Characterisation of the Filler Fraction in CAD/CAM Resin-Based Composites.

ABSTRACT: The performance of dental resin-based composites (RBCs) heavily depends on the characteristic properties of the individual filler fraction. As specific information regarding the properties of the filler fraction is often missing, the current study aims to characterize the filler fractions of several contemporary computer-aided design/computer-aided manufacturing (CAD/CAM) RBCs from a material science point of view. The filler fractions of seven commercially available CAD/CAM RBCs featuring different translucency variants were analysed using Scanning Electron Microscopy (SEM) with Energy Dispersive X-ray Spectroscopy (EDS), Micro-X-ray Computed Tomography (µXCT), Thermogravimetric Analysis (TG) and X-ray Diffractometry (XRD). All CAD/CAM RBCs investigated included midifill hybrid type filler fractions, and the size of the individual particles was clearly larger than the individual specifications of the manufacturer. The fillers in Shofu Block HC featured a sphericity of ≈0.8, while it was <0.7 in all other RBCs. All RBCs featured only X-ray amorphous phases. However, in Lava Ultimate, zircon crystals with low crystallinity were detected. In some CAD/CAM RBCs, inhomogeneities (X-ray opaque fillers or pores) with a size <80 µm were identified, but the effects were minor in relation to the total volume (<0.01 vol.%). The characteristic parameters of the filler fraction in RBCs are essential for the interpretation of the individual material's mechanical and optical properties.

SUBMITTER: Koenig A

PROVIDER: S-EPMC8071413 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Acid Resistance of CAD/CAM Resin Composites.

Project description:Acid resistance of CAD/CAM resin composites. Erosion-related tooth surface loss is closely related to acid exposure, such as contact with acidic beverages or disease-related reflux. As a result, dental restorations in affected patients are also exposed to acids, which indicates that the performance and longevity of a dental restoration is impacted by the acid resistance of the individually employed restorative materials. However, unlike for ceramic materials, the acid resistance of CAD/CAM resin composites is not commonly evaluated by the manufacturers, and no standardised test methods have yet been established. Against this background, the present in vitro study aimed to examine the long-term resistance of CAD/CAM resin composites (Brilliant Crios, Cerasmart, Grandio blocs, Lava Ultimate, Shofu Block HC) against three acidic media (tonic water, acetic acid, hydrochloric acid) as well as demineralized water and to investigate potential damage mechanisms. Changes in surface roughness (Sa) were detected by confocal laser scanning microscopy (CLSM), and changes in surface hardness were measured using Vickers hardness (HV). The damage mechanisms were analysed by scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS) and micro X-ray computer tomography (µXCT). For each material, few changes in either Sa or HV were identified for at least one of the different media; for Cerasmart, the sharpest deterioration in surface properties was observed. SEM-EDS revealed leaching of barium, aluminium, and titanium from fillers in a 2 µm zone on the rough but not on the polished surface of the specimen. Within the limitations of the current study, it can be concluded that polished CAD/CAM resin composites can be recommended for clinical use in patients with erosive conditions.

| S-EPMC9220078 | biostudies-literature

The influence of different storage media on Vickers hardness and surface roughness of CAD/CAM resin composites.

Project description:IntroductionThis study examined Vickers hardness as well as surface characteristics of different computer-aided design/computer-aided manufacturing (CAD/CAM) resin composites prior to and after storage in various media.Materials and methodsCAD/CAM resin composite blocks (Grandio Blocs (GB), Lava Ultimate (LU), Brilliant Crios (BC), Cerasmart (GC), Shofu Block HC (SB), Tetric CAD (TC), Luxacam Composite (LC); incl. different translucency variants) were prepared, polished and surface free energy was determined. The specimens were divided into four groups: dry conditions for 24 h (25 °C), demineralized water (37 °C), Pepsi Cola (37 °C) and 75% ethanol (37 °C). After seven and 28 days of storage, Vickers hardness was determined. Surface roughness was measured after the entire storage period.Results and discussionVickers hardness was in the range of about 150 HV for GB, around 115 HV for LU, and 80-100 HV for BC, GC, SB, TC and LC. Only minor differences (total: 50.2 (6.4)-56.2 (3.2) mN/m) in surface free energy could be detected. No relationship was observed between surface free energy and filler content. However, a correlation between filler content and Vickers hardness was evident. Artificial aging caused a decrease of Vickers hardness (up to -40 HV or 35%) depending on storage media, duration and material. The changes in surface texture after immersion in different media were below a value of ΔSa = 0.015 µm.ConclusionArtificial aging of CAD/CAM resin composites leads to a significant decrease of Vickers hardness for most materials, while only small changes in surface roughness were identified.

| S-EPMC10024666 | biostudies-literature

Fatigue resistance of CAD/CAM resin composite molar crowns.

Project description:To demonstrate the fatigue behavior of CAD/CAM resin composite molar crowns using a mouth-motion step-stress fatigue test. Monolithic leucite-reinforced glass-ceramic crowns were used as a reference.Fully anatomically shaped monolithic resin composite molar crowns (Lava Ultimate, n=24) and leucite reinforced glass-ceramic crowns (IPS Empress CAD, n=24) were fabricated using CAD/CAM systems. Crowns were cemented on aged dentin-like resin composite tooth replicas (Filtek Z100) with resin-based cements (RelyX Ultimate for Lava Ultimate or Multilink Automix for IPS Empress). Three step-stress profiles (aggressive, moderate and mild) were employed for the accelerated sliding-contact mouth-motion fatigue test. Twenty one crowns from each group were randomly distributed among these three profiles (1:2:4). Failure was designated as chip-off or bulk fracture. Optical and electron microscopes were used to examine the occlusal surface and subsurface damages, as well as the material microstructures.The resin composite crowns showed only minor occlusal damage during mouth-motion step-stress fatigue loading up to 1700N. Cross-sectional views revealed contact-induced cone cracks in all specimens, and flexural radial cracks in 2 crowns. Both cone and radial cracks were relatively small compared to the crown thickness. Extending these cracks to the threshold for catastrophic failure would require much higher indentation loads or more loading cycles. In contrast, all of the glass-ceramic crowns fractured, starting at loads of approximately 450N.Monolithic CAD/CAM resin composite crowns endure, with only superficial damage, fatigue loads 3-4 times higher than those causing catastrophic failure in glass-ceramic CAD crowns.

| S-EPMC4801772 | biostudies-literature

Thermoanalytical Investigations on the Influence of Storage Time in Water of Resin-Based CAD/CAM Materials.

Project description:New resin-based composites and resin-infiltrated ceramics are used to fabricate computer-aided design (CAD) and computer-aided manufacturing (CAM)-based restorations, although little information is available on the long-term performance of these materials. The aim of this investigation was to determine the effects of storage time (24 h, 90 days, 180 days) on the thermophysical properties of resin-based CAD/CAM materials. Thermogravimetric Analysis (TGA), differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) were used in the study. TGA provided insight into the composition of the resin-based materials and the influence of internal plasticization and water sorption. Resin-based composites showed different decomposition, heat energy and mechanical behavior, which was influenced by storage time in water. Individual materials such as Grandio bloc showed lower influence of water storage while maintaining good mechanical properties.

| S-EPMC8698771 | biostudies-literature

Influence of Filler Loading on the Mechanical Properties of Flowable Resin Composites.

Project description:The aim of this study was to evaluate the correlation between the percent of inorganic filler by weight (wt. %) and by volume (vol. %) of 11 flowable resin composites (FRCs) and their mechanical properties. To establish the correlation, the quantity of inorganic filler was determined by combustion and shape/size analyzed by SEM images. The compressive strength (CS), flexural strength (FS), and flexural modulus (FM) were determined. The CS values were between 182.87-310.38 MPa, the FS values ranged between 59.59 and 96.95 MPa, and the FM values were between 2.34 and 6.23 GPa. The percentage of inorganic filler registered values situated between 52.25 and 69.64 wt. % and 35.35 and 53.50 vol. %. There was a very good correlation between CS, FS, and FM vs. the inorganic filler by wt. % and vol. %. (R2 = 0.8899-0.9483). The highest regression was obtained for the FM values vs. vol. %. SEM images of the tested FRCs showed hybrid inorganic filler for Filtek Supreme XT (A3) and StarFlow (A2) and a homogeneous type of inorganic filler for the other investigated materials. All of the FS values were above 50 MPa, the ISO 4049/2019 limit for FRCs.

| S-EPMC7142558 | biostudies-literature

Urchin-like multiscale structured fluorinated hydroxyapatite as versatile filler for caries restoration dental resin composites

Project description: Not available

| S-EPMC10885616 | biostudies-literature

Effectiveness of Self-Adhesive Resin Luting Cement in CAD-CAM Blocks-A Systematic Review and Meta-Analysis.

Project description:Self-adhesive resin cements (SARCs) are used because of their mechanical properties, ease of cementation protocols, and lack of requirements for acid conditioning or adhesive systems. SARCs are generally dual-cured, photoactivated, and self-cured, with a slight increase in acidic pH, allowing self-adhesiveness and increasing resistance to hydrolysis. This systematic review assessed the adhesive strength of SARC systems luted to different substrates and computer-aided design and manufacturing (CAD/CAM) ceramic blocks. The PubMed/MedLine and Science Direct databases were searched using the Boolean formula [((dental or tooth) AND (self-adhesive) AND (luting or cement) AND CAD-CAM) NOT (endodontics or implants)]. Of the 199 articles obtained, 31 were selected for the quality assessment. Lava Ultimate (resin matrix filled with nanoceramic) and Vita Enamic (polymer-infiltrated ceramic) blocks were the most tested. Rely X Unicem 2 was the most tested resin cement, followed by Rely X Unicem > Ultimate > U200, and μTBS was the test most used. The meta-analysis confirmed the substrate-dependent adhesive strength of SARCs, with significant differences between them and between SARCs and conventional resin-based adhesive cement (α < 0.05). SARCs are promising. However, one must be aware of the differences in the adhesive strengths. An appropriate combination of materials must be considered to improve the durability and stability of restorations.

| S-EPMC10140979 | biostudies-literature

Erratum: Evaluation of the repair capacities and color stabilities of a resin nanoceramic and hybrid CAD/CAM blocks.

Project description:[This corrects the article on p. 140 in vol. 12, PMID: 32601533.].

| S-EPMC7449819 | biostudies-literature

Data on changes in flexural strength and elastic modulus of dental CAD/CAM composites after deterioration tests.

Project description:Mechanical properties of dental restorative materials are important for clinical success in prosthodontic care. However, open data on the mechanical properties of these materials are limited. This article provides data on the flexural strength and elastic modulus of dental composites in practical use for design/computer-aided manufacturing (CAD/CAM) systems. Eight brands of composites were subjected to deterioration tests: immersing in water at 37 °C for one day or seven days, or thermocycling (TC) in water at temperatures between 5 °C and 55 °C for 5000 or 10,000 cycles. The mechanical properties of the samples were measured by using a three-point bending test according to ISO 6872. The obtained values were statistically analyzed using one-way analysis of variance (ANOVA), followed by Tukey multiple comparison tests.

| S-EPMC6461697 | biostudies-literature

Effects of Filler Distribution on Magnetorheological Silicon-Based Composites.

Project description:The smart materials subclass of magnetorheological elastomer (MRE) composites is presented in this work, which aimed to investigate the influence of filler distribution on surface morphology. Iron particles with sizes ranging from 20 to 150 µm were incorporated into the elastomer matrix and a 30% volume fraction (V%) was chosen as the optimal quantity for the filler amount in the elastomer composite. The surface morphology of MRE composites was examined by 3D micro-computed tomography (µCT) and scanning electron microscopy (SEM) techniques. Isotropic and anisotropic distributions of the iron particles were estimated in the magnetorheological elastomer composites. The filler particle distribution at various heights of the MRE composites was examined. The isotropic distribution of filler particles was observed without any influence from the magnetic field during sample preparation. The anisotropic arrangement of iron fillers within the MRE composites was observed in the presence of a magnetic field during fabrication. It was shown that the linear arrangement of the iron particle chain induced magnetization within the composite. Simulation analysis was also performed to predict the particle distribution of magnetization in the MREs and make a comparison with the experimental observations.

| S-EPMC6766335 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data