Tailoring the Surface Chemistry of Anion Exchange Membranes with Zwitterions: Toward Antifouling RED Membranes.

ABSTRACT: Fouling is a pressing issue for harvesting salinity gradient energy with reverse electrodialysis (RED). In this work, antifouling membranes were fabricated by surface modification of a commercial anion exchange membrane with zwitterionic layers. Either zwitterionic monomers or zwitterionic brushes were applied on the surface. Zwitterionic monomers were grafted to the surface by deposition of a polydopamine layer followed by an aza-Michael reaction with sulfobetaine. Zwitterionic brushes were grafted on the surface by deposition of polydopamine modified with a surface initiator for subsequent atom transfer radical polymerization to obtain polysulfobetaine. As expected, the zwitterionic layers did increase the membrane hydrophilicity. The antifouling behavior of the membranes in RED was evaluated using artificial river and seawater and sodium dodecylbenzenesulfonate as the model foulant. The zwitterionic monomers are effective in delaying the fouling onset, but the further build-up of the fouling layer is hardly affected, resulting in similar power density losses as for the unmodified membranes. Membranes modified with zwitterionic brushes show a high potential for application in RED as they not only delay the onset of fouling but they also slow down the growth of the fouling layer, thus retaining higher power density outputs.

SUBMITTER: Pintossi D

PROVIDER: S-EPMC8153547 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Maximizing the grafting of zwitterions onto the surface of ultrafiltration membranes to improve antifouling properties.

Project description:Superhydrophilic zwitterions have been extensively exploited for surface modification to improve antifouling properties. However, it remains challenging to form layers of < 20 nm with high zwitterion content on the surfaces with different degrees of hydrophilicity. We demonstrate that amine-functionalized sulfobetaine (SBAm) can be co-deposited with dopamine on ultrafiltration (UF) membranes, leading to a thickness of 10 nm to 50 nm and an SBAm content of up to 31 mass% in the coating layers. The covalently grafted SBAm is stable underwater and improves the antifouling properties, as evidenced by the lower trans-membrane pressure required to retain targeted water fluxes than that required for the pristine membranes. The SBAm is also more effective than conventionally used sulfobetaine methacrylate (SBMA) for the zwitterion grafting on the surface to improve antifouling properties.

| S-EPMC7539668 | biostudies-literature

In Situ Ag-MOF Growth on Pre-Grafted Zwitterions Imparts Outstanding Antifouling Properties to Forward Osmosis Membranes.

Project description:In this study, a polyamide forward osmosis membrane was functionalized with zwitterions followed by the in situ growth of metal-organic frameworks with silver as a metal core (Ag-MOFs) to improve its antibacterial and antifouling activity. First, 3-bromopropionic acid was grafted onto the membrane surface after its activation with N,N-diethylethylenediamine. Then, the in situ growth of Ag-MOFs was achieved by a simple membrane immersion sequentially in a silver nitrate solution and in a ligand solution (2-methylimidazole), exploiting the underlying zwitterions as binding sites for the metal. The successful membrane functionalization and the enhanced surface wettability were verified through an array of characterization techniques. When evaluated in forward osmosis tests, the modified membranes exhibited high performance and improved permeability compared to pristine membranes. Static antibacterial experiments, evaluated by confocal microscopy and colony-forming unit plate count, resulted in a 77% increase in the bacterial inhibition rate due to the activity of the Ag-MOFs. Microscopy micrographs of the Escherichia coli bacteria suggested the deterioration of the biological cells. The antifouling properties of the functionalized membranes translated into a significantly lower flux decline in forward osmosis filtrations. These modified surfaces displayed negligible depletion of silver ions over 30 days, confirming the stable immobilization of Ag-MOFs on their surface.

| S-EPMC8009475 | biostudies-literature

Antifouling Electrospun Nanofiber Mats Functionalized with Polymer Zwitterions.

Project description:In this study, we exploit the excellent fouling resistance of polymer zwitterions and present electrospun nanofiber mats surface functionalized with poly(2-methacryloyloxyethyl phosphorylcholine) (polyMPC). This zwitterionic polymer coating maximizes the accessibility of the zwitterion to effectively limit biofouling on nanofiber membranes. Two facile, scalable methods yielded a coating on cellulose nanofibers: (i) a two-step sequential deposition featuring dopamine polymerization followed by the physioadsorption of polyMPC, and (ii) a one-step codeposition of polydopamine (PDA) with polyMPC. While the sequential and codeposited nanofiber mat assemblies have an equivalent average fiber diameter, hydrophilic contact angle, surface chemistry, and stability, the topography of nanofibers prepared by codeposition were smoother. Protein and microbial antifouling performance of the zwitterion modified nanofiber mats along with two controls, cellulose (unmodified) and PDA coated nanofiber mats were evaluated by dynamic protein fouling and prolonged bacterial exposure. Following 21 days of exposure to bovine serum albumin, the sequential nanofiber mats significantly resisted protein fouling, as indicated by their 95% flux recovery ratio in a water flux experiment, a 300% improvement over the cellulose nanofiber mats. When challenged with two model microbes Escherichia coli and Staphylococcus aureus for 24 h, both zwitterion modifications demonstrated superior fouling resistance by statistically reducing microbial attachment over the two controls. This study demonstrates that, by decorating the surfaces of chemically and mechanically robust cellulose nanofiber mats with polyMPC, we can generate high performance, free-standing nanofiber mats that hold potential in applications where antifouling materials are imperative, such as tissue engineering scaffolds and water purification technologies.

| S-EPMC5382136 | biostudies-literature

Surface Antifouling Modification on Polyethylene Filtration Membranes by Plasma Polymerization.

Project description:Surface modification on microporous polyethylene (PE) membranes was facilitated by plasma polymerizing with two hydrophilic precursors: ethylene oxide vinyl ether (EO1V) and diethylene oxide vinyl ether (EO2V) to effectively improve the fouling against mammalian cells (Chinese hamster ovary, CHO cells) and proteins (bovine serum albumin, BSA). The plasma polymerization procedure incorporated uniform and pin-hole free ethylene oxide-containing moieties on the filtration membrane in a dry single-step process. The successful deposition of the plasma polymers was verified by Fourier-transform infrared (FTIR), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) analyses. Water contact angle measurements and permeation experiments using cell and protein solutions were conducted to evaluate the change in hydrophilicity and fouling resistance for filtrating biomolecules. The EO1V and EO2V plasma deposited PE membranes showed about 1.45 fold higher filtration performance than the pristine membrane. Moreover, the flux recovery reached 80% and 90% by using deionized (DI) water and sodium hydroxide (NaOH) solution, indicating the efficacy of the modification and the good reusability of the modified PE membranes.

| S-EPMC7664414 | biostudies-literature

Electrospun Weak Anion-exchange Fibrous Membranes for Protein Purification.

Project description:Membrane based ion-exchange (IEX) and hydrophobic interaction chromatography (HIC) for protein purification is often used to remove impurities and aggregates operated under the flow-through mode. IEX and HIC are also limited by capacity and recovery when operated under bind-and-elute mode for the fractionation of proteins. Electrospun nanofibrous membrane is characterized by its high surface area to volume ratio and high permeability. Here tertiary amine ligands are grafted onto the electrospun polysulfone (PSf) and polyacrylonitrile (PAN) membrane substrates using UV-initiated polymerization. Static and dynamic binding capacities for model protein bovine serum albumin (BSA) were determined under appropriate bind and elute buffer conditions. Static and dynamic binding capacities in the order of ~100 mg/mL were obtained for the functionalized electrospun PAN membranes whereas these values reached ~200 mg/mL for the functionalized electrospun PSf membranes. Protein recovery of over 96% was obtained for PAN-based membranes. However, it is only 56% for PSf-based membranes. Our work indicates that surface modification of electrospun membranes by grafting polymeric ligands can enhance protein adsorption due to increased surface area-to-volume ratio.

| S-EPMC7143834 | biostudies-literature

Nitrate-Selective Anion Exchange Membranes Prepared using Discarded Reverse Osmosis Membranes as Support.

Project description:The present work shows a methodology for the preparation of membranes with a high affinity for nitrates. For this purpose, a polymeric mixture containing an anion exchange resin was extended on a recycled pressure filtration membrane used as mechanical support. Different ion exchange resins were tested. The influence in ion fractionation of (i) the type of ion exchange resin, (ii) the use of a recycled membrane as support and (iii) the operating current density during the separation process were studied. Results revealed that the employed anion exchange resin could tune up the transport numbers of the anions in the membrane and enhance the transport of nitrates over sulfates. The use of the recycled filtration membrane as support further increased the transport of nitrates in detriment of sulfates in nitrate-selective membranes. Moreover, it considerably improved the mechanical stability of the membranes. Lowering the operational current density also boosted ion fractionation. In addition, the use of recycled membranes as support in membrane preparation is presented as an alternative management route of discarded reverse osmosis membranes, coupling with the challenging management of waste generated by the desalination industry. These membranes could be used for nitrate recovery from wastewater or for nitrate separation from groundwater.

| S-EPMC7760365 | biostudies-literature

Mimicking the cell membrane: bio-inspired simultaneous functions with monovalent anion selectivity and antifouling properties of anion exchange membrane.

Project description:A new bio-inspired method was applied in this study to simultaneously improve the monovalent anion selectivity and antifouling properties of anion exchange membranes (AEMs). Three-layer architecture was developed by deposition of polydopamine (PDA) and electro-deposition of N-O-sulfonic acid benzyl chitosan (NSBC). The innermost and outermost layers were PDA with different deposition time. The middle layer was prepared by NSBC. Fourier transform infrared spectroscopy and scanning electron microscopy confirmed that PDA and NSBC were successfully modified on the surfaces of AEMs. The contact angle of the membranes indicated an improved hydrophilicity of the modified membranes. A series of electrodialysis experiments in which Cl-/SO42- separation was studied, demonstrating the monovalent anion selectivity of the samples. The Cl-/SO42- permselectivity of the modified membranes can reach up to 2.20, higher than that of the commercial membrane (only 0.78) during 90?minutes in electrodialysis (ED). The increase value of the resistance of the membranes was also measured to evaluate the antifouling properties. Sodium dodecyl benzene sulfonate (SDBS) was used as the fouling material in the ED process and the membrane area resistance of modified membrane increase value of was only 0.08??cm2 30?minutes later.

| S-EPMC5112527 | biostudies-literature

A Novel Methodology to Synthesize Highly Conductive Anion Exchange Membranes.

Project description:Alkaline polyelectrolyte fuel cell now receives growing attention as a promising candidate to serve as the next generation energy-generating device by enabling the use of non-precious metal catalysts (silver, cobalt, nickel et al.). However, the development and application of alkaline polyelectrolyte fuel cell is still blocked by the poor hydroxide conductivity of anion exchange membranes. In order to solve this problem, we demonstrate a methodology for the preparation of highly OH(-) conductive anion exchange polyelectrolytes with good alkaline tolerance and excellent dimensional stability. Polymer backbones were grafted with flexible aliphatic chains containing two or three quaternized ammonium groups. The highly flexible and hydrophilic multi-functionalized side chains prefer to aggregate together to facilitate the formation of well-defined hydrophilic-hydrophobic microphase separation, which is crucial for the superior OH(-) conductivity of 69 mS/cm at room temperature. Besides, the as-prepared AEMs also exhibit excellent alkaline tolerance as well as improved dimensional stability due to their carefully designed polymer architecture, which provide new directions to pursue high performance AEMs and are promising to serve as a candidate for fuel cell technology.

| S-EPMC4550832 | biostudies-literature

Natural Product Inspired Environmentally Friendly Strategy Based on Dopamine Chemistry toward Sustainable Marine Antifouling.

Project description:The combination of natural active antifouling composition and intelligent coatings has been regarded as a prospective approach to avoid marine biofouling. However, the relatively complex coating structure and the excessive rapid release of antifoulants maintain unresolved issues in their practical application. In this work, a novel environmentally friendly natural antifoulant (Stellera chamaejasme, SC) encapsulated in the polydopamine (PDA) microcapsule (SC@PDA) is prepared by emulsion interfacial polymerization and blended with the acrylate polymer to prepare a sustainable antifouling coating. Herein, the PDA shell acting as an "intelligent capsule" ensures the controlled release of the antifoulant SC, and the corresponding SC loading amount could be high up to 75.40%. As a model antifoulant, the impact of SC on the adsorption activity of the protein bovine serum albumin (BSA) is studied, as well as the settlement of presentative fouling communities (diatom Navicula sp. and red algae Porphyridium sp.) on the constructed coating. The experimental results demonstrate that the natural product SC integrated eco-friendly antifouling coating occupies the superior capacity of impeding the adsorption of both protein BSA and algae. Such antifoulant (SC) integrating with controlled release character is a great advance in terms of marine antifouling applications. It is, therefore, expected that this innovation will provide guiding significance for developing the next generation of antifouling techniques, especially in the field of marine antifouling.

| S-EPMC7469372 | biostudies-literature

Performances of Anion-Exchange Blend Membranes on Vanadium Redox Flow Batteries.

Project description:Anion exchange blend membranes (AEBMs) were prepared for use in Vanadium Redox Flow Batteries (VRFBs). These AEBMs consisted of 3 polymer components. Firstly, PBI-OO (nonfluorinated PBI) or F6-PBI (partially fluorinated PBI) were used as a matrix polymer. The second polymer, a bromomethylated PPO, was quaternized with 1,2,4,5-tetramethylimidazole (TMIm) which provided the anion exchange sites. Thirdly, a partially fluorinated polyether or a non-fluorinated poly (ether sulfone) was used as an ionical cross-linker. While the AEBMs were prepared with different combinations of the blend polymers, the same weight ratios of the three components were used. The AEBMs showed similar membrane properties such as ion exchange capacity, dimensional stability and thermal stability. For the VRFB application, comparable or better energy efficiencies were obtained when using the AEBMs compared to the commercial membranes included in this study, that is, Nafion (cation exchange membrane) and FAP 450 (anion exchange membrane). One of the blend membranes showed no capacity decay during a charge-discharge cycles test for 550 cycles run at 40 mA/cm² indicating superior performance compared to the commercial membranes tested.

| S-EPMC6410199 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data