The II-I Phase Transition Behavior of Butene-1 Copolymers with Hydroxyl Groups.

ABSTRACT: The crystallization and II-I phase transition of functionalized polybutene-1 with hydroxyl groups were investigated by differential scanning calorimetry. The results show that the incorporated hydroxyl groups increase the nucleation density but decrease the growth rate in melt crystallization. Interestingly, for the generated tetragonal form II, the presence of polar hydroxyl groups can effectively accelerate the phase transition into the thermodynamically stable modification of trigonal form I, especially with stepwise annealing and high incorporation. Using stepwise annealing, II-I phase transition was enhanced by an additional nucleation step performed at a relatively low temperature, and the optimal nucleation temperature to obtain the maximum transition degree was ‒10 °C, which is independent from the content of hydroxyl groups. Furthermore, the accelerating effect of hydroxyl groups on the II-I transition kinetics can be increased by reducing the crystallization temperature when preparing form II crystallites. These results provide a potential molecular design approach for developing polybutene-1 materials.

SUBMITTER: Li Y

PROVIDER: S-EPMC8074023 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Thermal Analysis of Crystallization and Phase Transition in Novel Polyethylene Glycol Grafted Butene-1 Copolymers.

Project description:Copolymerization is an effective strategy to regulate the molecular structure and tune crystalline structures. In this work, novel butene-1 copolymers with different polyethylene glycol (PEG) grafts (number-average molecular weight Mn = 750, 2000, and 4000 g/mol) were synthesized, for the first time introducing long-chain grafts to the polybutene-1 main chain. For these PEG-grafted copolymers, crystallization, melting, and phase transition behaviors were explored using differential scanning calorimetry. With respect to the linear homopolymer, the incorporation of a trimethylsilyl group decreases the cooling crystallization temperature (Tc), whereas the presence of the long PEG grafts unexpectedly elevates Tc. For isothermal crystallization, a critical temperature was found at 70 °C, below which all polyethylene glycol-grafted butene-1 (PB-PEG) copolymers have faster crystallization kinetics than polybutene-1 (PB). The subsequent melting process shows that for the identical crystallization temperature, generated PB-PEG crystallites always have lower melting temperatures than that of PB. Moreover, the II-I phase transition behavior of copolymers is also dependent on the length of PEG grafts. When form II, obtained from isothermal crystallization at 60 °C, was annealed at 25 °C, PB-PEG-750, with the shortest PEG grafts of Mn = 750 g/mol, could have the faster transition rate than PB. However, PB-PEG-750 exhibits a negative correlation between transition rate and crystallization temperature. Differently, in PB-PEG copolymers with PEG grafts Mn = 2000 and 4000 g/mol, transition rates rise with elevating crystallization temperature, which is similar with homopolymer PB. Therefore, the grafting of the PEG side chain provides the available method to tune phase transition without sacrificing crystallization capability in butene-1 copolymers.

| S-EPMC6572506 | biostudies-literature

Phase Behavior and Conformational Asymmetry near the Comb-to-Bottlebrush Transition in Linear-Brush Block Copolymers.

Project description:This study explores how conformational asymmetry influences the bulk phase behavior of linear-brush block copolymers. We synthesized 60 diblock copolymers composed of poly(trifluoroethyl methacrylate) as the linear block and poly[oligo(ethylene glycol) methyl ether methacrylate] as the brush block, varying the molecular weight, composition, and side-chain length to introduce different degrees of conformational asymmetry. Using small-angle X-ray scattering, we determined the morphology and phase diagrams for three different side-chain length systems, mainly observing lamellar and cylindrical phases. Increasing the side-chain length of the brush block from three to nine ethylene oxide units introduces sufficient asymmetry between the blocks to alter the phase behavior, shifting the lamellar-to-cylindrical transitions toward lower brush block compositions and transitioning the brush block from the dense comb-like regime to the bottlebrush regime. Coarse-grained simulations support our experimental observations and provide a mapping between the composition and conformational asymmetry. A comparison of our findings to strong stretching theory across multiple phase boundary predictions confirms the transition between the dense comb-like regime and the bottlebrush regime.

| S-EPMC10938885 | biostudies-literature

Melt-Crystallizations of α and γ Forms of Isotactic Polypropylene in Propene-Butene Copolymers.

Project description:Random isotactic propene-butene copolymers (iPPC4) of different stereoregularity have been synthesized with three different homogeneous single center metallocene catalysts having different stereoselectivity. All samples crystallize from the polymerization solution in mixtures of α and γ forms, and the relative amount of γ form increases with increasing concentrations of butene and of rr stereodefects. All samples crystallize from the melt in mixtures of α and γ forms and the fraction of γ form increases with decreasing cooling rate. At high cooling rates, the crystallization of the α form is always favored, even for samples that contain high total concentration of defects that should crystallize in the γ form. The results demonstrate that in iPPs containing significant concentrations of defects, such as stereodefects and comonomeric units, the γ form is the thermodynamically stable form of iPP and crystallizes in selective conditions of very slow crystallization, whereas the α form is the kinetically favored form and crystallizes in conditions of fast crystallization.

| S-EPMC9500696 | biostudies-literature

Phase behavior and interfacial tension of ternary polymer mixtures with block copolymers.

Project description:The phase behavior and interfacial tension of ternary polymeric mixtures (polystyrene/polystyrene-b-poly(methyl methacrylate)/poly(methyl methacrylate), PS/PS-b-PMMA/PMMA) are investigated by dissipative particle dynamics (DPD) simulations. Our simulation results show that, as the PS-b-PMMA diblock copolymer concentration increases, the interfacial tension decreases due to the decayed correlations between homopolymers PS and PMMA. When the chain lengths of copolymers are fixed, with the increase of the chain lengths of PS and PMMA homopolymers the interfacial width becomes wider and the interfacial tension becomes smaller, due to the copolymers presenting more stretched and swollen structures in the mixtures with the short length of homopolymers. However, with simultaneously increasing chain lengths of both diblock copolymer and homopolymers with a fixed ratio, the interfacial tension increases because the copolymer chains with longer chain length penetrate more deeply into the homopolymer phase and the interactions between diblock copolymers become weaker. These results will provide a way to mix incompatible homopolymers to improve material performances.

| S-EPMC9044050 | biostudies-literature

Synthesis of Amphiphilic Statistical Copolymers Bearing Methoxyethyl and Phosphorylcholine Groups and Their Self-Association Behavior in Water.

Project description:Biocompatible amphiphilic statistical copolymers P(MEA/MPCm) composed of 2-methoxyethyl acrylate (MEA) and 2-methacryloyloxyethyl phosphorylcholine (MPC) were prepared with three different mol% of the hydrophilic unit MPC (m = 6, 12 and 46 mol%). The monomer reactivity ratios of MEA (rMEA) and MPC (rMPC) were 0.53 and 2.21, respectively. The rMEA × rMPC value of 1.17 demonstrated that statistical copolymerization was successful. P(MEA/MPC12) and P(MEA/MPC46) copolymers did not undergo aggregation in water, whereas the P(MEA/MPC6) copolymer formed micelles in water with a hydrodynamic radius (Rh) of 96.9 nm and a critical aggregation concentration, which was determined using pyrene fluorescence, at 0.0082 g/L. The restricted motion of the protons in the hydrophobic MEA units in the micelles' cores provided additional evidence of self-association in P(MEA/MPC6).

| S-EPMC7464738 | biostudies-literature

A ribozyme that triphosphorylates RNA 5'-hydroxyl groups.

Project description:The RNA world hypothesis describes a stage in the early evolution of life in which RNA served as genome and as the only genome-encoded catalyst. To test whether RNA world organisms could have used cyclic trimetaphosphate as an energy source, we developed an in vitro selection strategy for isolating ribozymes that catalyze the triphosphorylation of RNA 5'-hydroxyl groups with trimetaphosphate. Several active sequences were isolated, and one ribozyme was analyzed in more detail. The ribozyme was truncated to 96 nt, while retaining full activity. It was converted to a trans-format and reacted with rates of 0.16 min(-1) under optimal conditions. The secondary structure appears to contain a four-helical junction motif. This study showed that ribozymes can use trimetaphosphate to triphosphorylate RNA 5'-hydroxyl groups and suggested that RNA world organisms could have used trimetaphosphate as their energy source.

| S-EPMC3985629 | biostudies-literature

pH-responsive non-ionic diblock copolymers: ionization of carboxylic acid end-groups induces an order-order morphological transition.

Project description:A carboxylic acid based reversible additionfragmentation transfer (RAFT) agent is used to prepare gels composed of worm-like diblock copolymers using two non-ionic monomers, glycerol monomethacrylate (GMA) and 2-hydroxypropyl methacrylate (HPMA). Ionization of the carboxylic acid end-group on the PGMA stabilizer block induces a worm-to-sphere transition, which in turn causes immediate degelation. This morphological transition is fully reversible as determined by TEM and rheology studies and occurs because of a subtle change in the packing parameter for the copolymer chains. A control experiment where the methyl ester derivative of the RAFT agent is used to prepare the same diblock copolymer confirms that no pH-responsive behavior occurs in this case. This end-group ionization approach is important for the design of new pH-responsive copolymer nano-objects as, unlike polyacids or polybases, only a minimal amount of added base (or acid) is required to drive the morphological transition.

| S-EPMC4312895 | biostudies-other

Investigating global phase diagrams (GPDs) with reentrant transition behavior.

Project description:In this paper we calculate the global phase diagrams with the closed-loop behavior for the phase transition of physical systems by means of the transverse field Ising model with nearest neighbor interaction. The 3D graph plotted by the various physical parameters gives a clear appreciation and qualitative understanding of the reentrant phase behavior of the system. Meanwhile the results show the close correlation between experimental phenomena and our theoretical calculation for the closed-loop behavior for the phase transition of the systems.

| S-EPMC6042702 | biostudies-literature

Poly (1-butene-ran-ethylene) Monomodal Copolymers from Metallocene Catalysts: Structural and Morphological Differences with Increasing Ethylene Content.

Project description:Samples of random poly(butene-ran-ethylene) copolymers produced with metallocene catalysts were studied in order to elucidate the different behaviors of this particular class of materials as a function of increasing ethylene (C2) content. The samples cooled down from the melt are semi-crystalline or amorphous and crystallize in different crystal modifications, depending on the amount of C2. Thermal analysis, X-ray diffraction, and microscopic techniques were used to follow the changes of the materials with aging time and to understand the structural and morphological behavior with the aim of highlighting possible peculiar properties, which may be of great interest in the application of such materials in the field of Hot Melt adhesives.

| S-EPMC6680423 | biostudies-literature

How are Hydroxyl Groups Localized on a Graphene Sheet?

Project description:Arrangements of hydroxyl groups on graphene sheets were systematically investigated using density functional theory calculations that included van der Waals interactions. Results show that hydroxyl groups tend to gather at para-positions on graphene sheets to generate perfect ring-like hexahydroxyl group adsorption. The close proximity of hydroxyl groups is in good agreement with the experimental separation between unoxidized, aromatic and oxidized, saturated regions in graphene oxide. The orientation of hydrogen atoms in hydroxyl groups creates both O-H···O and O-H···π hydrogen bonds. Calculations also indicated that the binding energy per hydroxyl group follows a logarithmic function with respect to the number of hydroxyl groups. Besides, the opening band gap was observed for several derivatives, and the relationship between the band gap and O/C ratio was found to be nonmonotonic. Analysis of the density of states showed that bands around the Fermi levels of derivatives between graphene and hydroxyl groups are mainly composed of 2p z orbitals of carbon and oxygen atoms.

| S-EPMC9608424 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data