Defect induced ferromagnetic ordering and room temperature negative magnetoresistance in MoTeP.
Ontology highlight
ABSTRACT:
SUBMITTER: Pal D
PROVIDER: S-EPMC8079386 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Despite theoretical predictions, the question of room-temperature magnetic order in graphene must be conclusively resolved before graphene can fully achieve its potential as a spintronic medium. Through scanning tunneling microscopy (STM) and point I-V measurements, the current study reveals that unlike pristine samples, graphene nanostructures, when functionalized with aryl radicals, can sustain magnetic order. STM images show 1-D and 2-D periodic super-lattices originating from the functionalization of a single sub-lattice of the bipartite graphene structure. Field-dependent super-lattices in 3-nm wide "zigzag" nanoribbons indicate local moments with parallel and anti-parallel ordering along and across the edges, respectively. Anti-parallel ordering is observed in 2-D segments with sizes of over 20 nm. The field dependence of STM images and point I-V curves indicates a spin polarized local density of states (LDOS), an out-of-plane anisotropy field of less than 10 Oe, and an exchange coupling field of 100 Oe at room temperature.
| S-EPMC3432455 | biostudies-literature
Project description:We report the synthesis of a room temperature ferromagnetic Mn-Ge system obtained by simple deposition of manganese on Ge(001), heated at relatively high temperature (starting with 250 °C). The samples were characterized by low energy electron diffraction (LEED), scanning tunneling microscopy (STM), high resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), superconducting quantum interference device (SQUID), and magneto-optical Kerr effect (MOKE). Samples deposited at relatively elevated temperature (350 °C) exhibited the formation of ~5-8 nm diameter Mn₅Ge₃ and Mn11Ge₈ agglomerates by HRTEM, while XPS identified at least two Mn-containing phases: the agglomerates, together with a Ge-rich MnGe~2.5 phase, or manganese diluted into the Ge(001) crystal. LEED revealed the persistence of long range order after a relatively high amount of Mn (100 nm) deposited on the single crystal substrate. STM probed the existence of dimer rows on the surface, slightly elongated as compared with Ge-Ge dimers on Ge(001). The films exhibited a clear ferromagnetism at room temperature, opening the possibility of forming a magnetic phase behind a nearly ideally terminated Ge surface, which could find applications in integration of magnetic functionalities on semiconductor bases. SQUID probed the co-existence of a superparamagnetic phase, with one phase which may be attributed to a diluted magnetic semiconductor. The hypothesis that the room temperature ferromagnetic phase might be the one with manganese diluted into the Ge crystal is formulated and discussed.
| S-EPMC5453147 | biostudies-other
Project description:Spin injection using ferromagnetic semiconductors at room temperature is a building block for the realization of spin-functional semiconductor devices. Nevertheless, this has been very challenging due to the lack of reliable room-temperature ferromagnetism in well-known group IV and III-V based semiconductors. Here, we demonstrate room-temperature spin injection by using spin pumping in a BiSb/(Ga,Fe)Sb heterostructure, where (Ga,Fe)Sb is a ferromagnetic semiconductor (FMS) with high Curie temperature (TC) and BiSb is a topological insulator (TI). Despite the very small magnetization of (Ga,Fe)Sb at room temperature (45 emu/cc), we detected spin injection from (Ga,Fe)Sb by utilizing the large inverse spin Hall effect (ISHE) in BiSb. Our study provides the first demonstration of spin injection at room temperature from a FMS.
| S-EPMC9905071 | biostudies-literature
Project description:Topological insulators (TI) have extremely high potential in spintronic applications. Here, a topological insulators thin-film (TITF) spin valve with the use of the segment gate-controlled potential exhibits a huge magnetoresistance (MR) value higher than 1000% at room temperature which is more than 50 times the MR of typical topological insulators (TI) spin-valves. A high spin-polarized current is provided by the band structure generated by the tunable segment potential. The results reveal a very large resistance difference between the parallel and antiparallel configurations. The MR effect is strongly influenced by the thin-film thickness, the gate potential, the gate size, and the distribution. The proposed results will help to not only improve the room-temperature performance of the spin-valves but also enhance the applications of magnetic memories and spintronic devices.
| S-EPMC8175690 | biostudies-literature
Project description:Manipulating electronic and magnetic properties of two-dimensional transitional-metal dichalcogenides has raised a lot of attention recently. Herein we report the synthesis and ferromagnetic properties of phase-transfer induced room temperature ferromagnetic behavior in 1 T@2H-MoSe2 nanosheets. Experimental results indicate the saturated magnetization of the 1 T@2H-MoSe2 compound increases first and then decreases as the increasing of 1 T-MoSe2 phase, where 65.58% 1 T-MoSe2 phase incorporation in 2H-MoSe2 could enhance the saturated magnetization from 0.32 memu/g to 8.36 memu/g. Besides, obvious magnetoresistance behaviors are observed in these samples, revealing their potential applications in future spintronics.
| S-EPMC5368601 | biostudies-literature
Project description:There is an urgent quest for room-temperature qubits in nanometer-sized, ultrasmall nanocrystals for quantum biosensing, hyperpolarization of biomolecules, and quantum information processing. Thus far, the preparation of such qubits at the nanoscale has remained futile. Here, we present a synthesis method that avoids any interaction of the solid with high-energy particles and uses self-propagated high-temperature synthesis with a subsequent electrochemical method, the no-photon exciton generation chemistry to produce room-temperature qubits in ultrasmall nanocrystals of sizes down to 3 nm with high yield. We first create the host silicon carbide (SiC) crystallites by high-temperature synthesis and then apply wet chemical etching, which results in ultrasmall SiC nanocrystals and facilitates the creation of thermally stable defect qubits in the material. We demonstrate room-temperature optically detected magnetic resonance signal of divacancy qubits with 3.5% contrast from these nanoparticles with emission wavelengths falling in the second biological window (1000-1380 nm). These results constitute the formation of nonperturbative bioagents for quantum sensing and efficient hyperpolarization.
| S-EPMC7307950 | biostudies-literature
Project description:Development of novel magnetic materials is of interest for fundamental studies and applications such as spintronics, permanent magnetics, and sensors. We report on the first experimental realization of single element ferromagnetism, since Fe, Co, and Ni, in metastable tetragonal Ru, which has been predicted. Body-centered tetragonal Ru phase is realized by use of strain via seed layer engineering. X-ray diffraction and electron microscopy confirm the epitaxial mechanism to obtain tetragonal phase Ru. We observed a saturation magnetization of 148 and 160?emu?cm-3 at room temperature and 10?K, respectively. Control samples ensure the ferromagnetism we report on is from tetragonal Ru and not from magnetic contamination. The effect of thickness on the magnetic properties is also studied, and it is observed that increasing thickness results in strain relaxation, and thus diluting the magnetization. Anomalous Hall measurements are used to confirm its ferromagnetic behavior.
| S-EPMC5970227 | biostudies-literature
Project description:Ultrathin epitaxial films of ferromagnetic insulators (FMIs) with Curie temperatures near room temperature are critically needed for use in dissipationless quantum computation and spintronic devices. However, such materials are extremely rare. Here, a room-temperature FMI is achieved in ultrathin La0.9Ba0.1MnO3 films grown on SrTiO3 substrates via an interface proximity effect. Detailed scanning transmission electron microscopy images clearly demonstrate that MnO6 octahedral rotations in La0.9Ba0.1MnO3 close to the interface are strongly suppressed. As determined from in situ X-ray photoemission spectroscopy, O K-edge X-ray absorption spectroscopy, and density functional theory, the realization of the FMI state arises from a reduction of Mn eg bandwidth caused by the quenched MnO6 octahedral rotations. The emerging FMI state in La0.9Ba0.1MnO3 together with necessary coherent interface achieved with the perovskite substrate gives very high potential for future high performance electronic devices.
| S-EPMC6947487 | biostudies-literature
Project description:We have investigated the effect of a magnetic field on the resistance (magnetoresistance, MR) of single-walled carbon nanotube (SWNT) arrays. The SWNT devices consist of a mixture of metallic and semiconducting SWNTs between palladium electrodes. The MR of the devices is studied at room temperature and in the presence of perpendicular magnetic fields up to 0.24 tesla. The resistance increases as the external magnetic field becomes higher, suggesting a positive MR of SWNTs. After etching the metallic SWNTs by electrical breakdown, the MR can be further enhanced. Large positive MR values about 15%, 20% and 25% were found in three different devices at 0.24 tesla for semiconducting SWNTs at room temperature. Our results show potential for the development of magneto-electronic devices that are operable at room temperature.
| S-EPMC9078853 | biostudies-literature
Project description:Ferromagnetic FexGe1-x with x = 2%-9% are obtained by Fe deposition onto Ge(001) at high temperatures (500 °C). Low energy electron diffraction (LEED) investigation evidenced the preservation of the (1 × 1) surface structure of Ge(001) with Fe deposition. X-ray photoelectron spectroscopy (XPS) at Ge 3d and Fe 2p core levels evidenced strong Fe diffusion into the Ge substrate and formation of Ge-rich compounds, from FeGe₃ to approximately FeGe₂, depending on the amount of Fe deposited. Room temperature magneto-optical Kerr effect (MOKE) evidenced ferromagnetic ordering at room temperature, with about 0.1 Bohr magnetons per Fe atom, and also a clear uniaxial magnetic anisotropy with the in-plane easy magnetization axis. This compound is a good candidate for promising applications in the field of semiconductor spintronics.
| S-EPMC5452101 | biostudies-other