Effects of Counter Anions on AC and DC Electrical Conductivity in Poly(Dimethylsiloxane) Crosslinked by Metal-Ligand Coordination

ABSTRACT: There is an urgent need for the development of elastic dielectric materials for flexible organic field effect transistors (OFETs). In this work, detailed analysis of the AC and DC electrical conductivity of a series of flexible poly(dimethylsiloxane) (PDMS) polymers crosslinked by metal-ligand coordination in comparison to neat PDMS was performed for the first time by means of broadband dielectric spectroscopy. The ligand was 2,2-bipyridine-4,4-dicarboxylic amide, and Ni2+, Mn2+, and Zn2+ were introduced for Cl−, Br−, and I− salts. Introduction of metal salt and creation of coordination bonds resulted in higher permittivity values increasing in an order: neat PDMS < Ni2+ < Mn2+ < Zn2+; accompanied by conductivity values of the materials increasing in an order: neat PDMS < Cl− < I− < Br−. Conductivity relaxation time plot as a function of temperature, showed Vogel-Fulcher–Tammann dependance for the Br− salts and Arrhenius type for the Cl− and I− salts. Performed study revealed that double-edged challenge can be obtained, i.e., dielectric materials with elevated value of dielectric permittivity without deterioration too much the non-conductive nature of the polymer. This opens up new perspectives for the production of flexible dielectrics suitable for gate insulators in OFETs. Among the synthesized organometallic materials, those with chlorides salts are the most promising for such applications.

SUBMITTER: Wrzesinska A

PROVIDER: S-EPMC8003853 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Dielectric Permittivity, AC Electrical Conductivity and Conduction Mechanism of High Crosslinked-Vinyl Polymers and Their Pd(OAc)2 Composites.

Project description:Semiconductor materials based on metal high crosslinked-vinyl polymer composites were prepared through loading of Pd(OAc)2 on both Poly(ethylene-1,2-diyl dimethacrylate) (poly(EDMA)) and poly(ethylene-1,2-diyl dimethacrylate-co-methyl methacrylate) (Poly(EDMA-co-MMA)). The thermochemical properties for both poly(EDMA) and poly(EDMA-co-MMA) were investigated by thermal gravimetric analysis TGA technique. The dielectric permittivity, AC electrical conductivity and conduction mechanism for all the prepared polymers and their Pd(OAc)2 composites were studied. The results showed that the loading of polymers with Pd(OAc)2 led to an increase in the magnitudes of both the dielectric permittivity and AC electrical conductivity (σac). The value of σac increased from 1.38 × 10-5 to 5.84 × 10-5 S m-1 and from 6.40 × 10-6 to 2.48 × 10-5 S m-1 for poly(EDMA) and poly(EDMA-co-MMA), respectively, at 1 MHz and 340 K after loading with Pd(OAc)2. Additionally, all the prepared polymers and composites were considered as semiconductors at all the test frequencies and in the temperature range of 300-340 K. Furthermore, it seems that a conduction mechanism for all the samples could be Quantum Mechanical Tunneling (QMT).

| S-EPMC8434503 | biostudies-literature

Toughening self-healing elastomer crosslinked by metal-ligand coordination through mixed counter anion dynamics.

Project description:Mechanically tough and self-healable polymeric materials have found widespread applications in a sustainable future. However, coherent strategies for mechanically tough self-healing polymers are still lacking due to a trade-off relationship between mechanical robustness and viscoelasticity. Here, we disclose a toughening strategy for self-healing elastomers crosslinked by metal-ligand coordination. Emphasis was placed on the effects of counter anions on the dynamic mechanical behaviors of polymer networks. As the coordinating ability of the counter anion increases, the binding of the anion leads to slower dynamics, thus limiting the stretchability and increasing the stiffness. Additionally, multimodal anions that can have diverse coordination modes provide unexpected dynamicity. By simply mixing multimodal and non-coordinating anions, we found a significant synergistic effect on mechanical toughness ( > 3 fold) and self-healing efficiency, which provides new insights into the design of coordination-based tough self-healing polymers.

| S-EPMC10439188 | biostudies-literature

Plasma Treatment of Poly(ethylene terephthalate) Films and Chitosan Deposition: DC- vs. AC-Discharge.

Project description:Plasma treatment is one of the most promising tools to control surface properties of materials tailored for biomedical application. Among a variety of processing conditions, such as the nature of the working gas and time of treatment, discharge type is rarely studied, because it is mainly fixed by equipment used. This study aimed to investigate the effect of discharge type (direct vs. alternated current) using air as the working gas on plasma treatment of poly(ethylene terephthalate) films, in terms of their surface chemical structure, morphology and properties using X-ray photoelectron spectroscopy, scanning electron microscopy, atomic force microscopy and contact angle measurements. The effect of the observed changes in terms of subsequent chitosan immobilization on plasma-treated films was also evaluated. The ability of native, plasma-treated and chitosan-coated films to support adhesion and growth of mesenchymal stem cells was studied to determine the practicability of this approach for the biomedical application of poly(ethylene terephthalate) films.

| S-EPMC7040612 | biostudies-literature

Surface Coating with Hyaluronic Acid-Gelatin-Crosslinked Hydrogel on Gelatin-Conjugated Poly(dimethylsiloxane) for Implantable Medical Device-Induced Fibrosis.

Project description:Polydimethylsiloxane (PDMS) is a biocompatible polymer that has been applied in many fields. However, the surface hydrophobicity of PDMS can limit successful implementation, and this must be reduced by surface modification to improve biocompatibility. In this study, we modified the PDMS surface with a hydrogel and investigated the effect of this on hydrophilicity, bacterial adhesion, cell viability, immune response, and biocompatibility of PDMS. Hydrogels were created from hyaluronic acid and gelatin using a Schiff-base reaction. The PDMS surface and hydrogel were characterized using nuclear magnetic resonance, X-ray photoelectron spectroscopy, attenuated total reflection Fourier-transform infrared spectroscopy, and scanning electron microscopy. The hydrophilicity of the surface was confirmed via a decrease in the water contact angle. Bacterial anti-adhesion was demonstrated for Pseudomonas aeruginosa, Ralstonia pickettii, and Staphylococcus epidermidis, and viability and improved distribution of human-derived adipose stem cells were also confirmed. Decreased capsular tissue responses were observed in vivo with looser collagen distribution and reduced cytokine expression on the hydrogel-coated surface. Hydrogel coating on treated PDMS is a promising method to improve the surface hydrophilicity and biocompatibility for surface modification of biomedical applications.

| S-EPMC7922955 | biostudies-literature

A two-dimensional ?-d conjugated coordination polymer with extremely high electrical conductivity and ambipolar transport behaviour.

Project description:Currently, studies on organic two-dimensional (2D) materials with special optic-electronic properties are attracting great research interest. However, 2D organic systems possessing promising electrical transport properties are still rare. Here a highly crystalline thin film of a copper coordination polymer, Cu-BHT (BHT=benzenehexathiol), is prepared via a liquid-liquid interface reaction between BHT/dichloromethane and copper(II) nitrate/H2O. The morphology and structure characterization reveal that this film is piled up by nanosheets of 2D lattice of [Cu3(C6S6)]n, which is further verified by quantum simulation. Four-probe measurements show that the room temperature conductivity of this material can reach up to 1,580?S?cm(-1), which is the highest value ever reported for coordination polymers. Meanwhile, it displays ambipolar charge transport behaviour and extremely high electron and hole mobilities (99?cm(2?)V(-1?)s(-1) for holes and 116?cm(2?)V(-1?)s(-1) for electrons) under field-effect modulation.

| S-EPMC4490364 | biostudies-literature

Pressure induced polymerization of acetylide anions in CaC<sub>2</sub> and 10<sup>7</sup> fold enhancement of electrical conductivity.

Project description:Transformation between different types of carbon-carbon bonding in carbides often results in a dramatic change of physical and chemical properties. Under external pressure, unsaturated carbon atoms form new covalent bonds regardless of the electrostatic repulsion. It was predicted that calcium acetylide (also known as calcium carbide, CaC2) polymerizes to form calcium polyacetylide, calcium polyacenide and calcium graphenide under high pressure. In this work, the phase transitions of CaC2 under external pressure were systematically investigated, and the amorphous phase was studied in detail for the first time. Polycarbide anions like C66- are identified with gas chromatography-mass spectrometry and several other techniques, which evidences the pressure induced polymerization of the acetylide anions and suggests the existence of the polyacenide fragment. Additionally, the process of polymerization is accompanied with a 107 fold enhancement of the electrical conductivity. The polymerization of acetylide anions demonstrates that high pressure compression is a viable route to synthesize novel metal polycarbides and materials with extended carbon networks, while shedding light on the synthesis of more complicated metal organics.

| S-EPMC5458717 | biostudies-literature

Ionic poly(dimethylsiloxane)–silica nanocomposites: Dispersion and self-healing

Project description:Abstract

| S-EPMC9947054 | biostudies-literature

Electrical conductivity of ice VII.

Project description:It was discovered that a peak appears near a pressure of Pc = 10 GPa in the electrical conductivity of ice VII as measured through impedance spectroscopy in a diamond anvil cell (DAC) during the process of compression from 2 GPa to 40 GPa at room temperature. The activation energy for the conductivity measured in the cooling/heating process between 278 K and 303 K reached a minimum near Pc. Theoretical modelling and molecular dynamics simulations suggest that the origin of this unique peak is the transition of the major charge carriers from the rotational defects to the ionic defects.

| S-EPMC4105784 | biostudies-literature

Green Composites of Poly(3-hydroxybutyrate) Containing Graphene Nanoplatelets with Desirable Electrical Conductivity and Oxygen Barrier Properties.

Project description:Poly(3-hydroxybutyrate), a green polymer originating from prokaryotic microbes, has been used to prepare composites with graphene nanoplatelets (GnP) at different concentrations. The films were fabricated by drop-casting and were hot-pressed at a temperature lower than their melting point to provide the molecular chains enough energy to reorientate while avoiding melting and degradation. It was found that hot-pressing increases crystallinity and improves mechanical properties. The Young's modulus increased from 1.2 to 1.6 GPa for the poly(3-hydroxybutyrate) (P(3HB)) films and from 0.5 to 2.2 GPa for the 15 wt % P(3HB)/GnP composites. Electrical resistivity decreases enormously with GnP concentration and hot-pressing, reaching 6 Ω sq-1 for the hot-pressed 30 wt % P(3HB)/GnP composite. Finally, the hot-pressed P(3HB) samples exhibit remarkable oxygen barrier properties, with oxygen permeability reaching 2800 mL μm m-2 day-1, which becomes 895 mL μm m-2 day-1 when 15% GnP is added to the biopolymer matrix, one of the lowest values known for biopolymers and biocomposites. We propose that these biocomposites are used for elastic packaging and electronics.

| S-EPMC6881833 | biostudies-literature

AC conductivity and correlation effects in nano-granular Pt/C.

Project description:Nano-granular metals are materials that fall into the general class of granular electronic systems in which the interplay of electronic correlations, disorder and finite size effects can be studied. The charge transport in nano-granular metals is dominated by thermally-assisted, sequential and correlated tunneling over a temperature-dependent number of metallic grains. Here we study the frequency-dependent conductivity (AC conductivity) of nano-granular Platinum with Pt nano-grains embedded into amorphous carbon (C). We focus on the transport regime on the insulating side of the insulator metal transition reflected by a set of samples covering a range of tunnel-coupling strengths. In this transport regime polarization contributions to the AC conductivity are small and correlation effects in the transport of free charges are expected to be particularly pronounced. We find a universal behavior in the frequency dependence that can be traced back to the temperature-dependent zero-frequency conductivity (DC conductivity) of Pt/C within a simple lumped-circuit analysis. Our results are in contradistinction to previous work on nano-granular Pd/[Formula: see text] in the very weak coupling regime where polarization contributions to the AC conductivity dominated. We describe possible future applications of nano-granular metals in proximity impedance spectroscopy of dielectric materials.

| S-EPMC8313567 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data