An Intelligent Fire-Protection Coating Based on Ammonium Polyphosphate/Epoxy Composites and Laser-Induced Graphene.

ABSTRACT: Fire-protection coatings with a self-monitoring ability play a critical role in safety and security. An intelligent fire-protection coating can protect humans from personal and property damage. In this work, we report the fabrication of a low-cost and facile intelligent fire coating based on a composite of ammonium polyphosphate and epoxy (APP/EP). The composite was processed using laser scribing, which led to a laser-induced graphene (LIG) layer on the APP/EP surface via a photothermal effect. The C-O, C=O, P-O, and N-C bonds in the flame-retardant APP/EP composite were broken during the laser scribing, while the remaining carbon atoms recombined to generate the graphene layer. A proof-of-concept was achieved by demonstrating the use of LIG in supercapacitors, as a temperature sensor, and as a hazard detection device based on the shape memory effect of the APP/EP composite. The intelligent flame protection coating had a high flame retardancy, which increased the time to ignition (TTI) from 21 s to 57 s, and the limiting oxygen index (LOI) value increased to 37%. The total amount of heat and smoke released during combustion was effectively suppressed by ≈ 71.1% and ≈ 74.1%, respectively. The maximum mass-specific supercapacitance could reach 245.6 F·g^-1. The additional LIG layer enables applications of the device as a LIG-APP/EP temperature sensor and allows for monitoring of the deformation according to its shape memory effect. The direct laser scribing of graphene from APP/EP in an air atmosphere provides a convenient and practical approach for the fabrication of flame-retardant electronics.

SUBMITTER: Yang W

PROVIDER: S-EPMC8004711 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Reinforcement of Epoxy Composites with Graphite-Graphene Structures.

Project description:As a result of the research, the possibility of directional control of the operational properties of epoxy composites by the use of small additives of thermally expanded graphite-graphene structures has been proved. The rational content of the structuring additive in the composition of the epoxy composite (0.05 parts by mass.) was selected, which ensured an increase in the studied complex of physico-mechanical properties. The influence of thermally expanded graphite on the process of structure formation of an epoxy composite has been established. The addition of thermally expanded graphite increases thermal, fire and heat resistance as well as the coefficient of heat-conducting epoxy composite.

| S-EPMC6838145 | biostudies-literature

Toward Sustainable Composites: Graphene-Modified Jute Fiber Composites with Bio-Based Epoxy Resin.

Project description:Sustainable natural fiber reinforced composites have attracted significant interest due to the growing environmental concerns with conventional synthetic fiber as well as petroleum-based resins. One promising approach to reducing the large carbon footprint of petroleum-based resins is the use of bio-based thermoset resins. However, current fiber-reinforced bio-based epoxy composites exhibit relatively lower mechanical properties such as tensile, flexural strength, and modulus, which limits their wider application. Here the fabrication of high-performance composites using jute fibers is reported, modified with graphene nanoplates (GNP) and graphene oxide (GO), and reinforced with bio-based epoxy resin. It is demonstrated that physical and chemical treatments of jute fibers significantly improve their fiber volume fraction (Vf) and matrix adhesion, leading to enhanced mechanical properties of the resulting Jute/Bio-epoxy (J/BE) composites. Furthermore, the incorporation of GNP and GO further increases the tensile and flexural strength of the J/BE composites. The study reveals the potential of graphene-based jute fiber-reinforced composites with bio-based epoxy resin as a sustainable and high-performance material for a wide range of applications. This work contributes to the development of sustainable composites that have the potential to reduce the negative environmental impact of conventional materials while also offering improved mechanical properties.

| S-EPMC10517308 | biostudies-literature

Graphene-graphite hybrid epoxy composites with controllable workability for thermal management.

Project description:The substantial heat generation in highly dense electronic devices requires the use of materials tailored to facilitate efficient thermal management. The design of such materials may be based on the loading of thermally conductive fillers into the polymer matrix applied - as a thermal interface material - on the interface between two surfaces to reduce contact resistance. On the one hand, these additives enhance the thermal conductivity of the composite, but on the other hand, they increase the viscosity of the composite and hence impair its workability. This in turn could negatively affect the device-matrix interface. To address this problem, we suggest a tunable composite material comprising a combination of two different carbon-based fillers, graphene nanoplatelets (GNPs) and graphite. By adjusting the GNP:graphite concentration ratio and the total concentration of the fillers, we were able to fine tune the thermal conductivity and the workability of the hybrid polymer composite. To facilitate the optimal design of materials for thermal management, we constructed a 'concentration-thermal conductivity-viscosity phase diagram'. This hybrid approach thus offers solutions for thermal management applications, providing both finely tuned composite thermal properties and workability. We demonstrate the utility of this approach by fabricating a thermal interface material with tunable workability and testing it in a model electronic device.

| S-EPMC6334801 | biostudies-literature

Self-Extinguishing Resin Transfer Molding Composites Using Non-Fire-Retardant Epoxy Resin.

Project description:Introducing fire-retardant additives or building blocks into resins is a widely adopted method used for improving the fire retardancy of epoxy composites. However, the increase in viscosity and the presence of insoluble additives accompanied by resin modification remain challenges for resin transfer molding (RTM) processing. We developed a robust approach for fabricating self-extinguishing RTM composites using unmodified and flammable resins. To avoid the effects on resin fluidity and processing, we loaded the flame retardant into tackifiers instead of resins. We found that the halogen-free flame retardant, a microencapsulated red phosphorus (MRP) additive, was enriched on fabric surfaces, which endowed the composites with excellent fire retardancy. The composites showed a 79.2% increase in the limiting oxygen index, a 29.2% reduction in heat release during combustion, and could self-extinguish within two seconds after ignition. Almost no effect on the mechanical properties was observed. This approach is simple, inexpensive, and basically applicable to all resins for fabricating RTM composites. This approach adapts insoluble flame retardants to RTM processing. We envision that this approach could be extended to load other functions (radar absorbing, conductivity, etc.) into RTM composites, broadening the application of RTM processing in the field of advanced functional materials.

| S-EPMC6315867 | biostudies-other

Variation of mechanical and thermal properties in sustainable graphene oxide/epoxy composites.

Project description:In this work, the functional graphene oxide (bGO) was facilely synthesized through a grafted reaction between graphene oxide (GO) and bio-based bis-furan di-epoxide (BFDE). The structure of bGO was confirmed by FTIR spectra and Raman spectra. The properties of polymer composite materials depend on the distribution of the nanofiller in the matrix and due to the presence of polymer chains our bGO sheets exhibit a better dispersibility in solvents and polymer matrix, which provides a potential opportunity for the preparation of BFDE composites with excellent performance. Bio-based BFDE composites containing 0.05-0.5 wt.% of bGO exhibit superior mechanical and thermal properties. The addition of just 0.5?wt% such bGO to an BFDE causes 80%, 49%, 21%, 69% and 97% enhancement in tensile strength, flexural strength, flexural modulus, critical stress intensity factor and critical strain energy release rate, respectively. The thermal decomposition temperature Td of bGO/BFDE composites was increased about ~17?°C compared to blank BFDE sample. In addition, we found that introducing unmodified GO to epoxy matrix lead to an insignificant increase of the thermal property of the resulting GO/BFDE composites. The enhanced mechanical properties and thermal properties of bGO/BFDE composites could be attributed to strong interfacial interactions and high affinity between bGO and epoxy matrix.

| S-EPMC6224379 | biostudies-literature

Graphene-Based Materials as Strain Sensors in Glass Fiber/Epoxy Model Composites.

Project description:The ability of graphene-based materials to act as strain sensors in glass fiber/epoxy model composites by using Raman spectroscopy has been investigated. The strain reporting performance of two types of graphene nanoplatelets (GNPs) was compared with that of graphene produced by chemical vapor deposition (CVD). The strain sensitivity of the thicker GNPs was impeded by their limited aspect ratio and weak interaction between flakes and fibers. The discontinuity of the GNP coating and inconsistency in properties among individual platelets led to scatter in the reported strains. In comparison, continuous and homogeneous CVD grown graphene was more accurate as a strain sensor and suitable for point-by-point strain reporting. The Raman mapping results of CVD graphene and its behavior under cyclic deformation show reversible and reliable strain sensing at low strain levels (up to 0.6% matrix strain), above which interfacial sliding of the CVD graphene layer was observed through an in situ Raman spectroscopic study.

| S-EPMC7007000 | biostudies-literature

Vitrimer Chemistry Assisted Fabrication of Aligned, Healable, and Recyclable Graphene/Epoxy Composites.

Project description:The alignment is a key factor to fully exploit the potential of graphene in reinforcement of polymer composites. However, it is still a challenge to orientate graphene in thermosets because of the insoluble and infusible features of the later. In this paper, we report a facile and scalable hot press method to fabricate aligned graphene nanoplate (GnP)/epoxy composites by utilizing the dynamic character of epoxy vitrimer. The bond exchange and topological rearrangement associated viscous flow of epoxy vitrimer during hot press allows the spontaneous orientation of GnP in matrix because the 2D structure and volume exclusion effect. SEM images demonstrate the orientation of GnP, while tensile test reveals the significantly increased reinforcement effect of GnP on matrix after hot press. Moreover, the dynamic reaction of epoxy vitrimer confers good healability and recyclability to the aligned composites as confirmed by the nearly fully recovered mechanical properties of the healed sample after cutting, and the recycled sample after grinding. This work is expected to provide new opportunity for fabrication of aligned thermosetting composites.

| S-EPMC6753619 | biostudies-literature

Improved Flame-Retardant and Ceramifiable Properties of EVA Composites by Combination of Ammonium Polyphosphate and Aluminum Hydroxide.

Project description:Ceramifiable flame-retardant ethylene-vinyl acetate (EVA) copolymer composites for wire and cable sheathing materials were prepared through melt compounding with ammonium polyphosphate (APP), aluminum hydroxide (ATH) and fluorophlogopite mica as the addition agents. The effects of ammonium polyphosphate, alumina trihydrate, and APP/ATH hybrid on the flame retardant, as well as on the thermal and ceramifiable properties of EVA composites, were investigated. The results demonstrated that the composites with the ratio of APP:ATH = 1:1 displayed the best flame retardancy and the greatest char residues among the various EVA composites. The tensile strength of the composites was 6.8 MPa, and the residue strength sintered at 1000 °C reached 5.2 MPa. The effect of sintering temperature on the ceramifiable properties, microstructures, and crystalline phases of the sintered specimen was subsequently investigated through X-ray diffraction, Fourier transform infrared, and scanning electron microscopy. The XRD and FTIR results demonstrated that the crystal structure of mica was disintegrated, while magnesium orthophosphate (Mg?(PO?)?) was simultaneously produced at an elevated temperature, indicating that the ceramization of EVA composites had occurred. The SEM results demonstrated that a more continuous and compact microstructure was produced with the rise in the sintering temperature. This contributed to the flexural strength improvement of the ceramics.

| S-EPMC6401787 | biostudies-literature

High Mechanical and Thermal Properties of Epoxy Composites with Liquid Crystalline Polyurethane Modified Graphene.

Project description:Graphene nanosheets (GNs) often result in incompatibility with the hydrophobic polymer matrix, and the tendency to form aggregates during processing. Herein, liquid crystalline polyurethane modified GNs (GPLP) were obtained by ??? stacking interactions between GNs and perylene bisimide derivatives, and then in-situ polymerization of liquid-crystalline polyurethane. Spectroscopic studies, elemental analysis, and thermal properties confirmed the successful ??? stacking and the integrated structure of GPLP. The good dispersion state of GPLP in the epoxy matrix (EP), and the strong interactions between GPLP and EP, lead to the significant improvement of the thermal and mechanical performance of the GPLP/EP composites. The impact strength, Young's modulus, tensile strength, and toughness of the GPLP/EP composites with 1.47 wt % GNs reached the highest values of 54.31 kJ/m², 530.8 MPa, 112.33 MPa and 863 J/m³, which significantly increased by 210%, 57%, 143%, and 122% compared to that of neat epoxy, respectively. As well, the glass transition temperature increased by a notable 33 °C. It is hoped that this work can be used to exploit more efficient methods to overcome the poor adhesion between GNs and polymers.

| S-EPMC6415506 | biostudies-literature

An intelligent artificial throat with sound-sensing ability based on laser induced graphene.

Project description:Traditional sound sources and sound detectors are usually independent and discrete in the human hearing range. To minimize the device size and integrate it with wearable electronics, there is an urgent requirement of realizing the functional integration of generating and detecting sound in a single device. Here we show an intelligent laser-induced graphene artificial throat, which can not only generate sound but also detect sound in a single device. More importantly, the intelligent artificial throat will significantly assist for the disabled, because the simple throat vibrations such as hum, cough and scream with different intensity or frequency from a mute person can be detected and converted into controllable sounds. Furthermore, the laser-induced graphene artificial throat has the advantage of one-step fabrication, high efficiency, excellent flexibility and low cost, and it will open practical applications in voice control, wearable electronics and many other areas.

| S-EPMC5333117 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data