Surface Enhanced Raman Spectroscopy With Electrodeposited Copper Ultramicro-Wires With/Without Silver Nanostars Decoration.

ABSTRACT: The electrochemical preparation of arrays of copper ultramicrowires (CuUWs) by using porous membranes as templates is critically revisited, with the goal of obtaining cheap but efficient substrates for surface enhanced Raman spectroscopy (SERS). The role of the materials used for the electrodeposition is examined, comparing membranes of anodized aluminum oxide (AAO) vs. track-etched polycarbonate (PC) as well as copper vs. glassy carbon (GC) as electrode material. A voltammetric study performed on bare electrodes and potentiostatic tests on membrane coated electrodes allowed the optimization of the deposition parameters. The final arrays of CuUWs were obtained by chemical etching of the template, with NaOH for AAO and CH2Cl2 for PC. After total etching of the template, SERS spectra were recorded on CuUWs using benzenethiol as SERS probe with known spectral features. The CuUW substrates displayed good SERS properties, providing enhancement factor in the 103-104 range. Finally, it was demonstrated that higher Raman enhancement can be achieved when CuUWs are decorated with silver nanostars, supporting the formation of SERS active hot-spots at the bimetallic interface.

SUBMITTER: Longoni M

PROVIDER: S-EPMC7922343 | biostudies-literature | 2021 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Surface Enhanced Raman Spectroscopy With Electrodeposited Copper Ultramicro-Wires With/Without Silver Nanostars Decoration.

Longoni Margherita M Zalaffi Maria Sole MS de Ferri Lavinia L Stortini Angela Maria AM Pojana Giulio G Ugo Paolo P

Nanomaterials (Basel, Switzerland) 20210218 2

The electrochemical preparation of arrays of copper ultramicrowires (CuUWs) by using porous membranes as templates is critically revisited, with the goal of obtaining cheap but efficient substrates for surface enhanced Raman spectroscopy (SERS). The role of the materials used for the electrodeposition is examined, comparing membranes of anodized aluminum oxide (AAO) vs. track-etched polycarbonate (PC) as well as copper vs. glassy carbon (GC) as electrode material. A voltammetric study performed ...[more]

PMID: 33670549

Similar Datasets

Project description:In this study, a widely used colloid of Creighton AgNPs (ORI, 1-100 nm, mostly ≤ 40 nm, ∼10 μg mL-1) was rapidly manipulated via tangential flow filtration (TFF) for highly reproducible surface-enhanced (resonance) Raman spectroscopy (SE(R)RS) experiments down to the single-molecule (SM) level. The quasi-spherical AgNPs were size-selected, purified, and concentrated in two TFF fractions of a cutoff diameter of ∼40 nm: AgNP ≤ 40 (∼900 μg mL-1) and AgNP ≥ 40 (∼100 μg mL-1). The SE(R)S-based sensing capabilities of the two TFF fractions were then tested under pre-resonance (632.8 nm) and resonance (532.1 nm) excitation conditions for rhodamine 6G (R6G, 10-6-10-15 M). Both TFF isolates, AgNP ≤ 40 and AgNP ≥ 40, were more effective in adsorbing the R6G analyte (≥91%) than the original colloid (≥78%) at submonolayer coverages. Furthermore, the surface enhancement factors (SEF) of the two TFF fractions were markedly superior to those of ORI under all excitation conditions. SERS at 632.8 nm: only AgNP ≥ 40 enabled the detection of R6G at 10-9 M and produced the largest SEF (2.1 × 106). SE(R)RS and SM-SERRS at 532.1 nm: AgNP ≥ 40 gave rise to the largest SEF values (2.5 × 1010) corresponding to the SM regime down to 10-15 M of R6G. Nevertheless, AgNP ≤ 40 compensated for the size-dependence of the electromagnetic enhancements by an increase in the silver concentration, which led to SEF values comparable to those of AgNP ≥ 40 through additional resonance enhancements. TFF resulted into a ∼100-fold increase (AgNP ≤ 40) in the number of negatively charged AgNPs that were available to electrostatically bridge R6G cations and form SERRS "hot-spots" (AgNP-R6G-AgNP) within the focal volume. Evidently, the interplay between AgNP size, AgNP concentration, and excitation wavelength governs the SE(R)RS enhancements. This study demonstrated that TFF can facilitate the ecofriendly isolation of spherical AgNPs of controlled morphological and plasmonic properties for further enhancing their sensing capabilities as SE(R)RS substrates.

Dataset Information

Surface Enhanced Raman Spectroscopy With Electrodeposited Copper Ultramicro-Wires With/Without Silver Nanostars Decoration.

Publications

Surface Enhanced Raman Spectroscopy With Electrodeposited Copper Ultramicro-Wires With/Without Silver Nanostars Decoration.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets