Biomimetic bone-like composites as osteo-odonto-keratoprosthesis skirt substitutes.

ABSTRACT: Osteo-odonto-keratoprostheses, incorporating dental laminate material as an anchoring skirt around a central poly(methyl methacrylate) (PMMA) optic, have been used to replace the cornea for many years. However, there are many intricacies associated with the use of autologous dental laminate material, surgical complexity and skirt erosion. Tissue engineering approaches to bone replacement may offer suitable alternatives in osteo-odonto-keratoprosthesis (OOKP) surgery. In this study, a hydrogel polymer composite was investigated as a synthetic substitute for the OOKP skirt. A novel high strength interpenetrating network (IPN) hydrogel composite with nano-crystalline hydroxyapatite (nHAp) coated poly (lactic-co-glycolic acid) PLGA microspheres was created to mimic the alveo-dental lamina by employing agarose and poly(ethylene glycol) diacrylate (PEGDA) polymers. The incorporation of nHAp coated PLGA microspheres into the hybrid IPN network provide a micro-environment similar to that of skeletal tissues and improve cellular response. Agarose was used as a first network to encapsulate keratocytes/3T3 fibroblasts and PEGDA (6000?Da) was used as a second network with varying concentrations (20 and 40?wt %) to produce a strong and biocompatible scaffold. An increased concentration of either agarose or PEG-DA and incorporation of nHAp coated PLGA microspheres led to an increase in the elastic modulus. The IPN hydrogel combinations supported the adhesion and proliferation of both fibroblast and ocular human keratocyte cell types during in in-vitro testing. The cells endured the encapsulation process into the IPN and remained viable at 1?week post-encapsulation in the presence of nHAp coated microspheres. The material did not induce significant production of inflammatory cytokine IL-6 in comparison to a positive control (p?

SUBMITTER: Avadhanam V

PROVIDER: S-EPMC7917574 | biostudies-literature | 2021 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Biomimetic bone-like composites as osteo-odonto-keratoprosthesis skirt substitutes.

Avadhanam Venkata V Ingavle Ganesh G Zheng Yishan Y Kumar Sandeep S Liu Christopher C Sandeman Susan S

Journal of biomaterials applications 20201111 8

Osteo-odonto-keratoprostheses, incorporating dental laminate material as an anchoring skirt around a central poly(methyl methacrylate) (PMMA) optic, have been used to replace the cornea for many years. However, there are many intricacies associated with the use of autologous dental laminate material, surgical complexity and skirt erosion. Tissue engineering approaches to bone replacement may offer suitable alternatives in osteo-odonto-keratoprosthesis (OOKP) surgery. In this study, a hydrogel po ...[more]

PMID: 33174770

Similar Datasets

Project description:UnlabelledThe vitreous humor of the eye is a biological hydrogel principally composed of collagen fibers interspersed with hyaluronic acid. Certain pathological conditions necessitate its removal and replacement. Current substitutes, like silicone oils and perfluorocarbons, are not biomimetic and have known complications. In this study, we have developed an in situ forming two-component biomimetic hydrogel with tunable mechanical and osmotic properties. The components are gellan, an analogue of collagen, and poly(methacrylamide-co-methacrylate), an analogue of hyaluronic acid; both endowed with thiol side groups. We used response surface methodology to consider seventeen possible hydrogels to determine how each component affects the optical, mechanical, sol-gel transition temperature and swelling properties. The optical and physical properties of the hydrogels were similar to vitreous. The shear storage moduli ranged from 3 to 358Pa at 1Hz and sol-gel transition temperatures from 35.5 to 43°C. The hydrogel had the ability to remain swollen without degradation for four weeks in vitro. Three hydrogels were tested for biocompatibility on primary porcine retinal pigment epithelial cells, human retinal pigment epithelial cells, and fibroblast (3T3/NIH) cells, by electric cell-substrate impedance sensing system. The two-component hydrogels allowed for the tuning and optimizing of mechanical, swelling, and transition temperature to obtain three biocompatible hydrogels with properties similar to the vitreous. Future studies include testing of the optimized hydrogels in animal models for use as a long-term substitute, whose preliminary results are mentioned.Statement of significanceAlthough hydrogels are researched as long-term vitreous substitute, none have advanced sufficiently to reach clinical application. Our work focuses on the development of a novel two component in situ forming hydrogel that bio-mimic the natural vitreous. Our thiol-containing copolymers can be injected as an aqueous solution into the vitreous cavity wherein, at physiological temperature, the rigid component will instantaneously form a physical gel imbedding the random coil copolymer. Upon subsequent oxidation, the two components will form disulfide cross-links and a stable reversible hydrogel capable of providing osmotic pressure to reattach the retina. It may be left in the eye permanently or easily removed by injection of a simple reducing agent to cleave the disulfide bonds, rather than surgery. This contribution is significant because it is expected to provide patients with a much better quality of life by improving surgical outcomes, creating much less post-operative burden, and reducing the need for secondary surgeries.

Project description:Advances in the field of stem cell technology have stimulated the development and increased use of allogenic bone grafts containing live mesenchymal stem cells (MSCs), also known as cellular bone matrices (CBMs). It is estimated that CBMs comprise greater than 17% of all bone grafts and bone graft substitutes used.To critically evaluate CBMs, specifically their technical specifications, existing published data supporting their use, US Food and Drug Administration (FDA) regulation, cost, potential pitfalls, and other aspects pertaining to their use.Areview of literature.A series of Ovid, Medline, and Pubmed-National Library of Medicine/National Institutes of Health (www.ncbi.nlm.nih.gov) searches were performed. Only articles in English journals or published with English language translations were included. Level of evidence of the selected articles was assessed. Specific technical information on each CBM was obtained by direct communication from the companies marketing the individual products.Five different CBMs are currently available for use in spinal fusion surgery. There is a wide variation between the products with regard to the average donor age at harvest, total cellular concentration, percentage of MSCs, shelf life, and cell viability after defrosting. Three retrospective studies evaluating CBMs and fusion have shown fusion rates ranging from 90.2% to 92.3%, and multiple industry-sponsored trials are underway. No independent studies evaluating spinal fusion rates with the use of CBMs exist. All the commercially available CBMs claim to meet the FDA criteria under Section 361, 21 CFR Part 1271, and are not undergoing FDA premarket review. The CBMs claim to provide viable MSCs and are offered at a premium cost. Numerous challenges exist in regard to MSCs' survival, function, osteoblastic potential, and cytokine production once implanted into the intended host.Cellular bone matrices may be a promising bone augmentation technology in spinal fusion surgery. Although CBMs appear to be safe for use as bone graft substitutes, their efficacy in spinal fusion surgery remains highly inconclusive. Large, nonindustry sponsored studies evaluating the efficacy of CBMs are required. Without results from such studies, surgeons must be made aware of the potential pitfalls of CBMs in spinal fusion surgery. With the currently available data, there is insufficient evidence to support the use of CBMs as bone graft substitutes in spinal fusion surgery.

Dataset Information

Biomimetic bone-like composites as osteo-odonto-keratoprosthesis skirt substitutes.

Publications

Biomimetic bone-like composites as osteo-odonto-keratoprosthesis skirt substitutes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets