Dataset Information

Characterization of Organosolv Birch Lignins: Toward Application-Specific Lignin Production.

ABSTRACT: Organosolv pretreatment represents one of the most promising biomass valorization strategies for renewable carbon-based products; meanwhile, there is an overall lack of holistic approach to how extraction conditions affect the suitable end-usages. In this context, lignin extracted from silver birch (Betula pendula L.) by a novel hybrid organosolv/steam-explosion treatment at varying process conditions (EtOH %; time; catalyst %) was analyzed by quantitative NMR (¹H-¹³C HSQC; ¹³C NMR; ³¹P NMR), gel permeation chromatography, Fourier transform infrared (FT-IR), Pyr-gas chromatography-mass spectroscopy (GC/MS), and thermogravimetric analysis, and the physicochemical characteristics of the lignins were discussed regarding their potential usages. Characteristic lignin interunit bonding motifs, such as ?-O-4', ?-?', and ?-5', were found to dominate in the extracted lignins, with their abundance varying with treatment conditions. Low-molecular-weight lignins with fairly unaltered characteristics were generated via extraction with the highest ethanol content potentially suitable for subsequent production of free phenolics. Furthermore, ?-?' and ?-5' structures were predominant at higher acid catalyst contents and prolonged treatment times. Higher acid catalyst content led to oxidation and ethoxylation of side-chains, with the concomitant gradual disappearance of p-hydroxycinnamyl alcohol and cinnamaldehyde. This said, the increasing application of acid generated a broad set of lignin characteristics with potential applications such as antioxidants, carbon fiber, nanoparticles, and water remediation purposes.

SUBMITTER: Paulsen Thoresen P

PROVIDER: S-EPMC7893791 | biostudies-literature | 2021 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Characterization of Organosolv Birch Lignins: Toward Application-Specific Lignin Production.

Paulsen Thoresen Petter P Lange Heiko H Crestini Claudia C Rova Ulrika U Matsakas Leonidas L Christakopoulos Paul P

ACS omega 20210201 6

Organosolv pretreatment represents one of the most promising biomass valorization strategies for renewable carbon-based products; meanwhile, there is an overall lack of holistic approach to how extraction conditions affect the suitable end-usages. In this context, lignin extracted from silver birch (Betula pendula L.) by a novel hybrid organosolv/steam-explosion treatment at varying process conditions (EtOH %; time; catalyst %) was analyzed by quantitative NMR (1H-13 ...[more]

PMID: 33623848

Similar Datasets

Project description:Lignin, being one of the main structural components of lignocellulosic biomass, is considered the most abundant natural source of phenolics and aromatics. Efforts for its valorisation were recently explored as it is mostly treated as waste from heat/energy production via combustion. Among them, polymer-based lignin composites are a promising approach to both valorise lignin and to fine tune the properties of polymers. In this work, organosolv lignin, from beech wood, was used as fillers in a poly (lactic acid) (PLA) matrix. The PLA/lignin composites were prepared using melt mixing of masterbatches with neat PLA in three different lignin contents: 0.5, 1.0 and 2.5 wt%. Lignin was used as-isolated, via the organosolv biomass pretreatment/fractionation process and after 8 h of ball milling. The composites were characterised with Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR) spectroscopy, X-ray Diffraction (XRD), and Differential Scanning Calorimetry (DSC). Additionally, their antioxidant activity was assessed with the 2,2-Diphenyil-1-picrylhydrazyl (DPPH) method, the colour was measured with a colorimeter and the mechanical properties were evaluated with tensile testing. Ball milling, at least under the conditions applied in this study, did not induce a further substantial decrease in the already relatively small organosolv lignin primary particles of ~1 μm. All the produced PLA/lignin composites had a uniform dispersion of lignin. Compression-moulded films were successfully prepared, and they were coloured brown, with ball-milled lignin, giving a slightly lighter colour in comparison with the as-received lignin. Hydrogen bonding was detected between the components of the composites, and crystallization of the PLA was suppressed by both lignin, with the suppression being less pronounced by the ball-milled lignin. All composites showed a significantly improved antioxidant activity, and their mechanical properties were maintained for filler content 1 wt%.

Dataset Information

Characterization of Organosolv Birch Lignins: Toward Application-Specific Lignin Production.

Publications

Characterization of Organosolv Birch Lignins: Toward Application-Specific Lignin Production.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets