The Effect of Fiber Type and Yarn Diameter on Superhydrophobicity, Self-Cleaning Property, and Water Spray Resistance.

ABSTRACT: In this study, we proved that micro/micro hierarchical structures are enough to achieve a superhydrophobic surface using polydimethylsiloxane (PDMS) dip-coating. Furthermore, the effect of fiber type and yarn diameter on superhydrophobicity and water spray resistance was investigated. Polyester fabrics with two types of fibers (staple fabric and filament) and three types of yarn diameters (177D, 314D, and 475D) were used. The changes in the surface properties and chemical composition were investigated. Static contact angles and shedding angles were measured for superhydrophobicity, and the self-cleaning test was conducted. Water spray repellency was also tested, as well as the water vapor transmission rate and air permeability. The PDMS-coated staple fabric showed better superhydrophobicity and oleophobicity than the PDMS-coated filament fabric, while the filament fabric showed good self-cleaning property and higher water spray repellency level. When the yarn diameter increased, the fabrics needed higher PDMS concentrations and longer coating durations for uniform coating. The water vapor transmission rate and air permeability did not change significantly after coating. Therefore, the superhydrophobic micro/micro hierarchical fabrics produced using the simple method of this study are more practical and have great potential for mass production than other superhydrophobic textiles prepared using the chemical methods.

SUBMITTER: Oh JH

PROVIDER: S-EPMC7962189 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The cross-linking of borates enhances the intercellular structural connection, resulting in the creation of a mechanically superior structural material composed of lignocellulose and borate. This is accomplished by employing a mechanical pretreatment procedure and a binder-free hot-pressing method. Nevertheless, these materials frequently encounter constraints in humid environments, making it challenging to simultaneously achieve the desired performance objectives. Here, the prepressed bulk of microfibrillated cellulose is modified and subjected to hot pressing, while ensuring that the enhanced physical and mechanical properties of lignocellulosic recombinant materials are maintained. This modified material is termed the microfibrillated cellulose composite laminate (MCCL). These findings indicate that the application of compression, shear, and friction forces during hot-pressing results in the formation of a compact laminated structure using pine lignocellulose. The self-cleaning MCCL exhibits significantly improved mechanical properties compared with untreated lignocellulose materials (ULM). Specifically, the flexural strength (MOR), modulus of elasticity (MOE), and internal bonding strength (IB) of self-cleaning MCCL are found to be 5 times, 2.5 times, and 4.1 times higher, respectively, than those of ULM. This improvement in the pine lignocellulose can be attributed to the enhanced layering and branching that occurs during mechanical milling. This results in a higher proportion of ester and hydrogen bonds, as well as an increased exposure of hydroxyl groups. As a result, the modified MCCL exhibits self-cleaning properties, as evidenced by its surface water contact angle (WCA) of 152°. The rolling/jumping water droplets, which contain pollutants, effectively remove graphite powder from the surface, leaving it clean. Moreover, MCCL demonstrates exceptional dimensional stability and flame-retardant self-extinguishing properties, making it highly promising as a structural material in engineering technology.

Dataset Information

The Effect of Fiber Type and Yarn Diameter on Superhydrophobicity, Self-Cleaning Property, and Water Spray Resistance.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets