Enhanced NO₂ Sensing Performance of Graphene with Thermally Induced Defects.

ABSTRACT: This paper demonstrates the enhanced NO₂ sensing performance of graphene with defects generated by rapid thermal annealing (RTA). A high temperature of RTA (300-700 °C) was applied to graphene under an argon atmosphere to form defects on sp² carbon lattices. The density of defects proportionally increased with increasing the RTA temperature. Raman scattering results confirmed significant changes in sp² bonding. After 700 °C RTA, I_D/I_G, I_2D/I_G, and FWHM (full width at half maximum)(G) values, which are used to indirectly investigate carbon-carbon bonds' chemical and physical properties, were markedly changed compared to the pristine graphene. Further evidence of the thermally-induced defects on graphene was found via electrical resistance measurements. The electrical resistance of the RTA-treated graphene linearly increased with increasing RTA temperature. Meanwhile, the NO₂ response of graphene sensors increased from 0 to 500 °C and reached maximum (R = ~24%) at 500 °C. Then, the response rather decreased at 700 °C (R = ~14%). The results imply that rich defects formed at above a critical temperature (~500 °C) may damage electrical paths of sp² chains and thus deteriorate NO₂ response. Compared to the existing functionalization process, the RTA treatment is very facile and allows precise control of the NO₂ sensing characteristics, contributing to manufacturing commercial low-cost, high-performance, integrated sensors.

SUBMITTER: Lim N

PROVIDER: S-EPMC8124493 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Thermally reduced kaolin-graphene oxide nanocomposites for gas sensing.

Project description:Highly sensitive graphene-based gas sensors can be made using large-area single layer graphene, but the cost of large-area pure graphene is high, making the simpler reduced graphene oxide (rGO) an attractive alternative. To use rGO for gas sensing, however, require a high active surface area and slightly different approach is needed. Here, we report on a simple method to produce kaolin-graphene oxide (GO) nanocomposites and an application of this nanocomposite as a gas sensor. The nanocomposite was made by binding the GO flakes to kaolin with the help of 3-Aminopropyltriethoxysilane (APTES). The GO flakes in the nanocomposite were contacting neighboring GO flakes as observed by electron microscopy. After thermal annealing, the nanocomposite become conductive as showed by sheet resistance measurements. Based on the conductance changes of the nanocomposite films, electrical gas sensing devices were made for detecting NH3 and HNO3. These devices had a higher sensitivity than thermally annealed multilayer GO films. This kaolin-GO nanocomposite might be useful in applications that require a low-cost material with large conductive surface area including the demonstrated gas sensors.

| S-EPMC5378989 | biostudies-literature

Highly Thermally Conductive Adhesion Elastomer Enhanced by Vertically Aligned Folded Graphene.

Project description:Heat and stress transfer at an interface are crucial for the contact-based tactile sensing to measure the temperature, morphology, and modulus. However, fabricating a smart sensing material that combines high thermal conductivity, elasticity, and good adhesion is challenging. In this study, a composite is fabricated using a directional template of vertically aligned folded graphene (VAFG) and a copolymer matrix of poly-2-[[(butylamino)carbonyl]oxy]ethyl ester and polydimethylsiloxane, vinyl-end-terminated polydimethylsiloxane (poly(PBAx-ran-PDMS)). With optimized chemical cross-linking and supermolecular interactions, the poly(PBA-ran-PDMS)/VAFG exhibits high thermal conductivity (15.49 W m-1 K-1 ), an high elastic deformation, and an interfacial adhesion of up to 6500 N m-1 . Poly(PBA-ran-PDMS)/VAFG is highly sensitive to temperature and pressure and demonstrates a self-learning capacity for manipulator applications. The smart manipulator can distinguish and selectively capture unknown materials in the dark. Thermally conductive, elastic, and adhesive poly(PBA-ran-PDMS)/VAFG can be developed into core materials in intelligent soft robots.

| S-EPMC9685443 | biostudies-literature

Three-Dimensional MoS2/Reduced Graphene Oxide Nanosheets/Graphene Quantum Dots Hybrids for High-Performance Room-Temperature NO2 Gas Sensors.

Project description:This study presents three-dimensional (3D) MoS2/reduced graphene oxide (rGO)/graphene quantum dots (GQDs) hybrids with improved gas sensing performance for NO2 sensors. GQDs were introduced to prevent the agglomeration of nanosheets during mixing of rGO and MoS2. The resultant MoS2/rGO/GQDs hybrids exhibit a well-defined 3D nanostructure, with a firm connection among components. The prepared MoS2/rGO/GQDs-based sensor exhibits a response of 23.2% toward 50 ppm NO2 at room temperature. Furthermore, when exposed to NO2 gas with a concentration as low as 5 ppm, the prepared sensor retains a response of 15.2%. Compared with the MoS2/rGO nanocomposites, the addition of GQDs improves the sensitivity to 21.1% and 23.2% when the sensor is exposed to 30 and 50 ppm NO2 gas, respectively. Additionally, the MoS2/rGO/GQDs-based sensor exhibits outstanding repeatability and gas selectivity. When exposed to certain typical interference gases, the MoS2/rGO/GQDs-based sensor has over 10 times higher sensitivity toward NO2 than the other gases. This study indicates that MoS2/rGO/GQDs hybrids are potential candidates for the development of NO2 sensors with excellent gas sensitivity.

| S-EPMC8954772 | biostudies-literature

High-Performance UV-Assisted NO2 Sensor Based on Chemical Vapor Deposition Graphene at Room Temperature.

Project description:Nitrogen dioxide (NO2) is one of the most dangerous air pollutants that can affect human health even at the ppb (part per billion) level. Thus, the superior sensing performance of nitrogen dioxide gas sensors is an imperative for real-time environmental monitoring. Traditional solid-state sensors based on metal-oxide transistors have the drawbacks of high power consumption, high operating temperature, poor selectivity, and difficult integration with other electronics. In that respect, graphene-based gas sensors have been extensively studied as potential replacements. However, their advantages of high sensing efficiency, low power consumption, and simple electronic integration have been countered by their slow response and poor repeatability. Here, we report the fabrication of high-performance ultraviolet (UV)-assisted room temperature NO2 sensors based on chemical vapor deposition-grown graphene. UV irradiation improves the response of the sensor sevenfold with respect to the dark condition attaining 26% change in resistance at 100 ppm NO2 concentration with a practical detection limit below 1 ppm (42.18 ppb). In addition, the recovery time was shortened fivefold to a few minutes and the excellent repeatability. This work may provide a promising and practical method to mass produce room-temperature NO2 gas sensors for real-time environment monitoring due to its simple fabrication process, low cost, and practicality.

| S-EPMC6732984 | biostudies-literature

Graphene Wrapping of Electrospun Nanofibers for Enhanced Electrochemical Sensing.

Project description:This paper presents a scalable method of developing ultrasensitive electrochemical biosensors. This is achieved by maximizing sensor conductivity through graphene wrapping of carbonized electrospun nanofibers. The effectiveness of the graphene wrap was determined visually by scanning electron microscopy and chemically by Fourier transform infrared spectroscopy, Raman spectroscopy, and X-ray diffraction. The sensing performance of different electrode samples was electrochemically characterized using cyclic voltammetry and electrochemical impedance spectroscopy, with the graphene-wrapped carbonized nanofiber electrode showing significantly improved performance. The graphene-wrapped carbonized nanofibers exhibited a relative conductivity of ∼14 times and an electroactive surface area of ∼2 times greater compared to the bare screen-printed carbon electrode despite experiencing inhibitive effects from the carbon glue used to bind the samples to the electrode. The results indicate potential for a highly conductive, inert sensing platform.

| S-EPMC8153741 | biostudies-literature

Impact of Thermally Reducing Temperature on Graphene Oxide Thin Films and Microsupercapacitor Performance.

Project description:In this work, a thermally reduced graphene oxide (TRGO) thin film on microscopic glass was prepared using spray coating and atmospheric pressure chemical vapour deposition. The structure of TRGO was analysed using X-ray diffraction (XRD) spectroscopy, scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDS), Fourier transform infrared (FTIR) spectroscopy, and ultraviolet-visible spectroscopy (UV-Vis) suggesting a decrease in oxygen functional groups (OFGs), leading to the restacking, change in colour, and transparency of the graphene sheets. Raman spectrum deconvolution detailed the film's parameters, such as the crystallite size, degree of defect, degree of amorphousness, and type of defect. The electrochemical performance of the microsupercapacitor (µ-SC) showed a rectangular cyclic voltammetry shape, which was maintained at a high scan rate, revealing phenomenal electric double-layer capacitor (EDLC) behaviour. The power law and Trasatti's analysis indicated that low-temperature TRGO µ-SC is dominated by diffusion-controlled behaviour, while higher temperature TRGO µ-SC is dominated by surface-controlled behaviour.

| S-EPMC9268352 | biostudies-literature

Fe-Doped ZnO/Reduced Graphene Oxide Nanocomposite with Synergic Enhanced Gas Sensing Performance for the Effective Detection of Formaldehyde.

Project description:Here, we report the synthesis of Fe-doped ZnO/reduced graphene oxide (rGO) nanocomposites for gas sensing applications via a one-pot hydrothermal process. A wide range of characterization techniques were used to confirm the successful fabrication of the nanocomposite material and to determine the surface area, the structural and morphological properties, the chemical composition, and the purity of the samples, such as Brunauer-Emmett-Teller, X-ray diffraction, Fourier transform infrared, Raman spectroscopy, scanning electron microscopy, transmission electron microscopy, UV-vis spectroscopy, and X-ray photoelectron spectroscopy techniques. The gas sensing performance to formaldehyde was studied thoroughly in a temperature-controlled test chamber. Compared to that of the bare ZnO and ZnO/rGO nanocomposites, the as-prepared 5 atom % Fe-doped ZnO/rGO nanocomposites presented significantly enhanced gas sensing performance to formaldehyde at relatively low temperatures. Whereas most formaldehyde sensors operate at 150 °C and can detect as low as 100 ppm concentrations, the presented sensor can detect 5 ppm formaldehyde at 120 °C. Its fast response-recovery time, high stability, and high selectivity make it an ideal sensor; however, it can exhibit degenerative gas sensing performance at elevated relative humidity. The enhanced gas sensing mechanism was explained as the synergic effect of rGO and Fe doping. The results demonstrate that Fe doping and decorating the nanocomposite with rGO are promising approaches for achieving a superior gas sensing performance for the development of ZnO gas sensors for the detection of formaldehyde.

| S-EPMC6648138 | biostudies-literature

Enhanced Photoelectrochemical Performance of Cuprous Oxide/Graphene Nanohybrids.

Project description:Combination of an oxide semiconductor with a highly conductive nanocarbon framework (such as graphene or carbon nanotubes) is an attractive avenue to assemble efficient photoelectrodes for solar fuel generation. To fully exploit the possible synergies of the hybrid formation, however, precise knowledge of these systems is required to allow rational design and morphological engineering. In this paper, we present the controlled electrochemical deposition of nanocrystalline p-Cu2O on the surface of different graphene substrates. The developed synthetic protocol allowed tuning of the morphological features of the hybrids as deduced from electron microscopy. (Photo)electrochemical measurements (including photovoltammetry, electrochemical impedance spectroscopy, photocurrent transient analysis) demonstrated better performance for the 2D graphene containing photoelectrodes, compared to the bare Cu2O films, the enhanced performance being rooted in suppressed charge carrier recombination. To elucidate the precise role of graphene, comparative studies were performed with carbon nanotube (CNT) films and 3D graphene foams. These studies revealed, after allowing for the effect of increased surface area, that the 3D graphene substrate outperformed the other two nanocarbons. Its interconnected structure facilitated effective charge separation and transport, leading to better harvesting of the generated photoelectrons. These hybrid assemblies are shown to be potentially attractive candidates in photoelectrochemical energy conversion schemes, namely CO2 reduction.

| S-EPMC5456415 | biostudies-literature

Ultrathin Functional Polymer Modified Graphene for Enhanced Enzymatic Electrochemical Sensing.

Project description:Grafting thin polymer layers on graphene enables coupling target biomolecules to graphene surfaces, especially through amide and aldehyde linkages with carboxylic acid and primary amine derivatives, respectively. However, functionalizing monolayer graphene with thin polymer layers without affecting their exceptional electrical properties remains challenging. Herein, we demonstrate the controlled modification of chemical vapor deposition (CVD) grown single layer graphene with ultrathin polymer 1,5-diaminonaphthalene (DAN) layers using the electropolymerization technique. It is observed that the controlled electropolymerization of DAN monomer offers continuous polymer layers with thickness ranging between 5?25 nm. The surface characteristics of pure and polymer modified graphene was examined. As anticipated, the number of surface amine groups increases with increases in the layer thickness. The effects of polymer thickness on the electron transfer rates were studied in detail and a simple route for the estimation of surface coverage of amine groups was demonstrated using the electrochemical analysis. The implications of grafting ultrathin polymer layers on graphene towards horseradish peroxidase (HRP) enzyme immobilization and enzymatic electrochemical sensing of H?O? were discussed elaborately.

| S-EPMC6468408 | biostudies-literature

Nitrogen-doped graphene: beyond single substitution and enhanced molecular sensing.

Project description:Graphene is a two-dimensional network in which sp(2)-hybridized carbon atoms are arranged in two different triangular sub-lattices (A and B). By incorporating nitrogen atoms into graphene, its physico-chemical properties could be significantly altered depending on the doping configuration within the sub-lattices. Here, we describe the synthesis of large-area, highly-crystalline monolayer N-doped graphene (NG) sheets via atmospheric-pressure chemical vapor deposition, yielding a unique N-doping site composed of two quasi-adjacent substitutional nitrogen atoms within the same graphene sub-lattice (N(2)(AA)). Scanning tunneling microscopy and spectroscopy (STM and STS) of NG revealed the presence of localized states in the conduction band induced by N(2)(AA)-doping, which was confirmed by ab initio calculations. Furthermore, we demonstrated for the first time that NG could be used to efficiently probe organic molecules via a highly improved graphene enhanced Raman scattering.

| S-EPMC3421434 | biostudies-literature