Green Synthesis of Luminescent Gold-Zinc Oxide Nanocomposites: Cell Imaging and Visible Light-Induced Dye Degradation.

ABSTRACT: Green synthesis of gold-zinc oxide (Au-ZnO) nanocomposite was successfully attempted under organic solvent-free conditions at room temperature. Prolonged stirring of the reaction mixture introduced crystallinity in the ZnO phase of Au-ZnO nanocomposites. Luminescence properties were observed in these crystalline Au-ZnO nanocomposites due to in situ embedding of gold nanoparticles (AuNP) of 5-6 nm diameter on the surface. This efficient strategy involved the reduction of Au(III) by Zn(0) powder in aqueous medium, where sodium citrate (NaCt) was the stabilizing agent. Reaction time and variation of reagent concentrations were investigated to control the Au:Zn ratio within the nanocomposites. The reaction with the least amount of NaCt for a long duration resulted in Au-ZnO/Zn(OH)₂ nanocomposite. X-ray photoelectron spectroscopy (XPS) confirmed the formation of Zn(OH)₂ and ZnO in the same nanocomposite. These nanocomposites were reconnoitered as bioimaging materials in human cells and applied for visible light-induced photodegradation of rhodamine-B dye.

SUBMITTER: Bharti K

PROVIDER: S-EPMC8080447 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Visible-Light Active and Magnetically Recyclable Nanocomposites for the Degradation of Organic Dye.

Project description:Recyclable visible-light photocatalyst Fe₃O₄@TiO₂ with core-shell structure was prepared by a simple synthetic strategy using solvothermal crystallization of titanium precursor on preformed Fe₃O₄ nanopartiles. The photo-degradation reaction of neutral red aqueous solution was tested to evaluate the visible-light photocatalytic activity of the as prepared Fe₃O₄@TiO₂ nanoparticles, which show excellent photocatalytic activity compared with commercial P25 catalyst. Moreover, the Fe₃O₄@TiO₂ nanocomposites can be easily separated from the reaction mixture, and maintain favorable photocatalytic activity after five cycles. The high visible light absorption of the Fe₃O₄@TiO₂ nanocomposites may originate from the absence of electronic heterojunction, excellently dispersity and the high specific surface area of the as-synthesized Fe₃O₄@TiO₂ samples.

| S-EPMC5453214 | biostudies-other

Effective Visible-Light-Driven Photocatalytic Degradation of Harmful Antibiotics Using Reduced Graphene Oxide-Zinc Sulfide-Copper Sulfide Nanocomposites as a Catalyst.

Project description:In recent decades, antibiotics have been found in aquatic environments, raising severe concerns. In this study, a unique reduced graphene oxide-zinc sulfide-copper sulfide (rGO-ZnS-CuS) nanocomposite (NC) prepared by using a straightforward surfactant-free in situ microwave method was used for antibiotic degradation via photocatalysis. The structural and morphological characteristics of the produced catalysts were characterized using various techniques, confirming the successful development of nanocomposite structures of better quality than that of the pure samples. The photocatalytic degradation of antibiotics containing ofloxacin was also investigated. The results suggest that the rGO-ZCS NC outperformed the other composites in terms of photocatalytic activity toward ofloxacin degradation. Superoxide and hydroxyl radicals were the main active species during the degradation process. According to our results, the catalytic activity of rGO-ZCS NC is much better than that of the other composites.

| S-EPMC10500589 | biostudies-literature

Importance of Plasmonic Heating on Visible Light Driven Photocatalysis of Gold Nanoparticle Decorated Zinc Oxide Nanorods.

Project description:Herein we explore the role of localized plasmonic heat generated by resonantly excited gold (Au) NPs on visible light driven photocatalysis process. Au NPs are deposited on the surface of vertically aligned zinc oxide nanorods (ZnO NRs). The localized heat generated by Au NPs under 532?nm continuous laser excitation (SPR excitation) was experimentally probed using Raman spectroscopy by following the phonon modes of ZnO. Under the resonant excitation the temperature at the surface of the Au-ZnO NRs reaches up to about 300?°C, resulting in almost 6 times higher apparent quantum yield (AQY) for photocatalytic degradation of methylene blue (MB) compared to the bare ZnO NRs. Under solar light irradiation the Au-ZnO NRs demonstrated visible light photocatalytic activity twice that of what was achieved with bare ZnO NRs, while significantly reduced the activation energy required for the photocatalytic reactions allowing the reactions to occur at a faster rate.

| S-EPMC4886257 | biostudies-literature

Controlled Defects of Zinc Oxide Nanorods for Efficient Visible Light Photocatalytic Degradation of Phenol.

Project description:Environmental pollution from human and industrial activities has received much attention as it adversely affects human health and bio-diversity. In this work we report efficient visible light photocatalytic degradation of phenol using supported zinc oxide (ZnO) nanorods and explore the role of surface defects in ZnO on the visible light photocatalytic activity. ZnO nanorods were synthesized on glass substrates using a microwave-assisted hydrothermal process, while the surface defect states were controlled by annealing the nanorods at various temperatures and were characterized by photoluminescence and X-ray photoelectron spectroscopy. High performance liquid chromatography (HPLC) was used for the evaluation of phenol photocatalytic degradation. ZnO nanorods with high surface defects exhibited maximum visible light photocatalytic activity, showing 50% degradation of 10 ppm phenol aqueous solution within 2.5 h, with a degradation rate almost four times higher than that of nanorods with lower surface defects. The mineralization process of phenol during degradation was also investigated, and it showed the evolution of different photocatalytic byproducts, such as benzoquinone, catechol, resorcinol and carboxylic acids, at different stages. The results from this study suggest that the presence of surface defects in ZnO nanorods is crucial for its efficient visible light photocatalytic activity, which is otherwise only active in the ultraviolet region.

| S-EPMC5502885 | biostudies-other

Degradation of Methylene Blue Dye in the Presence of Visible Light Using SiO₂@α-Fe₂O₃ Nanocomposites Deposited on SnS₂ Flowers.

Project description:Semiconductor materials have been shown to have good photocatalytic behavior and can be utilized for the photodegradation of organic pollutants. In this work, three-dimensional flower-like SnS₂ (tin sulfide) was synthesized by a facile hydrothermal method. Core-shell structured SiO₂@α-Fe₂O₃ nanocomposites were then deposited on the top of the SnS₂ flowers. The as-synthesized nanocomposites were characterized by X-ray diffraction (XRD), Raman spectroscopy, field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV⁻Vis Spectroscopy, Brunauer⁻Emmett⁻Teller (BET) surface area analysis, and photoluminescence (PL) spectroscopy. The photocatalytic behavior of the SnS₂-SiO₂@α-Fe₂O₃ nanocomposites was investigated by observing the degradation of methylene blue (MB). The results show an effective enhancement of photocatalytic activity for the degradation of MB especially for the 15 wt % SiO₂@α-Fe₂O₃ nanocomposites on SnS₂ flowers.

| S-EPMC6025432 | biostudies-literature

Optimization of green biosynthesized visible light active CuO/ZnO nano-photocatalysts for the degradation of organic methylene blue dye.

Project description:Herein, CuO/ZnO nanocomposites at different ratios were successfully synthesized through a green biosynthesis approach. This was performed by harnessing the fungal-secreted enzymes and proteins during the sol-gel process for nanocomposites seed growth. All fabricated nanoparticles/nanocomposites were characterized using Fourier Transform Infra-Red (FT-IR) Spectroscopy, X-Ray Diffraction (XRD), Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM-EDX) and X-ray Photoelectron Spectroscopy (XPS) analyses. The photocatalytic degradation efficacy of the synthesized nanocomposites was evaluated using a cationic methylene blue (MB) dye as a model of reaction. Results obtained from the FT-IR and EDX analyses revealed that CuO-NPs, ZnO-NPs, CuO/ZnO50/50, CuO/ZnO80/20, and CuO/ZnO20/80 were successfully prepared by harnessing the biomass filtrate of Penicillium corylophilum As-1. Furthermore, XRD and TEM revealed the variation in the particle size of the nanocomposites (10-55 nm) with the ratio of the nanoparticles. Notably, the size of the nanocomposites was proportionally increased with an increasing ratio of ZnO-NPs. XPS analysis affirmed the presence of both Cu and Zn in the nanocomposites with varying binding energies compared with individual nanoparticles. Furthermore, a high photo-degradation efficacy was achieved by increasing the ratio of ZnO-NPs in the nanocomposite formulation, and 97% of organic MB dye was removed after 85 min of irradiation using the CuO/ZnO20/80 nanocomposite.

| S-EPMC7511830 | biostudies-literature

Polyvinylidene Fluoride-Graphene Oxide Membranes for Dye Removal under Visible Light Irradiation.

Project description:In this study, polyvinylidene fluoride (PVDF)-graphene oxide (GO) membranes were obtained by employing triethyl phosphate (TEP) as a solvent. GO nanosheets were prepared and characterized in terms of scanning and transmission electron microscopy (SEM and TEM, respectively), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), chemical analysis and inductively coupled plasma mass spectroscopy (ICP). Two different phase inversion techniques, Non-Solvent Induced Phase Separation (NIPS) and Vapour-Induced Phase Separation (VIPS)/NIPS, were applied to study the effect of fabrication procedure on the membrane structure and properties. Membranes were characterized by SEM, AFM, pore size, porosity, contact angle and mechanical tests, and finally tested for photocatalytic methylene blue (MB+) degradation under visible light irradiation. The effect of different pH values of dye aqueous solutions on the photocatalytic efficiency was investigated. Finally, the influence of NaCl salt on the MB+ photodegradation process was also evaluated.

| S-EPMC7407290 | biostudies-literature

Photocatalytic dye degradation and photoexcited anti-microbial activities of green zinc oxide nanoparticles synthesized <i>via Sargassum muticum</i> extracts.

Project description:Drug-resistant superbugs (DRS) were isolated from hospital sewage waste and confirmed by a 16S rDNA molecular technique as B. filamentosus, B. flexus, P. stutzeri, and A. baumannii. Green nanotechnologies provide a new promising alternative pathway that was found to be much safer, eco-friendly, and has economic benefits over physical/chemical methods. Sargassum muticum (SM) mediated zinc oxide nanoparticles (ZnO-NPs) were proved to be photocatalytic and anti-microbial agents. Anti-microbial action was demonstrated by a maximal growth inhibition activity of 18 mm against A. baumannii and a minimal of 12 mm against B. flexus at 80 μg mL-1 concentrations. The anti-microbial mechanism of SMZnO-NPs employed a biphasic phenomenon persuaded by an osmotic shock that can attack the DRS bacterial cells directly and lead to death. In addition, photocatalytic activity was investigated by SMZnO-NPs for the degradation of methylene blue (MB) dye under different light conditions. Natural sunlight irradiation shows effective enhancement with the highest efficiencies of 96% being achieved within 60 min compared to UV-light and visible-light. The reusability of SMZnO-NPs provides up to 6 consecutive cycles towards MB decolorization for environmental water cleansing.

| S-EPMC8978881 | biostudies-literature

<i>Rubus ellipticus</i> Sm. Fruit Extract Mediated Zinc Oxide Nanoparticles: A Green Approach for Dye Degradation and Biomedical Applications.

Project description:Rubus ellipticus fruits aqueous extract derived ZnO-nanoparticles (NPs) were synthesized through a green synthesis method. The structural, optical, and morphological properties of ZnO-NPs were investigated using XRD, FTIR, UV-vis spectrophotometer, XPS, FESEM, and TEM. The Rietveld refinement confirmed the phase purity of ZnO-NPs with hexagonal wurtzite crystalline structure and p-63-mc space group with an average crystallite size of 20 nm. XPS revealed the presence of an oxygen chemisorbed species on the surface of ZnO-NPs. In addition, the nanoparticles exhibited significant in vitro antioxidant activity due to the attachment of the hydroxyl group of the phenols on the surface of the nanoparticles. Among all microbial strains, nanoparticles' maximum antibacterial and antifungal activity in terms of MIC was observed against Bacillus subtilis (31.2 µg/mL) and Rosellinia necatrix (15.62 µg/mL), respectively. The anticancer activity revealed 52.41% of A549 cells death (IC50: 158.1 ± 1.14 µg/mL) at 200 μg/mL concentration of nanoparticles, whereas photocatalytic activity showed about 17.5% degradation of the methylene blue within 60 min, with a final dye degradation efficiency of 72.7%. All these results suggest the medicinal potential of the synthesized ZnO-NPs and therefore can be recommended for use in wastewater treatment and medicinal purposes by pharmacological industries.

| S-EPMC9147757 | biostudies-literature

Green Synthesis of 8-Hydroxyquinoline Barium as Visible-Light-Excited Luminescent Material Using Mechanochemical Activation Method.

Project description:Using high-energy UV-light to excite 8-hydroxyquinoline barium (BaQ2) is a short slab for this emerging area of organic luminescent materials. However, using visible light to excite BaQ2 has not been reported. To solve this problem, this study proposes the mechanochemical activation method to synthesize luminescent material of visible-light-excited BaQ2. This research applies infrared spectroscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy, scanning electron microscopy, energy dispersive spectroscopy, and fluorescence spectrometry to analyze the structure and luminescence properties. XRD shows that BaQ2 has a high crystallinity, small crystalline size, and high purity. According to the Scherrer equation, the mean particle size is 56 nm. The results of fluorescence spectrometry show that the excitation spectrum of the product is red-shifted, and the maximum excitation wavelength is 408 nm. According to these results, the product has a high fluorescence and can be excited under visible light. This research explains the high efficiency of the mechanochemical-activation method by thermodynamic and dynamic principles. This research also exemplifies luminescence theory of BaQ2 and at the microlevel explains the theory of visible-light-excited theory and the principle of luminescent intensity enhancement from the point of crystallography.

| S-EPMC6888826 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data