Synthesis, Characterization and Non-Isothermal Crystallization Kinetics of a New Family of Poly (Ether-Block-Amide)s Based on Nylon 10T/10I.

ABSTRACT: A series of novel thermoplastic elastomers based on (poly(decamethylene terephthalamide/decamethylene isophthalamide), PA10T/10I) and poly(ethylene glycol) (PEG) were synthesized via a facile one-pot, efficient and pollution-free method. The thermal analysis demonstrates that the melting points of the resultant elastomers were in the range of 217.1-233.9 °C, and their initial decomposition temperatures were in the range of 385.3-387.5 °C. That is higher than most commercial polyamide-based thermoplastic elastomers. The tensile strength of the resultant elastomers ranges from 21.9 to 41.1 MPa. According to the high-temperature bending test results, the resultant samples still maintain considerably better mechanical properties than commercial products such as Pebax^® 5533 (Arkema, Paris, France), and these novel thermoplastic elastomers could potentially be applied in high-temperature scenes. The non-isothermal crystallization kinetics of the resultant elastomers and PA10T/10I was investigated by means of Jeziorny and Mo's methods. Both of them could successfully describe the crystallization behavior of the resultant elastomers. Additionally, the activation energy of non-isothermal crystallization was calculated by the Kissinger method and the Friedman equation. The results indicate that the crystallization rates follow the order of TPAE-2000 > TPAE-1500 > PA10T/10I > TPAE-1000. From the crystallization analysis, the crystallization kinetics and activation energies are deeply affected by the molecular weight of hard segment.

SUBMITTER: Tong X

PROVIDER: S-EPMC7795608 | biostudies-literature | 2020 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Synthesis, Characterization and Non-Isothermal Crystallization Kinetics of a New Family of Poly (Ether-Block-Amide)s Based on Nylon 10T/10I.

Tong Xin X Wang Zhao Z Zhang Mei-Ling ML Wang Xiao-Jun XJ Zhang Gang G Long Sheng-Ru SR Yang Jie J

Polymers 20201227 1

A series of novel thermoplastic elastomers based on (poly(decamethylene terephthalamide/decamethylene isophthalamide), PA10T/10I) and poly(ethylene glycol) (PEG) were synthesized via a facile one-pot, efficient and pollution-free method. The thermal analysis demonstrates that the melting points of the resultant elastomers were in the range of 217.1-233.9 °C, and their initial decomposition temperatures were in the range of 385.3-387.5 °C. That is higher than most commercial polyamide-based therm ...[more]

PMID: 33375409

Similar Datasets

Project description:In this study, nanocomposites were prepared by melt blending poly (ε-caprolactone) (PCL) with a (polycarbonate (PC)/multi-wall carbon nanotubes (MWCNTs)) masterbatch in a twin-screw extruder. The nanocomposites contained 0.5, 1.0, 2.0, and 4.0 wt % MWCNTs. Even though PCL and PC have been reported to be miscible, our DSC (Differential Scanning Calorimetry), SAXS (Small Angle X-ray Scattering), and WAXS (Wide Angle X-ray Scattering) results showed partial miscibility, where two phases were formed (PC-rich and PCL-rich phases). In the PC-rich phase, the small amount of PCL chains included within this phase plasticized the PC component and the PC-rich phase was therefore able to crystallize. In contrast, in the PCL-rich phase the amount of PC chains present generates changes in the glass transition temperature of the PCL phase that were much smaller than those predicted by the Fox equation. The presence of two phases was corroborated by SEM, TEM, and AFM observations where a fair number of MWCNTs diffused from the PC-rich phase to the PCL-rich phase, even though there were some MWCNTs agglomerates confined to PC-rich droplets. Standard DSC measurements demonstrated that the MWCNTs nucleation effects are saturated at a 1 wt % MWCNT concentration on the PCL-rich phase. This is consistent with the dielectric percolation threshold, which was found to be between 0.5 and 1 wt % MWCNTs. However, the nucleating efficiency was lower than literature reports for PCL/MWCNTs, due to limited phase mixing between the PC-rich and the PCL-rich phases. Isothermal crystallization experiments performed by DSC showed an increase in the overall crystallization kinetics of PCL with increases in MWCNTs as a result of their nucleating effect. Nevertheless, the crystallinity degree of the nanocomposite containing 4 wt % MWCNTs decreased by about 15% in comparison to neat PCL. This was attributed to the presence of the PC-rich phase, which was able to crystallize in view of the plasticization effect of the PCL component, since as the MWCNT content increases, the PC content in the blend also increases. The thermal conductivities (i.e., 4 wt % MWCNTs) were enhanced by 20% in comparison to the neat material. The nanocomposites prepared in this work could be employed in applications were electrical conductivity is required, as well as lightweight and tailored mechanical properties.

Dataset Information

Synthesis, Characterization and Non-Isothermal Crystallization Kinetics of a New Family of Poly (Ether-Block-Amide)s Based on Nylon 10T/10I.

Publications

Synthesis, Characterization and Non-Isothermal Crystallization Kinetics of a New Family of Poly (Ether-Block-Amide)s Based on Nylon 10T/10I.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets