Transparent Bioplastic Derived from CO₂-Based Polymer Functionalized with Oregano Waste Extract toward Active Food Packaging.

ABSTRACT: Active packaging materials, biodegradable and from renewable resources, are the most promising substitutes of nonbiodegradable, petroleum-based plastics, toward green and sustainable packaging solutions. In this study, an innovative bioplastic system, composed of carbon dioxide-derived poly(propylene carbonate) (PPC) and nature-originated cellulose acetate (CA), was developed. The extract from oregano waste was incorporated into the bioplastics as a low-cost and effective antioxidant resource. Thin, freestanding, and flexible PPC.CA bioplastic films were obtained by a simple, easily scalable solvent casting technique. The pristine films, without the oregano extract, featured good transparency and high water vapor barrier ability, along with suitable mechanical and thermal properties that are comparable to commercial plastics used for packaging. Interestingly, the incorporation of oregano waste extract added to the bioplastics high UV protection and high antioxidant activity, suitable features for active food packaging applications, without compromising the intriguing properties of the pristine films. The biocomposite films were not only biocompatible but also started biodegrading after just 1 week in seawater. The reported biocomposites are foreseen as promising candidates for several packaging applications, but in particular for sustainable active food packaging.

SUBMITTER: Tran TN

PROVIDER: S-EPMC8011794 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Complement activation and cell uptake responses toward polymer-functionalized protein nanocapsules.

Project description:Self-assembling protein nanocapsules can be engineered for various bionanotechnology applications. Using the dodecahedral scaffold of the E2 subunit from pyruvate dehydrogenase, we introduced non-native surface cysteines for site-directed functionalization. The modified nanoparticle's structural, assembly, and thermostability properties were comparable to the wild-type scaffold (E2-WT), and after conjugation of poly(ethylene glycol) (PEG) to these cysteines, the nanoparticle remained intact and stable up to 79.7 ± 1.8 °C. PEGylation of particles reduced uptake by human monocyte-derived macrophages and MDA-MB-231 breast cancer cells, with decreased uptake as PEG chain length is increased. In vitro C4-depletion and C5a-production assays yielded 97.6 ± 10.8% serum C4 remaining and 40.1 ± 6.0 ng/mL C5a for E2-WT, demonstrating that complement activation is weak for non-PEGylated E2 nanoparticles. Conjugation of PEG to these particles moderately increased complement response to give 79.7 ± 6.0% C4 remaining and 87.6 ± 10.1 ng/mL C5a. Our results demonstrate that PEGylation of the E2 protein nanocapsules can modulate cellular uptake and induce low levels of complement activation, likely via the classical/lectin pathways.

| S-EPMC3322319 | biostudies-literature

Optically transparent semiconducting polymer nanonetwork for flexible and transparent electronics.

Project description:Simultaneously achieving high optical transparency and excellent charge mobility in semiconducting polymers has presented a challenge for the application of these materials in future "flexible" and "transparent" electronics (FTEs). Here, by blending only a small amount (?15 wt %) of a diketopyrrolopyrrole-based semiconducting polymer (DPP2T) into an inert polystyrene (PS) matrix, we introduce a polymer blend system that demonstrates both high field-effect transistor (FET) mobility and excellent optical transparency that approaches 100%. We discover that in a PS matrix, DPP2T forms a web-like, continuously connected nanonetwork that spreads throughout the thin film and provides highly efficient 2D charge pathways through extended intrachain conjugation. The remarkable physical properties achieved using our approach enable us to develop prototype high-performance FTE devices, including colorless all-polymer FET arrays and fully transparent FET-integrated polymer light-emitting diodes.

| S-EPMC5167166 | biostudies-literature

Improving the Lifetime of CsPbBr3 Perovskite in Water Using Self-Healing and Transparent Elastic Polymer Matrix.

Project description:This study developed a simple and efficient strategy to stabilize inorganic halide perovskite CsPbX3 at high relative humidity by embedding it into the matrix with elastic and self-healing features. The polymer matrix has a naturally hydrophobic characteristic of n-butyl acrylate segment (n-BA) and cross-linkable and healable moiety from N-(hydroxymethyl) acrylamide segment (NMA). It was chosen due to the provisions of both a surrounding protective layer for inorganic perovskite and elastic, as well as healing ability to the whole organic-inorganic composite. This fabricated CsPbBr3/PBA-co-PNMA composite was demonstrated to stably persist against the suffering from hydrolysis of perovskites when exposed to a high moisture environment. The PL intensity of the composite after crosslinking was found to be relatively stable after 30 days of exposure to air. Upon water immersion, the PL intensity of composite only showed a decrease of 32% after the first 6 h, then remained stable for 6 h afterward. Furthermore, this fabricated composite was not only flexible and relatively transparent but also exhibited excellent self-healing capability in ambient conditions (T = 25°C), in which the self-healing efficiency after 24 h was above 40%. The tensile strength and stretching ability of 5 wt% perovskite content in the random copolymer were observed to be 3.8 MPa and 553.5% respectively. Overall, flexible and self-healing properties combining with high luminescence characteristics are very promising materials for next-generation soft optical devices.

| S-EPMC7573164 | biostudies-literature

Fluidic Patterning of Transparent Polymer Heaters.

Project description:Semi-conducting polymers are promising materials for current and next generations of electronic devices, sensors and actuators, especially regarding their ability to conform to flexibles architectures. In particular, aqueous-based dispersions of semi-conducting complexes such as PEDOT:PSS can be printed using a variety of coating techniques and the conductivity of the final deposit may reach high values upon a proper treatment. The micro-structuration of these polymeric deposits remains challenging and of prime importance for further integration. We show here that a microfluidic post-treatment of PEDOT:PSS films of permits us to boost locally only their conductivity by several orders of magnitude, with a micron scale resolution. This is a fast process (~second), straightforward to upscale, that yields conductive patterns within the pristine film. Taking advantage of the localized Joule's effect, we evidence using quantitative thermography a very efficient heating behaviour of the conductive tracks, which makes these polymeric structures promising candidates for low cost, clean-room free electrodes for lab-on-chip applications.

| S-EPMC6212434 | biostudies-literature

Nano-cellulose derived bioplastic biomaterial data for vehicle bio-bumper from banana peel waste biomass.

Project description:The innovative study was carried out to produce nano-cellulose based bioplastic biomaterials for vehicle use coming after bioprocess technology. The data show that nano-cellulose particle size was 20 nm and negligible water absorption was 0.03% in the bioplastic. Moreover, burning test, size and shape characterizations, spray coating dye, energy test and firmness of bioplastic have been explored and compared with the standardization of synthetic vehicle plastic bumper following the American Society for Testing and Materials (ASTM). Tensile test was observed 120 MPa/kg m(3). In addition to that pH and cellulose content were found positive in the bioplastic compared to the synthetic plastic. Chemical tests like K, CO3, Cl2, Na were determined and shown positive results compared to the synthetic plastic using the EN-14214 (European Norm) standardization.

| S-EPMC4906129 | biostudies-literature

Fe3O4 Nanoparticles Functionalized with Polymer Ligand for T1-Weighted MRI In Vitro and In Vivo.

Project description:Magnetic resonance imaging (MRI) has gained wide interest in early accurate diagnoses due to the high resolution and low toxicity of magnetic nanoparticles. In order to develop potential alternatives of toxic Gd- or Mn-based chelating agents, we report the synthesis of water soluble ultra-small Fe3O4 nanoparticles by a modified co-precipitation method as T1-weighted positive contrast agents. The magnetic iron oxide nanoparticles (MIONs) were functionalized by polymer ligand dodecanthiol-polymethacrylic acid (DDT-PMAA) to enhance their colloidal stability. These MIONs have high longitudinal relaxivity (r1 = 8.18 mM-1·S-1) and exhibited good results in the in vitro and in vivo MR imaging. No toxicity was observed in cytotoxicity assay and histology toxicity analysis. The MIONs@DDT-PMAA(magnetic iron oxide nanoparticles @ dodecanthiol-polymethacrylic acid) present great potential as positive contrast agents for tumor diagnosis.

| S-EPMC6572598 | biostudies-literature

A highly stretchable, transparent, and conductive polymer.

Project description:Previous breakthroughs in stretchable electronics stem from strain engineering and nanocomposite approaches. Routes toward intrinsically stretchable molecular materials remain scarce but, if successful, will enable simpler fabrication processes, such as direct printing and coating, mechanically robust devices, and more intimate contact with objects. We report a highly stretchable conducting polymer, realized with a range of enhancers that serve a dual function: (i) they change morphology and (ii) they act as conductivity-enhancing dopants in poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS). The polymer films exhibit conductivities comparable to the best reported values for PEDOT:PSS, with over 3100 S/cm under 0% strain and over 4100 S/cm under 100% strain-among the highest for reported stretchable conductors. It is highly durable under cyclic loading, with the conductivity maintained at 3600 S/cm even after 1000 cycles to 100% strain. The conductivity remained above 100 S/cm under 600% strain, with a fracture strain of 800%, which is superior to even the best silver nanowire- or carbon nanotube-based stretchable conductor films. The combination of excellent electrical and mechanical properties allowed it to serve as interconnects for field-effect transistor arrays with a device density that is five times higher than typical lithographically patterned wavy interconnects.

| S-EPMC5345924 | biostudies-literature

Label-Free Detection of Small Organic Molecules by Molecularly Imprinted Polymer Functionalized Thermocouples: Toward In Vivo Applications.

Project description:Molecularly imprinted polymers (MIPs), synthetic polymeric receptors, have been combined successfully with thermal transducers for the detection of small molecules in recent years. However, up until now they have been combined with planar electrodes which limits their use for in vivo applications. In this work, a new biosensor platform is developed by roll-coating MIP particles onto thermocouples, functionalized with polylactic acid (PLLA). As a first proof-of-principle, MIPs for the neurotransmitter dopamine were incorporated into PLLA-coated thermocouples. The response of the synthetic receptor layer to an increasing concentration of dopamine in buffer was analyzed using a homemade heat-transfer setup. Binding of the template to the MIP layer blocks the heat transport through the thermocouple, leading to less heat loss to the environment and an overall higher temperature in the measuring chamber. The measured temperature increase is correlated to the neurotransmitter concentration, which enables measurement of dopamine levels in the micromolar regime. To demonstrate the general applicability of the proposed biosensor platform, thermocouples were functionalized with similar MIPs for cortisol and serotonin, indicating a similar response and limit-of-detection. As the platform does not require planar electrodes, it can easily be integrated in, e.g., a catheter. In this way, it is an excellent fit for the current niche in the market of therapeutics and diagnostics. Moreover, the use of a biocompatible and disposable PLLA-layer further illustrates its potential for in vivo diagnostics.

| S-EPMC5414145 | biostudies-literature

Surface Carbon Shell-Functionalized ZrO2 as Nanofiller in Polymer Gel Electrolyte-Based Dye-Sensitized Solar Cells.

Project description:We prepare dye-sensitized solar cells (DSSCs) fabricated with a poly (ethylene glycol) based polymer gel electrolytes (PGEs) incorporating surface carbon shell-functionalized ZrO2 nanoparticles (ZrO2-C) as nanofillers (NFs). ZrO2 are polymerized via atom transfer radical polymerization (ATRP) using poly (ethylene glycol) methyl ether methacrylate (POEM) as a scaffold to prepare the ZrO2-C through carbonization. The power conversion efficiency of DSSC with 12 wt% ZrO2-C/PGEs is 5.6%, exceeding that with PGEs (4.4%). The enhanced efficiency is attributed to Lewis acid-base interactions of ZrO2-C and poly (ethylene glycol), catalytic effect of the carbon shells of ZrO2-C, which results in reduced crystallinity, enhanced ion conductivity of electrolytes, decreased counterelectrode/electrolyte interfacial resistance, and improved charge transfer rate. These results demonstrate that ZrO2-C introduction to PGEs effectively improves the performance of DSSCs.

| S-EPMC6836208 | biostudies-literature

Optically transparent recombinant silk-elastinlike protein polymer films.

Project description:Recombinant protein polymers, evaluated extensively as biomaterials for applications in drug delivery and tissue engineering, are rarely reported as being optically transparent. Here we report the notable optical transparency of films composed of a genetically engineered silk-elastinlike protein polymer SELP-47K. SELP-47K films of 100 ?m in thickness display a transmittance of 93% in the wavelength range of 350-800 nm. While covalent cross-linking of SELP-47K via glutaraldehyde decreases its transmittance to 77% at the wavelength of 800 nm, noncovalent cross-linking using methanol slightly increases it to 95%. Non- and covalent cross-linking of SELP-47K films also influences their secondary structures and water contents. Cell viability and proliferation analyses further reveal the excellent cytocompatibility of both non- and covalently cross-linked SELP-47K films. The combination of high optical transparency and cytocompatibility of SELP-47K films, together with their previously reported outstanding mechanical properties, suggests that this protein polymer may be useful in unique, new biomedical applications.

| S-EPMC3041846 | biostudies-literature