Anticancer Drug Release System Based on Hollow Silica Nanocarriers Triggered by Tumor Cellular Microenvironments.

ABSTRACT: Targeted release of anticancer drugs to tumor sites has a pivotal role in clinical oncology. pH-responsive drug delivery systems, with an intelligent and targeted release of anticancer drugs in a controllable manner based on sensitivities to the weakly acidic environments of tumor cellular microenvironments, are desirable. Herein, the design of such a pH-responsive drug delivery system is detailed using in situ amino-functionalized hollow mesoporous silica nanoparticles as carriers. The drug release behavior of the pH-responsive delivery system was evaluated under an in vitro simulation of tumor cellular microenvironments. The drug delivery system has efficient drug loadings and targeted release. Zorubicin hydrochloride releasing percentage is almost up to 100% at a buffer pH of 5.0. The drug release systems described demonstrating great potential in anticancer therapy.

SUBMITTER: Deng S

PROVIDER: S-EPMC7807753 | biostudies-literature | 2021 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Anticancer Drug Release System Based on Hollow Silica Nanocarriers Triggered by Tumor Cellular Microenvironments.

Deng Shaoxin S Cui Cheng-Xing CX Duan Lingyao L Hu Linfeng L Yang Xiaoxun X Wang Ji-Chao JC Qu Ling-Bo LB Zhang Yuping Y

ACS omega 20201229 1

Targeted release of anticancer drugs to tumor sites has a pivotal role in clinical oncology. pH-responsive drug delivery systems, with an intelligent and targeted release of anticancer drugs in a controllable manner based on sensitivities to the weakly acidic environments of tumor cellular microenvironments, are desirable. Herein, the design of such a pH-responsive drug delivery system is detailed using in situ amino-functionalized hollow mesoporous silica nanoparticles as carriers. The drug rel ...[more]

PMID: 33458507

Similar Datasets

Project description:Tunable glutathione (GSH)-sensitive hollow mesoporous silica nanoparticles (HMSiO2 NPs) were developed using a structural difference-based selective etching strategy. These organosilica hollow nanoparticles contained disulfide linkages (S-S) in the outer shell which were degraded by GSH. The particles were compared with their nonGSH-sensitive tetraethyl orthosilicate (TEOS) HMSiO2 counterparts in terms of their synthesis method, characterization, doxorubicin (DOX) release profile, and in vitro cytotoxicity in MCF-7 breast cancer cells. Transmission electron microscopy (TEM) of the particles indicated that the fabricated HMSiO2 NPs had an average diameter of 130?±?5?nm. Thermogravimetric analysis (TGA) revealed that GSH-sensitive particles had approximately 5.3% more weight loss than TEOS HMSiO2 NPs. Zeta potential of these redox-responsive particles was -23?±?1?mV at pH?6 in deionized (DI) water. Nitrogen adsorption-desorption isotherm revealed that the surface area of the hollow mesoporous nanoreservoirs was roughly 446?±?6?m2?g-1 and the average diameter of the pores was 2.3?±?0.5?nm. TEM images suggest that the nanoparticles started to lose mass integrity from Day 1. The particles showed a high loading capacity for DOX (8.9?±?0.5%) as a model drug, due to the large voids existing in the hollow structures. Approximately 58% of the incorporated DOX released within 14?days in phosphate buffered saline (PBS) at pH?6 and in the presence of 10?mM of GSH, mimicking intracellular tumor microenvironment while release from TEOS HMSiO2 NPs was only c.a. 18%. The uptake of these hollow nanospheres by MCF-7 cells and RAW 264.7 macrophages was evaluated using TEM and confocal microscopy. The nanospheres were shown to accumulate in the endolysosomal compartments after incubation for 24?h with the maximum uptake of c.a. 2.1?±?0.3% and 5.2?±?0.4%, respectively. Cytotoxicity of the nanospheres was investigated using CCK-8 assay. Results indicate that intact hollow particles (both GSH-sensitive and TEOS HMSiO2 NPs) were nontoxic to MCF-7 cells after incubation for 24?h within the concentration range of 0-1000??g?ml-1. DOX-loaded GSH-sensitive nanospheres containing 6??g?ml-1 of DOX killed c.a. 51% of MCF-7 cells after 24?h while TEOS HMSiO2 NPs killed c.a. 20% with the difference being statistically significant. Finally, cytotoxicity data in RAW 264.7 macrophages and NIH 3?T3 fibroblasts shows that intact GSH-sensitive HMSiO2 NPs did not show any toxic effects on these cells with the concentrations equal or <125??g?ml-1.

Dataset Information

Anticancer Drug Release System Based on Hollow Silica Nanocarriers Triggered by Tumor Cellular Microenvironments.

Publications

Anticancer Drug Release System Based on Hollow Silica Nanocarriers Triggered by Tumor Cellular Microenvironments.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets