Cellulose Nanocrystals as Template for Improving the Crystallinity of Two-Dimensional Covalent Organic Framework Films.

ABSTRACT: Despite the rapid development of two-dimensional covalent organic frameworks (2D COFs) in recent years, it remains a great challenge to synthesize highly crystalline COF materials. Here, a CNC-assisted approach was adopted to synthesize high crystallinity COF materials. A series of 2D COF films were synthesized at the air-water interface by using cellulose nanocrystals (CNCs) as the template. The occurrence of Schiff reactions based on the imine bond was demonstrated by Raman spectroscopy and Fourier transform infrared spectroscopy (FTIR). Scanning electron microscopy (SEM) exhibited the appearances of 2D COF films were flower-like. When CNCs were added to a certain extent, the size of a single petal in the flowers gradually increased with the amount of CNCs. The film with large petals was characterized by Ultraviolet-Visible diffuse reflectance spectroscopy (UV-Vis DRS), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and selected area electron diffraction (SAED). In UV-Vis DRS curves, the S-band of COF-366 film was red-shifted by 24 nm compared with that of 5,10,15,20-tetrakis(4-aminophenyl)-21H,23H-porphyrin (TAPP), confirming the existence of extended conjugation in COF-366 film. XPS was used to identify the surface composition of the sample. The N1s signal of the film indicated that each TAPP formed four imine bonds with 2,5-dihydroxyterephthalaldehyde (DHTA) in COF-366 film. TEM images showed that CNCs had an influence on the crystal size. It was observed from SAED that the crystallinity of the film with CNCs was higher than the film without CNCs. This work provided a new template for improving the crystallinity of 2D COF films.

SUBMITTER: Li Y

PROVIDER: S-EPMC8152767 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Oriented thin films of a benzodithiophene covalent organic framework.

Project description:A mesoporous electron-donor covalent organic framework based on a benzodithiophene core, BDT-COF, was obtained through condensation of a benzodithiophene-containing diboronic acid and hexahydroxytriphenylene (HHTP). BDT-COF is a highly porous, crystalline, and thermally stable material, which can be handled in air. Highly porous, crystalline oriented thin BDT-COF films were synthesized from solution on different polycrystalline surfaces, indicating the generality of the synthetic strategy. The favorable orientation, crystallinity, porosity, and the growth mode of the thin BDT-COF films were studied by means of X-ray diffraction (XRD), 2D grazing incidence diffraction (GID), transmission and scanning electron microscopy (TEM, SEM), and krypton sorption. The highly porous thin BDT-COF films were infiltrated with soluble fullerene derivatives, such as [6,6]-phenyl C61 butyric acid methyl ester (PCBM), to obtain an interpenetrated electron-donor/acceptor host-guest system. Light-induced charge transfer from the BDT-framework to PCBM acceptor molecules was indicated by efficient photoluminescence quenching. Moreover, we monitored the dynamics of photogenerated hole-polarons via transient absorption spectroscopy. This work represents a combined study of the structural and optical properties of highly oriented mesoporous thin COF films serving as host for the generation of periodic interpenetrated electron-donor and electron-acceptor systems.

| S-EPMC4762543 | biostudies-literature

Electrical conductivity in a non-covalent two-dimensional porous organic material with high crystallinity.

Project description:Electroactive macrocycle building blocks are a promising route to new types of functional two-dimensional porous organic frameworks. Our strategy uses conjugated macrocycles that organize into two dimensional porous sheets via non-covalent van der Waals interactions, to make ultrathin films that are just one molecule thick. In bulk, these two-dimensional (2D) sheets stack into a three-dimensional van der Waals crystal, where relatively weak alkyl-alkyl interactions constitute the interface between these sheets. With the liquid-phase exfoliation, we are able to obtain films as thin as two molecular layers. Further using a combination of liquid-phase and mechanical exfoliation, we are able to create non-covalent sheets over a large area (>100 μm2). The ultrathin porous films maintain the single crystal packing from the macrocyclic structure and are electrically conductive. We demonstrate that this new type of 2D non-covalent porous organic framework can be used as the active layer in a field effect transistor device with graphene source and drain contacts along with hexagonal boron nitride as the gate dielectric interface.

| S-EPMC8179372 | biostudies-literature

A Novel One-Dimensional Porphyrin-Based Covalent Organic Framework.

Project description:A novel one-dimensional covalent organic framework (COF-K) was firstly designed and synthesized through a Schiff-based reaction from a porphyrin building block and a nonlinear right-angle building block. The COF-K exhibited high BET surface area and narrow pore size of 1.25 nm and gave a CO2 adsorption capacity of 89 mg g-1 at 273K and 1bar.

| S-EPMC6767199 | biostudies-literature

A self-standing three-dimensional covalent organic framework film.

Project description:Covalent crystals such as diamonds are a class of fascinating materials that are challenging to fabricate in the form of thin films. This is because spatial kinetic control of bond formation is required to create covalently bonded crystal films. Directional crystal growth is commonly achieved by chemical vapor deposition, an approach that is hampered by technical complexity and associated high cost. Here we report on a liquid-liquid interfacial approach based on physical-organic considerations to synthesize an ultrathin covalent crystal film. By distributing reactants into separate phases using hydrophobicity, the chemical reaction is confined to an interface that orients the crystal growth. A molecular-smooth interface combined with in-plane isotropic conditions enables the synthesis of films on a centimeter size scale with a uniform thickness of 13 nm. The film exhibits considerable mechanical robustness enabling a free-standing length of 37 µm, as well as a clearly anisotropic chemical structure and crystal lattice alignment.

| S-EPMC9839775 | biostudies-literature

Layered 3D Covalent Organic Framework Films Based on Carbon-Carbon Bonds.

Project description:The development of covalent organic frameworks (COFs) during the past decades has led to a variety of promising applications within gas storage, catalysis, drug delivery, and sensing. Even though most described synthesis methods result in powdery COFs with uncontrolled grain size, several approaches to grow COF films have recently been explored. However, in all COFs so far presented, the isolated materials are chemically homogeneous, with all functionalities homogeneously distributed throughout the entire material. Strategies to synthetically manipulate the spatial distribution of functionalities in a single film would be game changing. Specifically, this would allow for the introduction of local functionalities and even consecutive functions in single frameworks, thus broadening their synthetic versatility and application potential. Here, we synthesize two 3D crystalline COF films. The frameworks, the ionic B-based and neutral C-based COFs, have similar unit cell parameters, which enables their epitaxial stacking in a layered 3D COF film. The film growth was monitored in real time using a quartz crystal microbalance, showing linear growth with respect to reaction time. The high degree of polymerization was confirmed by chemical analysis and vibrational spectroscopy. Their polycrystalline and anisotropic natures were confirmed with grazing incidence X-ray diffraction. We further expand the scope of the concept by making layered films from COF-300 and its iodinated derivative. Finally, the work presented here will pave the path for multifunctional COF films where concurrent functionalities are embedded in the same crystalline material.

| S-EPMC10450803 | biostudies-literature

Single crystal of a one-dimensional metallo-covalent organic framework.

Project description:Although polymers have been studied for well over a century, there are few examples of covalently linked polymer crystals synthesised directly from solution. One-dimensional (1D) covalent polymers that are packed into a framework structure can be viewed as a 1D covalent organic framework (COF), but making a single crystal of this has been elusive. Herein, by combining labile metal coordination and dynamic covalent chemistry, we discover a strategy to synthesise single-crystal metallo-COFs under solvothermal conditions. The single-crystal structure is rigorously solved using single-crystal electron diffraction technique. The non-centrosymmetric metallo-COF allows second harmonic generation. Due to the presence of syntactic pendant amine groups along the polymer chains, the metallopolymer crystal can be further cross-linked into a crystalline woven network.

| S-EPMC7080745 | biostudies-literature

Two-Dimensional Boronate Ester Covalent Organic Framework Thin Films with Large Single Crystalline Domains for a Neuromorphic Memory Device.

Project description:Despite the recent progress in the synthesis of crystalline boronate ester covalent organic frameworks (BECOFs) in powder and thin-film through solvothermal method and on-solid-surface synthesis, respectively, their applications in electronics, remain less explored due to the challenges in thin-film processability and device integration associated with the control of film thickness, layer orientation, stability and crystallinity. Moreover, although the crystalline domain sizes of the powder samples can reach micrometer scale (up to ?1.5??m), the reported thin-film samples have so far rather small crystalline domains up to 100?nm. Here we demonstrate a general and efficient synthesis of crystalline two-dimensional (2D) BECOF films composed of porphyrin macrocycles and phenyl or naphthyl linkers (named as 2D BECOF-PP or 2D BECOF-PN) by employing a surfactant-monolayer-assisted interfacial synthesis (SMAIS) on the water surface. The achieved 2D BECOF-PP is featured as free-standing thin film with large single-crystalline domains up to ?60??m2 and tunable thickness from 6 to 16?nm. A hybrid memory device composed of 2D BECOF-PP film on silicon nanowire-based field-effect transistor is demonstrated as a bio-inspired system to mimic neuronal synapses, displaying a learning-erasing-forgetting memory process.

| S-EPMC7317805 | biostudies-literature

Room temperature synthesis of covalent-organic framework films through vapor-assisted conversion.

Project description:We describe the facile synthesis of several two-dimensional covalent-organic frameworks (2D COFs) as films by vapor-assisted conversion at room temperature. High-quality films of benzodithiophene-containing BDT-COF and COF-5 with tunable thickness were synthesized under different conditions on various substrates. BDT-COF films of several micrometer thickness exhibit mesoporosity as well as textural porosity, whereas thinner BDT-COF films materialize as a cohesive dense layer. In addition, we studied the formation of COF-5 films with different solvent mixture compositions serving as vapor source. Room temperature vapor-assisted conversion is an excellent method to form COF films of fragile precursors and on sensitive substrates.

| S-EPMC4706366 | biostudies-literature

Mapping Grains, Boundaries, and Defects in 2D Covalent Organic Framework Thin Films.

Project description:To improve their synthesis and ultimately realize the technical promise of two-dimensional covalent organic frameworks (2D COFs), it is imperative that a robust understanding of their structure be developed. However, high-resolution transmission electron microscopy (HR-TEM) imaging of such beam-sensitive materials is an outstanding characterization challenge. Here, we overcome this challenge by leveraging low electron flux imaging conditions and high-speed direct electron counting detectors to acquire high-resolution images of 2D COF films. We developed a Fourier mapping technique to rapidly extract nanoscale structural information from these TEM images. This postprocessing script analyzes the evolution of 2D Fourier transforms across a TEM image, which yields information about polycrystalline domain orientations and enables quantification of average domain sizes. Moreover, this approach provides information about several types of defects present in a film, such as overlapping grains and various types of grain boundaries. We also find that the pre-eminent origin of defects in COF-5 films, a prototypical boronate ester-linked COF, arises as a consequence of broken B-O bonds formed during polymerization. These results suggest that the nanoscale features observed are a direct consequence of chemical phenomena. Taken together, this mapping approach provides information about the fundamental microstructure and crystallographic underpinnings of 2D COF films, which will guide the development of future 2D polymerization strategies and help realize the goal of using 2D COFs in a host of thin-film device architectures.

| S-EPMC8922717 | biostudies-literature

Directional Charge-Carrier Transport in Oriented Benzodithiophene Covalent Organic Framework Thin Films.

Project description:Charge-carrier transport in oriented COF thin films is an important factor for realizing COF-based optoelectronic devices. We describe how highly oriented electron-donating benzodithiophene BDT-COF thin films serve as a model system for a directed charge-transport study. Oriented BDT-COF films were deposited on different electrodes with excellent control over film roughness and topology, allowing for high-quality electrode-COF interfaces suitable for device fabrication. Hole-only devices were constructed to study the columnar hole mobility of the BDT-COF films. The transport measurements reveal a clear dependency of the measured hole mobilities on the BDT-COF film thickness, where thinner films showed about two orders of magnitude higher mobilities than thicker ones. Transport measurements under illumination yielded an order of magnitude higher mobility than in the dark. In-plane electrical conductivity values of up to 5 × 10-7 S cm-1 were obtained for the oriented films. Impedance measurements of the hole-only devices provided further electrical description of the oriented BDT-COF films in terms of capacitance, recombination resistance, and dielectric constant. An exceptionally low dielectric constant value of approximately 1.7 was estimated for the BDT-COF films, a further indication of their highly porous nature. DFT and molecular-dynamics simulations were carried out to gain further insights into the relationships between the COF layer interactions, electronic structure, and the potential device performance.

| S-EPMC6400429 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data