Synthesis, Characterization of Chitosan-Aluminum Oxide Nanocomposite for Green Synthesis of Annulated Imidazopyrazol Thione Derivatives.

ABSTRACT: Chitosan-aluminum oxide nanocomposite was synthesized, characterized, and used as a green heterogeneous catalyst to synthesize novel imidazopyrazolylthione derivatives. Nanocomposite polymeric material was characterized by EDS-SEM and XRD. The powerful catalytic activity, and its base character of the nanocomposite, was used to synthesize imidazopyrazolylthione (1) in a good yield compared to traditional cyclocondensation synthesis. Using the nanocomposite catalyst, substitution of the thiol group (1) afforded the corresponding thiourea (2) and the corresponding ester (3). The efficiency of the nanocomposite over the traditional base organic catalyst, Et₃N and NaOH, makes it an effective, economic, and reproducible nontoxic catalyst. Moreover, the heterogeneous nanocomposite polymeric film was easily isolated from the reaction medium, and recycled up to four times, without a significant loss of its catalytic activity. The newly synthesized derivatives were screened as antibacterial agents and showed high potency. Molecular docking was also performed for a more in-depth investigation. The results of the docking studies have demonstrated that the docked compounds have strong interaction energies with both Gram-positive and Gram-negative bacteria.

SUBMITTER: Abdel-Naby AS

PROVIDER: S-EPMC8038599 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Chitosan-Strontium Oxide Nanocomposite: Preparation, Characterization, and Catalytic Potency in Thiadiazoles Synthesis.

Project description:Recently, Strontium oxide (SrO) nanoparticles (NPs) and hybrids outperformed older commercial catalysts in terms of catalytic performance. Herein, we present a microwave-assisted easy in situ solution casting approach for the manufacture of strontium oxide nanoparticles doped within a naturally occurring polymer, chitosan (CS), at varying weight percentages (2.5, 5, 10, 15, and 20 wt.% SrO/chitosan). To construct the new hybrid material as a thin film, the produced nanocomposite solutions were cast in petri dishes. The aim of the research was to synthesize these hybrid nanocomposites, characterize them, and evaluate their catalytic potential in a variety of organic processes. The strontium oxide-chitosan nanocomposites were characterized using Fourier transform infrared (FTIR), X-ray diffraction (XRD), and scanning electron microscope (SEM) techniques. All the results confirmed the formation of chitosan-strontium oxide nanocomposite. FTIR spectrum of nanocomposite showed the presence of a characteristic peak of Sr-O bond. Furthermore, XRD revealed that SrO treatment increased the crystallinity of chitosan. The particle size was calculated using the Debye-Scherrer formula, and it was determined to be around 36 nm. The CS-SrO nanocomposite has been proven to be a highly efficient base promoter for the synthesis of 2-hydrazono [1,3,4]thiadiazole derivatives. To optimize the catalytic method, the reaction factors were investigated. The approach has various advantages, including higher reaction yields, shorter reaction durations, and milder reaction conditions, as well as the catalyst's reusability for several applications.

| S-EPMC9322490 | biostudies-literature

Biodegradable Hybrid Nanocomposite of Chitosan/Gelatin and Green Synthesized Zinc Oxide Nanoparticles for Food Packaging.

Project description:In the context of emerging global concerns with synthetic plastic packaging, alternative natural biodegradable packaging materials are gaining increasing attention for food packaging applications. In this study, chitosan and gelatin nanocomposite hybrid films containing green synthesized zinc oxide (ZnO) nanoparticles (NPs) were developed and microstructural properties were studied. Antimicrobial activity of the developed films was evaluated using both Gram negative (Escherichia coli) and Gram positive bacteria (Staphylococcus aureus). Green synthesis protocol was used for the precipitation of ZnO NPs using fruit extract of Cassia fistula. The as-synthesized polyhedral ZnO NPs were in the range of 20-40 nm (average size ?29 nm). Reinforcement with ZnO NPs in the hybrid films lead to improved thermal stability, elongation-at-break (EAB), and compactness properties. The developed films with 2% and 4% ZnO NPs showed a smooth, compact, and heterogeneous surface morphology compared to the control (chitosan-gelatin hybrid) films. Disc diffusion assays showed that the nanocomposite film had significant antimicrobial activity against E. coli. The developed hybrid nanocomposite films have potential to be developed as biodegradable alternative for postharvest packaging of fresh fruits and vegetables.

| S-EPMC7555077 | biostudies-literature

Solvent-free synthesis and characterization of allyl chitosan derivatives.

Project description:The solvent-free synthesis of allyl-substituted chitosan derivatives through reactive co-extrusion of chitosan powder with allyl bromide at shear deformation was performed. For the structural characterization, FTIR and NMR methods were employed. The results were confirmed by chemical analysis. The total content of allyl substituents from 5 to 50 per 100 chitosan units as a function of the component ratio in the reactive mixtures was revealed. Carrying out the reaction without any additives leads to the selective formation of N-alkylated derivatives, whereas in the presence of alkali the ethers of chitosan were preferentially formed. The results suggest that the proposed approach allows significantly higher yield of products to be obtained at high process speeds and significantly lower reagent consumption as compared with the liquid-phase synthesis in organic medium. The synthesized unsaturated derivatives are promising photosensitive components for use in laser stereolithography for fabrication of three-dimensional biocompatible structures with well-defined architectonics.

| S-EPMC9066023 | biostudies-literature

Aluminum Oxide Nanoparticle Films Deposited from a Nonthermal Plasma: Synthesis, Characterization, and Crystallization.

Project description:Aluminum oxide, both in amorphous and crystalline forms, is a widely used inorganic ceramic material because of its chemical and structural properties. In this work, we synthesized amorphous aluminum oxide nanoparticles using a capacitively coupled nonthermal plasma utilizing trimethylaluminum and oxygen as precursors and studied their crystallization and phase transformation behavior through postsynthetic annealing. The use of two reactor geometries resulted in amorphous aluminum oxide nanoparticles with similar compositions but different sizes. Size tuning of these nanoparticles was achieved by varying the reactor pressure to produce amorphous aluminum oxide nanoparticles ranging from 6 to 22 nm. During postsynthetic annealing, powder samples of amorphous nanoparticles began to crystallize at 800 °C, forming crystalline θ and γ phase alumina. Their phase transformation behavior was found to be size-dependent in that powders of small 6 nm amorphous particles transformed to form phase-pure α-Al2O3 at 1100 °C, while powders of large 11 nm particles remained in the θ and γ phases. This phenomenon is attributed to the fast rate of densification and neck formation in small amorphous aluminum oxide particles.

| S-EPMC7528284 | biostudies-literature

Self-Assembly of Soluble Chitosan Derivatives Nanoparticles for Vaccine: Synthesis, Characterization and Evaluation.

Project description:Herein, a novel chitosan derivative nanoparticle was proposed to function as a delivery carrier. First of all, an improvement was made to the way N-2-hydroxypropyl trimcthyl ammonium chloride chitosan (N-2-HACC) was synthesized. Moreover, the solution to one-step synthesis of N-2-HACC from chitosan (CS) was developed. Different from the previous report, the synthesis process was simplified, and there was a reduction in the amount of 2,3-epoxypropyl trimethyl ammonium chloride (EPTAC) used. With its excellent water solubility maintained, the relatively low degree of substitution was controlled to facilitate the cross-linking reaction. The results obtained from 1H-NMR, FTIR spectroscopy, and XRD indicated a smooth EPTAC onto CS for the formation of N-2-HACC with 59.33% the degree of substitution (DS). According to our results, N-2-HACC could be dissolved in various organic solvents, deionized water, 1% acetic acid aqueous solution, and others at room temperature. Finally, a novel chitosan nanoparticle material was prepared using the self-assembly method with β-glycerophosphate sodium (β-GC), with excellent immune properties achieved, thus providing a new strategy for chitosan self-assembled nanoparticles.

| S-EPMC8659217 | biostudies-literature

Synthesis, Characterization, and the Antioxidant Activity of Carboxymethyl Chitosan Derivatives Containing Thiourea Salts.

Project description:A new class of chitosan derivatives possessing thiourea salts were synthesized to improve the solubility and the antioxidant activity of chitosan. Firstly, chitosan was modified to carboxymethyl chitosan, combining carboxymethyl chitosan with thiourea salts that have different structures to form new chitosan derivatives. The chitosan and chitosan derivatives were characterized by FT-IR, 13C NMR, TGA, and elemental analyses. The new peaks of thiourea salts could be clearly observed at about 1240 cm-1 in the IR spectra, and the peak of C=S was clearly observed at around 180 ppm in the 13C NMR. IR spectra and 13C NMR of the structural units of these polymers validated the chitosan derivatives possessing thiourea salts were successfully synthesized. Their antioxidant properties were tested, including DPPH-radical scavenging ability, superoxide-radical scavenging ability, and hydroxyl-radical scavenging ability. Our results suggested the increase of thiourea salt groups in chitosan derivatives promotes the scavenging effect. The scavenging activity of 4TMCMCS, TMCMCS. 4,4DCMCS, and 4ACMCS against DPPH-radical and superoxide-radical were more than 90% at 1.6 mg/mL, respectively. In the cytotoxicity assay, no cytotoxicity was observed for the L929 cells with chitosan and its derivatives at all testing concentrations. These results demonstrated that the combination of chitosan and thiourea salt groups improved the antioxidant activity of chitosan, and the antioxidants or free radical scavengers based on natural polymers and thiourea salts showed potential applications.

| S-EPMC6918197 | biostudies-literature

Development of Covalent Chitosan-Polyethylenimine Derivatives as Gene Delivery Vehicle: Synthesis, Characterization, and Evaluation.

Project description:There is an increasing interest in cationic polymers as important constituents of non-viral gene delivery vectors. In the present study, we developed a versatile synthetic route for the production of covalent polymeric conjugates consisting of water-soluble depolymerized chitosan (dCS; MW 6-9 kDa) and low molecular weight polyethylenimine (PEI; 2.5 kDa linear, 1.8 kDa branched). dCS-PEI derivatives were evaluated based on their physicochemical properties, including purity, covalent bonding, solubility in aqueous media, ability for DNA condensation, and colloidal stability of the resulting polyplexes. They were complexed with non-integrating DNA vectors coding for reporter genes by simple admixing and assessed in vitro using liver-derived HuH-7 cells for their transfection efficiency and cytotoxicity. Using a rational screening cascade, a lead compound was selected (dCS-Suc-LPEI-14) displaying the best balance of biocompatibility, cytotoxicity, and transfection efficiency. Scale-up and in vivo evaluation in wild-type mice allowed for a direct comparison with a commercially available non-viral delivery vector (in vivo-jetPEI). Hepatic expression of the reporter gene luciferase resulted in liver-specific bioluminescence, upon intrabiliary infusion of the chitosan-based polyplexes, which exceeded the signal of the in vivo jetPEI reference formulation by a factor of 10. We conclude that the novel chitosan-derivative dCS-Suc-LPEI-14 shows promise and potential as an efficient polymeric conjugate for non-viral in vivo gene therapy.

| S-EPMC8067803 | biostudies-literature

Graphene Oxide-Chitosan Aerogels: Synthesis, Characterization, and Use as Adsorbent Material for Water Contaminants.

Project description:Porous aerogels, formed by subjecting precursor hydrogels using a freeze-drying process, are certainly one of the most studied and synthetized soft materials, thanks to their important features such as elasticity, swelling behavior, softness, and micro and nanosized pores, which guarantee their applicability in various fields. Typically, these systems are synthetized working with natural or synthetic polymers, but in the last years great interest has been given to proper formulated aerogels able to combine polymeric structures with other moieties such as graphene or graphene oxide. This working strategy can be pivotal in many cases to tune important properties of the final system such as toughness, porosity, elasticity, electrical conductivity, or responsive behavior. In this work we propose the synthesis of chitosan graphene oxide aerogels obtained through self-assembly of graphene oxide sheets and chitosan chains. These three-dimensional systems were chemically characterized with IR and XRD technique and their inner structure was investigated through the scanning electron microscopy (SEM). Moreover, we mechanically characterized the material through dynamic mechanical analysis, showing the stability of these systems. Finally, the adsorption ability of these soft materials has been demonstrated using model molecules to simulate water contaminants showing the efficacy of those graphene-based systems even for the removal of anionic dyes. Complete removal of contaminants was obtained at low concentration of dyes in solution (100 mg/L), while with a higher amount of pollutant in the solution (350 mg/L) high sorption capacity (q > 200 mg/g) was observed.

| S-EPMC8544572 | biostudies-literature

Green synthesis of chitosan/erythritol/graphene oxide composites for simultaneous removal of some toxic species from simulated solution.

Project description:In this study, chitosan (Ch) is adapted via green methodology including sonication induced crosslinking with different weight ratios of erythritol (Er) from (Ch-Er)1 to (Ch-Er)4. The products were casted in the form of thin films. The chemical modification was proved via FTIR spectroscopy. Then, the modified products were verified via an atomic force microscopy (AFM) investigation for their topography and surface properties. The data revealed that the optimized sample was (Ch-Er)3. This sample was further modified by different weight ratios of graphene oxide 0.1, 0.2, 0.4, and 0.8 wt./wt. (symbolized as (Ch-Er)3GO1, (Ch-Er)3GO2, (Ch-Er)3GO4, and (Ch-Er)3GO8 respectively). The prepared samples were investigated by different analytical tools. Then, the adjusted sample (Ch-Er)3GO2 was irradiated by electron beam (e-beam) at 10 and 20 kGy of irradiation doses to give samples (Ch-Er)3GO2R10 and (Ch-Er)3GO2R20, respectively. The AFM data of the irradiated samples showed that the pore size decreases, and surface roughness increases at higher energy e-beam due to the formation of more crosslinking points. The optimum samples of the prepared formulations were tested as sorbent materials for simultaneous elimination of methylene blue (MB) dye and mercury cation (Hg2+) from simulated solutions. The maximum removal of both MB dye and Hg2+ cation was achieved by (Ch-Er)3GO2R10 (186.23 mg g-1 and 205 mg g-1) respectively.

| S-EPMC9995588 | biostudies-literature

In-Situ Synthesis and Characterization of Chitosan/Hydroxyapatite Nanocomposite Coatings to Improve the Bioactive Properties of Ti6Al4V Substrates.

Project description:Ti6Al4V alloy is still attracting great interest because of its application as an implant material for hard tissue repair. This research aims to produce and investigate in-situ chitosan/hydroxyapatite (CS/HA) nanocomposite coatings based on different amounts of HA (10, 50 and 60 wt.%) on alkali-treated Ti6Al4V substrate through the sol-gel process to enhance in vitro bioactivity. The influence of different contents of HA on the morphology, contact angle, roughness, adhesion strength, and in vitro bioactivity of the CS/HA coatings was studied. Results confirmed that, with increasing the HA content, the surface morphology of crack-free CS/HA coatings changed for nucleation modification and HA nanocrystals growth, and consequently, the surface roughness of the coatings increased. Furthermore, the bioactivity of the CS/HA nanocomposite coatings enhanced bone-like apatite layer formation on the material surface with increasing HA content. Moreover, CS/HA nanocomposite coatings were biocompatible and, in particular, CS/10 wt.% HA composition significantly promoted human mesenchymal stem cells (hMSCs) proliferation. In particular, these results demonstrate that the treatment strategy used during the bioprocess was able to improve in vitro properties enough to meet the clinical performance. Indeed, it is predicted that the dense and crack-free CS/HA nanocomposite coatings suggest good potential application as dental implants.

| S-EPMC7503881 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data