Improved Bacteriostatic and Anticorrosion Effects of Polycaprolactone/Chitosan Coated Magnesium via Incorporation of Zinc Oxide.

ABSTRACT: Magnesium has been recognized as a groundbreaking biodegradable biomaterial for implant applications, but its use is limited because it degrades too quickly in physiological solutions. This paper describes the research on the influence of polycaprolactone (PCL)/chitosan (CS)/zinc oxide (ZnO) composite coating (PCL/CS/ZnO) on the corrosion resistance and antibacterial activity of magnesium. The PCL/CS film presented a porous structure with thickness of about 40-50 μm, while after incorporation of ZnO into the PCL/CS, a homogenous film without pores and defects was attained. The ZnO embedded in PCL/CS enhanced corrosion resistance by preventing corrosive ions diffusion in the magnesium substrate. The corrosion, antibacterial, and cell interaction mechanism of the PCL/CS/ZnO composite coating is discussed in this study. In vitro cell culture revealed that the PCL/CS coating with low loaded ZnO significantly improved cytocompatibility, but coatings with high loaded ZnO were able to induce some cytotoxicity osteoblastic cells. It was also found that enhanced antibacterial activity of the PCL/CS/ZnO coating against both Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) bacteria, while less significant antibacterial activity was detected for uncoated Mg and PCL/CS coating. Based on the results, the PCL/CS coatings loaded with low ZnO content may be recommended as a candidate material for biodegradable Mg-based orthopedic implant applications.

SUBMITTER: Bakhsheshi-Rad HR

PROVIDER: S-EPMC8070643 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

ALD based nanostructured zinc oxide coated antiviral silk fabric.

Project description:The COVID-19 pandemic has underscored the importance of research and development in maintaining public health. Facing unprecedented challenges, the scientific community developed antiviral drugs, virucides, and vaccines to combat the infection within the past two years. However, an ever-increasing list of highly infectious SARS-CoV-2 variants (gamma, delta, omicron, and now ba.2 stealth) has exacerbated the problem: again raising the issues of infection prevention strategies and the efficacy of personal protective equipment (PPE). Against this backdrop, we report an antimicrobial fabric for PPE applications. We have fabricated a nanofibrous silk-PEO material using electrospinning followed by zinc oxide thin film deposition by employing the atomic layer deposition technique. The composite fabric has shown 85% more antibacterial activity than the control fabric and was found to possess substantial superoxide dismutase-mimetic activity. The composite was further subjected to antiviral testing using two different respiratory tract viruses: coronavirus (OC43: enveloped) and rhinovirus (RV14: non-enveloped). We report a 95% reduction in infectious virus for both OC43 and RV14 from an initial load of ∼1 × 105 (sample size: 6 mm dia. disk), after 1 h of white light illumination. Furthermore, with 2 h of illumination, ∼99% reduction in viral infectivity was observed for RV14. High activity in a relatively small area of fabric (3.5 × 103 viral units per mm2) makes this antiviral fabric ideal for application in masks/PPE, with an enhanced ability to prevent antimicrobial infection overall.

| S-EPMC9251734 | biostudies-literature

Zinc Oxide and Copper Chitosan Composite Films with Antimicrobial Activity.

Project description:The role of the oral microbiome and its effect on dental diseases is gaining interest. Therefore, it has been sought to decrease the bacterial load to fight oral cavity diseases. In this study, composite materials based on chitosan, chitosan crosslinked with glutaraldehyde, chitosan with zinc oxide particles, and chitosan with copper nanoparticles were prepared in the form of thin films, to evaluate a new alternative with a more significant impact on the oral cavity bacteria. The chemical structures and physical properties of the films were characterized using by Fourier transform infrared spectroscopy (FTIR,) Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), elemental analysis (EDX), thermogravimetric analysis (TGA), X-ray diffraction (XRD), scanning electron microscopy (SEM), and contact angle measurements. Subsequently, the antimicrobial activity of each material was evaluated by agar diffusion tests. No differences were found in the hydrophilicity of the films with the incorporation of ZnO or copper particles. Antimicrobial activity was found against S. aureus in the chitosan film crosslinked with glutaraldehyde, but not in the other compositions. In contrast antimicrobial activity against S. typhimurium was found in all films. Based on the data of present investigation, chitosan composite films could be an option for the control of microorganisms with potential applications in various fields, such as medical and food industry.

| S-EPMC8619498 | biostudies-literature

Hexanoyl-Chitosan-PEG Copolymer Coated Iron Oxide Nanoparticles for Hydrophobic Drug Delivery.

Project description:Nanoparticle (NP) formulations may be used to improve in vivo efficacy of hydrophobic drugs by circumventing solubility issues and providing targeted delivery. In this study, we developed a hexanoyl-chitosan-PEG (CP6C) copolymer coated, paclitaxel (PTX)-loaded, and chlorotoxin (CTX) conjugated iron oxide NP (CTX-PTX-NP) for targeted delivery of PTX to human glioblastoma (GBM) cells. We modified chitosan with polyethylene glycol (PEG) and hexanoyl groups to obtain the amphiphilic CP6C. The resultant copolymer was then coated onto oleic acid-stabilized iron oxide NPs (OA-IONP) via hydrophobic interactions. PTX, a model hydrophobic drug, was loaded into the hydrophobic region of IONPs. CTX-PTX-NP showed high drug loading efficiency (>30%), slow drug release in PBS and the CTX-conjugated NP was shown to successfully target GBM cells. Importantly, the NPs showed great therapeutic efficacy when evaluated in GBM cell line U-118 MG. Our results indicate that this nanoparticle platform could be used for loading and targeted delivery of hydrophobic drugs.

| S-EPMC4755322 | biostudies-literature

Sodium Acetate Coated Tenofovir-Loaded Chitosan Nanoparticles for Improved Physico-Chemical Properties.

Project description:PurposeIt is hypothesized that sodium acetate (SA) can be used for in situ coating of drug loaded chitosan NPs for improved physico-chemical properties.MethodsTenofovir (TFV) is used as a model drug. Uncoated chitosan NPs are prepared by ionic gelation. SA is generated in situ from half neutralization of acetic acid with sodium hydroxide, and coats chitosan NPs during freeze-drying. The NPs' physico-chemical properties [e.g., particle mean diameters (PMD) zeta potential (ζ), EE%, drug release profile, morphology] are characterized by dynamic light scattering, spectrophotometry, Korsmeyer-Peppas model, transmission electron microscopy (TEM), respectively. Melting point (MP), non-aqueous titration, Fourier transform infrared (FTIR) analysis, and powder X-ray diffractometry (XRD) pattern evaluate the SA coated chitosan NPs. The NPs' cytotoxicity on macrophages Raw 264.7 is assessed by neutral red, resazurin, nitrite oxide (NO) and cytokines assays.ResultsCollectively, FTIR, ζ, XRD, MP, and TEM data confirm that SA coats chitosan NPs. The PMD range is 136-348 nm (uncoated) and 171-379 nm (coated NPs). The ζ values range is +24.3-28.5 mV (uncoated) and 0.1-3.1 mV (coated NPs). The EE% ranges from 5.5 to 11.7% (uncoated NPs) and increased up to 86.3-92.7%(8-17-fold) after coating. The SA also prevents NPs aggregation during the freeze-drying and aqueous dispersion. The core-shell NPs exhibited a sustain release of TFV following anomalous transport mechanism (R(2) ~ 0.99). The coated NPs are non-cytotoxic (cell viability ~100%) and without any proinflammatory response.ConclusionsThis SA coating chitosan NPs mechanism may be useful for (i) efficient encapsulation, (ii) stabilizing colloidal dispersions, (iii) controlling the release and solubility of bioactive agents.

| S-EPMC5755613 | biostudies-literature

Transcriptomics Library Data of Chitosan-coated Cavendish Banana

Project description:We report the first RNA sequencing data of 1.25% chitosan-coated and uncoated (control) fruit of Musa acuminata (AAA Group, Subgroup Cavendish) at unripe (day 1) and ripe (day 7) stage

2019-11-21 | GSE139457 | GEO

Bimodal Fucoidan-Coated Zinc Oxide/Iron Oxide-Based Nanoparticles for the Imaging of Atherothrombosis.

Project description:A polyol method was used to obtain ultrasmall ZnO nanoparticles (NPs) doped with iron ions and coated with a low molecular weight fucoidan in order to perform in vivo MR and ex vivo fluorescence imaging of athrothrombosis. During the synthesis, the early elimination of water by azeotropic distillation with toluene allowed us to produce NPs which size, determined by XRD and TEM, decreased from 7 nm to 4 nm with the increase of iron/zinc ratios from 0.05 to 0.50 respectively. For the highest iron content (NP-0.50) NPs were evidenced as a mixture of nanocrystals made of wurtzite and cubic phase with a molar ratio of 2.57:1, although it was not possible to distinguish one from the other by TEM. NP-0.50 were superparamagnetic and exhibited a large emission spectrum at 470 nm when excited at 370 nm. After surface functionalization of NP-0.50 with fucoidan (fuco-0.50), the hydrodynamic size in the physiological medium was 162.0 ± 0.4 nm, with a corresponding negative zeta potential of -48.7 ± 0.4 mV, respectively. The coating was evidenced by FT-IR spectra and thermogravimetric analysis. Aqueous suspensions of fuco-0.50 revealed high transverse proton relaxivities (T?) with an r? value of 173.5 mM-1 s-1 (300 K, 7.0 T) and remained stable for more than 3 months in water or in phosphate buffer saline without evolution of the hydrodynamic size and size distribution. No cytotoxic effect was observed on human endothelial cells up to 48 h with these NPs at a dose of 0.1 mg/mL. After injection into a rat model of atherothrombosis, MR imaging allowed the localization of diseased areas and the subsequent fluorescence imaging of thrombus on tissue slices.

| S-EPMC6429451 | biostudies-literature

<i>In vitro</i> toxicity assessment of chitosan oligosaccharide coated iron oxide nanoparticles.

Project description:Iron oxide nanoparticles (INPs) have potential biological, biomedical and environmental applications. These applications require surface modification of the iron oxide nanoparticles, which makes it non-toxic, biocompatible, stable and non-agglomerative in natural and biological surroundings. In the present study, iron oxide nanoparticles (INPs) and chitosan oligosaccharide coated iron oxide nanoparticles (CSO-INPs) were synthesized to evaluate the effect of surface coating on the stability and toxicity of nanoparticles. Comparative in vitro cytotoxicity of nanoparticles was evaluated in HeLa (human cervix carcinoma), A549 (human lung carcinoma) and Hek293 (human embryonic kidney) cells by using 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay along with flow cytometry study for cell viability, membrane integrity, mitochondrial membrane potential (MMP) and reactive oxygen species (ROS) production. Morphological alteration in nanoparticles treated cells was analyzed by Acridine orange/ethidium bromide double staining and electron microscopy. Synthesized nanoparticles were found to be spherical in shape, well dispersed and stable at various pH values, making them suitable for biomedical and environmental applications. The present study also indicates that the chitosan oligosaccharide coating on iron oxide nanoparticles results in the decrease in cellular damage and moderate ROS production, thereby, significantly decreasing the cytotoxic impact of bare iron oxide nanoparticles.

| S-EPMC5598369 | biostudies-literature

Chitosan-coated mesoporous MIL-100(Fe) nanoparticles as improved bio-compatible oral nanocarriers.

Project description:Nanometric biocompatible Metal-Organic Frameworks (nanoMOFs) are promising candidates for drug delivery. Up to now, most studies have targeted the intravenous route, related to pain and severe complications; whereas nanoMOFs for oral administration, a commonly used non-invasive and simpler route, remains however unexplored. We propose here the biofriendly preparation of a suitable oral nanocarrier based on the benchmarked biocompatible mesoporous iron(III) trimesate nanoparticles coated with the bioadhesive polysaccharide chitosan (CS). This method does not hamper the textural/structural properties and the sorption/release abilities of the nanoMOFs upon surface engineering. The interaction between the CS and the nanoparticles has been characterized through a combination of high resolution soft X-ray absorption and computing simulation, while the positive impact of the coating on the colloidal and chemical stability under oral simulated conditions is here demonstrated. Finally, the intestinal barrier bypass capability and biocompatibility of CS-coated nanoMOF have been assessed in vitro, leading to an increased intestinal permeability with respect to the non-coated material, maintaining an optimal biocompatibility. In conclusion, the preservation of the interesting physicochemical features of the CS-coated nanoMOF and their adapted colloidal stability and progressive biodegradation, together with their improved intestinal barrier bypass, make these nanoparticles a promising oral nanocarrier.

| S-EPMC5335263 | biostudies-literature

Magnetic removal of Entamoeba cysts from water using chitosan oligosaccharide-coated iron oxide nanoparticles.

Project description:Amebiasis, a major health problem in developing countries, is the second most common cause of death due to parasitic infection. Amebiasis is usually transmitted by the ingestion of Entamoeba histolytica cysts through oral-fecal route. Herein, we report on the use of chitosan oligosaccharide-functionalized iron oxide nanoparticles for efficient capture and removal of pathogenic protozoan cysts under the influence of an external magnetic field. These nanoparticles were synthesized through a chemical synthesis process. The synthesized particles were characterized by transmission electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction, and zeta potential analysis. The particles were found to be well dispersed and uniform in size. The capture and removal of pathogenic cysts were demonstrated by fluorescent microscopy, transmission electron microscopy, and scanning electron microscopy (SEM). Three-dimensional modeling of various biochemical components of cyst walls, and thereafter, flexible docking studies demonstrate the probable interaction mechanism of nanoparticles with various components of E. histolytica cyst walls. Results of the present study suggest that E. histolytica cysts can be efficiently captured and removed from contaminated aqueous systems through the application of synthesized nanoparticles.

| S-EPMC4527572 | biostudies-literature

Impact of Coated Zinc Oxide Nanoparticles on Photosystem II of Tomato Plants.

Project description:Zinc oxide nanoparticles (ZnO NPs) have emerged as a prominent tool in agriculture. Since photosynthetic function is a significant measurement of phytotoxicity and an assessment tool prior to large-scale agricultural applications, the impact of engineered irregular-shaped ZnO NPs coated with oleylamine (ZnO@OAm NPs) were tested. The ZnO@OAm NPs (crystalline size 19 nm) were solvothermally prepared in the sole presence of oleylamine (OAm) and evaluated on tomato (Lycopersicon esculentum Mill.) photosystem II (PSII) photochemistry. Foliar-sprayed 15 mg L-1 ZnO@OAm NPs on tomato leaflets increased chlorophyll content that initiated a higher amount of light energy capture, which resulted in about a 20% increased electron transport rate (ETR) and a quantum yield of PSII photochemistry (ΦPSII) at the growth light (GL, 600 μmol photons m-2 s-1). However, the ZnO@OAm NPs caused a malfunction in the oxygen-evolving complex (OEC) of PSII, which resulted in photoinhibition and increased ROS accumulation. The ROS accumulation was due to the decreased photoprotective mechanism of non-photochemical quenching (NPQ) and to the donor-side photoinhibition. Despite ROS accumulation, ZnO@OAm NPs decreased the excess excitation energy of the PSII, indicating improved PSII efficiency. Therefore, synthesized ZnO@OAm NPs can potentially be used as photosynthetic biostimulants for enhancing crop yields after being tested on other plant species.

| S-EPMC10488754 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data