Enhanced Cycling and Rate Capability by Epitaxially Matched Conductive Cubic TiO Coating on LiCoO₂ Cathode Films.

ABSTRACT: Layered lithium transition-metal oxides, such as LiCoO₂ and its doped and lithium-rich analogues, have become the most attractive cathode material for current lithium-ion batteries due to their excellent power and energy densities. However, parasitic reactions at the cathode-electrolyte interface, such as metal-ion dissolution and electrolyte degradation, instigate major safety and performance issues. Although metal oxide coatings can enhance the chemical and structural stability, their insulating nature and lattice mismatch with the adjacent cathode material can act as a physical barrier for ion transport, which increases the charge-transfer resistance across the interface and impedes cell performance at high rates. Here, epitaxial engineering is applied to stabilize a cubic (100)-oriented TiO layer on top of single (104)-oriented LiCoO₂ thin films to study the effect of a conductive coating on the electrochemical performance. Lattice matching between the (104) LiCoO₂ surface facets and the (100) TiO plane enables the formation of the titanium mono-oxide phase, which dramatically enhances the cycling stability as well as the rate capability of LiCoO₂. This cubic TiO coating enhances the preservation of the phase and structural stability across the (104) LiCoO₂ surface. The results suggest a more stable Co³⁺ oxidation state, which not only limits the cobalt-ion dissolution into the electrolyte but also suppresses the catalytic degradation of the liquid electrolyte. Furthermore, the high c-rate performance combined with high Columbic efficiency indicates that interstitial sites in the cubic TiO lattice offer facile pathways for fast lithium-ion transport.

SUBMITTER: Singh DP

PROVIDER: S-EPMC8153391 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Mesoporous TiO2 coating on carbon-sulfur cathode for high capacity Li-sulfur battery.

Project description:In this paper, a meso-porous TiO2 (titania) coating is shown to effectively protect a carbon-sulfur composite cathode from polysulfide dissolution. The cathode consisted of a sulfur impregnated carbon support coated with a few microns thick mesoporous titania layer. The carbon-sulfur cathode is made using activated carbon powder (ACP) derived from biomass. The mesoporous titania coated carbon-sulfur cathodes exhibit a retention capacity after 100 cycles at C/3 rate (433 mA g -1) and stabilized at a capacity around 980 mA h g-1. The electrochemical impedance spectroscopy (EIS) of the sulfur cathodes suggests that the charge transfer resistance at the anode, (R act) is stable for the titania coated sulfur electrode in comparison to a continuous increase in R act for the uncoated electrode implying mitigation of polysulfide shuttling for the protected cathode. Stability in the cyclic voltammetry (CV) data for the first 5 cycles further confirms the polysulfide containment in the titania coated cathode while the uncoated sulfur electrode shows significant irreversibility in the CV with considerable shifting of the voltage peak positions. Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) studies confirm the adsorption of soluble polysulfides by mesoporous titania.

| S-EPMC9079043 | biostudies-literature

Quantifying redox heterogeneity in single-crystalline LiCoO2 cathode particles.

Project description:Active cathode particles are fundamental architectural units for the composite electrode of Li-ion batteries. The microstructure of the particles has a profound impact on their behavior and, consequently, on the cell-level electrochemical performance. LiCoO2 (LCO, a dominant cathode material) is often in the form of well-shaped particles, a few micrometres in size, with good crystallinity. In contrast to secondary particles (an agglomeration of many fine primary grains), which are the other common form of battery particles populated with structural and chemical defects, it is often anticipated that good particle crystallinity leads to superior mechanical robustness and suppressed charge heterogeneity. Yet, sub-particle level charge inhomogeneity in LCO particles has been widely reported in the literature, posing a frontier challenge in this field. Herein, this topic is revisited and it is demonstrated that X-ray absorption spectra on single-crystalline particles with highly anisotropic lattice structures are sensitive to the polarization configuration of the incident X-rays, causing some degree of ambiguity in analyzing the local spectroscopic fingerprint. To tackle this issue, a methodology is developed that extracts the white-line peak energy in the X-ray absorption near-edge structure spectra as a key data attribute for representing the local state of charge in the LCO crystal. This method demonstrates significantly improved accuracy and reveals the mesoscale chemical complexity in LCO particles with better fidelity. In addition to the implications on the importance of particle engineering for LCO cathodes, the method developed herein also has significant impact on spectro-microscopic studies of single-crystalline materials at synchrotron facilities, which is broadly applicable to a wide range of scientific disciplines well beyond battery research.

| S-EPMC7285691 | biostudies-literature

LiNbO3 and LiTaO3 Coating Effects on the Interface of the LiCoO2 Cathode: A DFT Study of Li-Ion Transport.

Project description:In solid-state batteries, the interface between cathodes and solid electrolytes is crucial and coating layers play a vital role. LiNbO3 has been known as a promising coating material, whereas recent studies showed its degradation via releasing oxygen and lithium during cycling. This computational study addresses the elucidation of essential characteristics of the coating materials by examining LiNbO3 and its counterpart LiTaO3 interfaces to a representative layered cathode, LiCoO2. Employing the interface CALYPSO method, we constructed explicit models of both coatings on LiCoO2. Our findings indicate that LiTaO3 offers easier Li+ migration at the interface due to the smaller difference in Li adiabatic potential at the interface, whereas LiNbO3 more effectively suppresses oxygen activity at high delithiation states via lowering the O 2p states. This comparative analysis provides essential insights into optimizing coating materials for improved battery performance.

| S-EPMC11331435 | biostudies-literature

Multi-characterization of LiCoO2 cathode films using advanced AFM-based techniques with high resolution.

Project description:AbstarctThe thin film Li-ion batteries have been extensively used in micro-electronic devices due to their miniaturization, high capacity density and environmental friendliness, etc. In order to further prolong the lifetime of the film batteries, one of important tasks is to explore the aging mechanisms of the cathode films. In this paper, we especially focused on the multi-characterization of the LiCoO2 film in nanoscale, which is carried out by combining advanced AFM-based techniques with capacity measurement. The surface morphology, contact stiffness as well as surface potential were measured by amplitude modulation-frequency modulation (AM-FM) and kelvin probe force microscope (KPFM), respectively. Remarkable changes after different numbers of charge/discharge cycling were observed and the intrinsic reasons of them were discussed in detail. To acknowledge the relationship with these microscopic changes, the macro-capacity of the thin films was also measured by the galvanostatic charge/discharge method. These comprehensive results would provide a deep insight into the fading mechanism of the cathode film, being helpful for the design and selection of the cathode film materials for high performance batteries.

| S-EPMC5603513 | biostudies-literature

Chemical-state distributions in charged LiCoO2 cathode particles visualized by soft X-ray spectromicroscopy.

Project description:Lithium-ion deintercalation/intercalation during charge/discharge processes is one of the essential reactions that occur in the layered cathodes of lithium-ion batteries, and the performance of the cathode can be expressed as the sum of the reactions that occur in the local area of the individual cathode particles. In this study, the spatial distributions of the chemical states present in prototypical layered LiCoO2 cathode particles were determined at different charging conditions using scanning transmission X-ray microscopy (STXM) with a spatial resolution of approximately 100 nm. The Co L3- and O K-edge X-ray absorption spectroscopy (XAS) spectra, extracted from the same area of the corresponding STXM images, at the initial state as well as after charging to 4.5 V demonstrate the spatial distribution of the chemical state changes depending on individual particles. In addition to the Co L3-edge XAS spectra, the O K-edge XAS spectra of the initial and charged LiCoO2 particles are different, indicating that both the Co and O sites participate in charge compensation during the charging process possibly through the hybridization between the Co 3d and O 2p orbitals. Furthermore, the element maps of both the Co and O sites, derived from the STXM stack images, reveal the spatial distribution of the chemical states inside individual particles after charging to 4.5 V. The element mapping analysis suggests that inhomogeneous reactions occur on the active particles and confirm the existence of non-active particles. The results of this study demonstrate that an STXM-based spatially resolved electronic structural analysis method is useful for understanding the charging and discharging of battery materials.

| S-EPMC10030574 | biostudies-literature

Bipolar fluorinated covalent triazine framework cathode with high lithium storage and long cycling capability.

Project description:Organic materials with adjustable structures and wide sources are expected to become potential candidates for commercial cathodes of lithium-ion batteries (LIBs). However, most organic materials have unstable structures, poor conductivity, and are easily soluble in electrolytes, resulting in unsatisfactory lithium storage performance. Covalent-organic frameworks have attracted extensive attention due to their stable frame structures, adjustable pore structures and functionalized official groups. Herein, a fluorinated covalent triazine framework (FCTF) is synthesized by a simple ion-thermal method. Compared with the fluorine-free covalent triazine frameworks (CTFs), the introduction of fluorine improves the lithium storage performance of CTF. When used as a cathode for lithium ion batteries, FCTF can retain a reversible capacity of 125.6 mA h g-1 after 200 cycles at a current density of 100 mA g-1. Besides, it also delivers 106.3 mA h g-1 after 400 cycles at a current density of 200 mA g-1 with 0.03% decrease per cycle (from 40 to 400 cycles).

| S-EPMC9006349 | biostudies-literature

Highly conductive nano-sized Magneli phases titanium oxide (TiOx).

Project description:Despite the strong recent revival of Magnéli phase TiOx as a promising conductive material, synthesis of Magnéli phase TiOx nanoparticles has been a challenge because of the heavy sintering nature of TiO2 at elevated temperatures. We have successfully synthesized chain-structured Magnéli phases TiOx with diameters under 30 nm using a thermal-induced plasma process. The synthesized nanoparticles consisted of a mixture of several Magnéli phases. A post-synthesis heat-treatment was performed to reduce the electrical resistivity without changing the particle morphology. The resistivity of the heat-treated particle was as low as 0.04 Ω.cm, with a specific surface area of 52.9 m2 g-1. The effects of heat-treatment on changes in the crystal structure and their correlation with the electron conductivity are discussed based on transmission electron microscopy images, X-ray diffraction spectra, and X-ray adsorption fine structure spectra. Electrochemical characterization using cyclic voltammetry and potentiodynamic scan shows a remarkable electrochemical stability in a strongly oxidizing environment.

| S-EPMC5473814 | biostudies-literature

Construction of Uniform LiF Coating Layers for Stable High-Voltage LiCoO2 Cathodes in Lithium-Ion Batteries.

Project description:Stabilizing LiCoO2 (LCO) at 4.5 V rather than the common 4.2 V is important for the high specific capacity. In this study, we developed a simple and efficient way to improve the stability of LiCoO2 at high voltages. After a simple sol-gel method, we introduced trifluoroacetic acid (TA) to the surface of LCO via an afterwards calcination. Meanwhile, the TA reacted with residual lithium on the surface of LCO, further leading to the formation of uniform LiF nanoshells. The LiF nanoshells could effectively restrict the interfacial side reaction, hinder the transition metal dissolution and thus achieve a stable cathode-electrolyte interface at high working-voltages. As a result, the LCO@LiF demonstrated a much superior cycling stability with a capacity retention ratio of 83.54% after 100 cycles compared with the bare ones (43.3% for capacity retention), as well as high rate performances. Notably, LiF coating layers endow LCO with excellent high-temperature performances and outstanding full-cell performances. This work provides a simple and effective way to prepare stable LCO materials working at a high voltage.

| S-EPMC10974255 | biostudies-literature

Effect of Low-Temperature Al2O3 ALD Coating on Ni-Rich Layered Oxide Composite Cathode on the Long-Term Cycling Performance of Lithium-Ion Batteries.

Project description:Conformal coating of nm-thick Al2O3 layers on electrode material is an effective strategy for improving the longevity of rechargeable batteries. However, solid understanding of how and why surface coatings work the way they do has yet to be established. In this article, we report on low-temperature atomic layer deposition (ALD) of Al2O3 on practical, ready-to-use composite cathodes of NCM622 (60% Ni), a technologically important material for lithium-ion battery applications. Capacity retention and performance of Al2O3-coated cathodes (≤10 ALD growth cycles) are significantly improved over uncoated NCM622 reference cathodes, even under moderate cycling conditions. Notably, the Al2O3 surface shell is preserved after cycling in full-cell configuration for 1400 cycles as revealed by advanced electron microscopy and elemental mapping. While there are no significant differences in terms of bulk lattice structure and transition-metal leaching among the coated and uncoated NCM622 materials, the surface of the latter is found to be corroded to a much greater extent. In particular, detachment of active material from the secondary particles and side reactions with the electrolyte appear to lower the electrochemical activity, thereby leading to accelerated capacity degradation.

| S-EPMC6441043 | biostudies-literature

High mobility approaching the intrinsic limit in Ta-doped SnO2 films epitaxially grown on TiO2 (001) substrates.

Project description:Achieving high mobility in SnO2, which is a typical wide gap oxide semiconductor, has been pursued extensively for device applications such as field effect transistors, gas sensors, and transparent electrodes. In this study, we investigated the transport properties of lightly Ta-doped SnO2 (Sn1-xTaxO2, TTO) thin films epitaxially grown on TiO2 (001) substrates by pulsed laser deposition. The carrier density (ne) of the TTO films was systematically controlled by x. Optimized TTO (x = 3 × 10-3) films with ne ~ 1 × 1020 cm-3 exhibited a very high Hall mobility (μH) of 130 cm2V-1s-1 at room temperature, which is the highest among SnO2 films thus far reported. The μH value coincided well with the intrinsic limit of μH calculated on the assumption that only phonon and ionized impurities contribute to the carrier scattering. The suppressed grain-boundary scattering might be explained by the reduced density of the {101} crystallographic shear planes.

| S-EPMC7176643 | biostudies-literature