All-Solid-State Lithium-Ion Batteries with Oxide/Sulfide Composite Electrolytes.

ABSTRACT: Li_6.3La₃Zr_1.65W_0.35O₁₂ (LLZO)-Li₆PS₅Cl (LPSC) composite electrolytes and all-solid-state cells containing LLZO-LPSC were fabricated by cold pressing at room temperature. The LPSC:LLZO ratio was varied, and the microstructure, ionic conductivity, and electrochemical performance of the corresponding composite electrolytes were investigated; the ionic conductivity of the composite electrolytes was three or four orders of magnitude higher than that of LLZO. The high conductivity of the composite electrolytes was attributed to the enhanced relative density and the rule of mixture for soft LPSC particles with high lithium-ion conductivity (~10^-4 S·cm^-1). The specific capacities of all-solid-state cells (ASSCs) consisting of a LiNi_0.8Co_0.1Mn_0.1O₂ (NCM811) cathode and the composite electrolytes of LLZO:LPSC = 7:3 and 6:4 were 163 and 167 mAh·g^-1, respectively, at 0.1 C and room temperature. Moreover, the charge-discharge curves of the ASSCs with the composite electrolytes revealed that a good interfacial contact was successfully formed between the NCM811 cathode and the LLZO-LPSC composite electrolyte.

SUBMITTER: Park YS

PROVIDER: S-EPMC8073507 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Elucidating Ion Transport Phenomena in Sulfide/Polymer Composite Electrolytes for Practical Solid-State Batteries.

Project description:Despite the enormous interest in inorganic/polymer composite solid-state electrolytes (CSEs) for solid-state batteries (SSBs), the underlying ion transport phenomena in CSEs have not yet been elucidated. Here, we address this issue by formulating a mechanistic understanding of bi-percolating ion channels formation and ion conduction across inorganic-polymer electrolyte interfaces in CSEs. A model CSE is composed of argyrodite-type Li6PS5Cl (LPSCl) and gel polymer electrolyte (GPE, including Li+-glyme complex as an ion-conducting medium). The percolation threshold of the LPSCl phase in the CSE strongly depends on the elasticity of the GPE phase. Additionally, manipulating the solvation/desolvation behavior of the Li+-glyme complex in the GPE facilitates ion conduction across the LPSCl-GPE interface. The resulting scalable CSE (area = 8 × 6 (cm × cm), thickness ~ 40 μm) can be assembled with a high-mass-loading LiNi0.7Co0.15Mn0.15O2 cathode (areal-mass-loading = 39 mg cm-2) and a graphite anode (negative (N)/positive (P) capacity ratio = 1.1) in order to fabricate an SSB full cell with bi-cell configuration. Under this constrained cell condition, the SSB full cell exhibits high volumetric energy density (480 Wh Lcell-1) and stable cyclability at 25 °C, far exceeding the values reported by previous CSE-based SSBs.

| S-EPMC10344856 | biostudies-literature

Growth of lithium-indium dendrites in all-solid-state lithium-based batteries with sulfide electrolytes.

Project description:All-solid-state lithium-based batteries with inorganic solid electrolytes are considered a viable option for electrochemical energy storage applications. However, the application of lithium metal is hindered by issues associated with the growth of mossy and dendritic Li morphologies upon prolonged cell cycling and undesired reactions at the electrode/solid electrolyte interface. In this context, alloy materials such as lithium-indium (Li-In) alloys are widely used at the laboratory scale because of their (electro)chemical stability, although no in-depth investigations on their morphological stability have been reported yet. In this work, we report the growth of Li-In dendritic structures when the alloy material is used in combination with a Li6PS5Cl solid electrolyte and Li(Ni0.6Co0.2Mn0.2)O2 positive electrode active material and cycled at high currents (e.g., 3.8 mA cm-2) and high cathode loading (e.g., 4 mAh cm-2). Via ex situ measurements and simulations, we demonstrate that the irregular growth of Li-In dendrites leads to cell short circuits after room-temperature long-term cycling. Furthermore, the difference between Li and Li-In dendrites is investigated and discussed to demonstrate the distinct type of dendrite morphology.

| S-EPMC8630065 | biostudies-literature

Poly(ionic liquid) Based Composite Electrolytes for Lithium Ion Batteries.

Project description:Polymerized ionic liquids (PIL) are an interesting substance class, which is discussed to transfer the outstanding properties and tunability of ionic liquids into a solid material. In this study we extend our previous research on ammonium based PIL and discuss the influence of additives and their usability as polymer electrolyte membranes for lithium ion batteries. The polymer electrolyte is thereby used as replacement for the commercially widespread system of a separator that is soaked with liquid electrolyte. The influence of the material composition on the ionic conductivity (via electrochemical impedance spectroscopy) and the diffusion coefficients (via pulsed-field-gradient nuclear magnetic resonance spectroscopy) were studied and cell tests with adapted membrane materials were performed. High amounts of the additional ionic liquid (IL) MPPyrr-TFSI (1-methyl-1-propylpyrrolidinium bis(trifluoromethylsulfonyl)imide) increased the ionic conductivity of the materials up to 1.3·10-4 S·cm-1 but made the usage of a cross-linker necessary to obtain mechanically stable membranes. The application of liquid electrolyte mixtures with ethylene carbonate (EC) and MPPyrr-TFSI decreased ionic conductivity values down to the 10-9 S·cm-1 range, but increased 7Li diffusion coefficients with increasing amounts of EC up to 1.7·10-10 m2·s-1. Cell tests with two membrane mixtures proofed that it is possible to build electrolyte membranes on basis of the polymerized ionic liquids, but also showed that further research is necessary to ensure stable and efficient cell cycling.

| S-EPMC8707941 | biostudies-literature

Promoting favorable interfacial properties in lithium-based batteries using chlorine-rich sulfide inorganic solid-state electrolytes.

Project description:The use of inorganic solid-state electrolytes is considered a viable strategy for developing high-energy Li-based metal batteries. However, suppression of parasitic interfacial reactions and growth of unfavorable Li metal depositions upon cycling are challenging aspects and not yet fully addressed. Here, to better understand these phenomena, we investigate various sulfide inorganic solid electrolytes (SEs), i.e., Li7-xPS6-xClx (x = 0.6, 1.0, 1.3, 1.45, and 1.6), via ex situ and in situ physicochemical and electrochemical measurements. We found that the Cl distribution and the cooling process applied during the SE synthesis strongly influence the evolution of the Li|SE interface in terms of microstructure, interphase composition, and morphology. Indeed, for a SE with a moderate chlorine content (i.e., x = 1.3) and obtained via a slow cooling process after sintering, the Cl atoms are located on the surface of the SE grains as interconnected LiCl nanoparticles that form an extended LiCl-based framework. This peculiar microstructure facilitates the migration of the Cl ions to the Li|SE interface during electrochemical cycling, thus, favouring the formation of a LiCl-rich interphase layer capable of improving the battery cycling performances.

| S-EPMC8989881 | biostudies-literature

Cross-Linked Nanohybrid Polymer Electrolytes With POSS Cross-Linker for Solid-State Lithium Ion Batteries.

Project description:A new class of freestanding cross-linked hybrid polymer electrolytes (HPEs) with POSS as the cross-linker was prepared by a one-step free radical polymerization reaction. Octavinyl octasilsesquioxane (OV-POSS) with eight functional corner groups was used to provide cross-linking sites for the connection of polymer segments and the required mechanical strength to separate the cathode and anode. The unique cross-linked structure offers additional free volume for the motion of EO chains and provides fast and continuously interconnected ion-conducting channels along the nanoparticles/polymer matrix interface. The HPE exhibits the highest ionic conductivity of 1.39 × 10-3 S cm-1, as well as excellent interfacial compatibility with the Li electrode at 80°C. In particular, LiFePO4/Li cells based on the HPE deliver good rate capability and long-term cycling performance with an initial discharge capacity of 152.1 mAh g-1 and a capacity retention ratio of 88% after 150 cycles with a current density of 0.5 C at 80°C, demonstrating great potential application in high-performance LIBs at elevated temperatures.

| S-EPMC5981318 | biostudies-literature

Solid-state polymer electrolytes for high-performance lithium metal batteries.

Project description:Electrochemical cells based on alkali metal anodes are receiving intensive scientific interest as potentially transformative technology platforms for electrical energy storage. Chemical, morphological, mechanical and hydrodynamic instabilities at the metal anode produce uneven metal electrodeposition and poor anode reversibility, which, are among the many known challenges that limit progress. Here, we report that solid-state electrolytes based on crosslinked polymer networks can address all of these challenges in cells based on lithium metal anodes. By means of transport and electrochemical analyses, we show that manipulating thermodynamic interactions between polymer segments covalently anchored in the network and "free" segments belonging to an oligomeric electrolyte hosted in the network pores, one can facilely create hybrid electrolytes that simultaneously exhibit liquid-like barriers to ion transport and solid-like resistance to morphological and hydrodynamic instability.

| S-EPMC6765010 | biostudies-literature

Polyethylene Oxide-Based Composites as Solid-State Polymer Electrolytes for Lithium Metal Batteries: A Mini Review.

Project description:Solid-state polymer electrolytes (SPEs) have great processing flexibility and electrode-electrolyte contact and have been employed as the promising electrolytes for lithium metal batteries. Among them, poly(ethylene oxide) (PEO)-based SPEs have attracted widespread attention because of easy synthesis, low mass density, good mechanical stability, low binding energy with lithium salts, and excellent mobility of charge carriers. In order to overcome the low room-temperature ionic conductivity and the poor thermodynamic stability in high-voltage devices (>4.2 V) of the PEO materials, composition modulations by incorporating PEO with inorganic and/or organic components have been designed, which could effectively enable the applications of PEO-based SPEs with widened electro-stable voltage ranges. In this mini review, we describe recent progresses of several kinds of PEO composite structures for SPEs, and we compare the synthesis strategies and properties of these SPEs in lithium batteries. Further developments and improvements of the PEO-based materials for building better rechargeable batteries are also discussed.

| S-EPMC7431671 | biostudies-literature

Designing the Interface Layer of Solid Electrolytes for All-Solid-State Lithium Batteries.

Project description:Li1.3Al0.3Ti1.7(PO4)3 (LATP) is one of the most attractive solid-state electrolytes (SSEs) for application in all-solid-state lithium batteries (ASSLBs) due to its advantages of high ionic conductivity, air stability and low cost. However, the poor interfacial contact and slow Li-ion migration have greatly limited its practical application. Herein, a composite ion-conducting layer is designed at the Li/LATP interface, which a MoS2 film is constructed on LATP via chemical vapor deposition, followed by the introduction of a solid polymer (SP) liquid precursor to form a MoS2@SP protective layer. This protective layer not only achieves a lower Li-ion migration energy barrier, but also adsorbs more Li-ion, which is able to promote interfacial ion transport and improve interfacial contacts. Thanks to the improved migration and adsorption of Li-ion, the Li symmetric cell containing LATP-MoS2@SP exhibits a stable cycle of more than 1200 h at 0.1 mA cm-2. More remarkably, the capacity retention of the full cell assembled with LiFePO4 cathode is as high as 86.2% after 400 cycles at 1 C. This work provides a design strategy for significantly improving unstable interfaces of SSEs and realizing high-performance ASSLBs.

| S-EPMC11304316 | biostudies-literature

Progress and Perspective of Glass-Ceramic Solid-State Electrolytes for Lithium Batteries.

Project description:The all-solid-state lithium battery (ASSLIB) is one of the key points of future lithium battery technology development. Because solid-state electrolytes (SSEs) have higher safety performance than liquid electrolytes, and they can promote the application of Li-metal anodes to endow batteries with higher energy density. Glass-ceramic SSEs with excellent ionic conductivity and mechanical strength are one of the main focuses of SSE research. In this review paper, we discuss recent advances in the synthesis and characterization of glass-ceramic SSEs. Additionally, some discussions on the interface problems commonly found in glass-ceramic SSEs and their solutions are provided. At the end of this review, some drawbacks of glass-ceramic SSEs are summarized, and future development directions are prospected. We hope that this review paper can help the development of glass-ceramic solid-state electrolytes.

| S-EPMC10096416 | biostudies-literature

2D MXene-containing polymer electrolytes for all-solid-state lithium metal batteries.

Project description:Nanocomposite polymer electrolytes (CPEs) are promising materials for all-solid-state lithium metal batteries (LMBs) due to their enhanced ionic conductivities and stability to the lithium anode. MXenes are a new two-dimensional, 2D, family of early transition metal carbides and nitrides, which have a high aspect ratio and a hydrophilic surface. Herein, using a green, facile aqueous solution blending method, we uniformly dispersed small amounts of Ti3C2T x into a poly(ethylene oxide)/LiTFSI complex (PEO20-LiTFSI) to fabricate MXene-based CPEs (MCPEs). The addition of the 2D flakes to PEO simultaneously retards PEO crystallization and enhances its segmental motion. Compared to the 0D and 1D nanofillers, MXenes show higher efficiency in ionic conductivity enhancement and improvement in the performance of LMBs. The CPE with 3.6 wt% MXene shows the highest ionic conductivity at room temperature (2.2 × 10-5 S m-1 at 28 °C). An LMB using MCPE with only 1.5 wt% MXene shows rate capability and stability comparable with that of the state-of-the-art CPELMBs. We attribute the excellent performance to the 2D geometry of the filler, the good dispersion of the flakes in the polymer matrix, and the functional group-rich surface.

| S-EPMC9473207 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data