Fast Li-Ion Conduction in Spinel-Structured Solids.

ABSTRACT: Spinel-structured solids were studied to understand if fast Li⁺ ion conduction can be achieved with Li occupying multiple crystallographic sites of the structure to form a "Li-stuffed" spinel, and if the concept is applicable to prepare a high mixed electronic-ionic conductive, electrochemically active solid solution of the Li⁺ stuffed spinel with spinel-structured Li-ion battery electrodes. This could enable a single-phase fully solid electrode eliminating multi-phase interface incompatibility and impedance commonly observed in multi-phase solid electrolyte-cathode composites. Materials of composition Li_1.25M(III)_0.25TiO₄, M(III) = Cr or Al were prepared through solid-state methods. The room-temperature bulk Li⁺-ion conductivity is 1.63 × 10^-4 S cm^-1 for the composition Li_1.25Cr_0.25Ti_1.5O₄. Addition of Li₃BO₃ (LBO) increases ionic and electronic conductivity reaching a bulk Li⁺ ion conductivity averaging 6.8 × 10^-4 S cm^-1, a total Li-ion conductivity averaging 4.2 × 10^-4 S cm^-1, and electronic conductivity averaging 3.8 × 10^-4 S cm^-1 for the composition Li_1.25Cr_0.25Ti_1.5O₄ with 1 wt. % LBO. An electrochemically active solid solution of Li_1.25Cr_0.25Mn_1.5O₄ and LiNi_0.5Mn_1.5O₄ was prepared. This work proves that Li-stuffed spinels can achieve fast Li-ion conduction and that the concept is potentially useful to enable a single-phase fully solid electrode without interphase impedance.

SUBMITTER: Allen JL

PROVIDER: S-EPMC8124195 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Fast Lithium Ion Conduction in Lithium Phosphidoaluminates.

Project description:Solid electrolyte materials are crucial for the development of high-energy-density all-solid-state batteries (ASSB) using a nonflammable electrolyte. In order to retain a low lithium-ion transfer resistance, fast lithium ion conducting solid electrolytes are required. We report on the novel superionic conductor Li9 AlP4 which is easily synthesised from the elements via ball-milling and subsequent annealing at moderate temperatures and which is characterized by single-crystal and powder X-ray diffraction. This representative of the novel compound class of lithium phosphidoaluminates has, as an undoped material, a remarkable fast ionic conductivity of 3?mS?cm-1 and a low activation energy of 29?kJ?mol-1 as determined by impedance spectroscopy. Temperature-dependent 7 Li NMR spectroscopy supports the fast lithium motion. In addition, Li9 AlP4 combines a very high lithium content with a very low theoretical density of 1.703?g?cm-3 . The distribution of the Li atoms over the diverse crystallographic positions between the [AlP4 ]9- tetrahedra is analyzed by means of DFT calculations.

| S-EPMC7154659 | biostudies-literature

Robust and Adhesive Laminar Solid Electrolyte with Homogenous and Fast Li-Ion Conduction for High-Performance All-Solid-State Lithium Metal Battery.

Project description:Constructing composite solid electrolytes (CSEs) integrating the merits of inorganic and organic components is a promising approach to developing high-performance all-solid-state lithium metal batteries (ASSLMBs). CSEs are now capable of achieving homogeneous and fast Li-ion flux, but how to escape the trade-off between mechanical modulus and adhesion is still a challenge. Herein, a strategy to address this issue is proposed, that is, intercalating highly conductive, homogeneous, and viscous-fluid ionic conductors into robust coordination laminar framework to construct laminar solid electrolyte with homogeneous and fast Li-ion conduction (LSE-HFC). A 9 µm-thick LSH-HFC, in which poly(ethylene oxide)/succinonitrile is adsorbed by coordination laminar framework with metal-organic framework nanosheets as building blocks, is used here as an example to determine the validity. The Li-ion transfer mechanism is verified and works across the entire LSE-HFC, which facilitates homogeneous Li-ion flux and low migration energy barriers, endowing LSE-HFC with high ionic conductivity of 5.62 × 10-4 S cm-1 and Li-ion transference number of 0.78 at 25 °C. Combining the outstanding mechanical strength against punctures and the enhanced adhesion force with electrodes, LSE-HFC harvests uniform Li plating/stripping behavior. These enable the realization of high-energy-density ASSLMBs with excellent cycling stability when being assembled as LiFePO4/Li and LiNi0.6Mn0.2Co0.2O2/Li cells.

| S-EPMC11321704 | biostudies-literature

Protective Spinel Coating for Li1.17Ni0.17Mn0.50Co0.17O2 Cathode for Li-Ion Batteries through Single-Source Precursor Approach.

Project description:The Li1.17Ni0.17Mn0.50Co0.17O2 Li-rich NMC positive electrode (cathode) for lithium-ion batteries has been coated with nanocrystals of the LiMn1.5Co0.5O4 high-voltage spinel cathode material. The coating was applied through a single-source precursor approach by a deposition of the molecular precursor LiMn1.5Co0.5(thd)5 (thd = 2,2,6,6-tetramethyl-3,5-heptanedionate) dissolved in diethyl ether, followed by thermal decomposition at 400 °C inair resulting in a chemically homogeneous cubic spinel. The structure and chemical composition of the coatings, deposited on the model SiO2 spheres and Li-rich NMC crystallites, were analyzed using powder X-ray diffraction, electron diffraction, high angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and energy-dispersive X-ray (EDX) mapping. The coated material containing 12 wt.% of spinel demonstrates a significantly improved first cycle Coulombic efficiency of 92% with a high first cycle discharge capacity of 290 mAhg-1. The coating also improves the capacity and voltage retention monitored over 25 galvanostatic charge-discharge cycles, although a complete suppression of the capacity and voltage fade is not achieved.

| S-EPMC7558323 | biostudies-literature

Synthesis of ultrasmall Li-Mn spinel oxides exhibiting unusual ion exchange, electrochemical, and catalytic properties.

Project description:The efficient surface reaction and rapid ion diffusion of nanocrystalline metal oxides have prompted considerable research interest for the development of high functional materials. Herein, we present a novel low-temperature method to synthesize ultrasmall nanocrystalline spinel oxides by controlling the hydration of coexisting metal cations in an organic solvent. This method selectively led to Li-Mn spinel oxides by tuning the hydration of Li(+) ions under mild reaction conditions (i.e., low temperature and short reaction time). These particles exhibited an ultrasmall crystallite size of 2.3 nm and a large specific surface area of 371 ± 15 m(2) g(-1). They exhibited unique properties such as unusual topotactic Li(+)/H(+) ion exchange, high-rate discharge ability, and high catalytic performance for several aerobic oxidation reactions, by creating surface phenomena throughout the particles. These properties differed significantly from those of Li-Mn spinel oxides obtained by conventional solid-state methods.

| S-EPMC4601032 | biostudies-literature

Twin boundary defect engineering improves lithium-ion diffusion for fast-charging spinel cathode materials.

Project description:Defect engineering on electrode materials is considered an effective approach to improve the electrochemical performance of batteries since the presence of a variety of defects with different dimensions may promote ion diffusion and provide extra storage sites. However, manipulating defects and obtaining an in-depth understanding of their role in electrode materials remain challenging. Here, we deliberately introduce a considerable number of twin boundaries into spinel cathodes by adjusting the synthesis conditions. Through high-resolution scanning transmission electron microscopy and neutron diffraction, the detailed structures of the twin boundary defects are clarified, and the formation of twin boundary defects is attributed to agminated lithium atoms occupying the Mn sites around the twin boundary. In combination with electrochemical experiments and first-principles calculations, we demonstrate that the presence of twin boundaries in the spinel cathode enables fast lithium-ion diffusion, leading to excellent fast charging performance, namely, 75% and 58% capacity retention at 5 C and 10 C, respectively. These findings demonstrate a simple and effective approach for fabricating fast-charging cathodes through the use of defect engineering.

| S-EPMC8149699 | biostudies-literature

High-performance spinel-rich Li1.5MnTiO4+δ ultralong nanofibers as cathode materials for Li-ion batteries.

Project description:Recently, composite materials based on Li-Mn-Ti-O system were developed to target low cost and environmentally benign cathodes for Li-ion batteries. The spinel-layered Li1.5MnTiO4+δ bulk particles showed excellent cycle stability but poor rate performance. To address this drawback, ultralong nanofibers of a Li1.5MnTiO4+δ spinel-layered heterostructure were synthesized by electrospinning. Uniform nanofibers with diameters of about 80 nm were formed of tiny octahedral particles wrapped together into 30 μm long fibers. The Li1.5MnTiO4+δ nanofibers exhibited an improved rate capability compared to both Li1.5MnTiO4+δ nanoparticles and bulk particles. The uniform one-dimensional nanostructure of the composite cathode exhibited enhanced capacities of 235 and 170 mAh g-1 at C/5 and 1 C rates, respectively. Its unique structure provided a large effective contact area for Li+ diffusion, and low charge transfer resistance. Moreover, the layered phase contributed to its capacity in over 3 V region, which increased specific energy (726 Wh kg-1) compared to the bulk particles (534 Wh kg-1).

| S-EPMC5374536 | biostudies-literature

Gyroid structured aqua-sheets with sub-nanometer thickness enabling 3D fast proton relay conduction.

Project description:A polymerizable amphiphile having two zwitterionic head-groups has been designed. This compound co-organizes with an acid, bis(trifluoromethanesulfonyl)imide (HTf2N), into a gyroid bicontinuous cubic liquid-crystalline phase. In situ polymerization of this phase has been successfully achieved by UV irradiation in the presence of a photoinitiator, yielding a self-standing gyroid-nanostructured polymer film. When the polymer film is placed under different relative humidity conditions or in water, it absorbs water owing to the strong hydration ability of the zwitterionic parts. It has been found that the polymer film preserves the gyroid nanostructure after the water absorption. Based on reconstructed electron density maps, it is assumed that the absorbed water molecules form a 3D continuous network along the gyroid minimal surface, which satisfies several key conditions for inducing fast proton conduction. As expected, such hydrated films show high ionic conductivities in the order of 10-1 S cm-1 when the water content of the film reaches 15.6 wt% at RH = 90%. The high conductivity is attributed to the induction of the Grotthuss mechanism, that is, proton conduction via the hydrogen-bonding network of the incorporated water molecules.

| S-EPMC6615241 | biostudies-literature

Characteristic fast H- ion conduction in oxygen-substituted lanthanum hydride.

Project description:Fast ionic conductors have considerable potential to enable technological development for energy storage and conversion. Hydride (H-) ions are a unique species because of their natural abundance, light mass, and large polarizability. Herein, we investigate characteristic H- conduction, i.e., fast ionic conduction controlled by a pre-exponential factor. Oxygen-doped LaH3 (LaH3-2xOx) has an optimum ionic conductivity of 2.6 × 10-2 S cm-1, which to the best of our knowledge is the highest H- conductivity reported to date at intermediate temperatures. With increasing oxygen content, the relatively high activation energy remains unchanged, whereas the pre-exponential factor decreases dramatically. This extraordinarily large pre-exponential factor is explained by introducing temperature-dependent enthalpy, derived from H- trapped by lanthanum ions bonded to oxygen ions. Consequently, light mass and large polarizability of H-, and the framework comprising densely packed H- in LaH3-2xOx are crucial factors that impose significant temperature dependence on the potential energy and implement characteristic fast H- conduction.

| S-EPMC6561957 | biostudies-literature

High rate capability caused by surface cubic spinels in Li-rich layer-structured cathodes for Li-ion batteries.

Project description:Modified Li-rich layered cathode Li(Li0.2Mn0.54Ni0.13Co0.13)O2 has been synthesized by a simple strategy of using surface treatment with various amounts (0-30 wt.%) of Super P (carbon black). Based on detailed characterizations from X-ray diffraction (XRD), high resolution transmission electron microscope (HRTEM), X-ray photoelectron spectroscopy (XPS) and electrochemical impedance spectroscopy (EIS), it is suggested that the phase transformation from Li2MnO3-type of structure to spinel-like phase take place at the surface regions of particles during post annealing process at 350 °C, leading to increase in both first coulombic efficiency and rate capability, from 78% and 100 mAh · g(-1) (charge capacity at 2500 mA · g(-1)) of the pristine material to 93.4% and 200 mAh · g(-1). The evidences of spinel formation and the reasons for electrochemical enhancement are systematically investigated.

| S-EPMC3813932 | biostudies-literature

Crystal Structure of Garnet-Related Li-Ion Conductor Li7-3x Ga x La3Zr2O12: Fast Li-Ion Conduction Caused by a Different Cubic Modification?

Project description:Li-oxide garnets such as Li7La3Zr2O12 (LLZO) are among the most promising candidates for solid-state electrolytes to be used in next-generation Li-ion batteries. The garnet-structured cubic modification of LLZO, showing space group Ia-3d, has to be stabilized with supervalent cations. LLZO stabilized with Ga3+ shows superior properties compared to LLZO stabilized with similar cations; however, the reason for this behavior is still unknown. In this study, a comprehensive structural characterization of Ga-stabilized LLZO is performed by means of single-crystal X-ray diffraction. Coarse-grained samples with crystal sizes of several hundred micrometers are obtained by solid-state reaction. Single-crystal X-ray diffraction results show that Li7-3x Ga x La3Zr2O12 with x > 0.07 crystallizes in the acentric cubic space group I-43d. This is the first definite record of this cubic modification for LLZO materials and might explain the superior electrochemical performance of Ga-stabilized LLZO compared to its Al-stabilized counterpart. The phase transition seems to be caused by the site preference of Ga3+. 7Li NMR spectroscopy indicates an additional Li-ion diffusion process for LLZO with space group I-43d compared to space group Ia-3d. Despite all efforts undertaken to reveal structure-property relationships for this class of materials, this study highlights the potential for new discoveries.

| S-EPMC4806310 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data