Role of New Hydrophilic Surfaces on Early Success Rate and Implant Stability: 1-Year Post-loading Results of a Multicenter, Split-Mouth, Randomized Controlled Trial.

ABSTRACT:

Objective

?To compare early implant failure and implant stability of one-stage Hiossen ET III implants with its new hydrophilic (NH) surface, compared with Hiossen ET III implants with the sandblasted and acid-etched (SA) surface at 1-year follow-up.

Materials and methods

?This study was designed as a split-mouth, multicenter randomized controlled trial aimed to compare SA surface implants (SA group) and NH surface, (NH group). Outcomes were implant and prosthetic survival rates, complications, the insertion torque at implant placement, and implant stability quotient (ISQ) values.

Results

?Twenty-nine patients (mean age 59.9 ± 11.3 years) were treated and followed up to 1 year after loading. No patient dropped out. Fifty-eight implants (29 SA group and 29 NH group) were placed. No implants or prostheses failed and no complications were experienced during follow-up. The mean insertion torque was 40.5 ± 3.23 (38.17-41.83) Ncm in the SA group and 40.48 ± 3.49 (38.02-41.98) Ncm in the NH group (p = 0.981). There was a statistically significant difference at the second week (T2) with higher values in the NH group (p = 0.041). Similar results were found in the maxilla (p = 0.045), but not in the mandible (p = 0.362). A positive correlation was found between initial insertion torque and ISQ with higher value in the NH group (0.73 vs. 0.66).

Conclusions

?NH implants are a viable alternative to SA surface, as they seem to avoid the ISQ drop during the bone remodeling phase.

SUBMITTER: Tallarico M

PROVIDER: S-EPMC7902108 | biostudies-literature | 2021 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Role of New Hydrophilic Surfaces on Early Success Rate and Implant Stability: 1-Year Post-loading Results of a Multicenter, Split-Mouth, Randomized Controlled Trial.

Tallarico Marco M Baldini Nicola N Gatti Fulvio F Martinolli Matteo M Xhanari Erta E Meloni Silvio Mario SM Gabriele Cervino C Immacolata Lumbau Aurea LA

European journal of dentistry 20201126 1

<h4>Objective</h4> To compare early implant failure and implant stability of one-stage Hiossen ET III implants with its new hydrophilic (NH) surface, compared with Hiossen ET III implants with the sandblasted and acid-etched (SA) surface at 1-year follow-up.<h4>Materials and methods</h4> This study was designed as a split-mouth, multicenter randomized controlled trial aimed to compare SA surface implants (SA group) and NH surface, (NH group). Outcomes were implant and prosthetic survival rates, ...[more]

PMID: 33242915

Similar Datasets

Project description:Aim:To compare implant survival rate and marginal bone loss (MBL) of immediately loaded single implants inserted by using ultrasonic implant site preparation (UISP) (test) and conventional rotary instrumentation (control). Methods:Two single implants were inserted for each patient: after randomization, test site was prepared by using an ultrasonic device (Piezosurgery Touch, Mectron, Italy) and control site was prepared by using the drills of the selected implant system (Premium AZT, Sweden & Martina, Italy), until reaching a final diameter of 3?mm in both groups. Identical implants (3.8x11.5?mm) were inserted in all sites at crestal level. Impressions were taken and screwed resin single crowns with platform-switched provisional abutments were delivered with 48 hours. Periapical radiographs were taken at provisional crown insertion (T0), 6 months (T1) and one year (T2) after prosthetic loading to measure MBL. All data were tested for normality and subsequently analyzed by paired samples t-test and forward multiple linear regression. Results:Forty-eight patients were treated in six centers with the insertion of ninety-six implants (48 test; 48 control). Four implants in four patients failed within the first six months of healing (two in test group; two in control group; no difference between groups). Forty patients (age 60.1±10.7 years; 22 female, 18 male) were included in the final analysis. Mean MBL after six months of loading was 1.39±1.03?mm in the test group and 1.42±1.16?mm in the control group (p>0.05) and after one year was 1.92±1.14?mm and 2.14±1.55?mm in test and control, respectively (p>0.05). Conclusions:No differences in survival rate and MBL were demonstrated between UISP and conventional site preparation with rotary instruments in immediately loaded dental implants: UISP, with its characteristics of enhanced surgical control and safety in proximity of delicate structures, may be used as a reliable alternative to the traditional drilling systems.

Project description:The study aimed to clinically estimate an influence of a 635 nm diode laser on the stability of orthodontic mini-implants, to assess mini-implants loss, and to evaluate a pain level after the treatment. The randomized clinical split-mouth trial included 20 subjects (13 women and 7 men; age: 32.5 ± 6.1 years), 40 implants (RMO, West Colfax Ave., Denver, CO, USA) with a diameter 1.4 mm and length of 10 mm. Mini-implants were placed in the area of the attached gingiva between the second premolar and first molar teeth, 2 mm below the mucogingival junction of both sides of the maxilla. Each implant on the right side (G1, n = 20) of the maxilla was irradiated with a diode laser, and the implants on the opposite side (left, G2, n = 20) were a control group (without laser irradiation). The 635-nm laser parameters; dose: 10 J per point (20 J/cm2), time: 100 s per point, two points (irradiation on a buccal, and a palatal side of the alveolus/implant), the total energy per session 20 J. Laser application protocol: immediately and 3, 6, 9, 12, 15, and 30 days after surgery. The total energy after all therapeutic sessions was 140 J. The implants' stability was measured employing a Periotest device (Periotest Test Value-PTV) immediately and 3, 6, 9, 12, 15, 30, and 60 days after the insertion of the mini-implants. We found significantly higher secondary stability, lower mean PTV (6.18 ± 5.30) and (1.51 ± 2.25), for self-drilling mini-implants (G1, test group) in contrast to the control, G2 group (9.17 ± 8.25) and (5.00 ± 3.24), after 30 (p = 0.0003) and 60 days (p = 0.0000). Moreover, the analysis of the mini-implants stability after 635-nm diode laser application revealed significant higher stability in comparison with none irradiated implants (G2 group) after 3 days. (p = 0.0000) There was no significant difference in pain level measured on the NRS-11 scale on both sides of the maxilla. (p = 0.3665) An important finding was that all inserted mini-implants survived during a two-month observation period. 635-nm diode laser at laser irradiation increases the secondary stability of orthodontic mini-implants.

Dataset Information

Role of New Hydrophilic Surfaces on Early Success Rate and Implant Stability: 1-Year Post-loading Results of a Multicenter, Split-Mouth, Randomized Controlled Trial.

Objective

Materials and methods

Results

Conclusions

Publications

Role of New Hydrophilic Surfaces on Early Success Rate and Implant Stability: 1-Year Post-loading Results of a Multicenter, Split-Mouth, Randomized Controlled Trial.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets