Lignin as a Partial Polyol Replacement in Polyurethane Flexible Foam.

ABSTRACT: This study was focused on evaluating the suitability of a wide range of lignins, a natural polymer isolated from different plant sources and chemical extractions, in replacing 20 wt.% of petroleum-based polyol in the formulation of PU flexible foams. The main goal was to investigate the effect of unmodified lignin incorporation on the foam's structural, mechanical, and thermal properties. The hydroxyl contents of the commercial lignins were measured using phosphorus nuclear magnetic resonance (³¹P NMR) spectroscopy, molar mass distributions with gel permeation chromatography (GPC), and thermal properties with differential scanning calorimetry (DSC) techniques. The results showed that incorporating 20 wt.% lignin increased tensile, compression, tear propagation strengths, thermal stability, and the support factor of the developed PU flexible foams. Additionally, statistical analysis of the results showed that foam properties such as density and compression force deflection were positively correlated with lignin's total hydroxyl content. Studying correlations between lignin properties and the performance of the developed lignin-based PU foams showed that lignins with low hydroxyl content, high flexibility (low T_g), and high solubility in the co-polyol are better candidates for partially substituting petroleum-based polyols in the formulation of flexible PU foams intended for the automotive applications.

SUBMITTER: Gondaliya A

PROVIDER: S-EPMC8071504 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:This study aims to investigate the potential of integrating natural biochar (BC) derived from eggshell waste into flexible polyurethane (FPU) foam to enhance its mechanical and acoustic performance. The study explores the impact of incorporating BC at various weight ratios (0.1, 0.3, 0.5, and 0.7 wt. %) on the properties of the FPU foam. Additionally, the effects of modifying the BC with (3-aminopropyl)trimethoxysilane (APTMS) at different ratios (10, 20, and 30 wt. %) and the influence of diverse particle sizes of BC on the thermal, mechanical, and acoustic characteristics of the FPU composite are investigated. The functional groups, morphology, and elemental composition of the developed FPU composites are analyzed using Fourier-transform infrared spectroscopy (FTIR), field-emission scanning electron microscopy (FESEM), and energy-dispersive X-ray (EDX) techniques. Characteristics such as density, gel fraction, and porosity were also assessed. The results reveal that the density of FPU foam increased by 4.32% and 7.83% while the porosity decreased to 50.22% and 47.05% with the addition of 0.1 wt. % of unmodified BC and modified BC with 20 wt. % APTMS, respectively, compared to unfilled FPU. Additionally, the gel fraction of the FPU matrix increases by 1.91% and 3.55% with the inclusion of 0.1 wt. % unmodified BC and modified BC with 20 wt. % APTMS, respectively. Furthermore, TGA analysis revealed that all FPU composites demonstrate improved thermal stability compared to unfilled FPU, reaching a peak value of 312.17°C for the FPU sample incorporating BC modified with 20 wt. % APTMS. Compression strength increased with 0.1 wt. % untreated BC but decreased at higher concentrations. Modifying BC with 20% APTMS resulted in an 8.23% increase in compressive strength compared to unfilled FPU. Acoustic analysis showed that the addition of BC improved absorption, and modified BC enhanced absorption characteristics of FPU, reaching Class D with a 20 mm thickness. BC modified with APTMS further improved acoustic properties compared to the unfilled FPU sample (Class E), with 20% modification showing the best results. These composites present promising materials for sound absorption applications and address environmental issues related to eggshell waste.

Dataset Information

Lignin as a Partial Polyol Replacement in Polyurethane Flexible Foam.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets