The impact of surface treatment in 3-dimensional printed implants for early osseointegration: a comparison study of three different surfaces.

ABSTRACT: 3D printing technology has been gradually applied to various areas. In the present study, 3D-printed implants were fabricated with direct metal laser sintering technique for a dental single root with titanium. The 3D implants were allocated into following groups: not treated (3D-None), sandblasted with a large grit and acid-etched (3D-SLA), and target-ion-induced plasma-sputtered surface (3D-TIPS). Two holes were drilled in each tibia of rabbit, and the three groups of implants were randomly placed with a mallet. Rabbits were sacrificed at two, four, and twelve weeks after the surgery. Histologic and histomorphometric analyses were performed for the evaluation of mineralized bone-to-implant contact (mBIC), osteoid-to-implant contact (OIC), total bone-to-implant contact (tBIC), mineralized bone area fraction occupancy (mBAFO), osteoid area fraction occupancy (OAFO), and total bone area fraction occupancy (tBAFO) in the inner and outer areas of lattice structure. At two weeks, 3D-TIPS showed significantly higher inner and outer tBIC and inner tBAFO compared with other groups. At four weeks, 3D-TIPS showed significantly higher outer OIC than 3D-SLA, but there were no significant differences in other variables. At twelve weeks, there were no significant differences. The surface treatment with TIPS in 3D-printed implants could enhance the osseointegration process in the rabbit tibia model, meaning that earlier osseointegration could be achieved.

SUBMITTER: Lee J

PROVIDER: S-EPMC8129142 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Effects of local application of the ankaferd blood stopper on osseointegration in three different surface titanium implants.

Project description:ObjectiveResearchs of the effects of ankaferd blood stopper (ABS) on bone healing metabolism have revealed that it affects bone regeneration positively. The exact mechanism by which this positive effect on bone tissue metabolism is not known. The aim of this study is to biomechanic and biochemical analysis of the effects of the local ABS application on osseointegration of 3 different surfaced titanium implants.Material & methodsSpraque dawley rats were divided machined surfaced (MS) (n = 10), sandblasted and large acid grid (SLA) (n = 10) and resorbable blast material (RBM) (n = 10) surfaced implants. ABS applied locally during the surgical application of the titanium implant before insertion in bone sockets. After 4 weeks experimental period the rats sacrificed and implants with surrounding bone tissues were removed to reverse torque analysis (Newton), blood samples collected to biochemical analysis (ALP, calcium, P).ResultsBiomechanic bone implant contact ratio detected higher in SLA surfaced implants compared with the RBM and controls (P < 0,05). Phosphor levels detected lower in RBM implant group compared with the controls and SLA (P < 0,05). Additionally; phosphor levels detected highly in controls compared with the RBM implants.ConclusionAccording the biomechanical parameters ABS may be more effective in SLA and RBM surfaced implants when locally applied.

| S-EPMC8327665 | biostudies-literature

Effectiveness of Antibacterial Surfaces in Osseointegration of Titanium Dental Implants: A Systematic Review.

Project description:Titanium (Ti) dental implant failure as a result of infection has been established at 40%, being regarded as one of the most habitual and untreatable problems. Current research is focused on the design of new surfaces that can generate long-lasting, infection-free osseointegration. The purpose of our study was to assess studies on Ti implants coated with different antibacterial surfaces, assessing their osseointegration. The PubMed, Web of Science and Scopus databases were electronically searched for in vivo studies up to December 2020, selecting six studies that met the inclusion criteria. The quality of the selected studies was assessed using the ARRIVE (Animal Research: Reporting of In Vivo Experiments) criteria and Systematic Review Center for Laboratory animal Experimentation's (SYRCLE's) risk of bias tool. Although all the included studies, proved greater osseointegration capacity of the different antibacterial surfaces studied, the methodological quality and experimental models used in some of them make it difficult to draw predictable conclusions. Because of the foregoing, we recommend caution when interpreting the results obtained.

| S-EPMC8066819 | biostudies-literature

The osseointegration and stability of dental implants with different surface treatments in animal models: a network meta-analysis.

Project description:Dental implants are commonly used to repair missing teeth. The implant surface plays a critical role in promoting osseointegration and implant success. However, little information is available about which implant surface treatment technology best promotes osseointegration and implant stability. The aim of this network meta-analysis was to evaluate the osseointegration and stability of four commonly used dental implants (SLA, SLActive, TiUnite, and Osseotite). The protocol of the current meta-analysis is registered in PROSPERO (International Prospective Register of Systematic Reviews) under the code CRD42020190907 ( https://www.crd.york.ac.uk ). We conducted a systematic review following PRISMA and Cochrane Recommendations. Medline (PubMed), Cochrane Library, Embase, and the Web of Science databases were searched. Only randomized controlled trials were considered. Twelve studies were included in the current network meta-analysis, eleven studies were included concerning the osseointegration effect and five studies were included for stability analysis (four studies were used to assess both stability and osseointegration). Rank possibility shows that the SLActive surface best promoted bone formation at an early healing stage and TiUnite seemed to be the best surface for overall osseointegration. For stability, TiUnite seemed to be the best surface. The present network meta-analysis showed that the SLActive surface has the potential to promote osseointegration at an early stage. The TiUnite surface had the best effect on osseointegration regarding the overall healing period. The TiUnite surface also had the best effect in stability.

| S-EPMC8257659 | biostudies-literature

Sustained Release of VEGF to Promote Angiogenesis and Osteointegration of Three-Dimensional Printed Biomimetic Titanium Alloy Implants.

Project description:Tumor resection and treatment of trauma-related regional large bone defects have major challenges in the field of orthopedics. Scaffolds that treat bone defects are the focus of bone tissue engineering. 3D printing porous titanium alloy scaffolds, prepared via electron beam melting technology, possess customized structure and strength. The addition of a growth factor coating to the scaffold introduces a specific form of biological activation. Vascular endothelial growth factor (VEGF) is key to angiogenesis and osteogenesis in vivo. We designed a porous titanium alloy scaffold/thermosensitive collagen hydrogel system, equipped with VEGF, to promote local osseointegration and angiogenesis. We also verified the VEGF release via thermosensitive collagen and proliferation and induction of the human umbilical vein endothelial cells (HUVECs) via the composite system in vitro. In vivo, using microscopic computed tomography (Micro-CT), histology, and immunohistochemistry analysis, we confirmed that the composite scaffold aids in angiogenesis-mediated bone regeneration, and promotes significantly more bone integration. We also discovered that the composite scaffold has excellent biocompatibility, provides bioactive VEGF for angiogenesis and osteointegration, and provides an important theoretical basis for the restoration of local blood supply and strengthening of bone integration.

| S-EPMC8634467 | biostudies-literature

Three-dimensional-printed individualized porous implants: A new "implant-bone" interface fusion concept for large bone defect treatment.

Project description:Bone defect repairs are based on bone graft fusion or replacement. Current large bone defect treatments are inadequate and lack of reliable technology. Therefore, we aimed to investigate a simple technique using three-dimensional (3D)-printed individualized porous implants without any bone grafts, osteoinductive agents, or surface biofunctionalization to treat large bone defects, and systematically study its long-term therapeutic effects and osseointegration characteristics. Twenty-six patients with large bone defects caused by tumor, infection, or trauma received treatment with individualized porous implants; among them, three typical cases underwent a detailed study. Additionally, a large segmental femur defect sheep model was used to study the osseointegration characteristics. Immediate and long-term biomechanical stability was achieved, and the animal study revealed that the bone grew into the pores with gradual remodeling, resulting in a long-term mechanically stable implant-bone complex. Advantages of 3D-printed microporous implants for the repair of bone defects included 1) that the stabilization devices were immediately designed and constructed to achieve early postoperative mobility, and 2) that osseointegration between the host bone and implants was achieved without bone grafting. Our osseointegration method, in which the "implant-bone" interface fusion concept was used instead of "bone-bone" fusion, subverts the traditional idea of osseointegration.

| S-EPMC8056181 | biostudies-literature

Affordable Three-Dimensional Printed Heart Models.

Project description:This is a 7-years single institution study on low-cost cardiac three-dimensional (3D) printing based on the use of free open-source programs and affordable printers and materials. The process of 3D printing is based on several steps (image acquisition, segmentation, mesh optimization, slicing, and three-dimensional printing). The necessary technology and the processes to set up an affordable three-dimensional printing laboratory are hereby described in detail. Their impact on surgical and interventional planning, medical training, communication with patients and relatives, patients' perception on care, and new cardiac device development was analyzed. A total of 138 low-cost heart models were designed and printed from 2013 to 2020. All of them were from different congenital heart disease patients. The average time for segmentation and design of the hearts was 136 min; the average time for printing and cleaning the models was 13.5 h. The average production cost of the models was €85.7 per model. This is the most extensive series of 3D printed cardiac models published to date. In this study, the possibility of manufacturing three-dimensional printed heart models in a low-cost facility fulfilling the highest requirements from a technical and clinical point of view is demonstrated.

| S-EPMC8211988 | biostudies-literature

Three-Dimensional Krawtchouk Descriptors for Protein Local Surface Shape Comparison.

Project description:Direct comparison of three-dimensional (3D) objects is computationally expensive due to the need for translation, rotation, and scaling of the objects to evaluate their similarity. In applications of 3D object comparison, often identifying specific local regions of objects is of particular interest. We have recently developed a set of 2D moment invariants based on discrete orthogonal Krawtchouk polynomials for comparison of local image patches. In this work, we extend them to 3D and construct 3D Krawtchouk descriptors (3DKDs) that are invariant under translation, rotation, and scaling. The new descriptors have the ability to extract local features of a 3D surface from any region-of-interest. This property enables comparison of two arbitrary local surface regions from different 3D objects. We present the new formulation of 3DKDs and apply it to the local shape comparison of protein surfaces in order to predict ligand molecules that bind to query proteins.

| S-EPMC7009784 | biostudies-literature

Fabrication of malleable three-dimensional-printed customized bolus using three-dimensional scanner.

Project description:A three-dimensional (3D)-printed customized bolus (3D bolus) can be used for radiotherapy application to irregular surfaces. However, bolus fabrication based on computed tomography (CT) scans is complicated and also delivers unwanted irradiation. Consequently, we fabricated a bolus using a 3D scanner and evaluated its efficacy. The head of an Alderson Rando phantom was scanned with a 3D scanner. The 3D surface data were exported and reconstructed with Geomagic Design X software. A 3D bolus of 5-mm thickness designed to fit onto the nose was printed with the use of rubber-like printing material, and a radiotherapy plan was developed. We successfully fabricated the customized 3D bolus, and further, a CT simulation indicated an acceptable fit of the 3D bolus to the nose. There was no air gap between the bolus and the phantom surface. The percent depth dose (PDD) curve of the phantom with the 3D bolus showed an enhanced surface dose when compared with that of the phantom without the bolus. The PDD of the 3D bolus was comparable with that of a commercial superflab bolus. The radiotherapy plan considering the 3D bolus showed improved target coverage when compared with that without the bolus. Thus, we successfully fabricated a customized 3D bolus for an irregular surface using a 3D scanner instead of a CT scanner.

| S-EPMC5426771 | biostudies-literature

Direct comparison of additively manufactured porous titanium and tantalum implants towards in vivo osseointegration.

Project description:Material properties of implants such as volume porosity and nanoscale surface modification have been shown to enhance cell-material interactions in vitro and osseointegration in vivo. Porous tantalum (Ta) and titanium (Ti) coatings are widely used for non-cemented implants, which are fabricated using different processing routes. In recent years, some of those implants are being manufactured using additive manufacturing. However, limited knowledge is available on direct comparison of additively manufactured porous Ta and Ti structures towards early stage osseointegration. In this study, we have fabricated porous Ta and Ti6Al4V (Ti64) implants using laser engineered net shaping (LENS™) with similar volume fraction porosity to compare the influence of surface characteristics and material chemistry on in vivo response using a rat distal femur model for 5 and 12 weeks. We have also assessed whether surface modification on Ti64 can elicit similar in vivo response as porous Ta in a rat distal femur model for 5 and 12 weeks. The harvested implants were histologically analyzed for osteoid surface per bone surface. Field emission scanning electron microscopy (FESEM) was done to assess the bone-implant interface. The results presented here indicate comparable performance of porous Ta and surface modified porous Ti64 implants towards early stage osseointegration at 5 weeks post implantation through seamless bone-material interlocking. However, a continued and extended efficacy of porous Ta is found in terms of higher osteoid formation at 12 weeks post-surgery.

| S-EPMC6690615 | biostudies-literature

Osterix enhances BMSC-associated osseointegration of implants.

Project description:Cellular and molecular events in osseointegration at the dental implant surface remain largely unknown. We hypothesized that bone marrow stromal cells (BMSCs) participate in this process, and that osterix (Osx) promotes implant osseointegration. To prove this hypothesis, we tracked double-labeled BMSCs in implantation sites created in nude mice transplanted with these cells. We also inserted implants into the femurs of our established transgenic mice after local administration of viruses encoding Osx, to determine the osteogenic effects of Osx. Immunohistochemical results demonstrated that BMSCs can recruit from peripheral circulation and participate in wound healing and osseointegration after implantation. Microcomputed tomography (microCT) analysis revealed an increased bone density at the bone-to-implant interface in the Osx group, and histomorphometric analysis indicated an elevated level of bone-to-implant contact in the Osx group. We concluded that exogenous BMSCs participate in the osseointegration after implantation, and that Osx overexpression accelerates osseointegration.

| S-EPMC2831612 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data