumulation of antibiotics and organophosphites in the surface protrusions and that the existence of chemical bonds between antibiotics and the siloxane network was not evidenced.

| S-EPMC9317242 | biostudies-literature

Multifunctional Finishing of Cotton Fabric with Curcumin Derivatives Coatings Obtained by Sol-Gel Method.

Project description:Textile materials with fluorescent, repellent, or antimicrobial properties are increasingly used in common applications. Obtaining multi-functional coatings is of wide interest, especially for applications related to signaling or to the medical field. In order to increase the performance (color properties, fluorescence lifetime, self-cleaning or antimicrobial properties) of textile materials with special uses, a series of research was carried out regarding the modification of surfaces with nanosols. In this study, coatings with multiple properties were obtained by depositing nanosols on cotton fabrics generated through sol-gel reactions. These multifunctional coatings are hybrid materials in which the host matrix is generated using tetraethylorthosilicate (TEOS) and network modifying organosilanes:dimethoxydimethylsilane (DMDMS) or dimethoxydiphenylsilane (DMDPS) in a 1:1 mass ratio. Two curcumin derivatives were embedded in siloxane matrices, a yellow one (CY) that is identical to bis-demethoxycurcumin (one of the natural constituents in turmeric) and a red dye (CR) that has a N,N-dimethylamino group grafted in position 4 of the dicinnamoylmethane skeleton of curcumin. The nanocomposites obtained by embedding curcumin derivatives in siloxane matrices were deposited on cotton fabric and studied in relation to the dye and the type of host matrix. Fabrics coated with such systems provide a hydrophobic surface, have fluorescent and antimicrobial properties, change color depending on the pH, and therefore can be used in various fields where textiles provide signaling properties, self-cleaning, or antibacterial protection. The coated fabrics maintained their good multifunctional properties even after several washing cycles.

| S-EPMC10217195 | biostudies-literature

Self-assembly of iron oxide precursor micelles driven by magnetic stirring time in sol-gel coatings.

Project description:The purpose of this work is to fabricate self-assembled microstructures by the sol-gel method and study the morphological, structural and compositional dependence of ε-Fe2O3 nanoparticles embedded in silica when glycerol (GLY) and cetyl-trimethylammonium bromide (CTAB) are added as steric agents simultaneously. The combined action of a polyalcohol and a surfactant significantly modifies the morphology of the sample giving rise to a different microstructure in each of the studied cases (1, 3 and 7 days of magnetic stirring time). This is due to the fact that the addition of these two compounds leads to a considerable increase in gelation time as GLY can interact with the alkoxide group on the surface of the iron oxide precursor micelle and/or be incorporated into the hydrophilic chains of CTAB. This last effect causes the iron oxide precursor micelles to be interconnected forming aggregates whose size and structure depend on the magnetic stirring time of the sol-gel synthetic route. In this paper, crystalline structure, composition, purity and morphology of the sol-gel coatings densified at 960 °C are examined. Emphasis is placed on the nominal percentage of the different iron oxides found in the samples and on the morphological and structural differences. This work implies the possibility of patterning ε-Fe2O3 nanoparticles in coatings and controlling their purity by an easy one-pot sol-gel method.

| S-EPMC9064545 | biostudies-literature

Thermal Annealing Effect on Optical Properties of Binary TiO₂-SiO₂ Sol-Gel Coatings.

Project description:TiO₂-SiO₂ binary coatings were deposited by a sol-gel dip-coating method using tetrabutyl titanate and tetraethyl orthosilicate as precursors. The structure and chemical composition of the coatings annealed at different temperatures were analyzed by Raman spectroscopy and Fourier Transform Infrared (FTIR) spectroscopy. The refractive indices of the coatings were calculated from the measured transmittance and reflectance spectra. An increase in refractive index with the high temperature thermal annealing process was observed. The Raman and FTIR results indicate that the refractive index variation is due to changes in the removal of the organic component, phase separation and the crystal structure of the binary coatings.

| S-EPMC5452115 | biostudies-other

Quantifying the Dynamics of Bacterial Biofilm Formation on the Surface of Soft Contact Lens Materials Using Digital Holographic Tomography to Advance Biofilm Research.

Project description:The increase in bacterial resistance to antibiotics in recent years demands innovative strategies for the detection and combating of biofilms, which are notoriously resilient. Biofilms, particularly those on contact lenses, can lead to biofilm-related infections (e.g., conjunctivitis and keratitis), posing a significant risk to patients. Non-destructive and non-contact sensing techniques are essential in addressing this threat. Digital holographic tomography emerges as a promising solution. This allows for the 3D reconstruction of the refractive index distribution in biological samples, enabling label-free visualization and the quantitative analysis of biofilms. This tool provides insight into the dynamics of biofilm formation and maturation on the surface of transparent materials. Applying digital holographic tomography for biofilm examination has the potential to advance our ability to combat the antibiotic bacterial resistance crisis. A recent study focused on characterizing biofilm formation and maturation on six soft contact lens materials (three silicone hydrogels, three hydrogels), with a particular emphasis on Staphylococcus epidermis and Pseudomonas aeruginosa, both common culprits in ocular infections. The results revealed species- and time-dependent variations in the refractive indexes and volumes of biofilms, shedding light on cell dynamics, cell death, and contact lens material-related factors. The use of digital holographic tomography enables the quantitative analysis of biofilm dynamics, providing us with a better understanding and characterization of bacterial biofilms.

| S-EPMC10932241 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data