Conductive PEDOT: PSS-Based Organic/Inorganic Flexible Thermoelectric Films and Power Generators.

ABSTRACT: We present a simple thermoelectric device that consists of a conductive poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS)-based inorganic/organic thermoelectric film with high thermoelectric performance. The PEDOT:PSS-coated Se NWs were first chemically synthesized in situ, and then mixed with an Ag precursor solution to produce the PEDOT:PSS-coated Ag₂Se NWs. The PEDOT:PSS matrix was then treated with dimethyl sulfoxide (DMSO) prior to the production of flexible PEDOT:PSS-coated Ag₂Se NW/PEDOT:PSS composite films with various weight fractions of Ag₂Se via a simple drop-casting method. The thermoelectric properties (Seebeck coefficient, electrical conductivity, and power factor) of the composite films were then analyzed. The composite film with 50 wt.% NWs exhibited the highest power factor of 327.15 ?W/m·K² at room temperature. The excellent flexibility of this composite film was verified by bending tests, in which the thermoelectric properties were reduced by only ~5.9% after 1000 bending cycles. Finally, a simple thermoelectric device consisting of five strips of the proposed composite film was constructed and was shown to generate a voltage of 7.6 mV when the temperature difference was 20 K. Thus, the present study demonstrates that that the combination of a chalcogenide and a conductive composite film can produce a high-performance flexible thermoelectric composite film.

SUBMITTER: Park D

PROVIDER: S-EPMC7826913 | biostudies-literature | 2021 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Conductive PEDOT: PSS-Based Organic/Inorganic Flexible Thermoelectric Films and Power Generators.

Park Dabin D Kim Minsu M Kim Jooheon J

Polymers 20210108 2

We present a simple thermoelectric device that consists of a conductive poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS)-based inorganic/organic thermoelectric film with high thermoelectric performance. The PEDOT:PSS-coated Se NWs were first chemically synthesized in situ, and then mixed with an Ag precursor solution to produce the PEDOT:PSS-coated Ag<sub>2</sub>Se NWs. The PEDOT:PSS matrix was then treated with dimethyl sulfoxide (DMSO) prior to the production of flexible PED ...[more]

PMID: 33435612

Similar Datasets

Project description:Poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) is one of the most popular conducting polymers and widely used as polymer thermoelectric materials, and its thermoelectric performance could be improved by a variety of post-treatment processes. This paper reported two series of post-treatment methods to enhance the thermoelectric performance. The first series method included pre-treatment of PEDOT:PSS film with formamide, followed by imidazolium-based ionic liquids. The second series method included pre-treatment of PEDOT:PSS film with formamide, followed by sodium formaldehyde sulfoxylate, and finally imidazolium-based ionic liquids. Two series of post-treatment methods significantly improved the power factor of PEDOT:PSS when compared to that of PEDOT:PSS treated with formamide only. For example, using the first series post-treatment method with 40 vol.% ionic liquid 1-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl) amide, the Seebeck coefficient of the PEDOT:PSS film increased from 14.9 to 28.5 μV/K although the electrical conductivity reduced from 2,873 to 1,701 S/cm, resulting in a substantial improvement in the overall power factor from 63.6 to 137.8 μW/K2m. The electrical conductivity enhancement in the formamide-treatment process was in part ascribed to the removal of the insulating PSS component. Further treatment of PEDOT:PSS film with ionic liquid caused dedoping of PEDOT and hence increased in Seebeck coefficient. In contrast, second series post-treatment method led to the reduction in electrical conductivity from 2,873 to 641 S/cm but a big improvement in the Seebeck coefficient from 14.9 to 61.1 μV/K and thus the overall power factor reached up to ~239.2 μW/K2m. Apart from the improvement in electrical conductivity, the increase in Seebeck coefficient is on account of the substantial dedoping of PEDOT polymer to its neutral form and thus leads to the big improvement of its Seebeck coefficient. The environmental stability of ionic liquid-treated PEDOT:PSS films were examined. It was found that the ionic liquid treated PEDOT:PSS retained more than 70% Seebeck coefficient and electrical conductivity at 75% RH humidity and 70°C for 480 h. The improved long-term TE stability is attributed to the strong ionic interaction between sulfonate anions and bulky imidazolium cations that effectively block the penetration of water and lessen the tendency to take up water from the air.

Dataset Information

Conductive PEDOT: PSS-Based Organic/Inorganic Flexible Thermoelectric Films and Power Generators.

Publications

Conductive PEDOT: PSS-Based Organic/Inorganic Flexible Thermoelectric Films and Power Generators.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure