Humidity Effects on Domain Structure and Polarization Switching of Pb(Zn_1/3Nb_2/3)O₃-x%PbTiO₃ (PZN-x%PT) Single Crystals.

ABSTRACT: The effect of relative humidity on the domain structure imaging and polarization switching process of Pb(Zn_1/3Nb_2/3)O₃-x%PbTiO₃ (PZN-x%PT) ferroelectric single crystals has been investigated by means of the piezoresponse force microscopy (PFM) and piezoresponse force spectroscopy (PFS) techniques. It was found that the PFM amplitude increases with the relative humidity, and that the ferroelectric hysteresis loops at different relative humidity levels show that the coercive bias decreases with the increase in relative humidity. These observed phenomena are attributed to the existence of the water layer between the probe tip and the sample surface in a humid atmosphere, which could affect the effect of the electric field distribution and screening properties at the ferroelectric sample surface. These results provide a better understanding of the water adsorption phenomena at the nanoscale in regard to the fundamental understanding of ferroelectrics' properties.

SUBMITTER: Wang H

PROVIDER: S-EPMC8125925 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Influence of Domain Size on the Scaling Effects in Pb(Mg1/3Nb2/3)O3-PbTiO3 Ferroelectric Crystals.

Project description:The property degradation observed in thin Pb(Mg(1/3)Nb(2/3))O(3)-PbTiO(3) (PMN-PT) crystals is believed to relate to large domains and subsequent clamping induced by surface-boundary. In this work, the properties were investigated as function of domain size, using controlled poling. The degraded piezoelectric and dielectric properties of thin PMN-PT were found to increase significantly, by decreasing domain size. Furthermore, the fine domain structure was found to be stable at 3kV/cm after 7.0×10(5) negative-pulse cycles, hence, enabling PMN-PT crystals for high-frequency (>20 MHz) ultrasound-transducers.

| S-EPMC3086291 | biostudies-literature

Bipolar loop-like non-volatile strain in the (001)-oriented Pb(Mg1/3Nb2/3)O3-PbTiO3 single crystals.

Project description:Strain has been widely used to manipulate the properties of various kinds of materials, such as ferroelectrics, semiconductors, superconductors, magnetic materials, and "strain engineering" has become a very active field. For strain-based information storage, the non-volatile strain is very useful and highly desired. However, in most cases, the strain induced by converse piezoelectric effect is volatile. In this work, we report a non-volatile strain in the (001)-oriented Pb(Mg1/3Nb2/3)O3-PbTiO3 single crystals and demonstrate an approach to measure the non-volatile strain. A bipolar loop-like S-E curve is revealed and a mechanism involving 109° ferroelastic domain switching is proposed. The non-volatile high and low strain states should be significant for applications in information storage.

| S-EPMC3975321 | biostudies-literature

Complete set of elastic, dielectric, and piezoelectric constants of [011]C poled rhombohedral Pb(In0.5Nb0.5)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3:Mn single crystals.

Project description:Mn modified rhombohedral Pb(In0.5Nb0.5)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 (PIN-PMN-PT:Mn) single crystals poled along [011]C crystallographic direction exhibit a "2R" engineered domain configuration, with macroscopic mm2 symmetry. The complete sets of material constants were determined using combined resonance and ultrasonic methods, and compared to [001]C poled PIN-PMN-PT:Mn crystals. The thickness shear piezoelectric coefficient d15 and electromechanical coupling factor k15 were found to be on the order of ∼3000 pC/N and 0.92, respectively, with longitudinal piezoelectric coefficient d33 and coupling factor k33 being on the order of ∼1050 pC/N and 0.90. Of particular importance is that PIN-PMN-PT:Mn single crystals exhibited high mechanical quality factor Q33 ∼ 1000, comparable to "hard" PZT8 ceramics, which can also be confirmed by the low extrinsic contribution, being ≤2% from the Rayleigh analysis.

| S-EPMC3592883 | biostudies-other

Hydrostatic piezoelectric properties of [011] poled Pb(Mg1/3Nb2/3)O3-PbTiO3 single crystals and 2-2 lamellar composites.

Project description:The hydrostatic piezoelectric properties of [011] poled Pb(Mg1/3Nb2/3)O3-PbTiO3 (PMN-PT) crystals and corresponding 2-2 crystal/epoxy composites were investigated. The crystal volume ratio and compositional dependencies of the hydrostatic charge and voltage coefficients (dh and gh ) and hydrostatic figure of merit (FOM) dh × gh were determined, where large FOM value of 3.2 pm(2)/N with high stability as a function of hydrostatic pressure was achieved for rhombohedral crystal composites. In addition, the stress amplification effects of the face-plate and different epoxy matrixes were investigated, with maximum FOM value being on the order of 92 pm(2)/N, indicating that 2-2 crystal/epoxy composites are promising materials for hydrostatic applications.

| S-EPMC3977785 | biostudies-other

Temperature-Induced Phase Transition Characteristics of [001]-Oriented 0.93Pb(Zn1/3Nb2/3)O3-0.07PbTiO3 (PZN-7%PT) Single Crystal by Using Piezoresponse Force Microscopy.

Project description:The evolution of the domain structures of [001]-oriented relaxor ferroelectric 0.93PbZn1/3Nb2/3O3-0.07PbTiO3 (PZN-7%PT) single crystals as a function of temperature was investigated in situ by using piezoresponse force microscopy (PFM). It was found that the local domain structure of PZN-7%PT single crystals at room temperature is rhombohedral with nanoscale twins. Temperature-dependent domain structures showed that the phase transition process is a collective process and that the sample underwent a sequence of rhombohedral (R) → monoclinic (Mc) → tetragonal (T) → cubic (C) phase transformations when the temperature increased from 25 °C to 170 °C. The results provide direct observation of the phase transition evolution of PZN-7%PT single crystals as a function of temperature, which is of great significance to fully understand the relationships between the domain structure and phase structure of PZN-7%PT single crystals.

| S-EPMC7916775 | biostudies-literature

Electric field manipulation of magnetic and transport properties in SrRuO3/Pb(Mg1/3Nb2/3)O3-PbTiO3 heterostructure.

Project description:The electric field manipulation of magnetic properties is currently of great interest for the opportunities provided in low-energy-consuming spintronics devices. Here, we report the effect of electric field on magnetic and transport properties of the ferromagnetic SrRuO(3) film which is epitaxially grown on Pb(Mg(1/3)Nb(2/3))O3-PbTiO(3) ferroelectric substrate. With the application of electric field on the substrate, the magnetization, Curie temperature and resistivity of SrRuO(3) are effectively modified. The mechanism of the electric field manipulation of these properties is ascribed to the rotations of RuO6 oxygen octahedra caused by the electric-field-induced strain, which changes the overlap and hybridization between the Ru 4d orbitals and O 2p orbitals, resulting in the modification of the magnetic and electronic properties.

| S-EPMC4227015 | biostudies-other

Switching Characteristics and High-Temperature Dielectric Relaxation Behaviours of Pb(Zn1/3Nb2/3)0.91Ti0.09O₃ Single Crystal.

Project description:This work evaluated the resistance switching characteristics in the (100)-oriented Pb(Zn1/3Nb2/3)0.91Ti0.09O₃ (PZNT) single crystal. The current hysteresis can be closely related to the ferroelectric polarization and we provided a possible explanation using a model about oxygen vacancies to analyze the mechanism of switching. The obvious frequency dispersion of the relative permittivity signified the relaxer-type behavior of the sample. The value of the relaxation parameter γ = 1.48 was estimated from the linear fit of the modified Curie-Weiss law, indicating the relaxer nature. High-temperature dielectric relaxation behaviors were revealed in the temperature region of 400-650 °C. In addition, under the measuring frequency of 10 kHz, εr was tunable by changing the electric field and the largest tunability of εr reached 14.78%. At room temperature, the high pyroelectric coefficient and detectivity figure of merit were reported.

| S-EPMC5506977 | biostudies-other

Pb(Mg1/3Nb2/3)-PbTiO3-Based Ultrasonic Transducer for Detecting Infiltrated Water in Pressurized Water Reactor Fuel Rods.

Project description:In this study, a high-sensitivity Pb( Mg 1 / 3 Nb 2 / 3 ) O 3 - PbTiO 3 (PMN-PT)-based ultrasonic transducer was developed for detecting defective pressurized water reactor (PWR) fuel rods. To apply the PMN-PT substance to nuclear power plant facilities, given the need to guarantee their robustness against radioactive materials, the effects of neutron irradiation on PMN-PT were investigated. As a result, the major piezo-electric constants of PMN-PT, such as the electrical impedance, dielectric constant, and piezo-electric charge constant, were found to vary within acceptable ranges. This means that the PMN-PT could be used as the piezo-electric material in the ultrasonic transducer for nuclear power plants. The newly developed ultrasonic transducer was simulated using a modified KLM model for the through-transmission method and fabricated under the same conditions as in the simulation. The through-transmitted waveforms of normal and defective PWR fuel rods were obtained and compared with simulated results in the time and frequency domains. The response waveforms of the newly developed ultrasonic transducer for pressurized water reactor (PWR) fuel rods showed good agreement with the simulation outcome and could clearly detect defective specimens with high sensitivity.

| S-EPMC6630703 | biostudies-literature

Linear electro-optic properties of relaxor-based ferroelectric 0.24Pb(In1/2Nb1/2)O3-(0.76 - x)Pb(Mg1/3Nb2/3)O3-xPbTiO3 single crystals.

Project description:Linear electro-optic properties of 0.24Pb(In1/2Nb1/2)O3-(0.76 - x)Pb(Mg1/3Nb2/3)O3-xPbTiO3 single crystals, with compositions in the rhombohedral, morphotropic phase boundary (MPB) and tetragonal phases, have been investigated. Very large effective electro-optic coefficient [Formula: see text] (204 pm/V) was observed in a crystal with the MPB composition when it is poled along [001]. The rhombohedral phase (x = 0.27 and 0.30) single crystals poled along [111] direction and tetragonal phase (x = 0.39) single crystal poled along [001] direction are in single domain, and their electro-optic coefficients ([Formula: see text] = 76, 94, and 43 pm/V for the crystals with x = 0.27, 0.30, and 0.39, respectively) were found to be much higher than that of traditional electro-optic single crystal LiNbO3 ([Formula: see text] = 19.9 pm/V). The electro-optic coefficients of the single crystal in the rhombohedral phase have excellent temperature stability in the experimental temperature range of 10-40 °C. The half-wave voltage [Formula: see text] was calculated to be much lower (less than 1000 V) than that of LiNbO3 single crystal (2800 V). These superior properties make the ternary relaxor-PT single crystals very promising for electro-optic modulation applications.

| S-EPMC3724701 | biostudies-other

Study on dielectric and piezoelectric properties of 0.7 Pb(Mg1/3Nb2/3)O3-0.3 PbTiO3 single crystal with nano-patterned composite electrode.

Project description:Effect of nano-patterned composite electrode and backswitching poling technique on dielectric and piezoelectric properties of 0.7 Pb(Mg1/3Nb2/3)O3-0.3 PbTiO3 was studied in this paper. Composite electrode consists of Mn nano-patterns with pitch size of 200 nm, and a blanket layer of Ti/Au was fabricated using a nanolithography based lift-off process, heat treatment, and metal film sputtering. Composite electrode and backswitching poling resulted in 27% increase of d33 and 25% increase of dielectric constant, and we believe that this is attributed to regularly defined nano-domains and irreversible rhombohedral to monoclinic phase transition in crystal. The results indicate that nano-patterned composite electrode and backswitching poling has a great potential in domain engineering of relaxor single crystals for advanced devices.

| S-EPMC3790807 | biostudies-other