Multilayer Alginate-Polycaprolactone Electrospun Membranes as Skin Wound Patches with Drug Delivery Abilities.

ABSTRACT: A multilayer nanofibrous membrane consisting of a layer of polycaprolactone and one of physically cross-linked alginate-embedding ZnO nanoparticles is prepared via electrospinning technique as potential wound healing patches with drug delivery capabilities. A washing-cross-linking protocol is developed to obtain stable materials at the same time removing poly(ethylene oxide), which was used here as a cospinning agent for alginate, without interfering with the membrane's peculiar nanofibrous structure. The mechanical behavior of the samples is assessed via a uniaxial tensile test showing appropriate resistance and manageability together with a good thermal stability as proved via thermogravimetric analysis. The polycaprolactone external layer enriches the samples with good liquid-repellent properties, whereas the alginate layer is able to promote tissue regeneration owing to its capability to promote cell viability and allow exudate removal and gas exchanges. Moreover, using methylene blue and methyl orange as model molecules, promising drug delivery abilities are observed for the mats. Indeed, depending on the nature and on the dye-loading concentration, the release kinetic can be easily tuned to obtain a slow controlled or a fast burst release. Consequently, the proposed alginate-polycaprolactone membrane represents a promising class of innovative, simple, and cost-effective wound healing patches appropriate for large-scale production.

SUBMITTER: Dodero A

PROVIDER: S-EPMC8008386 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Aim:The aim of the present work was to develop biodegradable alginate (ALG)-containing fibrous membranes intended for tissue repair, acting as both drug delivery systems and cell growth guidance. Methods:Membranes were prepared by electrospinning. Since ALG can be electrospun only when blended with other spinnable polymers, dextran (DEX) and polyethylene oxide (PEO) were investigated as process adjuvants. ALG/DEX mixtures, characterized by different rheological and conductivity properties, were prepared in phosphate buffer or deionized water; surfactants were added to modulate polymer solution surface tension. The Design of Experiments (DoE) approach (full factorial design) was used to investigate the role of polymer solution features (rheological properties, surface tension, and conductivity) on electrospun fiber morphology. A high viscosity at 1,000 s-1 (1.3-1.9 Pa.s) or a high pseudoplasticity index (?1.7), combined with a low surface tension (30-32 mN/m) and a low conductivity (800-1,000 ?S/cm), was responsible for the production of ALG/DEX homogeneous fibers. Such ranges were successfully employed for the preparation of ALG-containing fibers, using PEO, instead of DEX, as process adjuvant. ALG/DEX and ALG/PEO fibers were subsequently subjected to cross-linking/coating processes to make them slowly biodegradable in aqueous medium. In particular, ALG/PEO fibers were cross-linked and coated with CaCl2/chitosan solutions in water/ethanol mixtures. Due to DEX high content, ALG/DEX fibers were soaked in a polylactide-co-glycolide (PLGA) solution in ethyl acetate. Results:Both cross-linking and coating processes made fibers insoluble in physiological medium and produced an increase in their mechanical resistance, assessed by means of a tensile test. PLGA-coated ALG/DEX and chitosan-coated ALG/PEO fibers were biocompatible and able to support fibroblast adhesion. Conclusion:The DoE approach allowed to draw up guidelines useful for the preparation of homogeneous fibers, starting from mixtures of ALG and non-ionic polymers. Such fibers, upon coating, resulted to be good cell substrates, allowing cell adhesion and growth.

Dataset Information

Multilayer Alginate-Polycaprolactone Electrospun Membranes as Skin Wound Patches with Drug Delivery Abilities.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets